CN109733023A - A kind of noctilucence compound nonwoven cloth - Google Patents
A kind of noctilucence compound nonwoven cloth Download PDFInfo
- Publication number
- CN109733023A CN109733023A CN201711031548.2A CN201711031548A CN109733023A CN 109733023 A CN109733023 A CN 109733023A CN 201711031548 A CN201711031548 A CN 201711031548A CN 109733023 A CN109733023 A CN 109733023A
- Authority
- CN
- China
- Prior art keywords
- layer
- fiber
- cloth
- parts
- cotton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of noctilucence compound nonwoven cloths, it is characterized by: the non-woven fabrics body surface is equipped with RE luminous fiber layer, the bottom of the RE luminous fiber layer is equipped with melt-blown non-woven fabric layer, the bottom of the melt-blown non-woven fabric layer is equipped with Calober heat generating fiber heat preservation layer, the bottom of the Calober heat generating fiber heat preservation layer is equipped with the netted inner sandwich layer, and the bottom of the netted inner sandwich layer is equipped with acupuncture nonwoven layer of cloth；RE luminous fiber layer of the present invention absorbs visible light 10 minutes, just can store luminous energy and store among fiber, can in the dark state continuous illumination 10 hours or more, is additionally provided with Calober heat generating fiber heat preservation layer, can independently generate heat, increases the warming sense of people.
Description
Technical field
The present invention relates to a kind of textile fabric, specially a kind of noctilucence compound nonwoven cloth.
Background technique
Non-woven fabrics is commonly called as non-woven cloth, it is to be oriented staple fiber or long filament or random alignment, forms fibre web knot
Then structure is reinforced, the non-woven cloth eventually formed using the methods of mechanical, hot rolling or chemistry.Traditional water suction non-woven fabrics
It is directly composed of multi-layer nonwoven fabrics mostly.Existing harmless cloth, does not have a noctilucent function, and existing luminous cloth mostly by
A kind of fiber composition, structure is single, and surface is not soft enough, and feel is poor, and gas permeability is not strong, easy fracture.
Summary of the invention
The purpose of the present invention is to provide a kind of noctilucence compound nonwoven cloths, to solve mentioned above in the background art ask
Topic.
To achieve the above object, the invention provides the following technical scheme: a kind of noctilucence compound nonwoven cloth, it is characterised in that:
The non-woven fabrics body surface is equipped with RE luminous fiber layer, and the bottom of the RE luminous fiber layer is equipped with melt spraying non-woven fabrics
The bottom of layer, the melt-blown non-woven fabric layer is equipped with Calober heat generating fiber heat preservation layer, the Calober heat generating fiber heat preservation layer
Bottom be equipped with the netted inner sandwich layer, the bottom of the netted inner sandwich layer is equipped with acupuncture nonwoven layer of cloth.
Further, the acupuncture nonwoven layer of cloth production method, including step is made in detail below:
A. by 100 parts of polyester fibers, 10 parts of corn stalk fibers, 3 parts of bamboo fibres, 2 parts of flaxen fibers, it is flat to be put in proportion into conveying
On curtain, it is sent to thick opener, the fiber of blocky curling compacting is made to obtain preliminary shredding, by the composite fibre of preliminary shredding,
It is sent by wind, so that it is evenly distributed on mixing chamber and deposited, guaranteed that cotton layer height is consistent, pass through being total to for flat curtain and the oblique curtain of brad
Same-action makes it be transported to smart booting；
B. raw material feeds refined opener, abundant shredding and pre-comb is carried out in refined opener, is made after mixed cotton is sufficiently mixed
The further shredding of fiber is straightened；
C. the fiber by essence booting enters the upper hopper of air pressure cotton box by air delivery pipe, passes through feed roll motor and doffer
Effect falls on fiber in lower hopper, and then fiber constant volume is provided in a manner of counterpressure, guarantees that cotton layer volume density is consistent；
D. carding machine receives the fiber that air pressure cotton box is fed according to technique initialization weight, after entering cotton-supplying roller, passes through double cylinders
The effect of two pass husband is combed into the uniform netted thin layer of 10-15 grams/m of double layer fibre；
E. the netted thin layer of double layer fibre, by reciprocating, makes its lapping reach 7-18 by the gripping conveying of clamping carbon curtain
Layer, cotton net use with a thickness of 15cm for next procedure；
F. it is fed before needing machine, makes web uniform clamping feeding needle area before needle thorn；It will be formed by combing, lapping
Web is tentatively tangled web sizing by pre-needling process, and the direction of guarantee fibrinogen net is constant, will pass through pre-needling
The web that machine tentatively tangles is tangled by the further needle thorn of main needing machine, and needle pierces 5-8 times, by what is tangled by main pinprick reinforcement
Acupuncture nonwoven layer of cloth reaches molding needle punched non-woven fabrics surfacing, impulse- free robustness, bone trace by needing machine tow sides needle thorn of having a shave
Phenomenon carries out storage cloth by storing up cloth tension bracket；
G. it on molding cloth, is uniformly applied with 18-19 parts of polyacrylic acid, 15-16 parts of polyvinyl alcohol, 0.2-0.3 parts of silane coupling agents
It scrapes, cloth cover is reinforced and is bonded, drying about 1-1.5 hours at a temperature of being re-fed into 80-90 in drying box, taking-up obtains acupuncture nonwoven
Layer of cloth.
Further, the netted inner sandwich layer is diamond-mesh structure made of mutually being woven as wire.
Further, it is fitted closely between the netted inner sandwich layer and the acupuncture nonwoven layer of cloth.
Compared with prior art, RE luminous fiber layer absorbs visible light 10 minutes in this textile fabric, just can be by luminous energy
Storage is stored among fiber, can in the dark state continuous illumination 10 hours or more, and it is warming to be additionally provided with Calober heat generating fiber
Layer, can independently generate heat, increase the warming sense of people.The present invention can be made light-emitting curtain, carpet, wall paper etc., even if dark
Place is still fairly obvious, convenient for the nocturnalism of people.
Detailed description of the invention
Fig. 1 is overall structure diagram of the invention.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Referring to Fig. 1, the present invention provides a kind of technical solution: a kind of noctilucence compound nonwoven cloth, 1 surface of non-woven fabrics ontology are set
There is RE luminous fiber layer 3, the bottom of RE luminous fiber layer 3 is equipped with melt-blown non-woven fabric layer 7, the bottom of melt-blown non-woven fabric layer 7
Equipped with Calober heat generating fiber heat preservation layer 9, the bottom of Calober heat generating fiber heat preservation layer 9 is equipped with the netted inner sandwich layer 10,
Netted inner sandwich layer 10 is diamond-mesh structure made of mutually being woven as wire, and the bottom of netted inner sandwich layer 10 is equipped with needle and pierces nothing
Woven fabric layer 11 fits closely between netted inner sandwich layer 10 and acupuncture nonwoven layer of cloth 11.
It is compound according to general technology that above each layer is sent into non-woven fabric compounded machine to obtain the final product.
Working principle: RE luminous fiber layer 3 makes textile fabric have photism, the bottom of RE luminous fiber layer 3
Equipped with melt-blown non-woven fabric layer 7, it can be equipped with Calober heat generating fiber heat preservation layer 9 with reinforcing structure, the bottom of melt-blown non-woven fabric layer 7,
Calober heat generating fiber heat preservation layer 9 can keep warm very well and generate certain heat, keep inner temperature of room, Calober heat generating fiber
The bottom of heat preservation layer 9 is equipped with netted inner sandwich layer 10, and netted inner sandwich layer 10 and acupuncture nonwoven layer of cloth 11 are fitted closely, be primarily used to
Fixed Calober heat generating fiber heat preservation layer and acupuncture nonwoven layer of cloth 11, are not easy it at random, while improving intensity, and raising resists quiet
Electrical property improves thermal property, extends the service life of entire textile fabric.
The acupuncture nonwoven layer of cloth production method, including step is made in detail below: A. is by 100 parts of polyester fibers, 10 parts
Corn stalk fiber, 3 parts of bamboo fibres, 2 parts of flaxen fibers are put in proportion on the flat curtain of conveying, are sent to thick opener, make bulk
The fiber of curling compacting obtains preliminary shredding, by the composite fibre of preliminary shredding, is sent by wind, it is made to be evenly distributed on mixed cotton
Storehouse is deposited, and is guaranteed that cotton layer height is consistent, by the collective effect of flat curtain and the oblique curtain of brad, it is made to be transported to smart booting；
B. raw material feeds refined opener, abundant shredding and pre-comb is carried out in refined opener, is made after mixed cotton is sufficiently mixed
The further shredding of fiber is straightened；
C. the fiber by essence booting enters the upper hopper of air pressure cotton box by air delivery pipe, passes through feed roll motor and doffer
Effect falls on fiber in lower hopper, and then fiber constant volume is provided in a manner of counterpressure, guarantees that cotton layer volume density is consistent；
D. carding machine receives the fiber that air pressure cotton box is fed according to technique initialization weight, after entering cotton-supplying roller, passes through double cylinders
The effect of two pass husband is combed into the uniform netted thin layer of 10-15 grams/m of double layer fibre；
E. the netted thin layer of double layer fibre, by reciprocating, makes its lapping reach 7-18 by the gripping conveying of clamping carbon curtain
Layer, cotton net use with a thickness of 15cm for next procedure；
F. it is fed before needing machine, makes web uniform clamping feeding needle area before needle thorn；It will be formed by combing, lapping
Web is tentatively tangled web sizing by pre-needling process, and the direction of guarantee fibrinogen net is constant, will pass through pre-needling
The web that machine tentatively tangles is tangled by the further needle thorn of main needing machine, and needle pierces 5-8 times, by what is tangled by main pinprick reinforcement
Acupuncture nonwoven layer of cloth reaches molding needle punched non-woven fabrics surfacing, impulse- free robustness, bone trace by needing machine tow sides needle thorn of having a shave
Phenomenon carries out storage cloth by storing up cloth tension bracket；
G. it on molding cloth, is uniformly applied with 18-19 parts of polyacrylic acid, 15-16 parts of polyvinyl alcohol, 0.2-0.3 parts of silane coupling agents
It scrapes, cloth cover is reinforced and is bonded, drying about 1-1.5 hours at a temperature of being re-fed into 80-90 in drying box, taking-up obtains acupuncture nonwoven
Layer of cloth.
Acupuncture nonwoven layer of cloth by above-mentioned preparation, is experimental data below:
Acupuncture nonwoven layer of cloth of the present invention is made of environment-friendly materials, and index is superior, alreadys exceed existing similar product.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (4)
1. a kind of noctilucence compound nonwoven cloth, it is characterised in that: non-woven fabrics ontology (1) surface is equipped with RE luminous fiber layer
(3), the bottom of the RE luminous fiber layer (3) is equipped with melt-blown non-woven fabric layer (7), the bottom of the melt-blown non-woven fabric layer (7)
Equipped with Calober heat generating fiber heat preservation layer (9), the bottom of the Calober heat generating fiber heat preservation layer (9) is equipped with described netted interior
The bottom of sandwich layer (10), the netted inner sandwich layer (10) is equipped with acupuncture nonwoven layer of cloth (11).
2. a kind of noctilucence compound nonwoven cloth according to claim 1, it is characterised in that: the netted inner sandwich layer (10) be by
Diamond-mesh structure made of wire mutually weaves.
3. a kind of noctilucence compound nonwoven cloth according to claim 1, it is characterised in that: the netted inner sandwich layer (10) and institute
It states and is fitted closely between acupuncture nonwoven layer of cloth (11).
4. a kind of noctilucence compound nonwoven cloth according to claim 1, it is characterised in that: the acupuncture nonwoven layer of cloth producer
Method, including step is made in detail below:
A. by 100 parts of polyester fibers, 10 parts of corn stalk fibers, 3 parts of bamboo fibres, 2 parts of flaxen fibers, it is flat to be put in proportion into conveying
On curtain, it is sent to thick opener, so that the fiber of blocky curling compacting is obtained preliminary shredding, the mixing by preliminary shredding is fine
Dimension, is sent by wind, so that it is evenly distributed on mixing chamber and deposited, and is guaranteed that cotton layer height is consistent, is passed through flat curtain and the oblique curtain of brad
Collective effect, so that it is transported to smart booting；
B. raw material feeds refined opener, abundant shredding and pre-comb is carried out in refined opener, is made after mixed cotton is sufficiently mixed
The further shredding of fiber is straightened；
C. the fiber by essence booting enters the upper hopper of air pressure cotton box by air delivery pipe, passes through feed roll motor and doffer
Effect falls on fiber in lower hopper, and then fiber constant volume is provided in a manner of counterpressure, guarantees that cotton layer volume density is consistent；
D. carding machine receives the fiber that air pressure cotton box is fed according to technique initialization weight, after entering cotton-supplying roller, passes through double cylinders
The effect of two pass husband is combed into the uniform netted thin layer of 10-15 grams/m of double layer fibre；
E. the netted thin layer of double layer fibre, by reciprocating, makes its lapping reach 7-18 by the gripping conveying of clamping carbon curtain
Layer, cotton net use with a thickness of 15cm for next procedure；
F. it is fed before needing machine, makes web uniform clamping feeding needle area before needle thorn；It will be formed by combing, lapping
Web web is tentatively tangled sizing by pre-needling process, the direction of guarantee fibrinogen net is constant, will pass through pre- needle
The web that thorn machine tentatively tangles is tangled by the further needle thorn of main needing machine, and needle pierces 5-8 times, will be tangled by main pinprick reinforcement
Acupuncture nonwoven layer of cloth by have a shave needing machine tow sides needle thorn, reach molding needle punched non-woven fabrics surfacing, impulse- free robustness,
Bone trace phenomenon carries out storage cloth by storing up cloth tension bracket；
G. it on molding cloth, is uniformly applied with 18-19 parts of polyacrylic acid, 15-16 parts of polyvinyl alcohol, 0.2-0.3 parts of silane coupling agents
It scrapes, cloth cover is reinforced and is bonded, drying about 1-1.5 hours at a temperature of being re-fed into 80-90 in drying box, taking-up obtains acupuncture nonwoven
Layer of cloth.