CN109942857A - A kind of explosion-proof release film - Google Patents
A kind of explosion-proof release film Download PDFInfo
- Publication number
- CN109942857A CN109942857A CN201910142231.9A CN201910142231A CN109942857A CN 109942857 A CN109942857 A CN 109942857A CN 201910142231 A CN201910142231 A CN 201910142231A CN 109942857 A CN109942857 A CN 109942857A
- Authority
- CN
- China
- Prior art keywords
- parts
- release
- stirred
- pet film
- explosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of explosion-proof release films, it include PET film, the PET film includes the corona surface by sided corona treatment, release layer is coated on the corona surface, the release layer is formed by being coated on corona surface after 58-65 parts of butanone, 20-60 parts of 120# gasoline, 10-25 parts of isopropanol, 75-85 parts of mould release, 18-25 parts of off-type force regulator, 10-14 parts of crosslinking agent, 3-6 parts of attachment additive, 3-8 parts of catalyst, 38-45 parts of toluene, 30-36 parts of ethyl ester hybrid modulation.Explosion-proof release film of the invention, can effective protection rupture pressure disc, and efficiently solve release film surface and have the problems such as crystal point, rainbow, piebald and lines, moreover it is possible to be effectively improved and control its stability, when use reduces the generation of defective products.
Description
Technical field
The invention belongs to release technical field of membrane, and in particular to a kind of explosion-proof release film.
Background technique
Release film refers to that film surface can have the film of differentiation, and release film contacts under limited conditions with specific material
Do not have viscosity or slight viscosity afterwards.The surface of release film has one layer of release layer, and release layer is by mould release, additive etc.
Mixing preparation forms.Rupture pressure disc is suitble to all glasswares and breakable object, and being fitted in above glass and vehicle window can effectively prevent
It is not scattered after glass breaking, people and object will not be hurt, moreover it is possible to effectively prevent the radiation of ultraviolet light.It is used on existing rupture pressure disc
Explosion-proof release film, the disadvantages of there are crystal point, rainbow, piebald and lines on surface, seriously affected the appearance of rupture pressure disc product,
It is unfavorable for the sale of rupture pressure disc.
Summary of the invention
In order to solve the above technical problems, the technical solution adopted by the present invention is that: a kind of explosion-proof release film includes PET thin
Film, the PET film include the corona surface by sided corona treatment, are coated with release layer, the release layer on the corona surface
By 58-65 parts of butanone, 20-60 parts of 120# gasoline, 10-25 parts of isopropanol, 75-85 parts of mould release, 18-25 parts from
Type power regulator, 10-14 parts of crosslinking agent, 3-6 parts of attachment additive, 3-8 parts of catalyst, 38-45 parts of toluene, 30-
It is coated on corona surface and is formed after 36 parts of ethyl ester hybrid modulation.
PET film be optical grade high transparency PET film or plain edition biaxial stretching polyester PET film, the PET film
With a thickness of 12um-188um, the mould release is 7458 type mould releases of Dow Corning Corporation's production, and the off-type force regulator is
7201 type mould releases of Dow Corning Corporation's production, the crosslinking agent are 7672 type crosslinking agents of the Dow Chemical Company, the attachment addition
Agent is that 9176 types of the Dow Chemical Company adhere to additive, and the catalyst is 4000 type catalyst of the Dow Chemical Company.
Release layer by 60 parts of butanone, 30 parts of 120# gasoline, 10 parts of isopropanol, 82 parts of mould release, 18 parts from
Type power regulator, 13 parts of crosslinking agent, 4 parts of attachment additive, 5 parts of catalyst, 40 parts of toluene, the mixing of 30 parts of ethyl ester
It is coated on corona surface and is formed after modulation.
The hybrid modulation process of release layer successively includes:
1) prepared and diluted agent: toluene, butanone, ethyl ester, 120# gasoline and isopropanol, which are successively sequentially added into agitator, to be made
2 minutes formation mixed solvents are at the uniform velocity stirred with agitator air;
2) mould release is slowly added into the in the mixed solvent stirred evenly and continues stirring 10 minutes;
3) off-type force regulator is slowly added into again after small glass is first stirred with glass bar, is stirred 3 minutes;
4) crosslinking agent is slowly added into again after small glass is first stirred with glass bar, is stirred 2 minutes;
5) attachment additive is slowly added into again after small glass is first stirred with glass bar, is stirred 1 minute;
6) catalyst is slowly added into again after small glass is first stirred with glass bar, is stirred 2 minutes.
The beneficial effects of the present invention are: explosion-proof release film of the invention, can effective protection rupture pressure disc, and effectively solve
Release film surface has the problems such as crystal point, rainbow, piebald and lines, moreover it is possible to be effectively improved and control its stability, when use subtracts
The generation of few defective products.
Specific embodiment
Embodiment 1
A kind of explosion-proof release film, includes PET film, and the PET film includes the corona surface by sided corona treatment, institute
It states and is coated with release layer on corona surface, the release layer is by 58 parts of butanone, 20 parts of 120# gasoline, 10 parts of isopropanol, 75
Part mould release, 18 parts of off-type force regulator, 10 parts of crosslinking agent, 3 parts of attachment additive, 3 parts of catalyst, 38 parts
It is coated on corona surface and is formed after toluene, 30 parts of ethyl ester hybrid modulation.PET film is optical grade high transparency PET film, described
The 7458 type mould releases of PET film produced with a thickness of 20um, the mould release for Dow Corning Corporation, the off-type force regulator
For 7201 type mould releases of Dow Corning Corporation's production, the crosslinking agent is 7672 type crosslinking agents of the Dow Chemical Company, and the attachment adds
9176 types that agent is the Dow Chemical Company are added to adhere to additive, the catalyst is 4000 type catalyst of the Dow Chemical Company.
The hybrid modulation process of release layer successively includes:
1) prepared and diluted agent: toluene, butanone, ethyl ester, 120# gasoline and isopropanol, which are successively sequentially added into agitator, to be made
2 minutes formation mixed solvents are at the uniform velocity stirred with agitator air;
2) mould release is slowly added into the in the mixed solvent stirred evenly and continues stirring 10 minutes;
3) off-type force regulator is slowly added into again after small glass is first stirred with glass bar, is stirred 3 minutes;
4) crosslinking agent is slowly added into again after small glass is first stirred with glass bar, is stirred 2 minutes;
5) attachment additive is slowly added into again after small glass is first stirred with glass bar, is stirred 1 minute;
6) catalyst is slowly added into again after small glass is first stirred with glass bar, is stirred 2 minutes.
Embodiment 2
A kind of explosion-proof release film, includes PET film, and the PET film includes the corona surface by sided corona treatment, institute
It states and is coated with release layer on corona surface, the release layer is by 65 parts of butanone, 60 parts of 120# gasoline, 25 parts of isopropanol, 85
Part mould release, 25 parts of off-type force regulator, 14 parts of crosslinking agent, 6 parts of attachment additive, 8 parts of catalyst, 45 parts
It is coated on corona surface and is formed after toluene, 36 parts of ethyl ester hybrid modulation.
PET film be plain edition biaxial stretching polyester PET film, the PET film with a thickness of 120um, it is described release
Agent is 7458 type mould releases of Dow Corning Corporation's production, and the off-type force regulator is that 7201 types of Dow Corning Corporation's production are release
Agent, the crosslinking agent are 7672 type crosslinking agents of the Dow Chemical Company, and the attachment additive is that the 9176 types attachment of the Dow Chemical Company adds
Add agent, the catalyst is 4000 type catalyst of the Dow Chemical Company.
Embodiment 3
A kind of explosion-proof release film, includes PET film, and the PET film includes the corona surface by sided corona treatment, institute
It states and is coated with release layer on corona surface, the release layer is by 60 parts of butanone, 30 parts of 120# gasoline, 10 parts of isopropanol, 82
Part mould release, 18 parts of off-type force regulator, 13 parts of crosslinking agent, 4 parts of attachment additive, 5 parts of catalyst, 40 parts
It is coated on corona surface and is formed after toluene, 30 parts of ethyl ester hybrid modulation.
PET film is PET film described in optical grade high transparency PET film with a thickness of 75um, and the mould release is road health
7458 type mould releases of Ning company production, the off-type force regulator is 7201 type mould releases of Dow Corning Corporation's production, described
Crosslinking agent is 7672 type crosslinking agents of the Dow Chemical Company, and the attachment additive is that 9176 types of the Dow Chemical Company adhere to additive, institute
State the 4000 type catalyst that catalyst is the Dow Chemical Company.
The preferred embodiment of the present invention has been described in detail above, it should be understood that those skilled in the art without
It needs creative work according to the present invention can conceive and makes many modifications and variations, therefore, all technologies in the art
Personnel are available by logical analysis, reasoning, or a limited experiment on the basis of existing technology under this invention's idea
Technical solution, all should be within the scope of protection determined by the claims.
Claims (4)
1. a kind of explosion-proof release film, which is characterized in that include PET film, the PET film includes by sided corona treatment
Corona surface, is coated with release layer on the corona surface, the release layer by 58-65 parts of butanone, 20-60 parts of 120# gasoline,
10-25 parts of isopropanol, 75-85 parts of mould release, 18-25 parts of off-type force regulator, 10-14 parts of crosslinking agent, 3-6 parts
It is coated on corona surface after adhering to additive, 3-8 parts of catalyst, 38-45 parts of toluene, 30-36 parts of ethyl ester hybrid modulation
It is formed.
2. explosion-proof release film as described in claim 1, which is characterized in that the PET film is optical grade high transparency PET film
Or plain edition biaxial stretching polyester PET film, the PET film with a thickness of 12um-188um, the mould release is DOW CORNING
7458 type mould releases of company's production, the off-type force regulator are 7201 type mould releases of Dow Corning Corporation's production, the friendship
Join the 7672 type crosslinking agents that agent is the Dow Chemical Company, the attachment additive is that 9176 types of the Dow Chemical Company adhere to additive, described
Catalyst is 4000 type catalyst of the Dow Chemical Company.
3. explosion-proof release film as claimed in claim 2, which is characterized in that the release layer by 60 parts butanone, 30 parts
120# gasoline, 10 parts of isopropanol, 82 parts of mould release, 18 parts of off-type force regulator, 13 parts of crosslinking agent, 4 parts of attachment
It is coated on corona surface and is formed after additive, 5 parts of catalyst, 40 parts of toluene, 30 parts of ethyl ester hybrid modulation.
4. explosion-proof release film as claimed in claim 3, which is characterized in that the hybrid modulation process of the release layer is successively wrapped
It includes:
1) prepared and diluted agent: toluene, butanone, ethyl ester, 120# gasoline and isopropanol are successively sequentially added into agitator and use gas
Dynamic blender at the uniform velocity stirs 2 minutes formation mixed solvents;
2) mould release is slowly added into the in the mixed solvent stirred evenly and continues stirring 10 minutes;
3) off-type force regulator is slowly added into again after small glass is first stirred with glass bar, is stirred 3 minutes;
4) crosslinking agent is slowly added into again after small glass is first stirred with glass bar, is stirred 2 minutes;
5) attachment additive is slowly added into again after small glass is first stirred with glass bar, is stirred 1 minute;
6) catalyst is slowly added into again after small glass is first stirred with glass bar, is stirred 2 minutes.