CN109970432A

CN109970432A - A kind of slurry method of Nixing pottery

Info

Publication number: CN109970432A
Application number: CN201910391167.8A
Authority: CN
Inventors: 邓波; 朱嬉妹
Original assignee: Individual
Current assignee: Individual
Priority date: 2019-05-11
Filing date: 2019-05-11
Publication date: 2019-07-05

Abstract

The present invention relates to a kind of slurry methods of Nixing pottery.This method is the mud that pug is modulated into water content 50%~80%, then in the billet surface starching of Nixing pottery, after the mud layer that starching obtains is consistent with green body water content, repairs smooth by mud layer and repairs and scrape smooth, can carry out subsequent engraving.Using this method the stereovision of lively picture sense and rich solid can be shown after carrying out Nixing pottery and being made.

Description

A kind of slurry method of Nixing pottery

Technical field

The invention belongs to ceramic technology fields, and in particular to a kind of slurry method of Nixing pottery.

Background technique

Nixing pottery originates from Guangxi Qinzhou, away from modern existing more than 1300 years history.1915, Nixing pottery is obtained to be lifted in Panama Capable " first world exposition gold medal " is one of the important international Grand Prix obtained China ceramics circle early stage, enjoys and very high knowing Name degree.Nixing pottery is with the distinctive eastern mud (or five flower muds, white cream mud) in Qiezhou and western mud (or purplish red mud, red pottery mud) Clay raw material is made by two kinds of clay rational proportions through processes such as mud refining, forming, decoration, firings.Eastern mud and western mud The western two sides in the east of a river by the emperor himself are originated from respectively, and Middle East mud shale is fine and smooth, soft and moist, and plasticity and associativity are strong；Western mud shale is hard, fire resisting Property it is good, shrinking percentage is small, but plasticity and associativity are poor, and two kinds of clay chemical components composition has larger difference.Traditional Nixing pottery Mud and western mud are formed by the proportions of 6:4 or 5:5 to the east of usually, and the base mud of composition is fine and smooth with quality, plasticity is good, green compact The features such as intensity is high, furnace inner support degree is strong.The process distinction of Nixing pottery essentially consists in its product in the characteristic of other three big name potteries Artistic carving on, traditional artistic carving only makees the conventional engraving mode such as embossment, line engraving in billet surface, and picture sense is insufficient.

Summary of the invention

It is an object of the invention in view of the above-mentioned drawbacks in the prior art, provide a kind of slurry method of Nixing pottery, energy Enough after being carved, being fired, the stereovision of lively picture sense and rich solid is shown.

To achieve the above object, present invention employs following technical solutions:

A kind of slurry method of Nixing pottery, is the mud that pug is modulated into water content 50%~80%, then in Nixing pottery Billet surface starching, after the mud layer that starching obtains is consistent with green body water content, by mud layer repair it is smooth and repair scrape it is smooth, It can carry out subsequent engraving.

In above-mentioned technical proposal:

The modulator approach of the mud are as follows: after mixing pug plus water, cross 60~200 meshes, remove generation after standing 3~4d Upper water obtains the mud of final water content 50%~80%.Preferably, the pug is Nixing pottery yellow mud.Pug can also be with The either a variety of pug allotments of other pugs are selected to mix.

The mud layer with a thickness of 0.05~0.15mm, the thickness of thickness and a piece of paper piece is suitable.

The method of the starching is that mud slurry uniform is applied to billet surface with flat hairbrush.

The starching can be entire surface starching, be also possible to regional area starching, selection mainly according to type and The requirement of depiction.It is described repair it is smooth is carried out with sheet, it is described repair to scrape smooth carried out with horn film.

Further, 16~32h of standing is needed after mud layer is consistent with green body water content, then repair smooth and repaired and scrape It is smooth.

Compared with the prior art, present invention has an advantage that

Slurry method provided by the invention, effect are similar to and coat one layer of background on Nixing pottery green body, carve on this basis Resulting product is carved, the stereovision of lively picture sense and rich solid can be shown, and the progress of native country original mud can be used in it Slurrying, raw material sources are extensive, environmentally protective.In addition, this method is not limited to the application on Nixing pottery, it may extend to other kinds Ceramics, the variation of upper pulp color can also be determined by deploying the color of pug, to increase the more of depiction Sample and aesthetics.

Specific embodiment

To better understand the objects, features and advantages of the present invention, With reference to embodiment Further unrestricted detailed description is made to technical solution of the present invention.

By taking Nixing pottery pot base as an example, the step of slurry method of the present embodiment, is as follows:

1) first by Nixing pottery pot base shaving polishing, it is convenient for starching after reparation is smooth, pot base water content is 30%；

2) it after adding water to mix Nixing pottery yellow mud, sieves with 100 mesh sieve, to remove impurity and bulky grain sand, filters out mud, mud is quiet Only 3~4 days, the upper water of generation is removed, the water content of mud is 80% at this time；

3) carry out equably starching on pot base surface with flat hairbrush, can regional area starching, can also whole pot starching, then stand make The water content of mud layer is consistent with pot base surface, then after standing 24 hours, mud layer and pot base repaired with sheet it is smooth, then Mud layer repaired with horn film and scrapes smooth, the bonding process of spout, pot handle is then carried out, carries out repairing for abutting edge again after bonding It scrapes, hereafter can carry out the processes such as subsequent engraving, firing.

Claims

1. a kind of slurry method of Nixing pottery, it is characterised in that: pug is modulated into the mud of water content 50%~80%, then Mud layer is repaired smooth after the mud layer that starching obtains is consistent with green body water content in the billet surface starching of Nixing pottery It scrapes smooth with repairing, subsequent engraving can be carried out.

2. slurry method according to claim 1, which is characterized in that the modulator approach of the mud are as follows: by pug plus water After mixing, 60~200 meshes are crossed, the upper water of generation is removed after 3~4d of standing, obtains the mud of final water content 50%~80% Slurry.

3. slurry method according to claim 1 or 2, it is characterised in that: the pug is Nixing pottery yellow mud.

4. slurry method according to claim 1, it is characterised in that: the mud layer with a thickness of 0.05~0.15mm.

5. slurry method according to claim 1, it is characterised in that: the method for the starching is with flat hairbrush that mud is equal It is even to be applied to billet surface.

6. slurry method according to claim 1 or 5, it is characterised in that: the starching is entire surface starching or part Region starching.

7. slurry method according to claim 1, it is characterised in that: need to stand after mud layer is consistent with green body water content 16~32h, then repair it is smooth and repair scrape it is smooth.

8. slurry method according to claim 1 or claim 7, it is characterised in that: the reparation is smooth to be carried out with sheet, described It repairs to scrape and smooth be carried out with horn film.