CN1100050C - Method for preparing tetrahydrofuran by utilizing dehydration and cyclization of 1,4-butanediol - Google Patents
Method for preparing tetrahydrofuran by utilizing dehydration and cyclization of 1,4-butanediol Download PDFInfo
- Publication number
- CN1100050C CN1100050C CN99106164A CN99106164A CN1100050C CN 1100050 C CN1100050 C CN 1100050C CN 99106164 A CN99106164 A CN 99106164A CN 99106164 A CN99106164 A CN 99106164A CN 1100050 C CN1100050 C CN 1100050C
- Authority
- CN
- China
- Prior art keywords
- butyleneglycol
- heteropolyacid
- accordance
- reaction
- catalyzer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention provides a method for preparing tetrahydrofuran by utilizing dehydration and cyclization of 1, 4-butanediol. At the temperature of 130 to 250 DEG C, a catalyst which contains heteropoly acid contacts 1, 4-butanediol, and the catalyst reacts with the 1, 4-butanediol. Because the method adopts the catalyst which contains the heteropoly acid, the treating capacity of the 1, 4-butanediol is obviously enhanced, and 1000 to 2000 grams of 1, 4-butanediol can be treated by each gram of heteropoly acid per hour.
Description
The invention relates to 1, the method for 4-butyleneglycol preparing tetrahydrofuran by dehydrating and cyclization.
1,4-butyleneglycol cyclodehydration is a preparation tetrahydrofuran (THF) topmost method, and is known 1, the catalyzer of 4-butyleneglycol dehydration preparation tetrahydrofuran (THF) have sulfuric acid and γ-, η-type Al
2O
3As everyone knows, if adopt corrosive sulfuric acid (US 4665205), then need special anticorrosion equipment, the investment of equipment is increased, the spent acid of generation also pollutes the environment.Also can produce burnt shape material in addition in the reaction process, the complicacy of reaction process is also increased greatly.
SU1158562 discloses a kind of with γ-Al
2O
3Or chloride γ-Al
2O
3Being the technology of Preparation of catalysts tetrahydrofuran (THF), is to react under 320 ℃, condition of normal pressure.When 1, the liquid hourly space velocity of 4-butyleneglycol is 7.0h
-1The time, 1, the transformation efficiency of 4-butyleneglycol is 100%, the selectivity of tetrahydrofuran (THF) is 100%.And when 1, the liquid hourly space velocity of 4-butyleneglycol is increased to 7.5h
-1The time, 1, the transformation efficiency of 4-butyleneglycol drops to 97.4%, and the selectivity of tetrahydrofuran (THF) drops to 93.6%.
SU1294805 discloses a kind of preparation method of tetrahydrofuran (THF), be be respectively 16.1nm, 35.4nm, 70nm with mean pore size pore, mesopore, macroporous silica gel as catalyzer, this catalyzer needs activate 30~45min before use under 400 ℃~420 ℃ inert atmospheres.Adopt above-mentioned catalyzer to react, 420 ℃, volume space velocity is 38g/cm when normal pressure, liquid
3.h under the reaction conditions, 1, the transformation efficiency 100% of 4-butyleneglycol, the tetrahydrofuran (THF) selectivity is 99.2%; And under identical temperature, when liquid hourly space velocity increases to 61.5g/cm
3.h the time, 1, the transformation efficiency of 4-butyleneglycol drops to 89.3%, and the selectivity of tetrahydrofuran (THF) reduces to 99.3%.
When TOSHIDE BABA has delivered heteropolyacid and has been catalyzer on Journal of Molecular Catalysis (37 (1986) 317~326), 1, the liquid phase reaction mechanism of 4-butyleneglycol preparing tetrahydrofuran by dehydrating and cyclization.Investigated in the literary composition under 398~435K (125~162 ℃) temperature, aqueous solvent and dioxane are to the influence of speed of response, and conclusion is that the activity of catalyzer in dioxane is greater than the activity in water, still, even in dioxane 1, the processing power of 4-butyleneglycol is also less than 7h
-1
In a word, have 1 now, all there is the low defective of processing power in the method that 4-butyleneglycol cyclodehydration is produced tetrahydrofuran (THF), and as improving processing power, raw material 1, the transformation efficiency of 4-butyleneglycol all obviously descend.
It is a kind of 1 that the object of the invention is to provide, and the method for 4-butyleneglycol preparing tetrahydrofuran by dehydrating and cyclization, this method have higher processing power than prior art under uniform temp.
The method for preparing tetrahydrofuran (THF) provided by the invention is under 130~250 ℃ of temperature, will contain the catalyzer and 1 of heteropolyacid, and the contact of 4-butyleneglycol is reacted.
Specifically, preparation tetrahydrofuran (THF) method provided by the invention is with 1, the 4-butyleneglycol feeds and is equipped with in the reactor of the catalyzer that contains heteropolyacid, in temperature is 130~250 ℃, preferred 163~230 ℃, more preferably 180~220 ℃, pressure is 0.1~1MPa, react under the condition of preferred 0.1~0.5MPa, collect the product tetrahydrofuran (THF) by condenser.
Among the preparation method provided by the invention, temperature of reaction can be 130~250 ℃.If reaction temperature is spent low, then catalyst reaction is active not enough, and the reaction times prolongs, and treatment capacity descends.When temperature was high, speed of response was fast, had on a small quantity 1 simultaneously, and the 4-butyleneglycol steams with product, therefore can add suitable pressure, and pressure range is advisable with 0.1~1MPa, preferred 0.1~0.5MPa.But for this reaction, the too high meeting of temperature increases side reaction, and intensified pressure is unfavorable for that also molecular balance moves to the direction that generates tetrahydrofuran (THF), and therefore preferred temperature is 163~230 ℃, in this temperature range, is reflected under the normal pressure and can carries out.
Said heteropolyacid has following general formula: H
8-xMZ
12O
40.nH
2O, wherein M is selected from one of elements such as P, Si, B, Ge or As, preferably is selected from P or Si, and Z is selected from one of elements such as W, Mo or V, preferably W or Mo, x is the valency of M, n is the crystal water number.Among the present invention, the crystal water number is to not influence of reaction result.
The said catalyzer that contains heteropolyacid comprises the heteropolyacid catalyst and the carried heteropoly acid catalyst of not load.Wherein the used carrier of carried heteropoly acid catalyst can be a kind of in the porous materials such as aluminum oxide, silica gel, gac, sieve and silica-sesquioxide, titanium dioxide, diatomite, preferred aluminum oxide, silica gel and gac.The charge capacity of heteropolyacid can be 0.5~60% of a catalyzer gross weight, preferred 1~50%.Charge capacity is too high, and the stability of catalyzer can descend.The heteropolyacid catalyst of said not load and carried heteropoly acid catalyst all can be made by oneself according to a conventional method, also can buy from market.
Provided by the invention 1, the method for 4-butyleneglycol preparing tetrahydrofuran by dehydrating and cyclization owing to adopted the catalyzer that contains heteropolyacid, makes 1, and the treatment capacity of 4-butyleneglycol significantly improves, and every gram heteropolyacid per hour can handle 1,4-butyleneglycol 1000~2000 grams.For example, when temperature of reaction is 195 ± 1 ℃, adopt 20% silicotungstic heteropolyacid/gac as catalyzer, 1, the treatment capacity of 4-butyleneglycol can be up to 1579g/g heteropolyacid hour.
Method equipment provided by the invention is simple, does not need solvent, and used catalyzer does not need any pre-treatment before using.Wherein carried heteropoly acid catalyst not only can be used for fixed bed reaction, also can stop the degraded of heteropolyacid, has favorable industrial application prospect.
Further specify the present invention below by embodiment, but not thereby limiting the invention.Embodiment 1
Present embodiment is the preparation of heteropolyacid.
With 20g sodium wolframate (Na
2WO
42H
2O, the CP level, Beijing Chemical Plant's product) and 10g SODIUM PHOSPHATE, MONOBASIC (CP level, Beijing Chemical Plant's product) be dissolved in the 40ml water, under 80 ℃, be evaporated to and thin crystalline film occurs, add 30ml hydrochloric acid, carry out aftertreatment through evaporation concentration to thickness, method is as follows: add ether and hydrochloric acid and extract, the oily matter that obtains is extracted through water again, after removing remaining ether, hydrochloric acid, crystallization just can obtain 8g phospho-wolframic acid (H
3PW
12O
40), code name is a.
Embodiment 2
Present embodiment is the preparation of heteropolyacid.
With 20g sodium wolframate Na
2WO
42H
2O (CP level, Beijing Chemical Plant's product) is with the 150ml water dissolution and add after hydrochloric acid (CP level, Beijing Chemical Plant's product) neutralizes, as solution A; At 2gNa
2SiO
39H
2Same dripping hydrochloric acid is isolated precipitation among the O, will precipitate to add in the solution A, boils, and filters out insolubles, carries out aftertreatment then, and post-treating method can obtain 9g silicotungstic acid (H with embodiment 1
4SiW
12O
40), code name is b.Embodiment 3
Present embodiment is the preparation of carried heteropoly acid catalyst.
Adopt immersion process for preparing, H
4SiW
12O
40With the weight ratio of silica gel be 1: 99.Earlier with H
4SiW
12O
40Add in the entry, treat that it dissolves fully after, again silica gel is added wherein, flood after 3 hours, in the shift-in loft drier,, promptly get the H of charge capacity 1% 110 ℃ of oven dry
4SiW
12O
40/ silica-gel catalyst A.
Embodiment 4
Present embodiment is the preparation of carried heteropoly acid catalyst.
Adopt immersion process for preparing, H
3PW
12O
40With the weight ratio of gac be 1: 9.Earlier with H
3PW
12O
40Add in the entry, treat that it dissolves fully after, again gac is added wherein, flood after 3 hours, in the shift-in loft drier,, promptly get charge capacity and be 10% H 80 ℃ of oven dry
3PW
12O
40/ activated-carbon catalyst B.
Embodiment 5
Present embodiment is the preparation of carried heteropoly acid catalyst.
Adopt immersion process for preparing, H
4SiW
12O
40With the weight ratio of gac be 1: 4.Earlier with H
4SiW
12O
40Add in the entry, treat that it dissolves fully after, again gac is added wherein, flood after 3 hours, in the shift-in loft drier,, promptly get charge capacity and be 20% H 110 ℃ of oven dry
4SiW
12O
40/ activated-carbon catalyst C.
Embodiment 6
Present embodiment is the preparation of carried heteropoly acid catalyst.
Adopt immersion process for preparing, H
3PW
12O
40And Al
2O
3Weight ratio be 1: 1.Earlier with H
3PW
12O
40Add in the entry, treat that it dissolves fully after, again with Al
2O
3Add wherein, flood after 3 hours, in the shift-in loft drier,, promptly get charge capacity and be 50% H 50 ℃ of oven dry
3PW
12O
40/ Al
2O
3Catalyzer D.
Embodiment 7
Present embodiment is the preparation of tetrahydrofuran (THF).
Getting phosphorus heteropoly tungstic acid a that 0.4g embodiment 1 the makes 1000ml that packs into has in the there-necked flask of stirring, and adding 575g 1, the 4-butyleneglycol, under the normal pressure temperature of reaction is risen to 190 ℃ ± 1 ℃, reaction steams product simultaneously, after reaction in 1 hour, steam product 568.4g altogether, with gc analysis (PEG 20000 packed columns, FID detects), the results are shown in Table 1.
Embodiment 8
Present embodiment is the preparation of tetrahydrofuran (THF).
Get silicotungstic heteropolyacid b that 0.4g embodiment 2 makes as catalyzer, add 590g 1, the 4-butyleneglycol, except that temperature of reaction is 188 ℃ ± 1 ℃, other condition after reacting in 1 hour, steams product 579.6g with embodiment 1 altogether, and reaction result sees Table 1.
Embodiment 9
Present embodiment is the preparation of tetrahydrofuran (THF).
Getting 40g catalyst A (heteropolyacid content the is 0.4 gram) 1000ml that packs into has in the there-necked flask of stirring, and adding 450g 1, the 4-butyleneglycol, under the normal pressure temperature of reaction is risen to 185 ± 1 ℃, reaction steams product simultaneously, after reaction in 1 hour, steam product 412.4g altogether, with gc analysis (PEG20000 packed column, FID detects), the results are shown in Table 1.
Embodiment 10
Present embodiment is the preparation of tetrahydrofuran (THF).
Getting 4g catalyst B (heteropolyacid content the is 0.4 gram) 1000ml that packs into has in the there-necked flask of stirring, and adds 600g 1,4-butyleneglycol, except that temperature of reaction was 203 ± 1 ℃, other condition was with embodiment 9, after reaction in 1 hour, steam product 524.4g altogether, reaction result sees Table 1.
Embodiment 11
Present embodiment is the preparation of tetrahydrofuran (THF).
Getting 2g catalyzer C (heteropolyacid content the is 0.4 gram) 1000ml that packs into has in the there-necked flask of stirring, and adds 700g 1,4-butyleneglycol, except that temperature of reaction was 195 ± 1 ℃, other condition was with embodiment 9, after reaction in 1 hour, steam product 613.7g altogether, reaction result sees Table 1.
Embodiment 12
Present embodiment is the preparation of tetrahydrofuran (THF).
Get the 0.8g catalyzer D 1000ml that packs into and have in the there-necked flask of stirring, and add 424g 1, the 4-butyleneglycol, except that temperature of reaction is 215 ± 1 ℃, other condition after reacting in 1 hour, steams product 409.6g with embodiment 9 altogether, and reaction result sees Table 1.Comparative Examples 1
Press the embodiment 1 among the US 4665205, as catalyzer, under normal pressure, 130 ℃ of conditions, per hour advance 1 with the sulfuric acid of 1.0g 97%, 4-butyleneglycol 90g, reaction result sees Table 1.
Table 1
Embodiment | Embodiment 7 | Embodiment 8 | Embodiment 9 | Embodiment 10 | Embodiment 11 | Embodiment 12 | Comparative Examples 1 * |
Catalyzer | a | b | A | B | C | D | Sulfuric acid |
Temperature of reaction, ℃ | 190±1 | 188±1 | 185±1 | 203±1 | 195±1 | 215±1 | 130 |
Reaction pressure, MPa | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 |
1,4-butyleneglycol treatment capacity, h -1 | 1421 | 1449 | 1013 | 1311 | 1579 | 1024 | 90 |
The tetrahydrofuran (THF) selectivity, mol% | 99.8 | 99.7 | 99.7 | 99.8 | 99.8 | 99.8 | 100 |
Annotate:
1.
*Get by the data computation of embodiment among the US4665205 1.
Claims (9)
1. 1, the method for 4-butyleneglycol preparing tetrahydrofuran by dehydrating and cyclization is characterized in that, under 130~250 ℃, will contain the catalyzer and 1 of heteropolyacid, and the contact of 4-butyleneglycol is reacted, and said heteropolyacid has following general formula: H
8-xMZ
12O
40.nH
2O, wherein M is selected from one of P, Si, B, Ge or As element, and Z is selected from one of W, Mo or V element, and x is the valency of M, and n is the crystal water number.
2. in accordance with the method for claim 1, it is characterized in that temperature of reaction is 163~230 ℃.
3. in accordance with the method for claim 1, it is characterized in that pressure is 0.1~1MPa.
4. in accordance with the method for claim 3, it is characterized in that pressure is 0.1~0.5MPa.
5. in accordance with the method for claim 1, it is characterized in that M is selected from P or Si, Z is selected from W or Mo.
6. in accordance with the method for claim 1, it is characterized in that the said catalyzer that contains heteropolyacid is a carried heteropoly acid catalyst.
7. in accordance with the method for claim 6, it is characterized in that the used carrier of carried heteropoly acid catalyst is selected from one of aluminum oxide, silica gel, gac, sieve and silica-sesquioxide, titanium dioxide or diatomite.
8. in accordance with the method for claim 7, it is characterized in that the used carrier of carried heteropoly acid catalyst is selected from aluminum oxide, silica gel or gac.
9. in accordance with the method for claim 6, it is characterized in that the charge capacity of heteropolyacid is 0.5~60% of a catalyzer gross weight.