CN109868000A - A kind of anti-dry spot additive and preparation method thereof and the application in aqueous cathode electrodip painting - Google Patents
A kind of anti-dry spot additive and preparation method thereof and the application in aqueous cathode electrodip painting Download PDFInfo
- Publication number
- CN109868000A CN109868000A CN201910245511.2A CN201910245511A CN109868000A CN 109868000 A CN109868000 A CN 109868000A CN 201910245511 A CN201910245511 A CN 201910245511A CN 109868000 A CN109868000 A CN 109868000A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- polyoxyethylene ether
- dry spot
- follows
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of anti-dry spot additives, alkyl imidazoline including 10-50 parts by weight, the acetylenic diols compound of 10-50 parts by weight, the acetylenic glycols polyoxyethylene ether of 10-50 parts by weight, the organosilicone polyoxyethylene ether of 0-30 parts by weight and the alkanolamide class compound of 0-30 parts by weight, this additive is used in commercially available commodity cathode electrophoresis dope, can be to avoid the generation of dry spot.
Description
Technical field
The present invention relates to chemical assistant technical fields, more particularly to a kind of anti-dry spot additive and its in aqueous cathode electricity
Application in swimming paint.
Background technique
Electrophoretic painting is one of coating metal workpiece most efficient method, electrophoretic coating as a kind of novel low pollution,
The energy, resource-saving, the coating for acting as protection and anticorrosive property are saved, automobile, automatic vehicle, electromechanics, household electrical appliances etc. five are widely used in
The coating of golden part.Electrophoretic coating can be divided into anode electrophoresis dope and cathode electrophoresis dope by by painting piece pole, and ability cathode electrophoresis applies
Material is divided into one-component electrophoretic coating and two-component electrophoretic coating.
Cathode electrodip painting when in use, coating link technique are as follows: electrophoresis → washing → baking and curing → subsequent technique, in reality
Border production process is it is possible that such problems: after workpiece takes out from electrophoresis tank, sometimes due to the operation reason of production line
The case where causing workpiece to hang waiting in air, cannot being washed immediately.And in this waiting process, due to wet film
There are inhomogeneities for performance of keeping humidity, and lacquer painting is caused locally to dehydrate, and the surface tension in washing at drying goes out in this way
Existing difference, repels the wetting action of water.So spot or patch phenomenon are shown in appearance herein, especially to large-scale workpiece
For, since its surface area is larger, the probability for dry spot occur can be relatively high.
Summary of the invention
The purpose of the present invention is dry spot is easy to appear between electrophoresis and washing for workpiece existing in the prior art
Problem, and a kind of anti-dry spot additive is provided.
It is a further object to provide a kind of application of anti-dry spot additive in aqueous cathode electrodip painting,
The additive can be used for can achieve expected improvement in commercially available commodity cathode electrophoresis dope.
The technical solution adopted to achieve the purpose of the present invention is:
A kind of anti-dry spot additive, the alkyl imidazoline including 10-50 parts by weight, the acetylenic diols of 10-50 parts by weight
Close object, the acetylenic glycols polyoxyethylene ether of 10-50 parts by weight, the organosilicone polyoxyethylene ethers of 0-30 parts by weight and 0-30 parts by weight
Alkanolamide class compound, wherein
The molecular structural formula of the alkyl imidazoline are as follows:
R1For C11-17Hydrocarbon chain, X OH;
The molecular structural formula of the acetylenic diols compound are as follows:
R2For C2-5Saturated hydrocarbon chains;
The molecular structural formula of the acetylenic glycols polyoxyethylene ether are as follows:
M+n=1-35;R3For C3-5Saturated hydrocarbon chains;R4For H or CH3;
The molecular structural formula of the organosilicone polyoxyethylene ether are as follows:
A, b are not 0, R5For H or CH3;
The molecular structural formula of the alkanolamide class compound are as follows:
R6For C11-17Hydrocarbon chain;X is OH.
In the above-mentioned technical solutions, the parts by weight of the alkyl imidazoline are 10-30, the acetylenic diols compound
Parts by weight are 12.5-35, and the parts by weight of the acetylenic glycols polyoxyethylene ether are 10-20, the organosilicone polyoxyethylene ether
Parts by weight be 1-3, the parts by weight of the alkanolamide class compound are 2-6.
It in the above-mentioned technical solutions, further include the solvent and/or 0-35 weight of 0-40 parts by weight in the anti-dry spot additive
Measure the water of part.
In the above-mentioned technical solutions, the anti-dry spot additive is prepared by the following method:
Step 1, under the conditions of 80-90 DEG C, in proportion by the alkanolamide class compound, alkyl imidazoline and acetylenic glycols
Class compound is uniformly mixed, and adjusting pH is 5-7;
Step 2, under the conditions of Yu Wendu 60-80 DEG C, the acetylenic glycols polyoxyethylene ether and organosilicon are added according still further to ratio
Polyoxyethylene ether stirs evenly, and obtains the anti-dry spot additive.
Another aspect of the present invention further includes application of the anti-dry spot additive in aqueous cathode electrodip painting.
Another aspect of the present invention, a kind of anti-dry spot additive, by the alkyl imidazoline of 10-50 parts by weight, 10-50 weight
The acetylenic diols compound of part, the acetylenic glycols polyoxyethylene ether of 10-50 parts by weight, the organosilicone polyoxyethylene ether of 0-30 parts by weight
It is formed with the water of the alkanolamide class compound of 0-30 parts by weight, the solvent of 0-40 parts by weight and 0-35 parts by weight, wherein
The molecular structural formula of the alkyl imidazoline are as follows:
R1For C11-17Hydrocarbon chain, X OH;
The molecular structural formula of the acetylenic diols compound are as follows:
R2For C2-5Saturated hydrocarbon chains;
The molecular structural formula of the acetylenic glycols polyoxyethylene ether are as follows:
M+n=1-35;R3For C3-5Saturated hydrocarbon chains;R4For H or CH3;
The molecular structural formula of the organosilicone polyoxyethylene ether are as follows:
A, b are not 0, R5For H or CH3;
The molecular structural formula of the alkanolamide class compound are as follows:
R6For C11-17Hydrocarbon chain;X is OH;
The solvent is in ethylene glycol, butyl glycol ether, propylene glycol, dipropylene glycol methyl ether, isopropanol or ethylene glycol phenyl ether
It is one or more.
In the above-mentioned technical solutions, the parts by weight of the alkyl imidazoline are 10-30, the acetylenic diols compound
Parts by weight are 12.5-35, and the parts by weight of the acetylenic glycols polyoxyethylene ether are 10-20, the organosilicone polyoxyethylene ether
Parts by weight be 1-3, the parts by weight of the alkanolamide class compound are 2-6, and the parts by weight of the solvent are 10-
20, the parts by weight of the water are 2.5-10.
In the above-mentioned technical solutions, the anti-dry spot additive is prepared by the following method:
Step 1, under the conditions of 80-90 DEG C, in proportion by the alkanolamide class compound, alkyl imidazoline and acetylenic glycols
Class compound is uniformly mixed, and adjusting pH is 5-7;
Step 2, under the conditions of 60-80 DEG C, the acetylenic glycols polyoxyethylene ether and organosilicon polyoxy are added according still further to ratio
Vinethene stirs evenly, and adds water and is uniformly dispersed after addition solvent, obtains the anti-dry spot additive.
Another aspect of the present invention further includes application of the anti-dry spot additive in aqueous cathode electrodip painting.
Compared with prior art, the beneficial effects of the present invention are:
1. can increase the mobility of paint film due to the mating reaction of alkyl imidazoline and acetylenic glycols polyoxyethylene ether, make
It obtains paint film and sprawls more uniform, raising drying uniformity, so that anti-dry spot additive application of the invention is in commercially available commodity yin
When in the electrophoretic coating of pole, have the function of it is good prevent paint film generate dryspot, the paint film appearance produced is more
It is smooth.
2. the preparation method of the anti-dry spot additive of the present invention is easy, mild condition is convenient for industrial application.
Specific embodiment
Below in conjunction with specific embodiment, invention is further described in detail.It should be appreciated that described herein specific
Embodiment is only used to explain the present invention, is not intended to limit the present invention.
Tu Yile AMINE C-17 (Carvedilol oil base hydroxyethyl imidazole quinoline, is originated from: the conspicuous Puffy in Tianjin is happy)
Tu Yile AMINE C-12 (cocoyl hydroxyethyl imidazole quinoline, is originated from: the conspicuous Puffy in Tianjin is happy)
Tu Yile FS-82 (3,6- dimethyl -4- octyne -3,6- glycol, is originated from: the conspicuous Puffy in Tianjin is happy)
Tu Yile FS-202 (4,7- dimethyl -5- decine -4,7- glycol, is originated from: the conspicuous Puffy in Tianjin is happy)
Tu Yile FS-204 (2,4,7,9- tetramethyl -5- decine -4,7- glycol, is originated from: the conspicuous Puffy in Tianjin is happy)
(2,5,8,11- tetramethyl -6- dodecyne alcohol -5,8- glycol, are originated from: Tianjin He Pufei Tu Yile FS-304
It is happy);
(2,5,8,11- tetramethyl -6- dodecyne alcohol -5,8- glycol polyethers, is originated from: day Tu Yile superwet-300
The conspicuous Puffy of saliva is happy)
Tu Yile superwet-300 includes applying easily happy superwet-320 (EO=4-5) and superwet-340 (EO=
6-8);
(2,4,7,9- tetramethyl -5- decine -4,7- glycol polyoxyethylene ether, is originated from: Tianjin He Pufei Tu Yile FS-600
It is happy)
Tu Yile FS-600 includes applying easily happy FS-640 (EO=4-5) and FS-680 (EO=20-30);
(organosilicone polyoxyethylene ether originates from Tego wet 270: Evonik)
Novol 1131 (alkanolamide originates from: flower king);
Solvent is domestic commercial product.Ethylene glycol, butyl glycol ether, propylene glycol, dipropylene glycol methyl ether, isopropanol or second two
One of alcohol phenylate is a variety of.
For evaluating additive disclosed in this invention in the formula of electrophoretic coating are as follows:
Component | Dosage |
F1 electrophoresis lotion | 40% |
Wherein: dispersion resin 1# | 38% |
Dry spot additive | 0.6% |
Defoaming agent | 0.3% |
F2 electrophoresis mill base | 11% |
Wherein: catalyst DBTO | 0.3% |
Kaolin | 1% |
Titanium dioxide | 1% |
Water | 49% |
The preparation of F2 electrophoresis mill base: after high speed dispersion, pigments and fillers high speed dispersion 30min is added in water in dispersion resin, turns
Sand mill 1800rpm is moved to, 2h is ground, until fineness≤10 μm.
The application method of this coating are as follows:
The F1 of coating, F2 are poured into 2000mm × 500mm × 1500mm electrophoresis tank after mixing slot, be put into
The surface treated steel plate of 1500mm × 6mm × 1000mm, and connected with cathode, it opens electrophoretic painting and sets
It is standby, electrophoresis experiment is completed according to coating equipment condition;Workpiece is taken out, hangs 15 minutes, workpiece is then rinsed with water, after stopping
There is color lump spot in observation workpiece surface;Workpiece is toasted, workpiece surface is observed after taking-up and the shape of color lump spot occurs
Condition.The improvement result of dry spot additive is judged according to the spot quantity of dry film and wet film.
Deposition condition: tank liquor temperature (30 ± 1) DEG C, 180~280V of voltage, time 150s, interpolar are away from 15~20cm, ultimate ratio
1: 4,175 DEG C of baking temperature, baking time 20min.
Embodiment 1-10
According to electrophoretic coating formula rate of the present invention, electrophoretic coating is made with the dry spot additive for being formulated different, presses
According to the coating application method, same execution conditions is taken to carry out coating.The formula of dry spot additive see the table below:
Embodiment | 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 |
AMINE C-12 | 0 | 10 | 0 | 10 | 0 | 0 | 50 | 0 | 15 | 0 |
AMINE C-17 | 20 | 0 | 10 | 10 | 30 | 40 | 0 | 0 | 0 | 15 |
FS-82 | 2.5 | 2.5 | 0 | 0 | 0 | 6 | 10 | 0 | 20 | 0 |
FS-202 | 0 | 0 | 2.5 | 3 | 5 | 0 | 0 | 30 | 0 | 30 |
FS-204 | 10 | 0 | 10 | 0 | 0 | 0 | 0 | 0 | 0 | 0 |
FS-304 | 0 | 10 | 0 | 10 | 30 | 0 | 0 | 0 | 0 | 0 |
FS-640 | 10 | 0 | 20 | 0 | 0 | 10 | 0 | 0 | 15 | 5 |
FS-680 | 0 | 50 | 0 | 0 | 20 | 0 | 0 | 0 | 15 | 0 |
superwet-320 | 0 | 0 | 30 | 0 | 0 | 0 | 15 | 0 | 0 | 10 |
superwet-340 | 0 | 0 | 0 | 40 | 15 | 0 | 0 | 15 | 0 | 0 |
Tego wet 270 | 2.5 | 0 | 3 | 1 | 0 | 0 | 15 | 0 | 15 | 0 |
Nivol 1131 | 0 | 5 | 2 | 6 | 0 | 0 | 0 | 15 | 10 | 20 |
Solvent | 20 | 20 | 20 | 10 | 0 | 10 | 5 | 40 | 10 | 0 |
Water | 35 | 2.5 | 2.5 | 10 | 0 | 34 | 5 | 0 | 0 | 20 |
It is total | 100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 |
The embodiment 1-10's the preparation method is as follows:
Step 1, under the conditions of 80-90 DEG C, in proportion by the alkanolamide class compound, alkyl imidazoline and acetylenic glycols
Class compound is uniformly mixed, and adjusting pH is 5-7;
Step 2, under the conditions of temperature 60 C, the acetylenic glycols polyoxyethylene ether and organosilicon polyoxy are added according still further to ratio
Vinethene stirs evenly, and adds solvent or adds water, the anti-dry spot additive is obtained after being uniformly dispersed.
During the preparation process, when temperature parameter and pH change in the range in the preparation method, gained dry spot additive
Performance is identical.
Comparative example 1
Electrophoretic coating formula rate as described above is made without dry spot additive electrophoretic coating, according to the coating
Application method takes same execution conditions to carry out coating.
Performance verification is carried out to embodiment 1-10 and comparative example 1, obtains result as shown in the table.
It can be seen that dry spot additive of the invention of the invention by the above table to be added in cathode electrodip painting and can improve
Dryspot during electrophoretic painting has the function of the paint film appearance positive.
The above is only a preferred embodiment of the present invention, it is noted that for the common skill of the art
For art personnel, various improvements and modifications may be made without departing from the principle of the present invention, these improvements and modifications
Also it should be regarded as protection scope of the present invention.
Claims (9)
1. a kind of anti-dry spot additive, which is characterized in that the alkyl imidazoline including 10-50 parts by weight, the alkynes of 10-50 parts by weight
Glycol compound, the acetylenic glycols polyoxyethylene ether of 10-50 parts by weight, the organosilicone polyoxyethylene ether and 0-30 of 0-30 parts by weight
The alkanolamide class compound of parts by weight, wherein
The molecular structural formula of the alkyl imidazoline are as follows:
R1For C11-17Hydrocarbon chain, X OH;
The molecular structural formula of the acetylenic diols compound are as follows:
R2For C2-5Saturated hydrocarbon chains;
The molecular structural formula of the acetylenic glycols polyoxyethylene ether are as follows:
M+n=1-35;R3For C3-5Saturated hydrocarbon chains;R4For H or CH3;
The molecular structural formula of the organosilicone polyoxyethylene ether are as follows:
A, b are not 0, R5For H or CH3;
The molecular structural formula of the alkanolamide class compound are as follows:
R6For C11-17Hydrocarbon chain;X is OH.
2. anti-dry spot additive as described in claim 1, which is characterized in that the parts by weight of the alkyl imidazoline are 10-
30, the parts by weight of the acetylenic diols compound are 12.5-35, and the parts by weight of the acetylenic glycols polyoxyethylene ether are 10-
20, the parts by weight of the organosilicone polyoxyethylene ether are 1-3, and the parts by weight of the alkanolamide class compound are 2-6.
3. anti-dry spot additive as described in claim 1, which is characterized in that further include 0-40 weight in the anti-dry spot additive
Measure the solvent of part and/or the water of 0-35 parts by weight.
4. anti-dry spot additive as described in claim 1, which is characterized in that be prepared by the following method:
Step 1, under the conditions of 80-90 DEG C, in proportion by the alkanolamide class compound, alkyl imidazoline and acetylenic diols
It closes object to be uniformly mixed, adjusting pH is 5-7;
Step 2, under the conditions of Yu Wendu 60-80 DEG C, the acetylenic glycols polyoxyethylene ether and organosilicon polyoxy are added according still further to ratio
Vinethene stirs evenly, and obtains the anti-dry spot additive.
5. application of the anti-dry spot additive in aqueous cathode electrodip painting as described in any one of claim 1-4.
6. a kind of anti-dry spot additive, which is characterized in that by the alkyl imidazoline of 10-50 parts by weight, the alkynes two of 10-50 parts by weight
Alcohol compound, the acetylenic glycols polyoxyethylene ether of 10-50 parts by weight, organosilicone polyoxyethylene ether and the 0-30 weight of 0-30 parts by weight
Measure the water composition of the alkanolamide class compound of part, the solvent of 0-40 parts by weight and 0-35 parts by weight, wherein
The molecular structural formula of the alkyl imidazoline are as follows:
R1For C11-17Hydrocarbon chain, X OH;
The molecular structural formula of the acetylenic diols compound are as follows:
R2For C2-5Saturated hydrocarbon chains;
The molecular structural formula of the acetylenic glycols polyoxyethylene ether are as follows:
M+n=1-35;R3For C3-5Saturated hydrocarbon chains;R4For H or CH3;
The molecular structural formula of the organosilicone polyoxyethylene ether are as follows:
A, b are not 0, R5For H or CH3;
The molecular structural formula of the alkanolamide class compound are as follows:
R6For C11-17Hydrocarbon chain;X is OH;
The solvent is one in ethylene glycol, butyl glycol ether, propylene glycol, dipropylene glycol methyl ether, isopropanol or ethylene glycol phenyl ether
Kind is a variety of.
7. anti-dry spot additive as claimed in claim 6, which is characterized in that the parts by weight of the alkyl imidazoline are 10-
30, the parts by weight of the acetylenic diols compound are 12.5-35, and the parts by weight of the acetylenic glycols polyoxyethylene ether are 10-
20, the parts by weight of the organosilicone polyoxyethylene ether are 1-3, and the parts by weight of the alkanolamide class compound are 2-6, institute
The parts by weight for stating solvent are 10-20, and the parts by weight of the water are 2.5-10.
8. anti-dry spot additive as claimed in claim 6, which is characterized in that be prepared by the following method:
Step 1, under the conditions of 80-90 DEG C, in proportion by the alkanolamide class compound, alkyl imidazoline and acetylenic diols
It closes object to be uniformly mixed, adjusting pH is 5-7;
Step 2, under the conditions of 60-80 DEG C, the acetylenic glycols polyoxyethylene ether and organosilicon polyoxyethylene are added according still further to ratio
Ether stirs evenly, and adds water and is uniformly dispersed after addition solvent, obtains the anti-dry spot additive.
9. application of the anti-dry spot additive in aqueous cathode electrodip painting as described in any one of claim 6-8.