CN110079133A - A kind of automatic cleaning coating material and preparation method thereof for outer surface of automobile - Google Patents
A kind of automatic cleaning coating material and preparation method thereof for outer surface of automobile Download PDFInfo
- Publication number
- CN110079133A CN110079133A CN201910438867.8A CN201910438867A CN110079133A CN 110079133 A CN110079133 A CN 110079133A CN 201910438867 A CN201910438867 A CN 201910438867A CN 110079133 A CN110079133 A CN 110079133A
- Authority
- CN
- China
- Prior art keywords
- nanoscale
- parts
- platinum
- automobile
- automatic cleaning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of automatic cleaning coating materials for outer surface of automobile, are grouped as by the group of following parts by weight: 50-70 parts of methanol；21-25 parts of water；1-5 parts of tin oxide；1.0-1.5 parts of platinum；0.5-1.0 parts of tungsten oxide；6-9 parts of silica；A kind of preparation method of the automatic cleaning coating material for outer surface of automobile, comprising: S1, stock；S2, solution is prepared；S3, mixing: compared with prior art, the invention has the advantages that there is self-cleaning effect by being formulated resulting coating, it is not easy adhering dust, and after by current scour, water droplet will not be formed on surface but form water curtain on surface, eliminating watermark and water curtain can further flush clean coat side, reduce automobile carwash frequency, to reduce living cost, improve environmental benefit, and there is high rigidity and chemical resistance, surface is still wear-resisting when automobile high-speed moves, it improves service life, and vehicle body resistance can be effectively reduced, achieve the effect that antistatic.
Description
Technical field
The present invention relates to automotive fields, and in particular to a kind of for the automatic cleaning coating material of outer surface of automobile and its preparation
Method.
Background technique
In recent years, countries in Asia's economic development is rapid.The common people of countries in Asia are at present for quality of making the life better, every family
Each household will buy automobile.Wherein, more rich some people, which is not merely only satisfied with, possesses automobile, they are in automobile
There are higher requirement, the satisfaction lain in spiritual level more on appearance, comfort level, performance and class.From now on
The maturation of countries in Asia's automobile market generates people for the various demands of automobile certainly.
The automobile industry national U.S. the most flourishing, Japan, Europe etc., car body coating is nearly all waterproof coating.
Have the self-cleaning film product of many photocatalysts on the market, just listing when get the attention, but due to construction high price,
Difficulty is high, and can not play ideal effect for pollutions such as exhaust, charcoal ash, and consumers is caused more to lose such product
It hopes, can not exploit market for many years.The cleaning charge of automobile is expensive on ordinary days, and the sewage that carwash generates is difficult to handle, substantially
In environmental protection and energy saving core concept, we take up to study use of the automatic cleaning coating on automobile, by nanotechnology system
Produce a kind of automatic cleaning coating for being used exclusively in automobile-exterior, the Nature wind and rain, allow automobile to reach self-cleaning
Effect, reduce carwash number, reduce living cost, improve environmental benefit.
Summary of the invention
Object of the present invention is to: a kind of automatic cleaning coating material and preparation method thereof for outer surface of automobile is provided.
The technical scheme is that a kind of automatic cleaning coating material for outer surface of automobile, by following parts by weight
Group is grouped as: 50-70 parts of methanol；21-25 parts of water；1-5 parts of tin oxide；1.0-1.5 parts of platinum；0.5-1.0 parts of tungsten oxide；Dioxy
6-9 parts of SiClx.
Further: the tin oxide is nanoscale tin particles, and the platinum is nanoscale platinum grain, the tungsten oxide
For nanoscale tungsten particle, the silica is nanosized silica particles.
It is further: the nanoscale tin particles, nanoscale platinum grain, nanoscale tungsten particle and nanoscale two
The partial size of silicon oxide particle is respectively less than or is equal to 30 nanometers.
A kind of preparation method of the automatic cleaning coating material for outer surface of automobile, comprising:
S1, stock: stocking up by the component of above-mentioned parts by weight, and nanoscale tin particles are made in tin oxide, will
Nanoscale platinum grain is made in platinum, and nanoscale tungsten particle is made in tungsten oxide, nanometer grade silica is made in silica
Particle, and control nanoscale tin particles, nanoscale platinum grain, nanoscale tungsten particle and nanosized silica particles
Partial size be respectively less than or be equal to 30 nanometers；
S2, it prepares solution: the first alcohol and water of proportional quantities successively being poured into cleaning container, and stir 3-5min, stood
11-15min obtains mixed solution；
S3, mixing: by nanoscale tin particles, nanoscale platinum grain obtained in S1, nanoscale tungsten particle and
Nanosized silica particles sequentially add in the resulting mixed solution of S2, and stir 30-35min, stand 40-50min, obtain
To product.
Compared with prior art, not easy to stick the invention has the advantages that there is self-cleaning effect by being formulated resulting coating
Attached dust, and after by current scour will not form water droplet on surface but form water curtain on surface, eliminate watermark and
Water curtain can further flush clean coat side, reduce automobile carwash frequency, to reduce living cost, improve environmental benefit, and
And there is high rigidity and chemical resistance, surface is still wear-resisting when automobile high-speed moves, and improves service life, and can be effective
Reduce vehicle body resistance, achievees the effect that antistatic.
Detailed description of the invention
Fig. 1 is the performance test results table of embodiment products obtained therefrom；
Specific embodiment
Embodiment 1: a kind of automatic cleaning coating material for outer surface of automobile is grouped as: first by the group of following parts by weight
50 parts of alcohol；21 parts of water；1 part of tin oxide；1 part of platinum；0.5 part of tungsten oxide；6 parts of silica.The tin oxide is nanoscale
Tin particles, the platinum are nanoscale platinum grain, and the tungsten oxide is nanoscale tungsten particle, and the silica is nanoscale
Silica dioxide granule.And the nanoscale tin particles, nanoscale platinum grain, nanoscale tungsten particle and nanoscale two
The partial size of silicon oxide particle is 30 nanometers.Nano granules of stannic oxide effectively reduces vehicle body resistance, to reduce vehicle body insulating properties, drops
The electrostatic of low accumulation prevents Electrostatic Absorption dust, and nanometer silicon dioxide particle has super hydrophilic shape, is capable of forming moisture
Sublayer plays the role of antistatic agent.Nano-platinum particle has chemical resistance, can resist the sour corrosions such as external rainwater, receive
Rice tungsten oxide particles then effectively improve the hardness of coating, can extend coating life.
A kind of preparation method of the automatic cleaning coating material for outer surface of automobile, comprising:
S1, stock: stocking up by the component of above-mentioned parts by weight, and nanoscale tin particles are made in tin oxide, will
Nanoscale platinum grain is made in platinum, and nanoscale tungsten particle is made in tungsten oxide, nanometer grade silica is made in silica
Particle, and control nanoscale tin particles, nanoscale platinum grain, nanoscale tungsten particle and nanosized silica particles
Partial size to 30 nanometers；
S2, it prepares solution: the first alcohol and water of proportional quantities successively being poured into cleaning container, and stir 3min, stood
11min obtains mixed solution；
S3, mixing: by nanoscale tin particles, nanoscale platinum grain obtained in S1, nanoscale tungsten particle and
Nanosized silica particles sequentially add in the resulting mixed solution of S2, and stir 30min, stand 40min, obtain product.
Performance detection is as shown in Figure 1.
Embodiment 2: a kind of automatic cleaning coating material for outer surface of automobile is grouped as: first by the group of following parts by weight
70 parts of alcohol；25 parts of water；5 parts of tin oxide；1.5 parts of platinum；1.0 parts of tungsten oxide；9 parts of silica.
The tin oxide is nanoscale tin particles, and the platinum is nanoscale platinum grain, and the tungsten oxide is nanoscale
Tungsten oxide particles, the silica are nanosized silica particles.The nanoscale tin particles, nanoscale platinum
The partial size of grain, nanoscale tungsten particle and nanosized silica particles is respectively less than 30 nanometers.Nano granules of stannic oxide is effective
Reduce vehicle body resistance, to reduce vehicle body insulating properties, reduce the electrostatic of vehicle body accumulation, prevents Electrostatic Absorption dust, and nanometer two
Silicon oxide particle has super hydrophilic shape, is capable of forming water molecule layer, plays the role of antistatic agent.Nano-platinum particle has resistance toization
The property learned, can resist the sour corrosions such as external rainwater, and nano oxidized tungsten particle then effectively improves the hardness of coating, can extend painting
The layer service life.
A kind of preparation method of the automatic cleaning coating material for outer surface of automobile, comprising:
S1, stock: stocking up by the component of above-mentioned parts by weight, and nanoscale tin particles are made in tin oxide, will
Nanoscale platinum grain is made in platinum, and nanoscale tungsten particle is made in tungsten oxide, nanometer grade silica is made in silica
Particle, and control nanoscale tin particles, nanoscale platinum grain, nanoscale tungsten particle and nanosized silica particles
Partial size be respectively less than or be equal to 30 nanometers；
S2, it prepares solution: the first alcohol and water of proportional quantities successively being poured into cleaning container, and stir 5min, stood
15min obtains mixed solution；
S3, mixing: by nanoscale tin particles, nanoscale platinum grain obtained in S1, nanoscale tungsten particle and
Nanosized silica particles sequentially add in the resulting mixed solution of S2, and stir 35min, stand 50min, obtain product.
Performance detection is as shown in Figure 1.
Embodiment 3: a kind of automatic cleaning coating material for outer surface of automobile is grouped as: first by the group of following parts by weight
60 parts of alcohol；23 parts of water；3 parts of tin oxide；1.3 parts of platinum；0.7 part of tungsten oxide；8 parts of silica.
The tin oxide is nanoscale tin particles, and the platinum is nanoscale platinum grain, and the tungsten oxide is nanoscale
Tungsten oxide particles, the silica are nanosized silica particles.Nano granules of stannic oxide effectively reduces vehicle body resistance, from
And vehicle body insulating properties is reduced, the electrostatic of vehicle body accumulation is reduced, Electrostatic Absorption dust is prevented, and nanometer silicon dioxide particle is with super
Hydrophilic shape, is capable of forming water molecule layer, plays the role of antistatic agent.Nano-platinum particle has chemical resistance, can resist outer
The sour corrosions such as portion's rainwater, nano oxidized tungsten particle then effectively improve the hardness of coating, can extend coating life.
The nanoscale tin particles, nanoscale platinum grain, nanoscale tungsten particle and nanometer grade silica
The partial size of grain is respectively less than 30 nanometers.
A kind of preparation method of the automatic cleaning coating material for outer surface of automobile, comprising:
S1, stock: stocking up by the component of above-mentioned parts by weight, and nanoscale tin particles are made in tin oxide, will
Nanoscale platinum grain is made in platinum, and nanoscale tungsten particle is made in tungsten oxide, nanometer grade silica is made in silica
Particle, and control nanoscale tin particles, nanoscale platinum grain, nanoscale tungsten particle and nanosized silica particles
Partial size be respectively less than 30 nanometers；
S2, it prepares solution: the first alcohol and water of proportional quantities successively being poured into cleaning container, and stir 4min, stood
15min obtains mixed solution；
S3, mixing: by nanoscale tin particles, nanoscale platinum grain obtained in S1, nanoscale tungsten particle and
Nanosized silica particles sequentially add in the resulting mixed solution of S2, and stir 31min, stand 45min, obtain product.
Performance detection is as shown in Figure 1.
Embodiment 4: a kind of automatic cleaning coating material for outer surface of automobile is grouped as: first by the group of following parts by weight
65 parts of alcohol；23 parts of water；3 parts of tin oxide；1.2 parts of platinum；0.8 part of tungsten oxide；7 parts of silica.
The tin oxide is nanoscale tin particles, and the platinum is nanoscale platinum grain, and the tungsten oxide is nanoscale
Tungsten oxide particles, the silica are nanosized silica particles.Nano granules of stannic oxide effectively reduces vehicle body resistance, from
And vehicle body insulating properties is reduced, the electrostatic of vehicle body accumulation is reduced, Electrostatic Absorption dust is prevented, and nanometer silicon dioxide particle is with super
Hydrophilic shape, is capable of forming water molecule layer, plays the role of antistatic agent.Nano-platinum particle has chemical resistance, can resist outer
The sour corrosions such as portion's rainwater, nano oxidized tungsten particle then effectively improve the hardness of coating, can extend coating life.
The nanoscale tin particles, nanoscale platinum grain, nanoscale tungsten particle and nanometer grade silica
The partial size of grain is respectively less than 30 nanometers.
A kind of preparation method of the automatic cleaning coating material for outer surface of automobile, comprising:
S1, stock: stocking up by the component of above-mentioned parts by weight, and nanoscale tin particles are made in tin oxide, will
Nanoscale platinum grain is made in platinum, and nanoscale tungsten particle is made in tungsten oxide, nanometer grade silica is made in silica
Particle, and control nanoscale tin particles, nanoscale platinum grain, nanoscale tungsten particle and nanosized silica particles
Partial size be respectively less than 30 nanometers；
S2, it prepares solution: the first alcohol and water of proportional quantities successively being poured into cleaning container, and stir 5min, stood
13min obtains mixed solution；
S3, mixing: by nanoscale tin particles, nanoscale platinum grain obtained in S1, nanoscale tungsten particle and
Nanosized silica particles sequentially add in the resulting mixed solution of S2, and stir 33min, stand 45min, obtain product.
Performance detection is as shown in Figure 1.
Certainly the above embodiments merely illustrate the technical concept and features of the present invention, and its object is to allow be familiar with technique
People can understand the content of the present invention and implement it accordingly, it is not intended to limit the scope of the present invention.It is all according to this hair
The modification that the Spirit Essence of bright main technical schemes is done, should be covered by the protection scope of the present invention.
Claims (4)
1. a kind of automatic cleaning coating material for outer surface of automobile, it is characterised in that: be grouped as by the group of following parts by weight: first
50-70 parts of alcohol；21-25 parts of water；1-5 parts of tin oxide；1.0-1.5 parts of platinum；
0.5-1.0 parts of tungsten oxide；6-9 parts of silica.
2. a kind of automatic cleaning coating material for outer surface of automobile according to claim 1, it is characterised in that: the oxygen
Change tin is nanoscale tin particles, and the platinum is nanoscale platinum grain, and the tungsten oxide is nanoscale tungsten particle, described
Silica is nanosized silica particles.
3. a kind of automatic cleaning coating material for outer surface of automobile according to claim 2, it is characterised in that: described to receive
Meter level granules of stannic oxide, nanoscale platinum grain, nanoscale tungsten particle and nanosized silica particles partial size be respectively less than
Or it is equal to 30 nanometers.
4. a kind of preparation method of automatic cleaning coating material for outer surface of automobile according to claim 1 or 2 or 3,
It is characterized by comprising:
S1, stock: stocking up by the component of above-mentioned parts by weight, and nanoscale tin particles are made in tin oxide, by platinum system
At nanoscale platinum grain, nanoscale tungsten particle is made in tungsten oxide, nanosized silica particles are made in silica,
And control the grain of nanoscale tin particles, nanoscale platinum grain, nanoscale tungsten particle and nanosized silica particles
Diameter is respectively less than or is equal to 30 nanometers；
S2, it prepares solution: the first alcohol and water of proportional quantities successively being poured into cleaning container, and stir 3-5min, stand 11-
15min obtains mixed solution；
S3, mixing: by nanoscale tin particles, nanoscale platinum grain obtained in S1, nanoscale tungsten particle and nanometer
Grade silicon dioxide particle sequentially adds in the resulting mixed solution of S2, and stirs 30-35min, stands 40-50min, is produced
Product.