CN109749551A - A kind of corrosion-resistant acrylic paint - Google Patents
A kind of corrosion-resistant acrylic paint Download PDFInfo
- Publication number
- CN109749551A CN109749551A CN201711089023.4A CN201711089023A CN109749551A CN 109749551 A CN109749551 A CN 109749551A CN 201711089023 A CN201711089023 A CN 201711089023A CN 109749551 A CN109749551 A CN 109749551A
- Authority
- CN
- China
- Prior art keywords
- parts
- acrylic resin
- corrosion
- acid
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of corrosion-resistant acrylic paints, are mainly made of the following component counted with mass fraction: 50-80 parts of Hydroxylated acrylic resin, 20-30 parts of thermoplastic acrylic resin, 20-30 parts of water-based acrylic resin, 15-30 parts of stearic acid, 5-8 parts of limonene, 3-6 parts of levelling agent, 0.5-1.0 parts of rare earth brightening agent, 3-8 parts of barium sulfate, 2-3 parts of caprylic acid, 5-10 parts of perlite, 5-10 parts of barium chromate, 2-3 parts of nano-disinfection agent, 5-10 parts of glacial acetic acid.Acrylic paint of the invention has preferable adhesive force, and especially acid and alkali-resistance, excellent in weather to various substrates.
Description
Technical field
The present invention relates to organic polymer paint field more particularly to a kind of corrosion-resistant acrylic paints.
Background technique
Contain a large amount of volatilizable organic compound (VOC), organic compound in now widely used solvent based coating
(VOC) toxic, inflammable, it pollutes the atmosphere, all causes damages to environment and human body.Therefore, in order to reduce these organic solvents pair
Water paint has been included in the developing direction of industrial coating from now on by the pollution of environment, China.But China is applied at present on floor
Aqueous industrial coating its water resistance, chemical resistance, wearability and weatherability on coating, metallic anti-rust paint and marine paint are paid no attention to
Think.
Summary of the invention
In order to solve the above-mentioned technical problem, the water paint for providing a kind of chemical resistance, having excellent weather resistance, the present invention provide
Following technical scheme:
A kind of corrosion-resistant acrylic paint is made of the following component counted with mass fraction: Hydroxylated acrylic resin 50-80
Part, 20-30 parts of thermoplastic acrylic resin, 20-30 parts of water-based acrylic resin, 15-30 parts of stearic acid, 5-8 parts of limonene, stream
Flat agent 3-6 parts, 0.5-1.0 parts of rare earth brightening agent, 3-8 parts of barium sulfate, 2-3 parts of caprylic acid, 5-10 parts of perlite, barium chromate 5-10
Part, 2-3 parts of nano-disinfection agent, 5-10 parts of glacial acetic acid.
It further, further include 2-5 parts of zinc oxide.
It further, further include 3-4 parts of sodium molybdate.
Further, it is made of the following component counted with mass fraction: 60 parts of Hydroxylated acrylic resin, thermoplastic acrylic
25 parts of resin, 25 parts of water-based acrylic resin, 20 parts of stearic acid, 6 parts of limonene, 5 parts of levelling agent, 0.7 part of rare earth brightening agent, sulphur
5 parts of sour barium, 2.5 parts of caprylic acid, 7 parts of perlite, 7 parts of barium chromate, 2.5 parts of nano-disinfection agent, 7 parts of glacial acetic acid.
The beneficial effects of the present invention are: there are preferable adhesive force, and especially acid and alkali-resistance, weatherability pole to various substrates
It is good, and VOC emission amount is extremely low.
Specific embodiment
Embodiment 1,
A kind of corrosion-resistant acrylic paint is made of the following component counted with mass fraction: 60 parts of Hydroxylated acrylic resin,
25 parts of thermoplastic acrylic resin, 25 parts of water-based acrylic resin, 20 parts of stearic acid, 6 parts of limonene, 5 parts of levelling agent, rare earth increase
White dose 0.7 part, 5 parts of barium sulfate, 2.5 parts of caprylic acid, 7 parts of perlite, 7 parts of barium chromate, 2.5 parts of nano-disinfection agent, glacial acetic acid 7
Part.
Embodiment 2,
A kind of corrosion-resistant acrylic paint is made of the following component counted with mass fraction: 50 parts of Hydroxylated acrylic resin,
20 parts of thermoplastic acrylic resin, 20 parts of water-based acrylic resin, 15 parts of stearic acid, 5 parts of limonene, 3 parts of levelling agent, rare earth increase
White dose 0.5 part, 3 parts of barium sulfate, 2 parts of caprylic acid, 5 parts of perlite, 5 parts of barium chromate, 2 parts of nano-disinfection agent, 5 parts of glacial acetic acid.
Embodiment 3,
A kind of corrosion-resistant acrylic paint is made of the following component counted with mass fraction: 80 parts of Hydroxylated acrylic resin,
30 parts of thermoplastic acrylic resin, 30 parts of water-based acrylic resin, 30 parts of stearic acid, 8 parts of limonene, 6 parts of levelling agent, rare earth increase
White dose 1.0 parts, 8 parts of barium sulfate, 3 parts of caprylic acid, 10 parts of perlite, 10 parts of barium chromate, 3 parts of nano-disinfection agent, 10 parts of glacial acetic acid,
5 parts of zinc oxide, 4 parts of sodium molybdate.
It is enlightenment with above-mentioned desirable embodiment according to the present invention, through the above description, relevant staff is complete
Various changes and amendments can be carried out without departing from the scope of the technological thought of the present invention'.This invention it is technical
Range is not limited to the contents of the specification, it is necessary to which the technical scope thereof is determined according to the scope of the claim.
Claims (4)
1. a kind of corrosion-resistant acrylic paint, it is characterised in that: be made of the following component counted with mass fraction: hydroxy acrylic acid
50-80 parts of resin, 20-30 parts of thermoplastic acrylic resin, 20-30 parts of water-based acrylic resin, 15-30 parts of stearic acid, lemon
5-8 parts of alkene, 3-6 parts of levelling agent, 0.5-1.0 parts of rare earth brightening agent, 3-8 parts of barium sulfate, 2-3 parts of caprylic acid, 5-10 parts of perlite,
5-10 parts of barium chromate, 2-3 parts of nano-disinfection agent, 5-10 parts of glacial acetic acid.
2. a kind of corrosion-resistant acrylic paint as described in claim 1, it is characterised in that: further include 2-5 parts of zinc oxide.
3. a kind of corrosion-resistant acrylic paint as described in claim 1, it is characterised in that: further include 3-4 parts of sodium molybdate.
4. a kind of corrosion-resistant acrylic paint as described in claim 1, it is characterised in that: by terms of mass fraction it is following at
Be grouped as: 60 parts of Hydroxylated acrylic resin, 25 parts of thermoplastic acrylic resin, 25 parts of water-based acrylic resin, 20 parts of stearic acid,
6 parts of limonene, 5 parts of levelling agent, 0.7 part of rare earth brightening agent, 5 parts of barium sulfate, 2.5 parts of caprylic acid, 7 parts of perlite, barium chromate 7
Part, 2.5 parts of nano-disinfection agent, 7 parts of glacial acetic acid.