CN109959557A - A kind of test device and measurement method of flaky material crease recovery coefficient - Google Patents
A kind of test device and measurement method of flaky material crease recovery coefficient Download PDFInfo
- Publication number
- CN109959557A CN109959557A CN201910354797.8A CN201910354797A CN109959557A CN 109959557 A CN109959557 A CN 109959557A CN 201910354797 A CN201910354797 A CN 201910354797A CN 109959557 A CN109959557 A CN 109959557A
- Authority
- CN
- China
- Prior art keywords
- flaky material
- screen resilience
- static side
- crease recovery
- moved end
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of flaky material crease recovery coefficient testing device specific technical solution is as follows: including push-press type tension pressurizing device, pressure sensor, the push-press type tension pressurizing device uses horizontal pressure, the device is divided into moved end and static side, it is moved from moved end with constant speed to static side, convenient for the distance between control sound end.The pressure sensor is put in static side, convenient for reacting the variation of flaky material screen resilience in pressure process at any time.Index -- the crease recovery coefficient of reflection flaky material crease recovery is obtained by image procossing, there is the advantages that simple and convenient, data are intuitive, and test effect is accurate.
Description
Technical field
The present invention relates to the flaky material performance test fields with certain elasticity, and in particular to a kind of flaky material wrinkle
Recovery factor test device and measurement method.
Background technique
Currently, with the continuous development of polymeric material field, existing flaky material performance indicator such as stiffness, pliability
The deficiencies of to reflect the practical performance of flaky material, therefore invention introduces the New Sets of reflection flaky material practical performance ---
Flaky material crease recovery coefficient.The competency degree that flaky material resists its overbending direction change in shape is known as flaky material wrinkle
Recovery factor can be used to the degree of rigidity for evaluating flaky material.
In life, textile material Western-style clothes, outdoor sports textile (such as sleeping bag, tent) and the industry of sheet are spun
Fabric (such as the airbag flaky material of receiving atmospheric pressure or various transmission belts), sheet more demanding to the practical value of its fabric
Material crease recovery coefficient directly reflects its fabric practicability performance;In industrial goods, such as metallic spring, organic matter is thin
Film etc. is more demanding to the crease resistant finishing of its material, and therefore, research flaky material crease recovery coefficient has biggish existing
Sincere justice.
Summary of the invention
In view of the deficiencies of the prior art, the present invention proposes a kind of flaky material crease recovery coefficient testing device and measurement sides
Method, a kind of flaky material crease recovery coefficient testing device specific technical solution are as follows:
A kind of flaky material crease recovery coefficient testing device, it is characterised in that: including push-press type tension pressurizing device, pressure
Force snesor (3), the push-press type tension pressurizing device are divided into moved end (1) and static side (5);
The pressure sensor (3) is put in static side (5), then clamping device (4) are equipped on the moved end (1), described
For sample material between the clamping device (4) and the pressure sensor (3), clamping device (4) clamping is described again
Sample material one end, the sample material other end abut against on the pressure sensor (3);
Moved end (1) is to drive sample material to move with constant speed to static side (5).
A kind of flaky material crease recovery coefficient testing method is specific as follows:
A kind of measurement method of flaky material crease recovery coefficient testing device, it is characterised in that: following steps are used,
Step 1: choosing the flaky material having a size of C, flaky material is arranged smooth;
Step 2: flaky material both ends are clamped in moved end and the static side of push-press type tension pressurizing device respectively;
Step 3: being equipped with preset recording distance set Q, Q={ s1,s2... ..., sn, s1To snIt is preset recording distance,
Equipped with the screen resilience set F for being initialized as empty set;
Step 4: successively to preset recording distance s each in preset recording distance set Qi:
It is pressurizeed to the movement of static side to flaky material by the moved end of push-press type tension pressurizing device, when moved end and static side
Distance reach preset recording distance siWhen, the moved end stop motion of push-press type tension pressurizing device;
Preset recording distance s is measured by mechanics sensoriCorresponding screen resilience fi, by screen resilience fiIt is added to screen resilience
In set F;
Obtain F={ f1,f2... ..., fn, si∈ Q, fi∈ F, i=1,2 ... n;
Step 5: obtaining point set P={ (si,fi)|si∈ Q, fi∈ F, i=1,2 ... n }, point set P is mapped in two-dimentional seat
In mark system, screen resilience is made -- range image;
Step 6: by screen resilience -- range image carries out data analysis and extracts crease recovery factor beta,
The crease recovery factor beta is specifically, according to screen resilience -- and range image finds out the corresponding slope of required point on curve
Absolute value k.
The invention has the benefit that insufficient for the flaky materials such as existing stiffness, pliability performance indicator
To reflect the status of the practicability index of flaky material, the New Set of reflection flaky material practical performance is introduced, and design one
Cover flaky material crease recovery coefficient testing device and method.The present invention obtains reflection flaky material wrinkle by image procossing and returns
Multiple index -- crease recovery coefficient has the advantages that simple and convenient, data are intuitive, and test effect is accurate.
Detailed description of the invention
Fig. 1 push-press type tension pressurizing device schematic diagram;
Fig. 2 screen resilience-range data variation diagram.
Specific embodiment
The preferred embodiments of the present invention will be described in detail with reference to the accompanying drawing, so that advantages and features of the invention energy
It is easier to be readily appreciated by one skilled in the art, so as to make a clearer definition of the protection scope of the present invention.
A kind of flaky material crease recovery coefficient testing device as shown in Figure 1:, including push-press type tension pressurizing device, pressure
Force snesor 3, the push-press type tension pressurizing device are divided into moved end 1 and static side 5, push-press type tension pressurizing device using horizontal plus
Pressure;
Pressure sensor 3 be put in static side 5, convenient for reacting the variation of flaky material screen resilience in pressure process at any time,
The sensitivity of pressure sensor will be according to flaky material to correct.
Clamping device 4 is installed on moved end 1, sample material is between clamping device 4 and pressure sensor 3, clamping
Sample material one end, the sample material other end abut against on pressure sensor 3 clamping of device 4 again;
Moved end 1 is to drive sample material to move with constant speed to static side 5.
A kind of test of flaky material crease recovery coefficient the following steps are included:
By flaky material to be measured arrange it is smooth after, be cut into the size of defined for warp, broadwise respectively.This example
The size of middle sample is through to a length of 5cm, a length of 2cm of broadwise.
Sample both ends are held on moved end and the static side of push-press type tension pressurizing device respectively, and it is in place to adjust flaky material institute
It sets.
It is pressurizeed to the movement of static side to fabric by push-press type tension pressurizing device moved end, when moved end is at a distance from static side
When reaching pre-determined distance, stops pressurization, screen resilience corresponding to pre-determined distance is measured by mechanics sensor;
The size for adjusting pre-determined distance, measures the screen resilience of multiple groups flaky material, by the size of the screen resilience measured and in advance
If screen resilience is made in distance -- range image simultaneously carries out data analysis, as shown in Figure 2.
Crease recovery coefficient extracts: according to screen resilience -- and range image finds out the absolute of the corresponding slope of required point on curve
Value is crease recovery factor beta.
According to screen resilience -- range image acquires, and 4mm goes out β=1.56
The big flaky material of rigidity, its usual crease recovery coefficient are bigger.Conversely, the flaky material that rigidity is small, usually
Its crease recovery coefficient is with regard to smaller.
Claims (2)
1. a kind of flaky material crease recovery coefficient testing device, it is characterised in that: including push-press type pressurizing device, pressure sensing
Device (3), the push-press type pressurizing device are divided into moved end (1) and static side (5);
The pressure sensor (3) is put in static side (5), and clamping device (4), the sample are equipped on the moved end (1)
For material between the clamping device (4) and the pressure sensor (3), the clamping device (4) is held on the sample
Material one end, the other end of the sample material abut against on the pressure sensor (3);
Moved end (1) drives sample material to move with constant speed to static side (5).
2. for a kind of measurement method of flaky material crease recovery coefficient testing device described in claim 1, it is characterised in that:
Using following steps,
Step 1: choosing the flaky material having a size of C, flaky material is arranged smooth;
Step 2: flaky material both ends are clamped in moved end and the static side of push-press type pressurizing device respectively;
Step 3: being equipped with preset recording distance set Q, Q={ s1,s2... ..., sn, s1To snIt is preset recording distance, is equipped with
It is initialized as the screen resilience set F of empty set;
Step 4: successively to preset recording distance s each in preset recording distance set Qi:
It is pressurizeed to the movement of static side to flaky material by the moved end of push-press type pressurizing device, when moved end reaches at a distance from static side
To preset recording distance siWhen, preset recording distance s is measured by mechanics sensoriCorresponding screen resilience fi, by screen resilience fiAdd
It is added in screen resilience set F;
Obtain F={ f1,f2... ..., fn, si∈ Q, fi∈ F, i=1,2 ... n;
Step 5: obtaining point set P={ (si,fi)|si∈ Q, fi∈ F, i=1,2 ... n }, point set P is mapped in two-dimensional coordinate system
In, screen resilience is made -- range image;
Step 6: by screen resilience -- range image carries out data analysis and extracts crease recovery factor beta,
The crease recovery factor beta is specifically, according to screen resilience -- and range image finds out the exhausted of the corresponding slope of required point on curve
To value k.