CN109880030A - One-step method prepares the high-efficiency water-reducing agent of poly-carboxylic acid of three arm branched structures - Google Patents
One-step method prepares the high-efficiency water-reducing agent of poly-carboxylic acid of three arm branched structures Download PDFInfo
- Publication number
- CN109880030A CN109880030A CN201910080973.3A CN201910080973A CN109880030A CN 109880030 A CN109880030 A CN 109880030A CN 201910080973 A CN201910080973 A CN 201910080973A CN 109880030 A CN109880030 A CN 109880030A
- Authority
- CN
- China
- Prior art keywords
- reducing agent
- solution
- poly
- carboxylic acid
- efficiency water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to the high-efficiency water-reducing agent of poly-carboxylic acid that one-step method prepares three arm branched structures, which is characterized in that this method has following processing step: using molecular weight regulator: 0.4~1%, acrylic acid: 16~20%, deionized water: 76~81%, stirring and dissolving, it is uniformly mixed, obtains solution A；Using trihydroxylic alcohol: 0.035~0.4%, unsaturated polyether: 41~47%, oxidant: 0.8~3%, deionized water: 51~53%, stirring dissolves unsaturated polyether, is uniformly mixed, obtains B solution；25~40 DEG C, solution A is added dropwise into B solution under constant temperature, stirring condition, rate of addition is 5~20 drops/min, the volume ratio of solution A and B solution is 1:3,3~6 h of isothermal reaction again after being added dropwise, end of reaction, after being cooled to room temperature, pH to 6~7 is adjusted with liquid alkaline, the high-efficiency water-reducing agent of poly-carboxylic acid with three arm branched structures can be obtained.
Description
Technical field
The invention belongs to technical field of concrete additives, the in particular to polycarboxylic acids of three arm branched structures of one-step method preparation
High efficiency water reducing agent.
Background technique
High-efficiency water-reducing agent of poly-carboxylic acid is a kind of important concrete admixture, be by carboxylic unsaturated monomer with it is other
The random copolymer that unsaturated monomer is obtained by Raolical polymerizable, molecular structure are in comb shape, higher with water-reducing rate,
The features such as slump ongoing change is small, good with cement adaptability.
The addition of high-efficiency water-reducing agent of poly-carboxylic acid, not only substantially increases the mechanical property of concrete, and realizes construction
The modernization of technique.Application and development based on high-efficiency water-reducing agent of poly-carboxylic acid, concrete material and the modernization of different performance
Construction technology is rapidly developed.
With the high speed development of building trade, it is inadequate that the polycarboxylate water-reducer of comb shaped structure also gradually exposes water-reducing rate
The deficiencies of high, anti-mud performance is poor is not able to satisfy with the requirement for all kinds of concrete that Machine-made Sand is main fine aggregate.
In view of deficiency existing for comb shape polycarboxylate water-reducer, the application of high-efficiency water-reducing agent of poly-carboxylic acid in order to better improve,
Scientific research personnel has synthesized the new structural polycarboxylate water-reducer such as star, hyper-branched.
102887979 B(publication date 2014.02.05 of patent CN) report a kind of star high performance water reducing agent of polyocarboxy acid
Preparation method.This method passes through esterification under the action of catalyst and first prepares the polymerizable active end of star, then passes through freedom
Base polymerization generates chain " arm ", realizes the high performance water reducing agent of polyocarboxy acid of star-shaped molecule structure.This method passes through esterification system
The standby polymerizable active end of star, reaction process is reversible, and reaction is not thorough, and synthesis technology is complicated, is not suitable for industrialization.
106519143 B(publication date 2018.01.26 of patent CN) report the preparation of star-like polycarboxylate water-reducer a kind of
Method.This method passes through polymerization using double bond containing monomer, more group nucleating agents, initiator, terminal double bond polyoxyethylene ether as raw material
Star polycarboxylate water-reducer has been made in reaction.The initiator that this method uses is persulfate, and initiation temperature is high, and persulfuric acid
Salt can generate free radicals at high temperature and cause double bond monomer polymerization, and more group nucleating agents might not participate in reacting, resulting
Polycarboxylate water-reducer is not necessarily star structure.
106117468 B(publication date 2018.03.30 of patent CN) report the highly resistance mud of graft copolymerization cationic side chain
The preparation method of type cement water reducing agent.This method reacts then graft copolymerization by first polymerizeing resterification with cationic side chain
Method synthesizes diminishing agent material.This method is prepared by esterification, and reaction process is reversible, and reaction is not thorough, and is adopted
With multistep reaction, synthesis technology is complicated, is not suitable for industrialization.
High, synthesis step is required for monomer existing for the high-efficiency water-reducing agent of poly-carboxylic acid prepared in above-mentioned patent and initiation system
It is rapid it is more, be not easy the problem of industrialization, the present invention uses ammonium ceric nitrate for oxidant, and reacting containing three-arm arrangement trihydroxylic alcohol,
Hydroxyl in trihydroxylic alcohol is oxidized to free radical, the free radical generated using oxidation is caused the existing comb shape polycarboxylic acids for preparing and efficiently subtracted
The monomer of aqua prepares the high-efficiency water-reducing agent of poly-carboxylic acid of three arm branched structures, this method technique by aqueous solution polymerization one-step method
Simply, easy to operate, it is suitble to industrialization.
Summary of the invention
In view of the deficiencies of the prior art, the problem to be solved in the present invention is to provide one-step method to prepare the poly- of three arm branched structures
Carboxylic acid high efficiency water reducing agent.
The high-efficiency water-reducing agent of poly-carboxylic acid of novel three arms branched structure described in this patent, it is characterised in that: the water-reducing agent is
Such as the compound of graph structure formula:
Or
Wherein:
The purpose of the present invention is achieved through the following technical solutions.
One-step method prepares the high-efficiency water-reducing agent of poly-carboxylic acid of three arm branched structures, which is characterized in that this method has following work
Skill step:
(1) solution A is prepared: in the reactor, it is added by mass percentage concentration, polymerizable chain transfer agents: 0.4~1%, and acrylic acid: 16
~20%, deionized water: 76~81%, each group point is combined into absolutely, and stirring and dissolving is uniformly mixed, obtains solution A；
(2) B solution is prepared: it in the reactor, is added by mass percentage, trihydroxylic alcohol: 0.035~0.4%, and unsaturated polyether: 41
~47%, ammonium ceric nitrate: 0.8~3%, deionized water: 51~53%, being combined into absolutely for each group point is uniformly mixed, obtains
To B solution；
(3) B solution is added in the reactor, temperature rises to 20~40 DEG C, and solution A is added dropwise under constant temperature, stirring condition, and speed is added dropwise
Degree is 5~20 drops/min, and the volume ratio of solution A and B solution is 1:3, and 3~6 h of isothermal reaction again after being added dropwise has reacted
Finish, after being cooled to room temperature, adjusts pH to 6~7 with liquid alkaline to get the high-efficiency water-reducing agent of poly-carboxylic acid of three arm branched structures.
Step (1) chain-transferring agent is thioacetic acid or mercaptopropionic acid；
Step (2) trihydroxylic alcohol is glycerine, trimethylolethane, trimethylolpropane etc.；
Step (2) unsaturated polyether is allyl polyethenoxy base ether (HPEG) or prenol polyoxyethylene ether
(TPEG), molecular weight 2400；
The mass ratio of trihydroxylic alcohol and ammonium ceric nitrate described above is 1:10-18.
Beneficial effects of the present invention:
(1) present invention carries out aqueous solution polymerization as the free radical that oxidant causes to prepare with three arm branch using ammonium ceric nitrate
Change the high-efficiency water-reducing agent of poly-carboxylic acid of structure.From Molecular Design, the hydroxyl on trihydroxylic alcohol is aoxidized by ammonium ceric nitrate and is produced
Raw free radical, then causes polymerization of unsaturated monomers again, obtains the high-efficiency water-reducing agent of poly-carboxylic acid of three arm branched structures.
(2) high-efficiency water-reducing agent of poly-carboxylic acid for the three arm branched structures that the present invention obtains can effectively increase diminishing agent molecule to water
The adsorption capacity of mud particle, while there is more high water reducing rate and better anti-mud.
(3) present invention has the high-efficiency water-reducing agent of poly-carboxylic acid of three arm branched structures, this method technique using one-step method preparation
Simply, easy to operate, it is suitble to industrialization.
Specific embodiment
More to be stated in detail to specific implementation method of the present invention below, it is therefore intended that illustrate design of the invention and
Feature, it is not intended to limit the scope of the present invention.Any equivalent change or modification in accordance with the spirit of the invention,
It should be covered by the protection scope of the present invention.
Embodiment 1
(1) solution A is prepared: in the reactor, 0.19 g thioacetic acid, 1.8 g ammonium ceric nitrates, 5.3 g acrylic acid, 23 g is added
Deionized water, stirring and dissolving are uniformly mixed, obtain solution A；
(2) B solution is prepared: in the reactor, 0.1 g glycerine, 34 g TPEG2400,40g deionized waters is added, stirring makes
TPEG2400 dissolution, solution are uniformly mixed, and obtain B solution；
(3) B solution is added in the reactor, temperature rises to 35 DEG C, and solution A, rate of addition are added dropwise under constant temperature, stirring condition
For 8 drops/min, 4 h of isothermal reaction, end of reaction after being cooled to room temperature, adjust pH to 6-7 with liquid alkaline, i.e., again after being added dropwise
There must be the high-efficiency water-reducing agent of poly-carboxylic acid of three arm branched structures (labeled as PC1).
Embodiment 2
The present embodiment prepares the high-efficiency water-reducing agent of poly-carboxylic acid (label with three arm branched structures according to the identical mode of embodiment 1
For PC2), difference is only that the amount of ammonium ceric nitrate in step (1) is 0.5 g.
Embodiment 3
The present embodiment prepares the high-efficiency water-reducing agent of poly-carboxylic acid (label with three arm branched structures according to the identical mode of embodiment 1
For PC3), difference is only that the middle reaction time of step (2) is 3 h.
Embodiment 4
The present embodiment prepares the high-efficiency water-reducing agent of poly-carboxylic acid (label with three arm branched structures according to the identical mode of embodiment 1
For PC4), difference is only that the molecular weight of the middle prenol polyoxyethylene ether of step (2) is 1200.
Comparative example 1
75.053 g TPEG, 2400,85.617 g water is added into reactor, opens and stirs and be warming up to 60 DEG C, to polymeric monomer
After being completely dissolved, 1.893 g, 30% hydrogenperoxide steam generator is added, while it is 80% propylene that 11.17 g concentration, which are added dropwise, into reactor
The solution of aqueous acid and 0.130 g Vc and 0.289 g thioacetic acid and 16.467 g water composition；3 h are added dropwise in the former, after
3.5 h, the reaction was continued 1 h after band is added dropwise to complete is added dropwise in person, wait react at the end of adjust pH to 6-7, polycarboxylic acids is made and efficiently subtracts
Aqua.Labeled as PC5.
Comparative example 2
Commercially available high-efficiency water-reducing agent of poly-carboxylic acid.Labeled as PC6.
Performance test
1. flowing degree of net paste of cement
The measurement of flowing degree of net paste of cement according to GB/T 8077-2012 " test of concrete admixture homogeneity " defined into
Row.Wherein, 300 g of ordinary portland cement, the ratio of mud 0.29, effective volume of water-reducing agent are the 1 ‰ of cement quality, real
Method is mixed before testing use.
Measurement result of the 1 polycarboxylate water-reducer PC1-PC6 of table to flowing degree of net paste of cement
From table 1 it follows that the high-efficiency water-reducing agent of poly-carboxylic acid with three arm branched structures of the method for the present invention synthesis with it is identical
Traditional comb shape high-efficiency water-reducing agent of poly-carboxylic acid and commercially available comb shape high-efficiency water-reducing agent of poly-carboxylic acid in the case of sour ether ratio compare, performance
Good dispersibility and dispersion holding performance are gone out..
2. the anti-mud ability of water-reducing agent
Test measurement in the case that clay there are reach identical fluidity (260 ± 5 mm) when water-reducing agent volume, and with not
It is compared when mixing clay.Select newly synthesized traditional comb shaped structure high-efficiency water-reducing agent of poly-carboxylic acid and existing commercially available traditional comb
Shape polycarboxylic acid series high efficiency water reducing agent (comparative example) is as a comparison sample.
Non-clay test: 300 g cement, 87 g water, the dosage for adjusting water-reducing agent reach paste flowing degree in 10 min
To 260 ± 5 mm;The test of 1% clay: 297 g cement, 87 g water, 3 g clays, the dosage for adjusting water-reducing agent make paste flowing degree
Reach 260 ± 5 mm after 10 min.
Test result is shown in Table 2.
The anti-mud ability Contrast on effect table of 2 water-reducing agent of table
From Table 2, it can be seen that the high-efficiency water-reducing agent of poly-carboxylic acid with three arm branched structures of the method for the present invention synthesis is more traditional
The comb shape polycarboxylate water-reducer and commercially available comb shape polycarboxylate water-reducer that preparation method obtains show excellent anti-mud effect.
The above embodiment is a preferred embodiment of the present invention, but embodiments of the present invention are not by the limit of embodiment
System, other any changes made without departing from the spirit and principles of the present invention, modification, combination, substitution, simplification should be
Equivalence replacement mode, is included within the scope of the present invention.
Claims (6)
1. the high-efficiency water-reducing agent of poly-carboxylic acid that one-step method prepares three arm branched structures, which is characterized in that this method has following technique
Step:
(1) solution A is prepared: in the reactor, it is added by mass percentage concentration, polymerizable chain transfer agents: 0.4~1%, and acrylic acid: 16
~20%, deionized water: 76~81%, each group point is combined into absolutely, and stirring and dissolving is uniformly mixed, obtains solution A；
(2) B solution is prepared: it in the reactor, is added by mass percentage, trihydroxylic alcohol: 0.035~0.4%, and unsaturated polyether: 41
~47%, ammonium ceric nitrate: 0.8~3%, deionized water: 51~53%, being combined into absolutely for each group point is uniformly mixed, obtains
To B solution；
(3) B solution is added in the reactor, temperature rises to 20~40 DEG C, and solution A is added dropwise under constant temperature, stirring condition, and speed is added dropwise
Degree is 5~20 drops/min, and the volume ratio of solution A and B solution is 1:3, and 3~6 h of isothermal reaction again after being added dropwise has reacted
Finish, after being cooled to room temperature, adjusts pH to 6~7 with liquid alkaline to get the high-efficiency water-reducing agent of poly-carboxylic acid of three arm branched structures.
2. the high-efficiency water-reducing agent of poly-carboxylic acid that one-step method according to claim 1 prepares three arm branched structures, which is characterized in that
Step (1) chain-transferring agent is thioacetic acid or mercaptopropionic acid.
3. the high-efficiency water-reducing agent of poly-carboxylic acid that one-step method according to claim 1 prepares three arm branched structures, which is characterized in that
Step (2) described unsaturated polyether is that polyethers is allyl polyethenoxy base ether or prenol polyoxyethylene ether, molecular weight
It is 2400.
4. the high-efficiency water-reducing agent of poly-carboxylic acid that one-step method according to claim 1 prepares three arm branched structures, which is characterized in that
Step (2) trihydroxylic alcohol is glycerine, trimethylolethane, trimethylolpropane etc..
5. the high-efficiency water-reducing agent of poly-carboxylic acid that one-step method according to claim 1 prepares three arm branched structures, which is characterized in that
The mass ratio of step (2) trihydroxylic alcohol and ammonium ceric nitrate is 1:10-18.
6. the high-efficiency water-reducing agent of poly-carboxylic acid that one-step method according to claim 1 prepares three arm branched structures, which is characterized in that
It is characterized in that structural formula is as follows:
Or；
Wherein:。