CN109852093A - 一种再生改性塑料颗粒 - Google Patents

一种再生改性塑料颗粒 Download PDF

Info

Publication number
CN109852093A
CN109852093A CN201711244853.XA CN201711244853A CN109852093A CN 109852093 A CN109852093 A CN 109852093A CN 201711244853 A CN201711244853 A CN 201711244853A CN 109852093 A CN109852093 A CN 109852093A
Authority
CN
China
Prior art keywords
parts
plastic grain
regenerating
coupling agent
plastic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711244853.XA
Other languages
English (en)
Inventor
侯增海
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIANJIN CHUANHAO PLASTICS Co Ltd
Original Assignee
TIANJIN CHUANHAO PLASTICS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANJIN CHUANHAO PLASTICS Co Ltd filed Critical TIANJIN CHUANHAO PLASTICS Co Ltd
Priority to CN201711244853.XA priority Critical patent/CN109852093A/zh
Publication of CN109852093A publication Critical patent/CN109852093A/zh
Pending legal-status Critical Current

Abstract

本发明属于塑料领域，尤其涉及一种再生改性塑料颗粒，其特征在于，各组分按质量份数组成为：废旧塑料20‑50份，秸秆粉10‑20份，干燥椰壳粉10‑20份，木屑颗粒5‑10份，增塑剂1‑5份，相容剂1‑5份，稳定剂1‑5份，抗氧化剂1‑5份，偶联剂1‑5份。本发明利用秸秆粉、椰壳粉及木屑颗粒对废旧塑料进行改性，制备出新型的塑料颗粒，塑料颗粒韧性好，强度高，耐腐蚀性强，塑料颗粒的稳定性强，还原塑料本身的特点和性能，能够使塑料颗粒保持原塑料的固有特性；将废旧塑料再次利用，既节约社会资源，又保护环境。

Description

一种再生改性塑料颗粒
技术领域
本发明属于塑料领域，尤其涉及一种再生改性塑料颗粒。
背景技术
随着塑料制品消费量不断增大，废弃塑料也不断增多。另外，我国汽车用塑料年消费量已达40万吨，电子电器及家电配套用塑料年消费量已达100多万吨，这些产品报废后成了废塑料的重要来源之一。据了解，2004年国内废塑料已达约1100万吨。这些废塑料的存放、运输、加工等待被加工的废弃塑料原料应用及后处理若不得当，势必会破坏环境，危害百姓健康。
全球原油价格的升高，作为石油衍生物之一的塑料制品价格自然也水涨船高，废塑料的再生利用也被提到了首要的位置。废弃塑料的回收再利用已经被现代化工企业普遍采用。废塑料经过人工筛检分类后，还要经过破碎，造粒，改性等流程，变成各种透明不透明塑料颗粒，再按照品相进行分类，最后成为可以再次利用的再生料。
目前再生塑料往往都由多种废旧塑料混合制成，利用此种再生塑料制备的塑料制品的性能不稳定，因此有必要对现有技术中的再生塑料进行改性，增强其稳定性，还原塑料本身的特点和性能，使其保持塑料的固有特性。
发明内容
本发明针对上述技术问题，提供了一种再生改性塑料颗粒，塑料颗粒的稳定性强，能够保持塑料的固有特性。
本发明所采用的技术方案为：
一种再生改性塑料颗粒，其特征在于，各组分按质量份数组成为：废旧塑料20-50份，秸秆粉10-20份，干燥椰壳粉10-20份，木屑颗粒5-10份，增塑剂1-5份，相容剂1-5份，稳定剂1-5份，抗氧化剂1-5份，偶联剂1-5份。
各组分按较优质量份数组成为：废旧塑料35份，秸秆粉15份，干燥椰壳粉15份，木屑颗粒7份，增塑剂3份，相容剂3份，稳定剂3份，抗氧化剂3份，偶联剂3份。
所述增塑剂为邻苯二甲酸二辛酯、邻苯二甲酸二丁酯、邻苯二甲酸二异壬酯或DIDP邻苯二甲酸二异癸酯。
所述相容剂为马来酸酐接枝聚乙烯、马来酸酐接枝聚丙烯、马来酸酐接枝聚丁烯。
所述稳定剂为硬质酸钙、环氧树脂或硬脂酸锌。
所述抗氧化剂为萘胺、二苯胺、对苯二胺、对苯二酚或硫代双酚。
所述偶联剂为硅烷偶联剂。
本发明的有益效果为：
本发明利用秸秆粉、椰壳粉及木屑颗粒对废旧塑料进行改性，制备出新型的塑料颗粒，塑料颗粒韧性好，强度高，耐腐蚀性强，塑料颗粒的稳定性强，还原塑料本身的特点和性能，能够使塑料颗粒保持原塑料的固有特性；将废旧塑料再次利用，既节约社会资源，又保护环境。
具体实施方式
实施例1
一种再生改性塑料颗粒，各组分按质量份数组成为：废旧塑料20份（以清洗干净并粉碎后的塑料颗粒计），秸秆粉20份，干燥椰壳粉20份，木屑颗粒8份，增塑剂1份，相容剂5份，稳定剂4份，抗氧化剂2份，偶联剂1份。
增塑剂为DIDP邻苯二甲酸二异癸酯，相容剂为马来酸酐接枝聚丁烯，稳定剂为硬脂酸锌，抗氧化剂为硫代双酚，偶联剂为硅烷偶联剂。
按照如下步骤制备：
（1）将废旧塑料清洗干净，烘干后充分粉碎；
（2）将粉碎后的废旧塑料、秸秆粉、干燥椰壳粉、木屑颗粒添加到混料机中进行共混，共混速度为1000-2000r/min，时间为20-60分钟；
（3）向经过共混后的混合物中添加增塑剂、相容剂、稳定剂、抗氧化剂、偶联剂，混合均匀后，经造粒机加热至170℃时熔化，经磨头挤出块状物，然后破碎，得到再生改性塑料颗粒。
实施例2
一种再生改性塑料颗粒，各组分按质量份数组成为：废旧塑料50份（以清洗干净并粉碎后的塑料颗粒计），秸秆粉10份，干燥椰壳粉15份，木屑颗粒10份，增塑剂5份，相容剂1份，稳定剂2份，抗氧化剂3份，偶联剂5份。
增塑剂为DIDP邻苯二甲酸二异癸酯，相容剂为马来酸酐接枝聚丁烯，稳定剂为硬质酸钙，抗氧化剂为对苯二酚，偶联剂为硅烷偶联剂。
按照如下步骤制备：
（1）将废旧塑料清洗干净，烘干后充分粉碎；
（2）将粉碎后的废旧塑料、秸秆粉、干燥椰壳粉、木屑颗粒添加到混料机中进行共混，共混速度为1000-2000r/min，时间为20-60分钟；
（3）向经过共混后的混合物中添加增塑剂、相容剂、稳定剂、抗氧化剂、偶联剂，混合均匀后，经造粒机加热至170℃时熔化，经磨头挤出块状物，然后破碎，得到再生改性塑料颗粒。
实施例3
一种再生改性塑料颗粒，各组分按质量份数组成为：废旧塑料35份，秸秆粉15份，干燥椰壳粉15份，木屑颗粒7份，增塑剂3份，相容剂3份，稳定剂3份，抗氧化剂3份，偶联剂3份。
增塑剂为邻苯二甲酸二异壬酯，相容剂为马来酸酐接枝聚丁烯，稳定剂为硬脂酸锌，抗氧化剂为对苯二胺，偶联剂为硅烷偶联剂。
按照如下步骤制备：
（1）将废旧塑料清洗干净，烘干后充分粉碎；
（2）将粉碎后的废旧塑料、秸秆粉、干燥椰壳粉、木屑颗粒添加到混料机中进行共混，共混速度为1000-2000r/min，时间为20-60分钟；
（3）向经过共混后的混合物中添加增塑剂、相容剂、稳定剂、抗氧化剂、偶联剂，混合均匀后，经造粒机加热至170℃时熔化，经磨头挤出块状物，然后破碎，得到再生改性塑料颗粒。
实施例4
一种再生改性塑料颗粒，各组分按质量份数组成为：废旧塑料30份（以清洗干净并粉碎后的塑料颗粒计），秸秆粉15份，干燥椰壳粉20份，木屑颗粒5份，增塑剂2份，相容剂4份，稳定剂5份，抗氧化剂1份，偶联剂4份。
增塑剂为邻苯二甲酸二丁酯，相容剂为马来酸酐接枝聚丙烯，稳定剂为环氧树脂，抗氧化剂为二苯胺，偶联剂为硅烷偶联剂。
按照如下步骤制备：
（1）将废旧塑料清洗干净，烘干后充分粉碎；
（2）将粉碎后的废旧塑料、秸秆粉、干燥椰壳粉、木屑颗粒添加到混料机中进行共混，共混速度为1000-2000r/min，时间为20-60分钟；
（3）向经过共混后的混合物中添加增塑剂、相容剂、稳定剂、抗氧化剂、偶联剂，混合均匀后，经造粒机加热至170℃时熔化，经磨头挤出块状物，然后破碎，得到再生改性塑料颗粒。
实施例5
一种再生改性塑料颗粒，各组分按质量份数组成为：废旧塑料40份（以清洗干净并粉碎后的塑料颗粒计），秸秆粉10份，干燥椰壳粉10份，木屑颗粒10份，增塑剂4份，相容剂2份，稳定剂1份，抗氧化剂5份，偶联剂2份。
增塑剂为邻苯二甲酸二辛酯，相容剂为马来酸酐接枝聚乙烯，稳定剂为硬质酸钙，抗氧化剂为萘胺，偶联剂为硅烷偶联剂。
按照如下步骤制备：
（1）将废旧塑料清洗干净，烘干后充分粉碎；
（2）将粉碎后的废旧塑料、秸秆粉、干燥椰壳粉、木屑颗粒添加到混料机中进行共混，共混速度为1000-2000r/min，时间为20-60分钟；
（3）向经过共混后的混合物中添加增塑剂、相容剂、稳定剂、抗氧化剂、偶联剂，混合均匀后，经造粒机加热至170℃时熔化，经磨头挤出块状物，然后破碎，得到再生改性塑料颗粒。
以上对本发明的5个实施例进行了详细说明，但所述内容仅为本发明的较佳实施例，不能被认为用于限定本发明的实施范围。凡依本发明申请范围所作的均等变化与改进等，均应仍归属于本发明的专利涵盖范围之内。

Claims (7)

1.一种再生改性塑料颗粒，其特征在于，各组分按质量份数组成为：废旧塑料20-50份，秸秆粉10-20份，干燥椰壳粉10-20份，木屑颗粒5-10份，增塑剂1-5份，相容剂1-5份，稳定剂1-5份，抗氧化剂1-5份，偶联剂1-5份。
2.根据权利要求1所述的一种再生改性塑料颗粒，其特征在于，各组分按较优质量份数组成为：废旧塑料35份，秸秆粉15份，干燥椰壳粉15份，木屑颗粒7份，增塑剂3份，相容剂3份，稳定剂3份，抗氧化剂3份，偶联剂3份。
3.根据权利要求1或2所述的一种再生改性塑料颗粒，其特征在于，所述增塑剂为邻苯二甲酸二辛酯、邻苯二甲酸二丁酯、邻苯二甲酸二异壬酯或DIDP邻苯二甲酸二异癸酯。
4.根据权利要求1或2所述的一种再生改性塑料颗粒，其特征在于，所述相容剂为马来酸酐接枝聚乙烯、马来酸酐接枝聚丙烯、马来酸酐接枝聚丁烯。
5.根据权利要求1或2所述的一种再生改性塑料颗粒，其特征在于，所述稳定剂为硬质酸钙、环氧树脂或硬脂酸锌。
6.根据权利要求1或2所述的一种再生改性塑料颗粒，其特征在于，所述抗氧化剂为萘胺、二苯胺、对苯二胺、对苯二酚或硫代双酚。
7.根据权利要求1或2所述的一种再生改性塑料颗粒，其特征在于，所述偶联剂为硅烷偶联剂。
CN201711244853.XA 2017-11-30 2017-11-30 一种再生改性塑料颗粒 Pending CN109852093A (zh)