CN110079231A - A kind of Weak solvent PP faces patch and its manufacture craft directly - Google Patents
A kind of Weak solvent PP faces patch and its manufacture craft directly Download PDFInfo
- Publication number
- CN110079231A CN110079231A CN201910328583.3A CN201910328583A CN110079231A CN 110079231 A CN110079231 A CN 110079231A CN 201910328583 A CN201910328583 A CN 201910328583A CN 110079231 A CN110079231 A CN 110079231A
- Authority
- CN
- China
- Prior art keywords
- weak solvent
- glue
- pet
- line
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of Weak solvent PP to face patch and its manufacture craft directly, including PET plane materiel, glue-line, the base stock being successively bonded, is bonded between PET plane materiel and base stock by glue-line, it is characterised in that: solidification bonding protective layer is equipped between the PET and glue-line.Patch is faced directly using the Weak solvent PP that the Weak solvent PP of this structure faces patch or the preparation of this technique directly, have the advantages that setting solidification bonding protective layer and PET, the combination of glue-line material, protection integral product prevents contraction distortion, and alice phenomenon is prevented when pasting, anticorrosive property or the contraction distortion of product entirety are effectively ensured when may be implemented in using Weak solvent printing, especially suitable for UV machine, LATEX, solvent and the printing of Weak solvent equipment, simultaneously in Latex printing, can high temperature resistant to 110c °, and it is dedicated to be used in shiny surface, after use, glue is protected 1 year and be can remove.
Description
Technical field
The present invention relates to Weak solvent PP to face patch technical field directly, more specifically to a kind of Weak solvent PP face directly patch and
Its manufacture craft.
Background technique
With the development of science and technology, all trades and professions can all use Weak solvent PP and face patch directly, such as be used to make marks in study
, it is used to do the wall T-me interior space on finishing, the Weak solvent PP of outdoor advertisement faces patch etc. directly.It much faces directly at present
Patch typically carries out printing pattern using aqueous solvent due to the requirement of the colorful more patterns of its decorative pattern；In solvent and weak
When solvent equipment print application, when due to big amount and full version out of ink printing, corrosion due to solvent to PVC generates PVC and shrinks and becomes
Shape, later period are easy to produce alice phenomenon when pasting, and when printing and heatproof is not high.
Therefore current Weak solvent PP faces patch directly and needs to improve.
Summary of the invention
To achieve the above object, the following technical solution of the present invention: a kind of Weak solvent PP faces patch directly, including what is be successively bonded
PET plane materiel, glue-line, base stock are bonded between PET plane materiel and base stock by glue-line, it is characterised in that: between the PET and glue-line
Protective layer is bonded equipped with solidification.
The glue-line is mixed by following raw material: 22.5 grams of lotion, brightening agent 0.204g, flatting silica 6.48g, defoaming agent
0.082g, wetting agent 0.17g, water seep through water 3.4g, PVA0.47g.
The solidification bonding protective layer is mixed by following raw material: lotion 0.75g, curing agent 0.243g, wetting agent
0.009g, defoaming agent 0.02g.
The PET plane materiel is coated with one layer of hollow oil reservoir.
The hollow oil reservoir is mixed by following raw material: white spirit 3.1g, silicone oil 0.385g, curing agent 0.0057g, stripping
Power agent 0.005g.
The PET with a thickness of 95~100um, glue-line with a thickness of 25~30um, 135~140g of thickness of base stock,
Solidify bonding protective layer with a thickness of 5~10um.
A kind of manufacture craft for facing patch directly such as above-mentioned Weak solvent PP, which comprises the following steps:
S1, above-mentioned raw materials are weighed by weight；
S2, glue-line is prepared:
1) water is weighed, 1500 turns of silica speed of agitator is added and stirs 30 minutes；
2) speed of agitator is transferred to 800 turns, sequentially adds lotion, defoaming agent, brightening agent, water seep through water, wetting agent；
3) after adding, 800 revolving speeds are stirred 30 minutes；
4) with after the filtering of 200 mesh filter screens, upper machine is spare after standing 4 hours；
S3, PET plane materiel is taken, it is stand-by apply one layer of hollow oil reservoir in surface thereof, include the following:
1) white spirit and silicone oil, are weighed, pneumatic stirring prestissimo stirs 5 minutes；
2), curing agent is weighed to stir 10 minutes；
3), remover is weighed to be stirred for 15 minutes；
4) 400 mesh filter screens filter when, using
5) PET facestock surface, is applied to using roll marks；
S4, modulation solidification bonding protective layer mixed liquor are stand-by:
1), Xian Jiashui, lotion and curing agent stir 5 minutes；
2), add defoaming agent and wetting agent to be stirred for 20 minutes again, 800 turns of speed of agitator, formed and solidify bonding protective layer
Mixed liquor；
S5, it is printed on the PET plane materiel of step S3 using scraper bonding protective layer mixed liquor is solidified；
S6, glue made of step 2 is bonded using coating machine with PET, finally uses base stock rewinding.
95 degree of the temperature of the coating of the step S6,80 meters of machine speed.
The roll marks of the step S3 is applied to the hollow oil reservoir of PET facestock surface, and roll marks temperature is 105 degree, and 110 meters of machine speed/
Minute.
It is 90 degree that the step S5 scraper, which scrapes temperature, 30 ms/min of machine speed.
Patch is faced directly using the Weak solvent PP that the Weak solvent PP of this structure faces patch or the preparation of this technique directly, is had below beneficial to effect
Fruit: setting solidifies the combination of bonding protective layer and PET, glue-line material, when protecting the contraction distortion that prevents of integral product, and pasting
Alice phenomenon is prevented, it can be achieved that the anticorrosive property of product entirety is effectively ensured when using Weak solvent printing or shrinks change
Shape, especially suitable for UV machine, LATEX, solvent and Weak solvent equipment print, while Latex printing when, can high temperature resistant extremely
110c °, and it is dedicated to be used in shiny surface, after use, glue is protected 1 year and be can remove, and used glue construction Applicable temperature is wide
(periodical temperature may be adapted between 0c ° to 40c ° up and down).
Detailed description of the invention
Specific embodiment
A kind of Weak solvent PP faces patch directly, including PET plane materiel, glue-line, the base stock being successively bonded, bonds PET plane materiel by glue-line
Between base stock, it is characterised in that: be equipped with solidification bonding protective layer between the PET and glue-line.
The glue-line is mixed by following raw material: 22.5 grams of lotion, brightening agent 0.204g, flatting silica 6.48g, defoaming agent
0.082g, wetting agent 0.17g, water seep through water 3.4g, PVA0.47g.
The solidification bonding protective layer is mixed by following raw material: lotion 0.75g, curing agent 0.243g, wetting agent
0.009g, defoaming agent 0.02g.
The PET plane materiel is coated with one layer of hollow oil reservoir.
The hollow oil reservoir is mixed by following raw material: white spirit 3.1g, silicone oil 0.385g, curing agent 0.0057g, stripping
Power agent 0.005g.
The PET with a thickness of 95~100um, glue-line with a thickness of 25~30um, 135~140g of thickness of base stock,
Solidify bonding protective layer with a thickness of 5~10um.
A kind of manufacture craft for facing patch directly such as above-mentioned Weak solvent PP, which comprises the following steps:
S1, above-mentioned raw materials are weighed by weight；
S2, glue-line is prepared:
1) water is weighed, 1500 turns of silica speed of agitator is added and stirs 30 minutes；
2) speed of agitator is transferred to 800 turns, sequentially adds lotion, defoaming agent, brightening agent, water seep through water, wetting agent；
5) after adding, 800 revolving speeds are stirred 30 minutes；
6) with after the filtering of 200 mesh filter screens, upper machine is spare after standing 4 hours；
S3, PET plane materiel is taken, it is stand-by apply one layer of hollow oil reservoir in surface thereof, include the following:
1) white spirit and silicone oil, are weighed, pneumatic stirring prestissimo stirs 5 minutes；
2), curing agent is weighed to stir 10 minutes；
3), remover is weighed to be stirred for 15 minutes；
4) 400 mesh filter screens filter when, using
5) PET facestock surface, is applied to using roll marks；
S4, modulation solidification bonding protective layer mixed liquor are stand-by:
1), Xian Jiashui, lotion and curing agent stir 5 minutes；
2), add defoaming agent and wetting agent to be stirred for 20 minutes again, 800 turns of speed of agitator, formed and solidify bonding protective layer
Mixed liquor；
S5, it is printed on the PET plane materiel of step S3 using scraper bonding protective layer mixed liquor is solidified；
S6, glue made of step 2 is bonded using coating machine with PET, finally uses base stock rewinding.
95 degree of the temperature of the coating of the step S6,80 meters of machine speed.
The roll marks of the step S3 is applied to the hollow oil reservoir of PET facestock surface, and roll marks temperature is 105 degree, and 110 meters of machine speed/
Minute.
It is 90 degree that the step S5 scraper, which scrapes temperature, 30 ms/min of machine speed.
Weak solvent PP of the invention faces patch directly, has the advantages that setting solidification bonding protective layer and PET, glue-line
The contraction distortion that prevents of integral product is protected in the combination of material, and prevents alice phenomenon when stickup, it can be achieved that using weak
Anticorrosive property or the contraction distortion of product entirety is effectively ensured in solvent when printing, especially suitable for UV machine, LATEX, solvent and weak
Solvent equipment printing, while in Latex printing, can high temperature resistant to 110c °, and it is dedicated to be used in shiny surface, after use, glue
Protecting 1 year can remove, and used glue construction Applicable temperature is wide (periodical temperature may be adapted between 0c ° to 40c ° up and down).
The present invention is described according to specific embodiment, but it will be understood by those skilled in the art that not departing from this hair
When bright range, various change and equivalent replacement can be carried out.In addition, to adapt to the specific occasion of the technology of the present invention, it can be to the present invention
Many modifications are carried out without departing from its protection scope.Therefore, the present invention is not limited to specific embodiments disclosed herein, and including
All embodiments for dropping into claims.
Claims (10)
1. a kind of Weak solvent PP faces patch directly, including PET plane materiel, glue-line, the base stock being successively bonded, by glue-line bonding PET plane materiel with
Between base stock, it is characterised in that: be equipped with solidification bonding protective layer between the PET and glue-line.
2. Weak solvent PP according to claim 1 faces patch directly, which is characterized in that the glue-line is mixed by following raw material and made
At: 22.5 grams of lotion, brightening agent 0.204g, flatting silica 6.48g, defoaming agent 0.082g, wetting agent 0.17g, water seep through water 3.4g,
PVA0.47g。
3. Weak solvent PP according to claim 1 faces patch directly, which is characterized in that the solidification bonding protective layer is by following original
Material is mixed: lotion 0.75g, curing agent 0.243g, wetting agent 0.009g, defoaming agent 0.02g.
4. Weak solvent PP according to claim 1 faces patch directly, which is characterized in that the PET plane materiel is coated with one layer of hollow oil
Layer.
5. Weak solvent PP according to claim 4 faces patch directly, which is characterized in that the hollow oil reservoir is mixed by following raw material
It is made: white spirit 3.1g, silicone oil 0.385g, curing agent 0.0057g, stripping power agent 0.005g.
6. Weak solvent PP according to claim 1 faces patch directly, which is characterized in that the PET with a thickness of 95~
100um, glue-line with a thickness of 25~30um, 135~140g of thickness of base stock, solidify bonding protective layer with a thickness of 5~10um.
7. the manufacture craft that a kind of Weak solvent PP as described in claim 1~6 faces patch directly, which is characterized in that including following step
It is rapid:
S1, above-mentioned raw materials are weighed by weight；
S2, glue-line is prepared:
1) water is weighed, 1500 turns of silica speed of agitator is added and stirs 30 minutes；
2) speed of agitator is transferred to 800 turns, sequentially adds lotion, defoaming agent, brightening agent, water seep through water, wetting agent；
3) after adding, 800 revolving speeds are stirred 30 minutes；
4) with after the filtering of 200 mesh filter screens, upper machine is spare after standing 4 hours；
S3, PET plane materiel is taken, it is stand-by apply one layer of hollow oil reservoir in surface thereof, include the following:
1) white spirit and silicone oil, are weighed, pneumatic stirring prestissimo stirs 5 minutes；
2), curing agent is weighed to stir 10 minutes；
3), remover is weighed to be stirred for 15 minutes；
4) 400 mesh filter screens filter when, using
5) PET facestock surface, is applied to using roll marks；
S4, modulation solidification bonding protective layer mixed liquor are stand-by:
1), Xian Jiashui, lotion and curing agent stir 5 minutes；
2), add defoaming agent and wetting agent to be stirred for 20 minutes again, 800 turns of speed of agitator, form the mixing for solidifying bonding protective layer
Liquid；
S5, it is printed on the PET plane materiel of step S3 using scraper bonding protective layer mixed liquor is solidified；
S6, glue made of step 2 is bonded using coating machine with PET, finally uses base stock rewinding.
8. the manufacture craft that Weak solvent PP according to claim 7 faces patch directly, which is characterized in that the coating of the step S6
95 degree of temperature, machine speed 80 meters.
9. the manufacture craft that Weak solvent PP according to claim 7 faces patch directly, which is characterized in that the roll marks of the step S3
It is applied to the hollow oil reservoir of PET facestock surface, roll marks temperature is 105 degree, 110 ms/min of machine speed.
10. the manufacture craft that Weak solvent PP according to claim 7 faces patch directly, which is characterized in that the step S5 scraper
Scraping temperature is 90 degree, 30 ms/min of machine speed.