CN110054449A - A kind of ceramic tile bond, preparation method and application method - Google Patents
A kind of ceramic tile bond, preparation method and application method Download PDFInfo
- Publication number
- CN110054449A CN110054449A CN201910502280.9A CN201910502280A CN110054449A CN 110054449 A CN110054449 A CN 110054449A CN 201910502280 A CN201910502280 A CN 201910502280A CN 110054449 A CN110054449 A CN 110054449A
- Authority
- CN
- China
- Prior art keywords
- ceramic tile
- parts
- brick
- bonding
- tile bond
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of ceramic tile bonds, including below according to the raw material of parts by weight: 30-35 parts of high quality cement, 65-70 parts of filler, 0.15-0.35 parts of cellulose ether, 0.5-1 parts of re-dispersible glue powder, ceramic tile bond is nontoxic, odorless, the free of contamination environment-friendly products of one kind come into being with the development of building tile, and with superpower bonding, versatile, flexibility is good, consistency of performance, elevation construction, need not fix, be pre-mixed, using characteristics such as environmental protection；Have the characteristics that adhesion strength is high, construction efficiency is high, saves material utilization amount in application, thoroughly solves directly with the drawbacks such as the cohesive force of cement stickup is weak, durability is poor, be easy to fall, construction material dosage is big.
Description
Technical field
The present invention relates to tile paste technical field, specifically a kind of ceramic tile bond, preparation method and application method.
Background technique
The rapid development of architectural pottery is made that major contribution for beautifying city and domestic environment.Traditional tile paste
Method mostly uses cement mortar, i.e., sand and cement scene is mixed and made into simple cement mortar, and this mortar is coated in preimpregnation
Or the ceramic tile back side is pre-wetted, the ceramic tile for being coated with mortar is pressed on the surface soaked in advance, touches ceramic tile, then to guarantee ceramic tile
With consistent flatness.The main purpose of this process is to be compacted mortar, and cement granules is made to enter the porous back side of ceramic tile
In internal and porous substrate.The shortcomings that this mortar, is that cohesive force is weak, durability is poor, is easy to peel off.
Summary of the invention
The purpose of the present invention is to provide a kind of ceramic tile bond, preparation method and application methods, to solve above-mentioned background
The problem of being proposed in technology.
To achieve the above object, the invention provides the following technical scheme:
A kind of ceramic tile bond, including below according to the raw material of parts by weight: 30-35 parts of high quality cement, filler 65-70
Part, 0.15-0.35 parts of cellulose ether, 0.5-1 parts of re-dispersible glue powder.
As a further solution of the present invention: a kind of ceramic tile bond, including below according to the raw material of parts by weight: high quality
32 parts of cement, 68 parts of filler, 0.25 part of cellulose ether, 0.7 part of re-dispersible glue powder.
As a further solution of the present invention: the filler is one of quartz sand, river sand, lime stone or any ratio
Example combination.
A kind of preparation method of ceramic tile bond, steps are as follows:
S1, the various raw material prepared needed for being ready in advance according to formula and formulation tool, open tank body blender, so
It is prepared afterwards according to recipe requirements, and fills in preparation record in time；
The quantity of S2, the sequence that industrial chemicals is added and addition must be executed in strict accordance with process recipe, must not arbitrarily be changed
Become, the necessary thorough cleaning of remaining raw material is clean in Raw material pail；
S3, it is fitly placed on specified region, after the completion of stirring binder, notice quality inspection portion examines its solid content
It surveys；
In S4, preparation and metering process, it is necessary to ensure that measuring equipment is corrected and used correct；Entire binder making station pipe
Road will be checked and be cleared up in time, avoid blocking phenomenon.
A kind of application method of ceramic tile bond, steps are as follows:
S21, the usable sumble construction of small-sized tapestry brick is bonded on smooth basal plane, select suitable tooth form scraper plate
By the rubber cement being stirred blade coating in wall or ground, glue-spread is no more than the open assembly time under prevailing condition with the construction time
Standard, the bottom of tapestry brick should equably bond no less than 70% contact area.Jointing can be carried out after completing 24-36h by pasting；
S2, tapestry brick, or the biggish tapestry brick of bonding, stone slab are bonded on the basal plane of out-of-flatness, preferably use palette knife work
(being constructed using grey spoon)；More small-sized tapestry brick is pasted or has seepage resistance demand to wall, and ceramic tile bottom 100% should be made to touch
Rubber cement；Wall pastes biggish stone slab, polished bricks material bottom should equably bond no less than 75% contact area, paste complete
It can carry out jointing after 24-36h, metope will be moistened and (be done in exogenous damp) when construction, and keep certain flatness, be uneven or pole
Its coarse position is using the leveling of the materials such as cement mortar；
S23, base must remove floating ash, greasy dirt, wax, in order to avoid influence caking ability；Mixed adhesive is applied to
The back side of brick material is pasted, is then firmly pressed, until plain；
S24, because finishing material size is different, practical consumption is different, general 1m2At least about 4.5-6kg binder glues
Paste thickness about 2-3mm；Select suitable flute profile scraper with ensure effective bonding area at least plate, ceramic tile homalographic 65%,
Mortar is completely spread with dedicated flute profile scraper basal plane 3-5mm thickness, then there is one side of tooth form to pull out with straight line or S-shaped with flute profile scraper
Striated, scraper plane and planar substrate intersection are in 45 ° -60 °；
Subproblem and solution when S25, use:
S25.1, when bonding biggish brick, stone material, be not easy to be adjusted correction；The reason for this is that basal plane and brick bottom are equal
100% ground bonding, causes the air pressure of vacuum, so that brick can only move left and right, and cannot be pressed into or pull out；Solution can
Brick is first carried out pre- (sky) paving before stickup, to avoid there is vacuum defect；
Occurs hollowing or cohesive force decline after S25.2, bonding.Cause the reason of this phenomenon is there are three aspect: first is that viscous
Open assembly time is had been subjected to when patch, there are two the methods for solving the problems, such as this: 1) pasting in open assembly time；2) paste when slightly with
Pressing is moved, is very helpful to the viscous subsidy effect of guarantee；Second is that going to adjust again after having crossed adjustment time.Its solution is
Adjustment time smears slurry later if you need to adjust again after should removing；
When S25.3, stickup large size tapestry brick, the dosage of rubber cement is insufficient, causes to pull out excessively when front and back adjusts, makes rubber cement
Delamination, solution have: when 1) being overlay, rubber cement dosage as accurate as possible mostly adjusts front and back using the mode for beating pressure
Distance；2) rubber cement thickness should be not less than 3mm, and pulling out adjustment distance is approximately the 25% of rubber cement thickness；
When the relatively thin white or light-colored stone material of S25.4, bonding, perceived color is dimmed.The reason of generating this problem is shallow
Color and loose stone material is easily revealed the exact details, using the binder color susceptible of grey, can using white ceramic tile bond into
Row bonding is to solve the problems, such as this.
Compared with prior art, the beneficial effects of the present invention are:
1, ceramic tile bond is nontoxic, odorless, the free of contamination environmental protection of one kind come into being with the development of building tile
Product, with superpower bonding, versatile, flexibility is good, consistency of performance, elevation construction, need not fix, be pre-mixed, use
The characteristics such as environmental protection；
2, have the characteristics that adhesion strength is high, construction efficiency is high in application, save material utilization amount, thoroughly solve directly
The drawbacks such as the cohesive force pasted with cement is weak, durability is poor, be easy to fall, construction material dosage is big, are widely portable to inner-outer wall
The tile paste of the facing decoration places of the buildings such as face, ground, bathroom, kitchen；
3, what is occurred in the construction process is not easy adjustment correction, hollowing or cohesive force decline, the problems such as color is dimmed, also can
There is corresponding solution, is a kind of tile laying material with boundless market prospects.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
Embodiment 1
A kind of ceramic tile bond, including below according to the raw material of parts by weight: 30 parts of high quality cement, 65 parts of filler, fiber
0.15 part of plain ether, 0.5 part of re-dispersible glue powder.
Further: the filler is quartz sand.
A kind of preparation method of ceramic tile bond, steps are as follows:
S1, the various raw material prepared needed for being ready in advance according to formula and formulation tool, open tank body blender, so
It is prepared afterwards according to recipe requirements, and fills in preparation record in time；
The quantity of S2, the sequence that industrial chemicals is added and addition must be executed in strict accordance with process recipe, must not arbitrarily be changed
Become, the necessary thorough cleaning of remaining raw material is clean in Raw material pail；
S3, it is fitly placed on specified region, after the completion of stirring binder, notice quality inspection portion examines its solid content
It surveys；
In S4, preparation and metering process, it is necessary to ensure that measuring equipment is corrected and used correct；Entire binder making station pipe
Road will be checked and be cleared up in time, avoid blocking phenomenon.
A kind of application method of ceramic tile bond, steps are as follows:
S21, the usable sumble construction of small-sized tapestry brick is bonded on smooth basal plane, select suitable tooth form scraper plate
By the rubber cement being stirred blade coating in wall or ground, glue-spread is no more than the open assembly time under prevailing condition with the construction time
Standard, the bottom of tapestry brick should equably bond no less than 70% contact area, and jointing can be carried out after completing for 24 hours by pasting；
S2, tapestry brick, or the biggish tapestry brick of bonding, stone slab are bonded on the basal plane of out-of-flatness, preferably use palette knife work
(being constructed using grey spoon)；More small-sized tapestry brick is pasted or has seepage resistance demand to wall, and ceramic tile bottom 100% should be made to touch
Rubber cement；Wall pastes biggish stone slab, polished bricks material bottom should equably bond no less than 75% contact area, paste complete
It can carry out jointing after for 24 hours, metope will be moistened and (be done in exogenous damp) when construction, and keep certain flatness, be uneven or extremely
Coarse position is using the leveling of the materials such as cement mortar；
S23, base must remove floating ash, greasy dirt, wax, in order to avoid influence caking ability；Mixed adhesive is applied to
The back side of brick material is pasted, is then firmly pressed, until plain；
S24, because finishing material size is different, practical consumption is different, general 1m2At least about 4.5kg binder is pasted
Thickness about 2mm；Select suitable flute profile scraper with ensure effective bonding area at least plate, ceramic tile homalographic 65%, with special
Mortar is completely spread with flute profile scraper basal plane 3mm thickness, then there is one side of tooth form to pull out striped with straight line or S-shaped with flute profile scraper
Shape, scraper plane and planar substrate intersection are in 45 °；
Subproblem and solution when S25, use:
S25.1, when bonding biggish brick, stone material, be not easy to be adjusted correction；The reason for this is that basal plane and brick bottom are equal
100% ground bonding, causes the air pressure of vacuum, so that brick can only move left and right, and cannot be pressed into or pull out；Solution can
Brick is first carried out pre- (sky) paving before stickup, to avoid there is vacuum defect；
Occurs hollowing or cohesive force decline after S25.2, bonding.Cause the reason of this phenomenon is there are three aspect: first is that viscous
Open assembly time is had been subjected to when patch, there are two the methods for solving the problems, such as this: 1) pasting in open assembly time；2) paste when slightly with
Pressing is moved, is very helpful to the viscous subsidy effect of guarantee；Second is that going to adjust again after having crossed adjustment time.Its solution is
Adjustment time smears slurry later if you need to adjust again after should removing；
When S25.3, stickup large size tapestry brick, the dosage of rubber cement is insufficient, causes to pull out excessively when front and back adjusts, makes rubber cement
Delamination.Its solution has: when 1) being overlay, rubber cement dosage as accurate as possible mostly adjusts front and back using the mode for beating pressure
Distance；2) rubber cement thickness should be not less than 3mm, and pulling out adjustment distance is approximately the 25% of rubber cement thickness；
When the relatively thin white or light-colored stone material of S25.4, bonding, perceived color is dimmed；The reason of generating this problem is shallow
Color and loose stone material is easily revealed the exact details, using the binder color susceptible of grey, can using white ceramic tile bond into
Row bonding is to solve the problems, such as this.
Embodiment 2
A kind of ceramic tile bond, including below according to the raw material of parts by weight: 32 parts of high quality cement, 68 parts of filler, fiber
0.25 part of plain ether, 0.7 part of re-dispersible glue powder.
Further, the filler is river sand.
A kind of preparation method of ceramic tile bond, steps are as follows:
S1, the various raw material prepared needed for being ready in advance according to formula and formulation tool, open tank body blender, so
It is prepared afterwards according to recipe requirements, and fills in preparation record in time；
The quantity of S2, the sequence that industrial chemicals is added and addition must be executed in strict accordance with process recipe, must not arbitrarily be changed
Become, the necessary thorough cleaning of remaining raw material is clean in Raw material pail；
S3, it is fitly placed on specified region, after the completion of stirring binder, notice quality inspection portion examines its solid content
It surveys；
In S4, preparation and metering process, it is necessary to ensure that measuring equipment is corrected and used correct；Entire binder making station pipe
Road will be checked and be cleared up in time, avoid blocking phenomenon.
A kind of application method of ceramic tile bond, steps are as follows:
S21, the usable sumble construction of small-sized tapestry brick is bonded on smooth basal plane, select suitable tooth form scraper plate
By the rubber cement being stirred blade coating in wall or ground, glue-spread is no more than the open assembly time under prevailing condition with the construction time
Standard, the bottom of tapestry brick should equably bond no less than 70% contact area.Jointing can be carried out after completing 30h by pasting；
S2, tapestry brick, or the biggish tapestry brick of bonding, stone slab are bonded on the basal plane of out-of-flatness, preferably use palette knife work
(being constructed using grey spoon)；More small-sized tapestry brick is pasted or has seepage resistance demand to wall, and ceramic tile bottom 100% should be made to touch
Rubber cement；Wall pastes biggish stone slab, polished bricks material bottom should equably bond no less than 75% contact area, paste complete
It can carry out jointing after 30h, metope will be moistened and (be done in exogenous damp) when construction, and keep certain flatness, be uneven or extremely
Coarse position is using the leveling of the materials such as cement mortar；
S23, base must remove floating ash, greasy dirt, wax, in order to avoid influence caking ability；Mixed adhesive is applied to
The back side of brick material is pasted, is then firmly pressed, until plain；
S24, because finishing material size is different, practical consumption is different, general 1m2At least about 5kg binder is pasted thick
Spend about 2.5mm；Select suitable flute profile scraper with ensure effective bonding area at least plate, ceramic tile homalographic 65%, with special
Mortar is completely spread with flute profile scraper basal plane 4mm thickness, then there is one side of tooth form to pull out striped with straight line or S-shaped with flute profile scraper
Shape, scraper plane and planar substrate intersection are in 53 °；
Subproblem and solution when S25, use:
S25.1, when bonding biggish brick, stone material, be not easy to be adjusted correction；The reason for this is that basal plane and brick bottom are equal
100% ground bonding, causes the air pressure of vacuum, so that brick can only move left and right, and cannot be pressed into or pull out；Solution can
Brick is first carried out pre- (sky) paving before stickup, to avoid there is vacuum defect；
Occurs hollowing or cohesive force decline after S25.2, bonding.Cause the reason of this phenomenon is there are three aspect: first is that viscous
Open assembly time is had been subjected to when patch, there are two the methods for solving the problems, such as this: 1) pasting in open assembly time；2) paste when slightly with
Pressing is moved, is very helpful to the viscous subsidy effect of guarantee；Second is that going to adjust again after having crossed adjustment time.Its solution is
Adjustment time smears slurry later if you need to adjust again after should removing；
When S25.3, stickup large size tapestry brick, the dosage of rubber cement is insufficient, causes to pull out excessively when front and back adjusts, makes rubber cement
Delamination；Its solution has: when 1) being overlay, rubber cement dosage as accurate as possible mostly adjusts front and back using the mode for beating pressure
Distance；2) rubber cement thickness should be not less than 3mm, and pulling out adjustment distance is approximately the 25% of rubber cement thickness；
When the relatively thin white or light-colored stone material of S25.4, bonding, perceived color is dimmed.The reason of generating this problem is shallow
Color and loose stone material is easily revealed the exact details, using the binder color susceptible of grey, can using white ceramic tile bond into
Row bonding is to solve the problems, such as this.
Embodiment 3
A kind of ceramic tile bond, including below according to the raw material of parts by weight: 35 parts of high quality cement, 70 parts of filler, fiber
0.35 part of plain ether, 1 part of re-dispersible glue powder.
Further: the filler is the arbitrary proportion combination of quartz sand, river sand, lime stone.
A kind of preparation method of ceramic tile bond, steps are as follows:
S1, the various raw material prepared needed for being ready in advance according to formula and formulation tool, open tank body blender, so
It is prepared afterwards according to recipe requirements, and fills in preparation record in time；
The quantity of S2, the sequence that industrial chemicals is added and addition must be executed in strict accordance with process recipe, must not arbitrarily be changed
Become, the necessary thorough cleaning of remaining raw material is clean in Raw material pail；
S3, it is fitly placed on specified region, after the completion of stirring binder, notice quality inspection portion examines its solid content
It surveys；
In S4, preparation and metering process, it is necessary to ensure that measuring equipment is corrected and used correct；Entire binder making station pipe
Road will be checked and be cleared up in time, avoid blocking phenomenon.
A kind of application method of ceramic tile bond, steps are as follows:
S21, the usable sumble construction of small-sized tapestry brick is bonded on smooth basal plane, select suitable tooth form scraper plate
By the rubber cement being stirred blade coating in wall or ground, glue-spread is no more than the open assembly time under prevailing condition with the construction time
Standard, the bottom of tapestry brick should equably bond no less than 70% contact area；Jointing can be carried out after completing 36h by pasting；
S2, tapestry brick, or the biggish tapestry brick of bonding, stone slab are bonded on the basal plane of out-of-flatness, preferably use palette knife work
(being constructed using grey spoon)；More small-sized tapestry brick is pasted or has seepage resistance demand to wall, and ceramic tile bottom 100% should be made to touch
Rubber cement；Wall pastes biggish stone slab, polished bricks material bottom should equably bond no less than 75% contact area, paste complete
It can carry out jointing after 36h, metope will be moistened and (be done in exogenous damp) when construction, and keep certain flatness, be uneven or extremely
Coarse position is using the leveling of the materials such as cement mortar；
S23, base must remove floating ash, greasy dirt, wax, in order to avoid influence caking ability；Mixed adhesive is applied to
The back side of brick material is pasted, is then firmly pressed, until plain；
S24, because finishing material size is different, practical consumption is different, general 1m2At least about 6kg binder is pasted thick
Spend about 3mm；Select suitable flute profile scraper with ensure effective bonding area at least plate, ceramic tile homalographic 65%, use is dedicated
Flute profile scraper completely spreads mortar basal plane 5mm thickness, then has one side of tooth form to pull out striated with straight line or S-shaped with flute profile scraper,
Scraper plane and planar substrate intersection are in 60 °；
Subproblem and solution when S25, use:
S25.1, when bonding biggish brick, stone material, be not easy to be adjusted correction；The reason for this is that basal plane and brick bottom are equal
100% ground bonding, causes the air pressure of vacuum, so that brick can only move left and right, and cannot be pressed into or pull out；Solution can
Brick is first carried out pre- (sky) paving before stickup, to avoid there is vacuum defect；
Occurs hollowing or cohesive force decline after S25.2, bonding.Cause the reason of this phenomenon is there are three aspect: first is that viscous
Open assembly time is had been subjected to when patch, there are two the methods for solving the problems, such as this: 1) pasting in open assembly time；2) paste when slightly with
Pressing is moved, is very helpful to the viscous subsidy effect of guarantee；Second is that going to adjust again after having crossed adjustment time.Its solution is
Adjustment time smears slurry later if you need to adjust again after should removing；
When S25.3, stickup large size tapestry brick, the dosage of rubber cement is insufficient, causes to pull out excessively when front and back adjusts, makes rubber cement
Delamination；Its solution has: when 1) being overlay, rubber cement dosage as accurate as possible mostly adjusts front and back using the mode for beating pressure
Distance；2) rubber cement thickness should be not less than 3mm, and pulling out adjustment distance is approximately the 25% of rubber cement thickness；
When the relatively thin white or light-colored stone material of S25.4, bonding, perceived color is dimmed；The reason of generating this problem is shallow
Color and loose stone material is easily revealed the exact details, using the binder color susceptible of grey, can using white ceramic tile bond into
Row bonding is to solve the problems, such as this.
Embodiment 1-3's carries out adhesive strength test according to standard JC/T 547-2017C1 type, and experimental result is as follows:
Comparative example:
Other products carry out adhesive strength test according to standard GB/T 25181-2010 in the market, and experimental result is as follows:
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims
Variation is included within the present invention.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (7)
1. a kind of ceramic tile bond, which is characterized in that including below according to the raw material of parts by weight: 30-35 parts of high quality cement is filled out
Expect 65-70 parts, 0.15-0.35 parts of cellulose ether, 0.5-1 parts of re-dispersible glue powder.
2. ceramic tile bond according to claim 1, which is characterized in that including below according to the raw material of parts by weight: high-quality
Measure 32 parts of cement, 68 parts of filler, 0.25 part of cellulose ether, 0.7 part of re-dispersible glue powder.
3. ceramic tile bond according to claim 2, which is characterized in that the filler is quartz sand, in river sand, lime stone
One or any ratio combination.
4. the preparation method of ceramic tile bond according to claim 1 to 3, which is characterized in that steps are as follows:
S1, the various raw material prepared needed for being ready in advance according to formula and formulation tool, open tank body blender, then press
It is prepared according to recipe requirements, and fills in preparation record in time；
The quantity of S2, the sequence that industrial chemicals is added and addition are executed in strict accordance with process recipe, remaining raw material in Raw material pail
Thorough cleaning is clean；
S3, it is fitly placed on specified region, after the completion of stirring binder, carries out solid content detection；
In S4, preparation and metering process, it is ensured that measuring equipment is corrected and used correct；Entire binder making station pipeline is timely
It checks and clears up.
5. a kind of application method of ceramic tile bond, including any ceramic tile bond of claim 1-3, feature exists
In steps are as follows:
S21, small-sized tapestry brick is bonded on smooth basal plane constructed using sumble, the glue for selecting tooth form scraper plate that will be stirred
Slurry blade coating is not more than the open assembly time under prevailing condition in wall or ground, glue-spread construction time, and the bottom of tapestry brick is uniform
The contact area of ground bonding no less than 70%；Jointing is carried out after the completion of pasting；
S2, tapestry brick is bonded on the basal plane of out-of-flatness, or the biggish tapestry brick of bonding, stone slab use ash using palette knife work
Spoon construction；More small-sized tapestry brick is pasted or has seepage resistance demand to wall, and ceramic tile bottom 100% is made to touch rubber cement；Wall patch
Biggish stone slab, polished bricks material bottom equably bond no less than 75% contact area, paste and are hooked after completing 24-36h
Seam, metope will moisten when construction, and keep certain flatness, be uneven or extremely coarse position is flattened with cement bonded sand；
S23, base remove floating ash, greasy dirt, wax；Mixed adhesive is applied to the back side for pasting brick material, is then exerted oneself
It presses, until plain；
S24, because finishing material size is different, practical consumption is different, 1m24.5-6kg binder is consumed, thickness 2-3mm is pasted；
Suitable flute profile scraper is selected, mortar is completely spread with flute profile scraper basal plane 3-5mm thickness；
Subproblem and solution when S25, use:
S25.1, when bonding biggish brick, stone material, be not easy to be adjusted correction；Solution is first to carry out brick before stickup
Pre- paving；
Occur hollowing or cohesive force decline after S25.2, bonding, solves the problems, such as this method are as follows: 1) paste in open assembly time；2)
Pressing is moved when stickup；
When S25.3, stickup large size tapestry brick, the dosage of rubber cement is insufficient, solution are as follows: when 1) being overlay, accurate glue
Dosage is starched, adjusts longitudinal separation using the mode for beating pressure；2) rubber cement thickness is not less than 3mm, and pulling out adjustment distance is rubber cement thickness
25%；
When the relatively thin white or light-colored stone material of S25.4, bonding, color is dimmed, is glued at this time using the ceramic tile bond of white
Knot is to solve the problems, such as this.
6. the application method of ceramic tile bond according to claim 5, which is characterized in that in step S21, paste and complete
Jointing is carried out after 24-36h.
7. the application method of ceramic tile bond according to claim 5, which is characterized in that in step S24, with flute profile scraper
There is one side of tooth form to pull out striated with straight line or S-shaped, scraper plane and planar substrate intersection are in 45 ° -60 °.