CN1099943C - Wood-plastic material - Google Patents
Wood-plastic material Download PDFInfo
- Publication number
- CN1099943C CN1099943C CN99111051A CN99111051A CN1099943C CN 1099943 C CN1099943 C CN 1099943C CN 99111051 A CN99111051 A CN 99111051A CN 99111051 A CN99111051 A CN 99111051A CN 1099943 C CN1099943 C CN 1099943C
- Authority
- CN
- China
- Prior art keywords
- plastic material
- ester
- waste
- wood
- cementing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a novel wood plastic material which is composed of waste polyethylene materials, lignocelluloses, red mud of industrial waste, etc. The wood plastic material is formed by the steps of compounding, kneading, high-temperature and high-pressure compounding, formation, material blocking, check, packaging and warehousing. The wood plastic material not only can replace wood packaging and bedding materials, but also can be used for building templates, floors, window frames, pallets, packaging box, etc. The mechanical property of the wood plastic material is equal to that of hardwood. The present invention can be pinned, sawed and planned, and has the advantages of little water absorption, little possibility of wetting, little possibility of deformation, low price, insect damage resistance, no fungus growth, acid and alkali resistance, shock resistance and strong stability, and the present invention is not only favourable for environmental protection and pollution prevention, but also protects natural resources.
Description
Technical field
The present invention relates to a kind of Wood-plastic material, relate to a kind of type material that forms by processing and fabricatings such as waste or used plastics and waste and old wood fibre and industrial residue red soil specifically.
Background technology
At present, along with science and technology development, various material of construction are enriching market, to satisfy the needs after people's living standard improves, particularly various and type material successively comes out, people's attention and attention have been subjected to, white pollution has also appearred thereupon, industrial residue etc., the serious pollution that has caused environment, influenced people's living space, on the other hand, the felling of forest has caused the loss of water and soil and the generation of natural disaster, for this reason, people are in order to protect environment, resources conseravtion, waste or used plastics that utilizes of trying every means all, waste and old wood fibre (comprises sawdust, the branch fork of trees, the tangerine bar, the chaff shell, Pericarppium arachidis hypogaeae etc.) and industrial residue etc. make new building material, but that more existing its mechanical property of building materials is compared with hardwood is not ideal enough, can not follow closely, saw, dig; Also have some water-absorbents too strong, non-moistureproof, the sheet material of making (as shaving board, saw a board) is yielding; Also have some expensive, in a word, existing material of construction is not ideal enough.
Summary of the invention
The invention provides a kind of Wood-plastic material that adopts waste or used plastics and processing and fabricatings such as waste and old wood fibre and industrial residue red soil to form.
The present invention is achieved in that it is made up of high density polyethylene(HDPE), waste polyethylene material, lignocellulose, industrial waste ballast red soil, light active calcium carbonate, four seasons the eleventh of the twelve Earthly Branches tetrol ester, triphenyl phosphite, 2.6-ditertbutylparacresol, double acid double phenol A ester, octabromo-diphenyl, ANTIMONY TRIOXIDE SB 203 99.8 PCT, chlorinatedpolyethylene, polyacrylic ester, calcium stearate, stearic acid, polyethylene wax, cementing agent, through with waste or used plastics go-no-go, cleaning, processing granulation; The preparation cementing agent; Compound through batching, kneading, High Temperature High Pressure again, moulding, fracture, check, packing warehouse-in form, and it is characterized in that it is the material of being made by the following weight proportion raw material:
Density polyethylene 2.0-8.0 waste polyethylene material 37.0-47.0
Lignocellulose 30.0-40.0 industrial waste ballast red soil 1.5-4.5
Light active calcium carbonate 0.5-3.5 four seasons the eleventh of the twelve Earthly Branches tetrol ester 0.25-0.35
Triphenyl phosphite 0.3 2.6-ditertbutylparacresol 0.4
Double acid double phenol A ester 0.4 octabromo-diphenyl 2.0-4.0
ANTIMONY TRIOXIDE SB 203 99.8 PCT 1.0 chlorinatedpolyethylenees 0.4
Polyacrylic ester 0.3 calcium stearate 0.2
Stearic acid 0.2 polyethylene wax 2.0-4.0
Cementing agent 1.0-5.0
It is prepared by the following weight proportion raw material to it is characterized in that described cementing agent:
Polyamide resin 89 triphenylphosphates 9
Paraffin 2.
The present invention compared with prior art, it not only may substitute wooden package and laying material, can also be used for products such as building template, floor, sash, pallet, tr; its mechanical property and hardwood are suitable, can follow closely, saw, dig, and water regain is little; moisture-sensitive is not yielding, low price; do not damaged by worms not long fungi, antiacid alkali by any; shock-resistant; stability is strong, is a kind of both favourable environmental protection, prevents and remedies pollution, again the Wood-plastic material that can protect national resource.
Embodiment
Embodiment
(1) through with waste or used plastics go-no-go, cleaning, processing granulation;
(2) be purchased polyamide resin 89Kg, triphenylphosphate 9Kg, paraffin 2Kg prepares cementing agent;
(3) (Kg) the following raw material that is equipped with and weighs,
Density polyethylene (HDPE) 5 waste polyethylene material 42
Lignocellulose 35 industrial waste ballast red soil 3
2 four seasons of light active calcium carbonate the eleventh of the twelve Earthly Branches tetrol ester 0.3
Triphenyl phosphite 0.3 2.6-ditertbutylparacresol 0.4
Double acid double phenol A ester 0.4 octabromo-diphenyl 3
ANTIMONY TRIOXIDE SB 203 99.8 PCT 1.0 chlorinatedpolyethylenees 0.4
Polyacrylic ester 0.3 calcium stearate 0.2
Stearic acid 0.2 polyethylene wax 3
Cementing agent 3
(4) through machinery mediate, High Temperature High Pressure is compound, moulding, fracture, check, packing warehouse-in, Wood-plastic material of the present invention.
Claims (2)
1, a kind of Wood-plastic material, it is made up of high density polyethylene(HDPE), waste polyethylene material, lignocellulose, industrial waste ballast red soil, light active calcium carbonate, four seasons the eleventh of the twelve Earthly Branches tetrol ester, triphenyl phosphite, 2.6-ditertbutylparacresol, double acid double phenol A ester, octabromo-diphenyl, ANTIMONY TRIOXIDE SB 203 99.8 PCT, chlorinatedpolyethylene, polyacrylic ester, calcium stearate, stearic acid, polyethylene wax, cementing agent, through with waste or used plastics go-on-go, cleaning, processing granulation; The preparation cementing agent; Compound through batching, kneading, High Temperature High Pressure again, moulding, fracture, check, packing warehouse-in form, and it is characterized in that: it is the material of being made by following weight (%) proportion raw material:
High density polyethylene(HDPE) 2.0-8.0 waste polyethylene material 37.0-47.0
Lignocellulose 30.0-40.0 industrial waste ballast red soil 1.5-4.5
Light active calcium carbonate 0.5-3.5 four seasons the eleventh of the twelve Earthly Branches tetrol ester 0.25-0.35
Triphenyl phosphite 0.3 2.6-ditertbutylparacresol 0.4
Double acid double phenol A ester 0.4 octabromo-diphenyl 2.0-4.0
ANTIMONY TRIOXIDE SB 203 99.8 PCT 1.0 chlorinatedpolyethylenees 0.4
Polyacrylic ester 0.3 calcium stearate 0.2
Stearic acid 0.2 polyethylene wax 2.0-4.0
Cementing agent 1.0-5.0.
2, Wood-plastic material according to claim 1, its feature also is: it is prepared described cementing agent by following weight (%) proportion raw material:
Polyamide resin 89
Triphenylphosphate 9
Paraffin 2.