CN110093127A - A kind of mating polyethylene hot-melt adhesive of Pipeline joint anticorrosion shrink belt - Google Patents
A kind of mating polyethylene hot-melt adhesive of Pipeline joint anticorrosion shrink belt Download PDFInfo
- Publication number
- CN110093127A CN110093127A CN201910342914.9A CN201910342914A CN110093127A CN 110093127 A CN110093127 A CN 110093127A CN 201910342914 A CN201910342914 A CN 201910342914A CN 110093127 A CN110093127 A CN 110093127A
- Authority
- CN
- China
- Prior art keywords
- polyethylene
- melt adhesive
- mating
- pipeline joint
- hot
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of mating polyethylene hot-melt adhesives of Pipeline joint anticorrosion shrink belt, are made by matrix resin component and graft component by melting graft reaction;Matrix resin component includes polyethylene, ethylene-octene copolymer, tackifying resin;Graft component includes maleic anhydride, cumyl peroxide, four [β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol esters, three [2,4- di-tert-butyl-phenyl] phosphite esters.Polyethylene hot-melt adhesive of the invention is used for Pipeline joint anticorrosion, and cementability and preserving and sealing are excellent, softening point is high, high temperature resistance is good, shear strength and peel strength with higher, performance stabilization;Polyethylene hot-melt adhesive of the invention can reach 0.61MPa in 100 DEG C of shear strengths, peel strength can reach 22N/cm, the requirement run under the conditions of can satisfy long-term 100 DEG C of pipeline, the pipeline corrosion protection effect in the area high to environment temperature is fairly obvious, fills up the blank of related repaired mouth hot melt adhesive product both at home and abroad.
Description
Technical field
The present invention relates to shrink belt field more particularly to a kind of mating polyethylene heat of Pipeline joint anticorrosion shrink belt
Melten gel.
Background technique
Three-layer polyethylene (3PE) corrosion-inhibiting coating belongs to multilayer coating system, by bottom epoxy powder, middle layer bonding agent and
Outer layer PE (polyethylene) is constituted.Conventional 3PE repaired mouth pyrocondensation belt can achieve 80 DEG C with the general heatproof of hot melt adhesive, and polyethylene is mended
Mouth pyrocondensation belt is more significant with polyethylene hot-melt adhesive heatproof odds ratio, can achieve 110 DEG C.Many petroleum resources country ground abundant
Such as Iraq, the Sudan etc., environmental condition is more severe in area, and common hot melt glue type repaire belt is due to the lower coating temperature of sunshine
Raising causes coating machinery reduced performance, is not able to satisfy the requirement in these areas, and polyethylene repaire belt is using temperature
On advantage, enable it to meet the application in above-mentioned area.But the heat resistance of polyethylene repaire belt also needs at present
It improves.Polyethylene hot-melt adhesive is the key components of polyethylene shrink belt, and performance directly decides polyethylene heat
The performance of shrinkage band.
Summary of the invention
The present invention overcomes the deficiencies in the prior art, provide a kind of 3PE Pipeline joint anticorrosion heat receipts that temperature resistant grade is high
Contracting fills up the blank of domestic and international related fields with mating high-performance polyethylene hot melt adhesive material.
In order to achieve the above objectives, the technical solution adopted by the present invention are as follows: provide a kind of Pipeline joint anticorrosion thermal contraction
With mating polyethylene hot-melt adhesive, it is characterised in that: be made by matrix resin component and graft component by melting graft reaction;Institute
Stating matrix resin component includes polyethylene, ethylene-octene copolymer, tackifying resin;The graft component includes maleic anhydride, mistake
Aoxidize diisopropylbenzene (DIPB), four [β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol esters, three [2,4- di-tert-butyls
Base] phosphite ester;The mass ratio of described matrix resin Composition and graft component are as follows: 100:0.7-100:1.5.
As a preferred embodiment, described matrix resin Composition is by polyethylene 60-75wt%, ethylene-octene copolymer 20-
35wt%, tackifying resin 2-5wt% composition;The graft component is by maleic anhydride 50-60wt%, cumyl peroxide 15-
20wt%, four [β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester 15-20wt %, three [2.4- di-t-butyls
Phenyl] phosphite ester 10-15wt% composition.
As a preferred embodiment, the polyethylene is linear low density polyethylene, one kind of low density polyethylene (LDPE) or two
Kind.
As a kind of more preferable scheme, the polyethylene melt index is 5-10g/ under conditions of 190 DEG C, 2.16kg
10min。
As a preferred embodiment, the ethylene-octene copolymer melt index is under conditions of 190 DEG C, 2.16kg
5-15g/10min。
As a preferred embodiment, the tackifying resin ring and ball softening point is 100-120 DEG C.
As a preferred embodiment, by described matrix resin Composition and graft component, fusion-grafting is anti-at 155-170 DEG C
It after answering 2min, is squeezed out by double screw extruder, granulation is made.
The beneficial technical effect of the present invention lies in: polyethylene hot-melt adhesive of the invention is used for Pipeline joint anticorrosion,
Cementability and preserving and sealing are excellent, softening point is high, high temperature resistance is good, shear strength and peel strength with higher, property
It can stablize;Polyethylene hot-melt adhesive of the invention can reach 0.61MPa in 100 DEG C of shear strengths, and peel strength can reach 22N/cm,
The pipeline corrosion protection effect ten of the requirement run under the conditions of can satisfy long-term 100 DEG C of pipeline, the area high to environment temperature is clearly demarcated
It is aobvious, fill up the blank of related repaired mouth hot melt adhesive product both at home and abroad.
Specific embodiment
The invention will be further described combined with specific embodiments below.Following embodiment is only used for clearly illustrating
Technical solution of the present invention, and not intended to limit the protection scope of the present invention.
Embodiment 1
A kind of mating polyethylene hot-melt adhesive of Pipeline joint anticorrosion shrink belt: by matrix resin component and graft component 155
It at DEG C after melting graft reaction 2min, is squeezed out by double screw extruder, granulation is made.
Matrix resin is by linear low density polyethylene polyethylene 33.5wt%, low density polyethylene (LDPE) 26.5wt%, ethylene-octene
Copolymer 35wt%, tackifying resin 5wt% composition.
Wherein linear low density polyethylene polyethylene and low density polyethylene (LDPE) play improve hot melt adhesive heat resistance and provide and
The effect of the bonding force of polyethylene, the melt index (190 DEG C, 2.16kg) of mixture are 5g/10min.Ethylene-octene copolymerization
Object plays the role of increasing toughness and trickling property, while improving the bonding force with polar material;Its melt index (190 DEG C,
It 2.16kg) is 10g/10min.Tackifying resin plays the role of increasing adhesive adhesive property;Its ring and ball softening point is 120 DEG C.
Graft component is by maleic anhydride 59.3wt%, cumyl peroxide 11.1wt%, four [β-(3,5- di-t-butyl -4-
Hydroxy phenyl) propionic acid] pentaerythritol ester 18.5wt%, three [2,4- di-tert-butyl-phenyl] phosphite ester 11.1wt%.
Wherein maleic anhydride is grafted monomers, can improve the compatibility of matrix resin and the bonding force to polar material.It crosses
Aoxidizing diisopropylbenzene (DIPB) is crosslinking agent, improves grafting rate of the maleic anhydride on matrix resin.
Four [β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol esters, three [2,4- di-tert-butyl-phenyls] are sub-
Phosphate is antioxidant, plays the role of slowing down material aging;Four [β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid]
Pentaerythritol ester is Hinered phenols antioxidant, as primary antioxidant;Three [2,4- di-tert-butyl-phenyl] phosphite esters are phosphorous acid
Esters antioxygen, as secondary antioxidant.
The mass ratio of matrix resin component and graft component are as follows: 100:1.5.
1 polyethylene hot-melt adhesive the performance test results of table
Project | Test temperature | Unit | Test result | Standard requirements |
Room temperature lap shear strength | 23℃ | MPa | 5.5 | ≥5 |
High temperature lap shears intensity | 100℃ | MPa | 0.61 | ≥0.5 |
Softening point (ring and ball method) | —— | ℃ | 177 | ≥150 |
Room temperature peel strength | 23℃ | N/cm | 54 | ≥40 |
High temperature peel strength | 100℃ | N/cm | 22 | ≥20 |
Embodiment 2
A kind of mating polyethylene hot-melt adhesive of Pipeline joint anticorrosion shrink belt: by matrix resin component and graft component 170
It at DEG C after melting graft reaction 2min, is squeezed out by double screw extruder, granulation is made.
Matrix resin is by linear low density polyethylene polyethylene 35wt%, low density polyethylene (LDPE) 40wt%, ethylene-octene copolymerization
Object 20wt%, tackifying resin 5wt% composition.
Wherein the mixture of linear low density polyethylene polyethylene and low density polyethylene (LDPE) melt index (190 DEG C,
It 2.16kg) is 10g/10min;The melt index (190 DEG C, 2.16kg) of ethylene-octene copolymer is 5g/10min;Tackifying resin
Ring and ball softening point be 100 DEG C.
Graft component is by maleic anhydride 60wt%, cumyl peroxide 15wt%, four [β-(3,5- di-t-butyl -4- hydroxyls
Phenyl) propionic acid] pentaerythritol ester 15wt%, three [2,4- di-tert-butyl-phenyl] phosphite ester 10wt% composition.
The mass ratio of matrix resin component and graft component are as follows: 100:0.7.
The above components are played the role of with embodiment 1.
2 polyethylene hot-melt adhesive the performance test results of table
Project | Test temperature | Unit | Test result | Standard requirements |
Room temperature lap shear strength | 23℃ | MPa | 6.3 | ≥5 |
High temperature lap shears intensity | 100℃ | MPa | 0.73 | ≥0.5 |
Softening point (ring and ball method) | —— | ℃ | 185 | ≥150 |
Room temperature peel strength | 23℃ | N/cm | 45 | ≥40 |
High temperature peel strength | 100℃ | N/cm | 31 | ≥20 |
Embodiment 3
A kind of mating polyethylene hot-melt adhesive of Pipeline joint anticorrosion shrink belt: by matrix resin component and graft component 165
It at DEG C after melting graft reaction 2min, is squeezed out by double screw extruder, granulation is made.
Matrix resin is by linear low density polyethylene polyethylene 35wt%, low density polyethylene (LDPE) 35wt%, ethylene-octene copolymerization
Object 28wt%, tackifying resin 2wt% composition.
Wherein the mixture of linear low density polyethylene polyethylene and low density polyethylene (LDPE) melt index (190 DEG C,
It 2.16kg) is 8g/10min;The melt index (190 DEG C, 2.16kg) of ethylene-octene copolymer is 15g/10min;Tackifying resin
Ring and ball softening point be 100 DEG C.
Graft component is by maleic anhydride 50wt%, cumyl peroxide 19.5wt%, four [β-(3,5- di-t-butyl -4- hydroxyls
Base phenyl) propionic acid] pentaerythritol ester 15.5wt%, three [2,4- di-tert-butyl-phenyl] phosphite ester 15wt% composition.
The mass ratio of matrix resin component and graft component are as follows: 100:1.0.
The above components are played the role of with embodiment 1.
3 polyethylene hot-melt adhesive the performance test results of table
Project | Test temperature | Unit | Test result | Standard requirements |
Room temperature lap shear strength | 23℃ | MPa | 5.8 | ≥5 |
High temperature lap shears intensity | 100℃ | MPa | 0.64 | ≥0.5 |
Softening point (ring and ball method) | —— | ℃ | 168 | ≥150 |
Room temperature peel strength | 23℃ | N/cm | 51 | ≥40 |
High temperature peel strength | 100℃ | N/cm | 33 | ≥20 |
The present invention is through test of many times, and the polyethylene hot-melt adhesive high temperature resistance is superior, high temperature bonding intensity is high, shear at high temperature intensity
Greatly, good airproof performance, it can be ensured that the quality of pipeline anticorrosion coating and joint coating on pipeline.
Based on the above description of the preferred embodiments of the present invention, through the above description, related personnel completely can be with
Without departing from the scope of the technological thought of the present invention', various changes and amendments are carried out.The technical scope of this invention
It is not limited to the contents of the specification, it is necessary to determine the technical scope according to the scope of the claims.
Claims (7)
1. a kind of mating polyethylene hot-melt adhesive of Pipeline joint anticorrosion shrink belt, it is characterised in that: by matrix resin component with
Graft component is made by melting graft reaction;Described matrix resin Composition includes polyethylene, ethylene-octene copolymer, thickening
Resin;The graft component includes maleic anhydride, cumyl peroxide, four [β-(3,5- di-tert-butyl-hydroxy phenyl) third
Acid] pentaerythritol ester, three [2,4- di-tert-butyl-phenyl] phosphite esters;The mass ratio of described matrix resin Composition and graft component
Are as follows: 100:0.7-100:1.5.
2. the mating polyethylene hot-melt adhesive of Pipeline joint anticorrosion shrink belt according to claim 1, it is characterised in that:
Described matrix resin Composition is made of polyethylene 60-75wt%, ethylene-octene copolymer 20-35wt%, tackifying resin 2-5wt%;
The graft component is by maleic anhydride 50-60wt%, cumyl peroxide 15-20wt%, four [β-(3,5- di-t-butyl -4- hydroxyls
Base phenyl) propionic acid] pentaerythritol ester 15-20wt %, three [2.4- di-tert-butyl-phenyl] phosphite ester 10-15wt% composition.
3. the mating polyethylene hot-melt adhesive of Pipeline joint anticorrosion shrink belt according to claim 1 or 2, feature exist
In: the polyethylene is linear low density polyethylene, the one or two of low density polyethylene (LDPE).
4. the mating polyethylene hot-melt adhesive of Pipeline joint anticorrosion shrink belt according to claim 3, it is characterised in that: institute
It is 5-10g/10min that polyethylene melt index, which is stated, under conditions of 190 DEG C, 2.16kg.
5. the mating polyethylene hot-melt adhesive of Pipeline joint anticorrosion shrink belt according to claim 1 or 2, feature exist
In: the ethylene-octene copolymer melt index is 5-15g/10min under conditions of 190 DEG C, 2.16kg.
6. the mating polyethylene hot-melt adhesive of Pipeline joint anticorrosion shrink belt according to claim 1 or 2, feature exist
In: the tackifying resin ring and ball softening point is 100-120 DEG C.
7. the mating polyethylene hot-melt adhesive of Pipeline joint anticorrosion shrink belt according to claim 1 or 2, feature exist
In: after melting graft reaction 2min, pass through twin-screw extrusion at 155-170 DEG C by described matrix resin Composition and graft component
Machine squeezes out, is granulated and is made.