CN110079890A - A kind of bicomponent composite fibre and preparation method thereof - Google Patents
A kind of bicomponent composite fibre and preparation method thereof Download PDFInfo
- Publication number
- CN110079890A CN110079890A CN201910345219.8A CN201910345219A CN110079890A CN 110079890 A CN110079890 A CN 110079890A CN 201910345219 A CN201910345219 A CN 201910345219A CN 110079890 A CN110079890 A CN 110079890A
- Authority
- CN
- China
- Prior art keywords
- cortex
- composite fibre
- sandwich layer
- bicomponent composite
- fibre according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of fibres in differentiation, to solve current traditional stains method, there are coloured materials to fall off from fiber in use, migrates, situations such as to cause staining, discoloration, pollution, damage health, the invention proposes a kind of bicomponent composite fibres and preparation method thereof, are made with the sandwich layer containing functional material through two-component composite spinning by cortex.Efficiently solving the problems, such as colored fibre, coloured material falls off and fades in use, and preparation method is simple.
Description
Technical field
The present invention relates to a kind of fibres in differentiation, and in particular to a kind of bicomponent composite fibre and preparation method thereof.
Background technique
There are many multiplicity for the coloring mode of fiber.From processing method, there are original liquid coloring and dyeing two ways.Stoste
Coloring is that coloured material is added during the spinning process, and coloured material is evenly distributed in entire matrix.Dyeing is then rear
Coloured material is added on fiber by special process in road, different dyestuffs and fiber have different coloring process.For example divide
Scattered dyestuff is entered using the gap of fiber;Reactive dye are that anti-life is reacted with the hydroxyl on cellulose fibre;Acid dyes is then
It is in conjunction with carrying out ionic bond with the amino on wool, nylon.These above-mentioned coloring modes, either original liquid coloring or rear road
Coloring, all inevitably will appear coloring material and falls off, migrates from fiber in use, to cause staining, discoloration, dirt
Situations such as dye, damage health.
Summary of the invention
To solve current traditional stains method, there are coloured materials to fall off from fiber in use, migrates, thus
Situations such as causing staining, discoloration, pollution, damage health, the invention proposes a kind of bicomponent composite fibre and preparation method thereof,
Efficiently solving the problems, such as colored fibre, coloured material falls off and fades in use, and preparation method is simple.
The present invention is achieved by the following technical solutions: a kind of bicomponent composite fibre section is skin-core structure, by skin
Layer is made with the sandwich layer containing functional material through two-component composite spinning.
The mass ratio of the cortex and sandwich layer is 15-30:70-85.Coloured material is present in sandwich layer, skin quality accounting
Cannot be too high, otherwise color can not penetrate cortex, be unfavorable for sandwich layer colour developing.
The sandwich layer is mixed by functional material and core material.The functional material includes coloured material, also
Including matte powder, magnetic powder.
Sandwich layer is only added in functional material, and coloured material is not added in cortex, plays closing package action, prevents coloring material from escaping.
A kind of bicomponent composite fibre, coloured material are confined to sandwich layer, and there is no migration, cortex is free of coloring material.It should
Coloured composite fibre can be effectively prevented coloring material and escape in use, to improve the color fastness of colored fibre and make
With safety.
Core material include polyester, modified poly ester, polypropylene, modified polypropene, polyamide, modified polyamide, polyethylene,
Modified poly ethylene.
The coloured material, including inorganic pigment and organic dyestuff.Since organic dye molecule is easy migration, dissolution,
It is added to and is more easier to escape in fiber, preferably, coloured material is selected from inorganic pigment.
Cortex includes polyester, modified poly ester, polypropylene, modified polypropene, polyamide, modified polyamide, polyethylene, modification
Polyethylene, and coloring material is zero.
In preparation process, if cortex contains a small amount of matte powder, although can also develop the color, color can become dim.Make
To be preferred, the cortical material is to have light transparent materials, and wherein delustring powder content is zero.It is more conducive to color transmission in this way
Cortex.
In preparation process, if cortex and sandwich layer use compatible material, although during the spinning process, coloring material may be sent out
Raw migration, but to improving the color fastness of fiber, and have and greatly improve, preferably, the cortical material and sandwich layer material
Material be it is mutual exclusive, before being beneficial to prevent in spinning process strand solidification in this way, coloured material moves to cortex from sandwich layer.
A kind of preparation method of bicomponent composite fibre is following steps:
(1) coloring material and core material are mixed and made into sandwich layer;
(2) bicomponent composite fibre is prepared using core/sheath bicomponent composite spinning technology in sandwich layer and cortex.
Cortex and sandwich layer are melted by screw rod specifically, then melted the spinning of two kinds of different chemical compositions by metering pump
Body, is delivered to filament spinning component, while the distribution system and spinneret of skin-core structure can be prepared by one, enter spinneret orifice it
Before, two kinds of ingredients are separated from each other, and are not mixed mutually, and in the moment for entering spinneret orifice, two kinds of melt contacts simultaneously spray, and then solidification is viscous
Piece strand with skin-core structure of synthesis.
During the spinning process, by controlling the spinning temperature of sandwich layer and cortex, melt viscosity and melt are adjusted from spinneret orifice
After ejection, cooling wind temperature, humidity, wind speed etc. are adjusted, coloured material is beneficial to prevent and migrates from sandwich layer to cortex.
The bicomponent composite fibre can be processed into short fibre, drafting silk, preoriented yarn by different manufacturing procedures,
Preoriented yarn can be further processed into stretch textured yarn.
Compared with prior art, the beneficial effects of the present invention are: the bicomponent composite fibre effectively prevent coloring material
Material escapes in use, to improve the color fastness of colored fibre and using safe.
Specific embodiment
Below by embodiment, invention is further described in detail, raw materials used commercially available in embodiment or use
Conventional method preparation.
Embodiment 1
A kind of compound short fibre of bi-component, cortical material are the polypropylene (trade mark Z30S) without matte powder, and core material is
Normal polyester (PET) (perseverance ease produce), carbon black (accounting for sandwich layer mass ratio 3%) is added in core material and is mixed, cortex and sandwich layer
Quality accounting is 1:4, cortex is incompatible with sandwich layer medium.This is compound short fine using core-skin type two-component composite spinning equipment, warp
After melting, being cooling, into pre-stretching machine pre-stretching, then tow enters barrel cluster progress anxiety, relaxation heat setting, then through cutting off
Packing prepares the compound short fibre of black two-component.
Specific preparation process are as follows: cortex spinning temperature is 260 ~ 270 DEG C, 283 ~ 290 DEG C of sandwich layer spinning temperature, cools down wind speed
For 1.5 ~ 2.9m/min, spinning speed is 850 ~ 1250m/min, and draft temperature is 50 ~ 60 DEG C, nervous heat setting temperature 100 ~
115 DEG C, 70 ~ 80 DEG C of relaxation heat setting temperature.
By doing fiber cross section slice, cortex be it is transparent, carbon black does not migrate to cortex, and fiber color is black, and normal
Black silk is advised to be no different.The coloured compound short fibre can be effectively prevented coloring material and escape in use, to improve coloured fibre
The color fastness of dimension and use are safe.
The short fibre of black prepared by embodiment 1, fastness to washing reach 5 grades.
Embodiment 2
A kind of blue bi-component composite drafting silk (FDY), cortex are to have light polyamide 6 (perseverance ease produces), and core material is conventional
Polyester (PET) (perseverance ease produce), blue master batch (accounting for sandwich layer mass ratio 1%) are added to sandwich layer, and the mass ratio of cortex and sandwich layer is 3:7,
Cortex is incompatible with sandwich layer medium.The composite drafting silk uses core-skin type two-component composite spinning technology, after being melted, being cooled down,
Drawing and heat-setting is carried out again, and winding is prepared.
Specific preparation process are as follows: cortex spinning temperature is 263 ~ 272 DEG C, 283 ~ 290 DEG C of sandwich layer spinning temperature, cools down wind speed
For 0.3 ~ 0.5m/min, spinning speed is 3900 ~ 4500m/min, and drawing temperature is 70 ~ 80 DEG C, heat setting temperature 110 ~ 120
℃。
By doing fiber cross section slice, cortex be it is transparent, blue pigment does not migrate to cortex, and fiber color is blue,
It is no different with conventional blue silk.It is outer in use that coloring material can be effectively prevented in the blue bi-component composite drafting silk (FDY)
Ease, to improve the color fastness of colored fibre and using safe.
Blue drafting silk prepared by embodiment 2, fastness to washing reach 5 grades.
Embodiment 3
It is a kind of red bi-component composit false twisting textured filament (DTY), cortical material be have light low-melting point polyester (230 DEG C of fusing point, newly
Raw customization), core material is conventional semi-gloss polyamide 6 (perseverance ease produces), and red master batch (accounting for sandwich layer mass ratio 2%) is added to sandwich layer
It is mixed and made into sandwich layer in material, the mass ratio of cortex and sandwich layer is 18:72, and cortex is incompatible with sandwich layer medium.The false twist texturing
Silk uses core-skin type two-component composite spinning technology, is melted, is cooled down, and winds, is prepared into preoriented yarn (POY), then right again
POY carries out false twist texturing processing, finally obtains red bi-component composit false twisting textured filament (DTY).
Specific preparation process are as follows:
1) spinning technique: cortex spinning temperature is 260 ~ 270 DEG C, 263 ~ 272 DEG C of sandwich layer spinning temperature, cooling wind speed is 0.3 ~
0.5m/min, spinning speed 3500m/min.
2) false twisting process: speed 500m/min, 150 DEG C of false twisting temperature, speed ratio 1.6, draw ratio 1.25.
By doing fiber cross section slice, cortex be it is transparent, red pigment does not migrate to cortex, and fiber color is red,
It is no different with conventional red silk.Coloring material can be effectively prevented in use process in the red bi-component composit false twisting textured filament (DTY)
In escape, to improve the color fastness of colored fibre and using safe.
Red stretch textured yarn prepared by embodiment 3, fastness to washing reach 5 grades.
Claims (9)
1. a kind of bicomponent composite fibre, which is characterized in that the bicomponent composite fibre section is skin-core structure, by cortex
It is made with the sandwich layer containing functional material through two-component composite spinning.
2. a kind of bicomponent composite fibre according to claim 1, which is characterized in that the quality of the cortex and sandwich layer
Than for 15-30:70-85.
3. a kind of bicomponent composite fibre according to claim 1 or 2, which is characterized in that the sandwich layer is by function material
Material is mixed with core material.
4. a kind of bicomponent composite fibre according to claim 3, which is characterized in that core material includes polyester, modification
Polyester, polypropylene, modified polypropene, polyamide, modified polyamide, polyethylene, modified poly ethylene.
5. a kind of bicomponent composite fibre according to claim 3, which is characterized in that the functional material includes coloring
Material.
6. a kind of bicomponent composite fibre according to claim 1 or 2, which is characterized in that cortex includes polyester, is modified and gathers
Ester, polypropylene, modified polypropene, polyamide, modified polyamide, polyethylene, modified poly ethylene, wherein coloured material is zero.
7. a kind of bicomponent composite fibre according to claim 6, which is characterized in that the cortex is to have light transparent material
Material, wherein delustring powder content is zero.
8. a kind of bicomponent composite fibre according to claim 1 or 2, which is characterized in that the cortex is with sandwich layer
Incompatible.
9. a kind of preparation method of bicomponent composite fibre according to claim 1, which is characterized in that the preparation method
For following steps:
(1) functional material and core material are mixed and made into sandwich layer;
(2) bicomponent composite fibre is prepared using core/sheath bicomponent composite spinning technology in sandwich layer and cortex.