CN109826390A - The pseudo-classic floor tile of environment-friendly type and its production technology - Google Patents
The pseudo-classic floor tile of environment-friendly type and its production technology Download PDFInfo
- Publication number
- CN109826390A CN109826390A CN201910157789.4A CN201910157789A CN109826390A CN 109826390 A CN109826390 A CN 109826390A CN 201910157789 A CN201910157789 A CN 201910157789A CN 109826390 A CN109826390 A CN 109826390A
- Authority
- CN
- China
- Prior art keywords
- gold brick
- floor tile
- decorative layer
- layer
- gold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to building board fields, more specifically, it relates to the pseudo-classic floor tile of environment-friendly type.Its key points of the technical solution are that: including basal layer and gold brick decorative layer, adhesive layer is bonded between gold brick decorative layer and basal layer；Gold brick decorative layer is made of several pieces of decorating units；Wherein basal layer material is natural marble, artificial marble or plank.It by gold brick material in conjunction with common basal layer, that is, realizes and discarded gold brick is made full use of, a kind of floor tile for novel environment friendly of having got back enriches the type of floor tile.Gold brick material hardness is high, is conducive to the structural strength for increasing floor tile；Gold brick material seepage of water is fabulous, floor tile is used for ground, ground is not allowed to tend to have ponding；And gold brick material surface is frosting, it is not easy to be skidded.Gold brick decorative layer is made of several pieces of decorating units, on the one hand can use smaller discarded gold brick, on the other hand convenient for combining more patterns, increases the pattern of floor tile by diversification.
Description
Technical field
The present invention relates to building board fields, more specifically, it relates to the pseudo-classic floor tile of environment-friendly type and its production technology.
Background technique
The also known as imperial kiln gold brick of gold brick, is the treasure in Chinese tradition kiln brick firing industry, and ancient times specializes in the Important buildings such as palace
A kind of floor file square brick of the high quality used.
Gold brick is actually the large-scale fines square brick that specification is seven cun of two cun of two ruler, two rulers and a ruler square, because belonging to emperor
Family is dedicated, and paves the ground or floor and build the interior in main palace in Ming and Qing imperial family and to wanting position, have rivers and mountains is forever solid, family estate it is stable as
Sign means hard brick solid, Buddha's warrior attendant is not bad so being known as " gold brick ".It is civil also to have such explanation: to aim at imperial palace firing
Fines square brick, because particle exquisiteness, quality is closely knit, and that strikes makees the sound of metal and stone, and cost is huge, there is " one liang one piece of gold
Brick " is said, so claiming " gold brick.
The production technology of gold brick is extremely complex, and lasts up to even one or two years some months, meeting during production
Have certain disqualification rate, some gold bricks are also had during transport can be damaged, the reparation of imperial family's building require it is very strict,
Once it is unqualified or have breakage that will be dropped, it wastes very much.
Summary of the invention
In view of the deficienciess of the prior art, the purpose of the present invention one is to provide environment-friendly type pseudo-classic floor tile, it can be right
The gold brick of discarding is recycled, energy conservation and environmental protection.
Above-mentioned technical purpose one of the invention has the technical scheme that the pseudo-classic floor tile of environment-friendly type,
Including basal layer and gold brick decorative layer, adhesive layer is bonded between gold brick decorative layer and basal layer；Gold brick decorative layer is by several pieces
Decorating unit composition splicing forms, and gap is equipped between adjacent decoration unit, and the width in gap is less than 2mm；Wherein basal layer material
Matter is natural marble, artificial marble or plank.
By using above-mentioned technical proposal, by gold brick material in conjunction with common basal layer, that is, realize to discarded gold brick
Make full use of, a kind of floor tile for novel environment friendly of having got back enriches the type of floor tile.Gold brick material hardness is high, has
Conducive to the structural strength for increasing floor tile；Gold brick material seepage of water is fabulous, floor tile is used for ground, ground is not allowed to tend to have product
Water；And gold brick material surface is frosting, it is not easy to be skidded.Gold brick decorative layer is made of several pieces of decorating units, on the one hand
It can use smaller discarded gold brick, on the other hand convenient for combining more patterns, increase the pattern of floor tile
Diversification.Gold brick decorative layer is bonded on the base layer by adhesive layer, and structure is simple, and prepares also simpler, basal layer
Use be convenient for the stay aligned of decorating unit, and gold brick material needed for gold brick decorative layer is fewer, be conducive to save at
This.
Marble is from a wealth of sources, and cost compares lower；And marble and the compound of gold brick decorative layer can make ground
Brick structure intensity is stronger.It is lighter that the combination of plank and gold brick decorative layer sets floor tile weight, convenient for saving transportation cost, Er Qiemu
The surfaces versus rough of plate, relative to marble, plank and the bonding of gold brick decorative layer are more easier.
Temperature difference is bigger throughout the year, and decorating unit reserves certain gap, and when hot weather, decoration is single
Member expansion is not easy mutual extrusion deformation；And gap width will not influence whole structural strength less than 2mm.
The present invention is further arranged to: being equipped with gap between adjacent decoration unit, is filled with gap filler or compound in gap
Glue；Gap filler is the mixture of curing agent and glue.
By using above-mentioned technical proposal, the use of gap filler and compound adhesive is more conducive to the splicing of decorating unit, and decoration is single
First stitching portion is more smooth, and bonding is also stronger, a kind of lines of other style is also capable of forming at gap filler and compound adhesive, more
Design sense.
The present invention is further arranged to: the basal layer and the thickness of gold brick decorative layer ratio are (2-8): 1
By using above-mentioned technical proposal, from the perspective of cost, the cost of material and cost of manufacture of gold brick decorative layer are more
Basal layer and gold brick decorative layer are used in combination, greatly reduce cost by height, convenient for promoting；Substrate thickness is some, fills to gold brick
The undertaking effect for adoring layer is more preferable, conducive to the structural strength for improving gold brick ornamentally face brick.After tested, the thickness of gold brick decorative layer exists
0.5-2cm, can not only guarantee the structural strength of gold brick decorative layer, but also can control cost.
The purpose of the present invention two is to provide the production technology of the pseudo-classic floor tile of environment-friendly type, and processing step is simple, convenient for pushing away
Extensively, floor tile obtained can recycle the gold brick of discarding, energy conservation and environmental protection.
Above-mentioned technical purpose two of the invention has the technical scheme that the pseudo-classic floor tile of environment-friendly type
Production technology, comprising the following steps:
Step 1: the gold brick of recycling is thinly sliced；
Step 2: breaking gold brick thin slice in step 1 to form multiple decorating units；
Step 3: the decorating unit in step 2 is carried out splicing assembling；
Step 4: adding gap filler at the gap of adjacent decoration unit forms gold brick decorative layer, to gold brick after gap filler is dry
Decorative layer, which carries out polishing, keeps gold brick decor surface smooth；
Step 5: coating compound adhesive in gold brick decorative layer, basal layer is pressed together in gold brick decorative layer；Or on the base layer
Compound adhesive is coated, on the base layer by the pressing of gold brick decorative layer；Adjust the depth of parallelism of basal layer and gold brick decorative layer.
By using above-mentioned technical proposal, gold brick is cut into breaking convenient for step 2 after thin slice, and early period is sliced
It is more easier；Gold brick thin slice forms the decorating unit of irregular shape after being broken, then splices and assemble, and is formed a variety of more
The lines of sample enriches the aesthetic feeling of the design of floor tile；Gap filler keeps gap more obvious, and lines is also more obvious；Entire production
Simple process is convenient for commercial introduction without excessively professional worker without special equipment.
The present invention is further arranged to: gold brick is cut into the thin slice of 1-2cm in step 1；The medium gap filler of step 4 parches
Afterwards again by gold brick decorative layer to cutting at the thin slice of 0.5-1.5cm.
By using above-mentioned technical proposal, after tested, if gold brick is cut at the very start below thin with a thickness of 1cm
Piece is broken and splices the process of assembling after thin slice and be easy decorating unit is whole broken, therefore after first tentatively thinly slicing gold brick, beats
Broken, splicing be completed after again to cut open do not allow it is easily broken.
The present invention is further arranged to: by gold brick decorative layer to after cuing open again use gap filler joint filling.
By using above-mentioned technical proposal, to cuing open during may some are broken, can be with guarantee fund with gap filler joint filling
Brick decor surface it is smooth, product quality is higher.
The present invention is further arranged to: uniformly being applied compound adhesive in step 5 and is scraped in basal layer or gold brick decorative layer, every time
Construct 0.8-1.2m2。
By using above-mentioned technical proposal, the volume of each gluing is controlled, can preferably control rubberization thickness, gluing knot
The effect of time, bonding are more preferable.
The present invention is further arranged to: the compound adhesive be stone material glue and clear water according to the ratio mixing of volume ratio 4:1 and
At.
By using above-mentioned technical proposal, stone material glue adhesion strength with higher and certain flexibility, and can be with
Avoiding the alkaline components in adhesive from permeating into stone material causes stone surface lesion occur.Resist with good water-fast, waterproof
Performance is seeped, can be improved water-fast, the waterproof impervious characteristic of floor tile；And stone material glue anti-aging property is good, gold brick decorating glue and
Basal layer bonds stronger, it is not easy to crack.Stone material glue is environment-protecting and non-poisonous, good to environment, might as well to personal safety；Stone material glue
It is more preferable with mobility after clear water mixing, it is convenient for gluing.
The present invention is further arranged to: the preparation method of compound adhesive is: stone material glue and clear water being mixed, cream is stirred into
Paste, standing to stir again after curing 2-3min can be used.
By using above-mentioned technical proposal, more evenly, later period performance is more stable for stone material glue and clear water mixing.
The present invention is further arranged to: Step 6: conserving after being firmly bonded in step 5 in gold brick decor surface brushing
Material, maintenance material are tung oil, wood wax oil or polyurethane.
By using above-mentioned technical proposal, maintenance material has certain moist maintenance action to floor tile, is conducive to increase ground
The structural strength of brick and other performances, if tung oil penetrates into gold brick decorative layer, can be improved floor tile waterproof, it is heat-resisting, acidproof,
Alkaline-resisting, antiseptic property, and floor tile surface is not allowed to tend to have scratch；Wood wax oil penetrates into gold brick decorative layer, enhances surface hardness,
Water proof anti-soil；Polyurethane also has good waterproof performance.
In conclusion the invention has the following advantages:
First, realize and make full use of to discarded gold brick by gold brick material in conjunction with common basal layer, one has been got back
The floor tile of kind novel environment friendly, enriches the type of floor tile.Gold brick material hardness is high, and the structure for being conducive to increase floor tile is strong
Degree；Gold brick material seepage of water is fabulous, floor tile is used for ground, ground is not allowed to tend to have ponding；And gold brick material surface is mill
Sand face, it is not easy to skid.Gold brick decorative layer is made of several pieces of decorating units, on the one hand can also even if smaller discarded gold brick
To utilize, on the other hand convenient for combining more patterns, increase the pattern of floor tile by diversification.Gold brick decorative layer passes through gluing
On the base layer, structure is simple for layer bonding, and preparation is also simpler, and the smooth row of decorating unit is convenient in the use of basal layer
Column, and gold brick material needed for gold brick decorative layer is fewer, is conducive to save cost.
Second, marble is from a wealth of sources, cost compares lower；And marble can make with the compound of gold brick decorative layer
Floor tile structure intensity is stronger.It is lighter that the combination of plank and gold brick decorative layer sets floor tile weight, convenient for saving transportation cost, and
And the surfaces versus rough of plank, relative to marble, plank and the bonding of gold brick decorative layer are more easier.
Third, gold brick is cut into breaking convenient for step 2 after thin slice, and early period, slice was also more easier；Gold brick thin slice
The decorating unit of irregular shape is formd after being broken, then splices and assembles, and is formed diversified lines, is enriched ground
The aesthetic feeling of the design of face brick；Gap filler keeps gap more obvious, and lines is also more obvious；Entire simple production process, without special
Equipment be convenient for commercial introduction without excessively professional worker.
Detailed description of the invention
Fig. 1 is the overall structure diagram of embodiment 1；
Fig. 2 is the overall structure diagram of embodiment 2.
Appended drawing reference: 1, basal layer；2, adhesive layer；3, gold brick decorative layer；31, decorating unit；32, gap filler.
Specific embodiment
1-2 and embodiment with reference to the accompanying drawing, the present invention will be described in detail.
The glue of adhesive layer is the stone material glue bought by Guangzhou Le Jiang construction material Co., Ltd or use section's prestige board stone
Material compound adhesive.Gap filler can buy the black external wall waterproof gap filler that Foshan City's U.S.A builds the production of material Co., Ltd jointly, can also be with
It is mixed by marble cloud stone glue and cloud stone glue curing agent, the weight ratio of marble cloud stone glue and curing agent is 100:5.
Embodiment 1
The pseudo-classic floor tile of environment-friendly type, as shown in Figure 1, including basal layer 1 and gold brick decorative layer 3, gold brick decorative layer 3 and basal layer 1
Between be bonded with adhesive layer 2；Gold brick decorative layer 3 is made of several pieces of decorating units 31.
Gold brick material is combined with common basal layer 1, that is, realizes and discarded gold brick is made full use of, has got back one
The floor tile of kind novel environment friendly, enriches the type of floor tile.Gold brick material hardness is high, and the structure for being conducive to increase floor tile is strong
Degree；Gold brick material seepage of water is fabulous, floor tile is used for ground, ground is not allowed to tend to have ponding；And gold brick material surface is mill
Sand face, it is not easy to skid.Gold brick decorative layer 3 is made of several pieces of decorating units 31, even if on the one hand smaller discarded gold brick
Also it can use, on the other hand convenient for combining more patterns, increase the pattern of floor tile by diversification.Gold brick decorative layer 3 is logical
It crosses adhesive layer 2 to be bonded on basal layer 1, structure is simple, and preparation is also simpler, and the use of basal layer 1 is single convenient for decoration
The stay aligned of member 31, and gold brick material needed for gold brick decorative layer 3 is fewer, is conducive to save cost.
Gap is equipped between adjacent decoration unit 31, the width in gap is less than 2mm, and temperature difference is bigger throughout the year,
Decorating unit 31 reserves certain gap, and when hot weather, the expansion of decorating unit 31 is not easy mutual extrusion deformation；And
And gap width will not influence whole structural strength less than 2mm.Gap filler 32 is filled in gap.The use of gap filler 32
The more conducively splicing of decorating unit 31,31 stitching portion of decorating unit is more smooth, and bonding is also stronger, at gap filler 32
It is capable of forming a kind of lines of other style, more design sense.
Basal layer 1 and the thickness of gold brick decorative layer 3 ratio are (2-8): 1, preferred thickness ratio is (4-6): 1.From the angle of cost
From the point of view of degree, the cost of material and cost of manufacture of gold brick decorative layer 3 are higher, and basal layer 1 and gold brick decorative layer 3 are used in combination,
Cost is greatly reduced, convenient for promoting；Basal layer 1 is thick, more preferable to the undertaking effect of gold brick decorative layer 3, is conducive to improve gold
The structural strength of brick ornamentally face brick.
Gold brick decorative layer 3 with a thickness of 0.5-2cm, after tested, the thickness of gold brick decorative layer 3 can both be protected in 0.5-2cm
The structural strength of gold brick decorative layer 3 is demonstrate,proved, and can control cost.
Decorating unit 31 is to be set as quadrangle on one side far from basal layer 1, convenient for arrangement.It decorates in other embodiments
Unit 31 can also be triangle, pentagon, hexagon, heptagon, round or ellipse, greatly enrich gold brick decorative layer
3 design sense, is more favored by people.3 surface of gold brick decorative layer is also coated with conservation layer (not shown).Conservation layer is over the ground
Face brick has certain maintenance action, conducive to the structural strength and other performances for increasing floor tile.
1 material of basal layer is natural marble, artificial marble or plank, can select substrate according to occasion, cost etc.
The material of layer 1, enriches the product type of floor tile.Marble is from a wealth of sources, and cost compares lower；And marble with
The compound of gold brick decorative layer 3 can make floor tile structure intensity stronger.The combination of plank and gold brick decorative layer 3 sets floor tile weight
It is lighter, convenient for saving transportation cost, and the surfaces versus rough of plank, relative to marble, plank and gold brick decorative layer 3
Bonding is more easier.
Embodiment 2
The pseudo-classic floor tile of environment-friendly type, embodiment 2 is difference from example 1 is that decorating unit 31 is set as irregular shape
Shape is assembled again after being broken by gold brick and is formed, and a face surface area of the separate basal layer 1 of adjacent decoration unit 31 is unequal, makes ground
The combination that tile surface takes on any of a number of shapes, more design sense.
The production technology of the pseudo-classic floor tile of environment-friendly type, comprising the following steps:
Step 1: the gold brick of recycling is thinly sliced；
Step 2: breaking gold brick thin slice in step 1 to form multiple decorating units；
Step 3: the decorating unit in step 2 is carried out splicing assembling；
Step 4: adding gap filler at the gap of adjacent decoration unit, gold brick decorative layer is formed after gap filler is dry, to gold brick
Decorative layer, which carries out polishing, keeps gold brick decor surface smooth；
Step 5: gold brick decorative layer with basal layer bond compound；Compound adhesive is uniformly applied and is scraped in basal layer or gold brick dress
Adorn layer, the pressing of gold brick decorative layer be pressed together in gold brick decorative layer on the base layer or by basal layer, and adjust basal layer and
The depth of parallelism of gold brick decorative layer, construct 0.8-1.2m every time2.Compound adhesive is polished after parching according to determining thickness, makes ground
Tile surface is more flat and smooth, then is cut into the finished product plate of different size.
Wherein compound adhesive is that stone material glue and clear water are mixed according to the ratio of volume ratio 4:1.The preparation method of compound adhesive
It is: stone material glue and clear water is mixed, be stirred into cream paste, standing to stir again after curing 2-3min can be used.It is compound
Glue with a thickness of 1-2mm.The thickness of gold brick is substantially in 10cm, a kind of thin slice that gold brick is cut into 1-2cm of step.
When should paste the ceramic tile or stone material for requiring stickup back ditch deeper when if pasting in step 5 from bottom to top, work is removed
Make that rubber cement should be smeared at the back ditch of ceramic tile or stone material also outside basal plane to avoid hollowing.
Gold brick decorative layer and basal layer carry out bonding compound tense in step 5, and the pressure of application is P, apply the time of pressure
For t1, the edge of basal layer and gold brick decorative layer is equipped with elastic footrest during pressing plate, carries out after compound to floor tile
Drying, the temperature and time dried in vacuum oven are respectively T and t2, wherein P=0.1-0.3MPa, t1=3-10s, T
=25-42 DEG C, t2=8-15.Specific value see the table below:
| P/MPa | t1/s | T/℃ | t2/h | |
| Embodiment 3 | 0.1 | 10 | 40 | 8 |
| Embodiment 4 | 0.2 | 5 | 40 | 8 |
| Embodiment 5 | 0.3 | 3 | 40 | 8 |
| Embodiment 6 | 0.2 | 5 | 25 | 15 |
| Embodiment 7 | 0.2 | 5 | 35 | 10 |
| Embodiment 8 | 0.2 | 5 | 42 | 8.5 |
| Comparative example 1 | 0.2 | 5 | 50 | 6 |
| Comparative example 2 | 0.5 | 5 | 40 | 8 |
| Comparative example 3 | 0.2 | 2 | 40 | 8 |
Embodiment 9
The production technology of the pseudo-classic floor tile of environment-friendly type, embodiment 9 and embodiment 4 are the difference is that the medium gap filler of step 4
After parching again by gold brick decorative layer to cutting at the thin slice of 0.5-1.5cm；Gold brick decorative layer is filled out with gap filler again to after cuing open
Seam.
Embodiment 10
The production technology of the pseudo-classic floor tile of environment-friendly type, embodiment 10 and embodiment 4 are the difference is that Step 6: in step 5
It conserves and expects in gold brick decor surface brushing after being firmly bonded, maintenance material is tung oil.
Embodiment 11
The production technology of the pseudo-classic floor tile of environment-friendly type, embodiment 11 and embodiment 10 are the difference is that maintenance material is haze tallow
Oil.
Embodiment 12
The production technology of the pseudo-classic floor tile of environment-friendly type, embodiment 12 and embodiment 10 are the difference is that maintenance material is poly- ammonia
Ester.
Embodiment 13
The production technology of the pseudo-classic floor tile of environment-friendly type, embodiment 13 and embodiment 9 are the difference is that by floor tile obtained
3h is impregnated in clear water, then the natural air drying after taking out in water；The temperature of clear water is room temperature, and actual temp is 20-25 DEG C.
Comparative example 4
The production technology of the pseudo-classic floor tile of environment-friendly type, comparative example 4 and embodiment 4 are the difference is that gold brick is decorated in step 5
Layer and basal layer bond it is compound after directly dry in air, temperature is 25 DEG C.
Floor tile made from embodiment 3-12 and comparative example 1-4 is tested for the property, test result is as follows:
Remarks: 1. basal layers are marble, marble with a thickness of 3cm, gold brick decorative layer with a thickness of 0.6cm；
2. the test method of seepage of water is that 100ml clear water is poured on to surface area for 1m3Floor tile on, see infiltration situation；
3. pore amount is the bubble number in every square metre, when bubble number is less than 7 be it is good, when number of bubbles is a in 7-18
When be general, be very poor when number of bubbles is greater than 30 when number of bubbles is at 18-30 to be poor；
4. the test of adhesion strength is, floor tile is placed vertically, is inhaled on the face that basal layer and gold brick decorative layer are located remotely from each other
Two suckers, apply certain pulling force to sucker, just tear basal layer and gold brick decorative layer bonding part, needed for record
Pulling force；
5. hardness test: the apex angle and central part struck using iron hammer 50kg impact force, listening, and it is broken to observe floor tile
Split situation.
It should be apparent that the permeance property of embodiment 3-9 is very good from upper table, embodiment 3-5 especially with
And 100ml clear water can be permeated completely in floor tile 10s made from embodiment 8-9, it is laid on ground and is not easy to skid, then
In addition the non-skid property of gold brick itself is fine, it is more preferable to be accordingly used in laying ground security performance；The surface embodiment 10-12 is coated with
Maintenance material, therefore permeance property substantially reduces, but gold brick non-skid property itself is fine, there will not be too big influence, for one
The occasion of waterproof is needed to can also be applied a bit.Because impregnating in water, permeability reduces embodiment 13.
There is not too many stomata at floor tile gap made from embodiment 3-13, in addition to 6 drying temperature of embodiment is lower,
Bubble is not removed completely, does not all there is bubble at the gap of other several embodiments, and floor tile quality is higher, and structural strength is also more
It is high.1 medium temperature of comparative example spends height, and gas evolution is too fast during drying, therefore bubble ratio is more；To substrate in comparative example 2
Layer and gold brick decorative laminate resultant force are excessive, are also easy to produce the more bubbles of comparison；To basal layer and gold brick decorative laminate in comparative example 3
The conjunction time is too short, does not give gap filler enough filling times, and bubble is also very much.It is dried in air between comparative example 4, bubble produces
Life is also very much.The adhesion strength of embodiment 3-19 is also very high, very secured, the embodiment 10- of basal layer and gold brick decorative layer bonding
12 nourishings for having maintenance to expect, adhesion strength further increase；13 compound adhesive of embodiment reacts in water, and adhesive effect is more
By force, therefore rainwater not only will not influence the bonding of basal layer and gold brick decorative layer, has reinforced cementitious effect instead, further increases
The quality of floor tile.Since drying temperature, pressing Lee, pressing time control are bad in comparative example 1-4, base has all been significantly affected
The adhesion strength of bottom and gold brick decorative layer.
Hardness is particularly important for brick, can be with the method for listening sound is tapped, and by tapping, sound is relatively clear
Crisp, provable inherent quality is preferable, and hardness is good；Sound is stiff, and internal soundness is not good enough, is easily broken.It can be with from upper table
It being clear that, floor tile made from embodiment 1-13 is clear, and it is unbroken, and bubble is more in comparative example 1-4, hardness is not
It reaches, sound is stiff when percussion, there is obvious crackle.
The applicant is also tested the anti-scratch colored performance of embodiment 10 and embodiment 11, applies one with metal pocket knife
Fixed power is drawn on floor tile surface, as a result, it has been found that the anti-scratch colored ability of embodiment 10 than embodiment 11 anti-scratch colored ability by force very
It is more.It is rubbed repeatedly with steel wire lump floor tile surface made from embodiment 10 and embodiment 11, does not also occur brick powder, wearability is non-
Chang Hao.
The above is only a preferred embodiment of the present invention, protection scope of the present invention is not limited merely to above-mentioned implementation
Example, all technical solutions belonged under thinking of the present invention all belong to the scope of protection of the present invention.It should be pointed out that for the art
Those of ordinary skill for, several improvements and modifications without departing from the principles of the present invention, these improvements and modifications
It should be regarded as protection scope of the present invention.
Claims (10)
1. the pseudo-classic floor tile of environment-friendly type, it is characterised in that: including basal layer (1) and gold brick decorative layer (3), gold brick decorative layer (3)
Adhesive layer (2) are bonded between basal layer (1)；Gold brick decorative layer (3) is made of several pieces of decorating unit (31) splicings, adjacent
Gap is equipped between decorating unit (31), the width in gap is less than 2mm；Wherein basal layer (1) material is natural marble, artificial
Marble or plank.
2. the pseudo-classic floor tile of environment-friendly type according to claim 1, it is characterised in that: adjacent decoration unit is equipped between (31)
Gap is filled with gap filler (32) or compound adhesive in gap；Gap filler (32) is the mixture of curing agent and glue.
3. the pseudo-classic floor tile of environment-friendly type according to claim 2, it is characterised in that: the basal layer (1) and gold brick decoration
The thickness ratio of layer (3) is (2-8): 1；The gold brick decorative layer (3) with a thickness of 0.5-2cm.
4. the production technology of the pseudo-classic floor tile of environment-friendly type according to claim 1 to 3, it is characterised in that: including
Following steps:
Step 1: the gold brick of recycling is thinly sliced；
Step 2: gold brick thin slice in step 1 is broken to form multiple decorating units (31)；
Step 3: the decorating unit (31) in step 2 is carried out splicing assembling；
Step 4: gap filler (32) are added at the gap of adjacent decoration unit (31) forms gold brick decorative layer (3), gap filler
(32) carrying out polishing to gold brick decorative layer (3) after drying makes gold brick decorative layer (3) surfacing；
Step 5: coating compound adhesive on gold brick decorative layer (3), basal layer (1) is pressed together on gold brick decorative layer (3)；Or
Compound adhesive is coated on basal layer (1), gold brick decorative layer (3) is pressed together on basal layer (1)；Adjust basal layer (1) and gold brick
The depth of parallelism of decorative layer (3).
5. the production technology of the pseudo-classic floor tile of environment-friendly type according to claim 4, it is characterised in that: by gold brick in step 1
It is cut into the thin slice of 1-2cm；The medium gap filler of step 4 (32) parch after again by gold brick decorative layer (3) to cutting at 0.5-1.5cm
Thin slice.
6. the production technology of the pseudo-classic floor tile of environment-friendly type according to claim 5, it is characterised in that: by gold brick decorative layer
(3) to after cuing open again use gap filler (32) joint filling.
7. the production technology of the pseudo-classic floor tile of environment-friendly type according to claim 6, it is characterised in that: will be compound in step 5
Glue, which uniformly applies, to be scraped in basal layer (1) or gold brick decorative layer (3), and construct 0.8-1.2 m every time2。
8. the production technology of the pseudo-classic floor tile of environment-friendly type according to claim 7, it is characterised in that: the compound adhesive is stone
Material glue and clear water are mixed according to the ratio of volume ratio 4:1.
9. the production technology of the pseudo-classic floor tile of environment-friendly type according to claim 8, it is characterised in that: the preparation side of compound adhesive
Method is: stone material glue and clear water being mixed, cream paste is stirred into, standing to stir again after curing 2-3min can be used.
10. the production technology of the pseudo-classic floor tile of environment-friendly type according to claim 6, it is characterised in that: Step 6: step 5
In be firmly bonded after gold brick decorative layer (3) external coating conserve expect, maintenance material be tung oil, wood wax oil or polyurethane.