CN109852881A - 一种45CrNiMoVA钎具用钢及其生产方法 - Google Patents
一种45CrNiMoVA钎具用钢及其生产方法 Download PDFInfo
- Publication number
- CN109852881A CN109852881A CN201910129156.2A CN201910129156A CN109852881A CN 109852881 A CN109852881 A CN 109852881A CN 201910129156 A CN201910129156 A CN 201910129156A CN 109852881 A CN109852881 A CN 109852881A
- Authority
- CN
- China
- Prior art keywords
- steel
- 45crnimova
- slag
- ingot
- drilling tool
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明具体涉及一种45CrNiMoVA钎具用钢,按照重量百分比,化学成分为C:0.43~0.47,Si:0.20~0.35,Mn:0.52~0.70,P≤0.015,S:≤0.012,Cr:0.82~1.00,Ni:1.32~1.70,Mo:0.21~0.28,V:0.11~0.18,Cu:≤0.15,其余为Fe及不控制的杂质。同时还提供了一种45CrNiMoVA钎具用钢的生产方法,包括如下工艺流程,高炉铁水→铁水预处理→50t电炉冶炼→精炼炉LF→真空脱气VD→浇铸3t电极锭→电渣重熔3t锭→均热炉加热→高压水除鳞→初轧机轧制→连轧机组→缓冷→退火→精整→探伤→检验→入库;采用50t电炉+LF+VD+3t电极锭+电渣重熔3t锭流程生产凿岩钎具用钢45CrNiMoVA,解决了高致密度、高纯净度钎具钢冶炼技术,有效控制钢质纯净度。
Description
技术领域
本发明属于钢产品生产技术领域,具体涉及一种45CrNiMoVA钎具用钢,以及提供了该钎具用钢的生产方法。
背景技术
随着我国工业的快速发展,国内各行业对矿山资源产品和电力能源的需求量不断增长,对钎钢、钎具质量要求越来越高。与国际先进钎具钢相比,我国钎钢的钢种成分制成的钎具产品使用寿命和质量相差较大,不能完全满足生产需要,本钢成功开发电炉+电渣重熔流程生产凿岩钎具用钢45CrNiMoVA,各项性能指标均达到高级优质要求,填补了钎具市场空白。
发明内容
本技术方案提供了一种45CrNiMoVA钎具用钢,按照重量百分比,化学成分为:C:0.43~0.47,Si:0.20~0.35,Mn:0.52~0.70,P≤0.015,S:≤0.012,Cr:0.82~1.00,Ni:1.32~1.70,Mo:0.21~0.28,V:0.11~0.18,Cu:≤0.15,其余为Fe及不控制的杂质。
进一步地,按照重量百分比,化学成分为,C:0.45、Si:0.26、Mn:0.65、P≤0.015、S:≤0.012、Cr:0.96、Mo:0.24、Ni:1.56、V:0.14、Cu:≤0.15,余量为Fe及不可避免的杂质。
根据本发明的另一方面还提供了一种45CrNiMoVA钎具用钢的生产方法,包括如下工艺流程,高炉铁水→铁水预处理→50t电炉冶炼→精炼炉LF→真空脱气VD→浇铸3t电极锭→电渣重熔3t锭→均热炉加热→高压水除鳞→初轧机轧制→连轧机组→缓冷→退火→精整→探伤→检验→入库;
电炉冶炼:在50t电炉冶炼过程中,通过均衡装料、控制电极升温时间、吹碳粉造泡沫渣等手段,监控炉内冶炼情况,碳达到目标要求后出钢脱氧合金化;
LF精炼:要求白渣操作,在保证渣流动性的条件下,控制渣碱度(CaO/SiO2)和渣中的氧势;对钢水时时检测,进行微调合金,保证钢水成分达到标准要求;
VD精炼:VD精炼为抽真空过程,在较高的真空度下真空脱气,以保证脱气效果和促进夹杂物上浮,要求真空25min以上,成分调整至满足内控要求后进行钙处理,使钢中的夹杂物进一步上浮进入渣中,提高了钢水纯净度;
电渣重熔3t锭:采用二元渣系,CaF2:Al2O3=70%:30%;
退火工艺:钢材以恒定升温速度加热到670±10℃,保温3h以上,然后出炉冷却,确保钢材组织均匀性。
采用50t电炉+LF+VD+3t电极锭+电渣重熔3t锭流程生产凿岩钎具用钢45CrNiMoVA,解决了高致密度、高纯净度钎具钢冶炼技术,有效控制钢质纯净度。精炼过程实现了Si、Mn、Cr、Ni、Mo、V成分的均匀控制,VD真空脱气处理,能够充分降低钢水中[O]、[H]等气体含量,钙处理保证夹杂物充分上浮,保证钢水纯净度。电渣重熔采用合理的二元渣系,保证钢质纯净度、致密度。加热过程保证电渣锭烧透,轧制过程进行控温轧制,减小了轧机对钢材抗力的影响,保证钢材组织的均匀性。合理的退火工艺后保证钢材组织均匀性,满足标准要求。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白,以下结合实施例,对本发明进行进一步详细说明。应当理解,此处所描述的具体实施例仅仅用以解释本发明,并不用于限定本发明。
本发明提供了一种45CrNiMoVA钎具用钢,按照重量百分比,化学成分为:C:0.43~0.47,Si:0.20~0.35,Mn:0.52~0.70,P≤0.015,S:≤0.012,Cr:0.82~1.00,Ni:1.32~1.70,Mo:0.21~0.28,V:0.11~0.18,Cu:≤0.15,其余为Fe及不控制的杂质。
作为方案的改进,按照重量百分比,化学成分为,C:0.45、Si:0.26、Mn:0.65、P≤0.015、S:≤0.012、Cr:0.96、Mo:0.24、Ni:1.56、V:0.14、Cu:≤0.15,余量为Fe及不可避免的杂质。
作为方案的改进,按照重量百分比,化学成分为,C:0.43、Si:0.35、Mn:0.70、P≤0.015、S:≤0.012、Cr:1.00、Mo:0.28、Ni:1.32、V:0.11、Cu:≤0.15,余量为Fe及不可避免的杂质。
作为方案的改进,按照重量百分比,化学成分为,C:0.47、Si:0.20、Mn:0.52、P≤0.015、S:≤0.012、Cr:0.82、Mo:0.21、Ni:1.70、V:0.18、Cu:≤0.15,余量为Fe及不可避免的杂质。
本发明还提供了一种45CrNiMoVA钎具用钢的生产方法,包括如下工艺流程,高炉铁水→铁水预处理→50t电炉冶炼→精炼炉LF→真空脱气VD→浇铸3t电极锭→电渣重熔3t锭→均热炉加热→高压水除鳞→初轧机轧制→连轧机组→缓冷→退火→精整→探伤→检验→入库;
电炉冶炼:在50t电炉冶炼过程中,通过均衡装料、控制电极升温时间、吹碳粉造泡沫渣等手段,监控炉内冶炼情况,碳达到目标要求后出钢脱氧合金化;
LF精炼:要求白渣操作,在保证渣流动性的条件下,控制渣碱度(CaO/SiO2)和渣中的氧势;对钢水时时检测,进行微调合金,保证钢水成分达到标准要求;
VD精炼:VD精炼为抽真空过程,在较高的真空度下真空脱气,以保证脱气效果和促进夹杂物上浮,要求真空25min以上,成分调整至满足内控要求后进行钙处理,使钢中的夹杂物进一步上浮进入渣中,提高了钢水纯净度;
电渣重熔3t锭:采用二元渣系,CaF2:Al2O3=70%:30%;
退火工艺:钢材以恒定升温速度加热到670±10℃,保温3h以上,然后出炉冷却,确保钢材组织均匀性。
通过上述工艺制得的45CrNiMoVA钎具用钢,
以上所述仅为本发明的较佳实施例而已,并不用以限制本发明,凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等,均应包含在本发明的保护范围之内。
Claims (3)
1.一种45CrNiMoVA钎具用钢,其特征在于:按照重量百分比,化学成分为C:0.43~0.47,Si:0.20~0.35,Mn:0.52~0.70,P≤0.015,S:≤0.012,Cr:0.82~1.00,Ni:1.32~1.70,Mo:0.21~0.28,V:0.11~0.18,Cu:≤0.15,其余为Fe及不控制的杂质。
2.如权利要求1所述的一种45CrNiMoVA钎具用钢,其特征在于:按照重量百分比,化学成分为,C:0.45、Si:0.26、Mn:0.65、P≤0.015、S:≤0.012、Cr:0.96、Mo:0.24、Ni:1.56、V:0.14、Cu:≤0.15,余量为Fe及不可避免的杂质。
3.一种45CrNiMoVA钎具用钢的生产方法,其特征在于:包括如下工艺流程,高炉铁水→铁水预处理→50t电炉冶炼→精炼炉LF→真空脱气VD→浇铸3t电极锭→电渣重熔3t锭→均热炉加热→高压水除鳞→初轧机轧制→连轧机组→缓冷→退火→精整→探伤→检验→入库;
电炉冶炼:在50t电炉冶炼过程中,通过均衡装料、控制电极升温时间、吹碳粉造泡沫渣等手段,监控炉内冶炼情况,碳达到目标要求后出钢脱氧合金化;
LF精炼:要求白渣操作,在保证渣流动性的条件下,控制渣碱度和渣中的氧势;对钢水时时检测,进行微调合金,保证钢水成分达到标准要求;
VD精炼:VD精炼为抽真空过程,在较高的真空度下真空脱气,以保证脱气效果和促进夹杂物上浮,要求真空25min以上,成分调整至满足内控要求后进行钙处理,使钢中的夹杂物进一步上浮进入渣中,提高了钢水纯净度;
电渣重熔3t锭:采用二元渣系,CaF2:Al2O3=70%:30%;
退火工艺:钢材以恒定升温速度加热到670±10℃,保温3h以上,出炉冷却。