CN109677048A - A kind of waterproof uvioresistant fabrics - Google Patents
A kind of waterproof uvioresistant fabrics Download PDFInfo
- Publication number
- CN109677048A CN109677048A CN201910120589.1A CN201910120589A CN109677048A CN 109677048 A CN109677048 A CN 109677048A CN 201910120589 A CN201910120589 A CN 201910120589A CN 109677048 A CN109677048 A CN 109677048A
- Authority
- CN
- China
- Prior art keywords
- parts
- waterproof
- layer
- uvioresistant
- fabrics according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of waterproof uvioresistant fabrics, fabric includes waterproof layer, uvioresistant layer and absorbed layer, and uvioresistant layer is wrapped up by waterproof layer and absorbed layer;Waterproof layer is formed using the raw material hybrid woven of following parts by weight composition: 50~60 parts of Fypro;20~30 parts of waterproof polypropylene fibre.Waterproof uvioresistant fabrics of the invention, fabric includes waterproof layer, uvioresistant layer and absorbed layer, and uvioresistant layer is wrapped up by waterproof layer and absorbed layer, not only has the function of strong reflection to ultraviolet light, it can effectively prevent ultraviolet light from penetrating clothes and injure human body, and there is good waterproof performance.
Description
Technical field
The present invention relates to a kind of fabrics, more particularly to a kind of waterproof uvioresistant fabrics.
Background technique
With information, scientific and technological high development, fabric development is gradually mature, and various novel high-tech synthetic fabrics are asked successively
Generation.People's health consciousness awakening changes with lifestyle, in addition to paying attention to sports and leisure life, open air life, tourism, does not forget clothing also
The beauty of product, emphasize the comfortable and protective performance of various clothing, clothes not only cover body, it is even more warming, adjust body temperature,
Decorating figure wears product clothes in addition to Design modelling to be considered, it is necessary to have both protectiveness, exempt from by wind, rain, dew, cold, sun
The intrusion of light etc., the following clothing fabric will develop towards comfortable, healthy direction, and the moisture absorbing and sweat releasing performance of fabric is it
In one of most important project.
The ray of solar radiation to earth's surface is wavelength 280-400nm, and wavelength is penetrated in 280nm ultraviolet light below with other
Line is almost absorbed by ozone layer.But with the deterioration year by year of earth environment, ozone layer is increasingly thin in earth surface atmosphere, makes
The ultraviolet energy that ground must be reached constantly enhances, it is easier to allow people by intensive ultraviolet radiation, and cause skin disease and its
His lesion.The fabric of existing production clothes is generally made of a kind of material, and feature is also relatively simple, causes the waterproof of fabric
The features such as property and uvioresistant, can not get both, this will greatly reduce the comfort level to wear clothes, while the silk thread mechanism of fabric
It is fairly simple, it is badly in need of a kind of existing and flexible, breathable currently on the market, there are also the fabrics of the anti-ultraviolet effect of waterproof.
Summary of the invention
In view of the above shortcomings, it is an object of the invention to develop a waterproof uvioresistant fabrics, with excellent
Waterproof performance and anti-ultraviolet performance.
Technical solution of the present invention is summarized as follows:
A kind of waterproof uvioresistant fabrics, wherein the fabric includes waterproof layer, uvioresistant layer and absorbed layer, described
Uvioresistant layer is wrapped up by waterproof layer and absorbed layer;The waterproof layer using following parts by weight composition raw material hybrid woven and
At:
50~60 parts of Fypro;
20~30 parts of waterproof polypropylene fibre.
Preferably, the waterproof uvioresistant fabrics, wherein the waterproof polypropylene fibre contains 6~8wt%'s
Waterproofing agent.
Preferably, the waterproof uvioresistant fabrics, wherein the waterproofing agent includes 20~25 parts of hydroxypropyl methyls
Cellulose-hydroxyethyl cellulose-cellulose ether and 12~14 parts of polyoxyethylene ether trisiloxanes.
Preferably, the waterproof uvioresistant fabrics, wherein the uvioresistant layer includes following parts by weight composition
Raw material:
30~34 parts of polyacrylonitrile fibre;
20~25 parts of acid fiber by polylactic.
Preferably, the waterproof uvioresistant fabrics, wherein further include 4~6 parts of mint fibers.
Preferably, the waterproof uvioresistant fabrics, wherein the mint fibers further include the anti-purple of 3~7wt%
Outside line agent.
Preferably, the waterproof uvioresistant fabrics, wherein the UV resistant agent includes 10~12 parts
Ti2AlC, 3~5 parts of metrafenones, 2~4 parts of hexamethylphosphoramide and 2~4 parts of sulfated castor oils.
Preferably, the waterproof uvioresistant fabrics, wherein the absorbed layer includes the original of following parts by weight composition
Material:
40~42 parts of cotton fiber;
24~26 parts of flax fiber.
Preferably, the waterproof uvioresistant fabrics, wherein the absorbed layer further includes 3~5 parts of bamboo fibre.
Preferably, the waterproof uvioresistant fabrics, wherein the waterproof is placed on outermost layer, antibacterial to be placed on
Centre, absorption are placed on most inner side, and three layers pass through the logical bonding of binder.
The beneficial effects of the present invention are:
Waterproof uvioresistant fabrics of the invention, fabric include waterproof layer, uvioresistant layer and absorbed layer, uvioresistant layer
It is wrapped up by waterproof layer and absorbed layer, not only has the function of strong reflection to ultraviolet light, ultraviolet light can effectively be prevented to penetrate clothes wound
And human body, and there is good waterproof performance.
Specific embodiment
The present invention will be further described in detail below with reference to the embodiments, to enable those skilled in the art referring to specification
Text can be implemented accordingly.
This case proposes that a kind of waterproof uvioresistant fabrics, fabric include waterproof layer, uvioresistant layer and absorbed layer, uvioresistant
Line layer is wrapped up by waterproof layer and absorbed layer;The waterproof layer is formed using the raw material hybrid woven of following parts by weight composition:
50~60 parts of Fypro;
20~30 parts of waterproof polypropylene fibre.
Fypro has good comprehensive performance, including mechanical property, heat resistance, wear resistance, chemical-resistant resistance
Property and self-lubrication, and coefficient of friction is low, there is certain anti-flammability, it is easy to process;Polypropylene fibre intensity is high, elasticity is good, resistance to
It grinds, is corrosion-resistant;
As the another embodiment of this case, wherein waterproof polypropylene fibre contains the waterproofing agent of 6~8wt%.
As the another embodiment of this case, wherein waterproofing agent includes 20~25 parts of hydroxypropyl methyl cellulose-hydroxy ethyl fibers
Element-cellulose ether and 12~14 parts of polyoxyethylene ether trisiloxanes.
Polyoxyethylene ether trisiloxanes is a kind of fine particle of triplet, by dust carrier, colloid covering material and easily
It is formed in the silicone active ingredient of dispersion, active constituent stabilization can be stored in powder by colloid covering material, and in Jia Shui
After can discharge in due course, it is good to water repellency after solidification, have stronger hydrophobicity and durability;Hydroxypropyl methyl cellulose-hydroxyl
Ethyl cellulose-cellulose ether prevents liquid water from penetrating into waterproof layer by surface or capillarity;
As the another embodiment of this case, wherein uvioresistant layer includes the raw material of following parts by weight composition:
30~34 parts of polyacrylonitrile fibre;
20~25 parts of acid fiber by polylactic.
As the another embodiment of this case, wherein further include 4~6 parts of mint fibers.Mint fibers are to Escherichia coli, gold
Yellow staphylococcus, Candida albicans have resistance and inhibiting effect, wash 30-50 holding antibacterial functions.
As the another embodiment of this case, wherein mint fibers further include the UV resistant agent of 3~7wt%.
As the another embodiment of this case, wherein UV resistant agent includes 10~12 parts of Ti2AlC, 3~5 parts of metrafenones, 2~
4 parts of hexamethylphosphoramide and 2~4 parts of sulfated castor oils.Metrafenone can absorbing wavelength be strongly the ultraviolet of 270~380nm
Line, chemical stability are good;Hexamethylphosphoramide can capture living radical caused by polymer degradation, decompose hydroperoxidation
The energy of object and transmitting excited state molecule;The superpower ultraviolet absorption ability of sulfated castor oil;Ti2AlC, metrafenone, pregnancy
Base phosphoric triamide and sulfated castor oil collaboration are used as UV resistant agent, so that UV absorption reaches best.
As the another embodiment of this case, wherein absorbed layer includes the raw material of following parts by weight composition:
40~42 parts of cotton fiber;
24~26 parts of flax fiber.
Cotton fiber is porous material, and there are many hydrophilic radicals (- OH) on its cellulose macromolecule, so it is inhaled
Moist preferable, under the conditions of general atmosphere, the regain of cotton fiber is up to 8.5% or so;Due to the main comprise material of cotton fiber
It is cellulose, so it is more alkaline-resisting without acidproof;Caustic soda can make the violent extruding of cotton fiber, and diameter becomes larger, and length shortens, so that drawing
Play the strong contraction of cotton products.At this point, limit its contraction if applying tension, cotton products surface can become smooth and significantly
Improve dyeability, this processing is known as mercerising;If tension is not added to be allowed to shrink, referred to as alkali contracts.Knitted fabric can become after alkali contracts
Closely high resilience, and conformality is good.Acid can make Cotton Fiber Strength be deteriorated, and especially strong acid concentrated acid should avoid use, it is solvable
In 70% or more the concentrated sulfuric acid, concentrated hydrochloric acid, concentrated nitric acid also seriously affect its intensity.Fabric is improved by the way that flax fiber is added
Moisture absorption heat dissipation, health care is antibacterial, antifouling antistatic, antiultraviolet, flame retardant property.
As the another embodiment of this case, wherein absorbed layer further includes 3~5 parts of bamboo fibre.Bamboo fiber has good
Moisture absorption, gas permeability, drapability and dyeability are also relatively good, have gloss and feel as silk, and have antibacterial, anti-
Smelly, anti-ultraviolet function.
As the another embodiment of this case, wherein waterproof is placed on outermost layer, antibacterial to be placed on centre, and absorption is placed on most
Inside, three layers pass through the logical bonding of binder.
Specific embodiment and comparative example is listed below:
Embodiment 1:
A kind of waterproof uvioresistant fabrics, fabric include waterproof layer, uvioresistant layer and absorbed layer, and uvioresistant layer is prevented
Water layer and absorbed layer package;Waterproof layer is formed using the raw material hybrid woven of following parts by weight composition:
50 parts of Fypro;
20 parts of waterproof polypropylene fibre.
Waterproof polypropylene fibre contains the waterproofing agent of 6wt%;Waterproofing agent includes 20 parts of hydroxypropyl methyl cellulose-ethoxys
Cellulose-cellulose ether and 12 parts of polyoxyethylene ether trisiloxanes.
Uvioresistant layer includes the raw material of following parts by weight composition:
30 parts of polyacrylonitrile fibre;
20 parts of acid fiber by polylactic;
4 parts of mint fibers;
Mint fibers further include the UV resistant agent of 3wt%;UV resistant agent includes 10 parts of Ti2AlC, 3 parts of metrafenones, 2
Part hexamethylphosphoramide and 2 parts of sulfated castor oils.
Absorbed layer includes the raw material of following parts by weight composition:
40 parts of cotton fiber;
24 parts of flax fiber;
3 parts of bamboo fibre.
Waterproof is placed on outermost layer, antibacterial to be placed on centre, and absorption is placed on most inner side, and three layers logical viscous by binder
It closes.
Embodiment 2:
A kind of waterproof uvioresistant fabrics, fabric include waterproof layer, uvioresistant layer and absorbed layer, and uvioresistant layer is prevented
Water layer and absorbed layer package;Waterproof layer is formed using the raw material hybrid woven of following parts by weight composition:
54 parts of Fypro;
22 parts of waterproof polypropylene fibre.
Waterproof polypropylene fibre contains the waterproofing agent of 7wt%;Waterproofing agent includes 22 parts of hydroxypropyl methyl cellulose-ethoxys
Cellulose-cellulose ether and 13 parts of polyoxyethylene ether trisiloxanes.
Uvioresistant layer includes the raw material of following parts by weight composition:
32 parts of polyacrylonitrile fibre;
24 parts of acid fiber by polylactic;
5 parts of mint fibers;
Mint fibers further include the UV resistant agent of 5wt%;UV resistant agent includes 11 parts of Ti2AlC, 3~5 parts of benzene bacterium
Ketone, 3 parts of hexamethylphosphoramide and 3 parts of sulfated castor oils;
Absorbed layer includes the raw material of following parts by weight composition:
41 parts of cotton fiber;
25 parts of flax fiber;
4 parts of bamboo fibre;
Waterproof is placed on outermost layer, antibacterial to be placed on centre, and absorption is placed on most inner side, and three layers logical viscous by binder
It closes.
Embodiment 3:
A kind of waterproof uvioresistant fabrics, fabric include waterproof layer, uvioresistant layer and absorbed layer, and uvioresistant layer is prevented
Water layer and absorbed layer package;Waterproof layer is formed using the raw material hybrid woven of following parts by weight composition:
60 parts of Fypro;
30 parts of waterproof polypropylene fibre.
Waterproof polypropylene fibre contains the waterproofing agent of 8wt%;Waterproofing agent includes 25 parts of hydroxypropyl methyl cellulose-ethoxys
Cellulose-cellulose ether and 14 parts of polyoxyethylene ether trisiloxanes.
Uvioresistant layer includes the raw material of following parts by weight composition:
34 parts of polyacrylonitrile fibre;
25 parts of acid fiber by polylactic;
6 parts of mint fibers.
Mint fibers further include the UV resistant agent of 7wt%;UV resistant agent includes 12 parts of Ti2AlC, 5 parts of metrafenones, 4
Part hexamethylphosphoramide and 4 parts of sulfated castor oils.
Absorbed layer includes the raw material of following parts by weight composition:
42 parts of cotton fiber;
26 parts of flax fiber;
5 parts of bamboo fibre.
Waterproof is placed on outermost layer, antibacterial to be placed on centre, and absorption is placed on most inner side, and three layers logical viscous by binder
It closes.
Comparative example 1:
A kind of waterproof uvioresistant fabrics, fabric include waterproof layer, uvioresistant layer and absorbed layer, and uvioresistant layer is prevented
Water layer and absorbed layer package;Waterproof layer is formed using the raw material hybrid woven of following parts by weight composition:
50 parts of Fypro;
20 parts of waterproof polypropylene fibre.
Waterproof polypropylene fibre contains the waterproofing agent of 6wt%;Waterproofing agent is hydroxypropyl methyl cellulose-hydroxy ethyl fiber
Element-cellulose ether.
Uvioresistant layer includes the raw material of following parts by weight composition:
30 parts of polyacrylonitrile fibre;
20 parts of acid fiber by polylactic;
4 parts of mint fibers;
Mint fibers further include the UV resistant agent of 3wt%;UV resistant agent includes 10 parts of Ti2AlC, 3 parts of metrafenones, 2
Part hexamethylphosphoramide and 2 parts of sulfated castor oils.
Absorbed layer includes the raw material of following parts by weight composition:
40 parts of cotton fiber;
24 parts of flax fiber;
3 parts of bamboo fibre.
Waterproof is placed on outermost layer, antibacterial to be placed on centre, and absorption is placed on most inner side, and three layers logical viscous by binder
It closes.
Comparative example 2:
A kind of waterproof uvioresistant fabrics, fabric include waterproof layer, uvioresistant layer and absorbed layer, and uvioresistant layer is prevented
Water layer and absorbed layer package;Waterproof layer is formed using the raw material hybrid woven of following parts by weight composition:
50 parts of Fypro;
20 parts of waterproof polypropylene fibre.
Waterproof polypropylene fibre contains the waterproofing agent of 6wt%;Waterproofing agent is polyoxyethylene ether trisiloxanes.
Uvioresistant layer includes the raw material of following parts by weight composition:
30 parts of polyacrylonitrile fibre;
20 parts of acid fiber by polylactic;
4 parts of mint fibers;
Mint fibers further include the UV resistant agent of 3wt%;UV resistant agent includes 10 parts of Ti2AlC, 3 parts of metrafenones, 2
Part hexamethylphosphoramide and 2 parts of sulfated castor oils.
Absorbed layer includes the raw material of following parts by weight composition:
40 parts of cotton fiber;
24 parts of flax fiber;
3 parts of bamboo fibre.
Waterproof is placed on outermost layer, antibacterial to be placed on centre, and absorption is placed on most inner side, and three layers logical viscous by binder
It closes.
Comparative example 3:
A kind of waterproof uvioresistant fabrics, fabric include waterproof layer, uvioresistant layer and absorbed layer, and uvioresistant layer is prevented
Water layer and absorbed layer package;Waterproof layer is formed using the raw material hybrid woven of following parts by weight composition:
54 parts of Fypro;
22 parts of waterproof polypropylene fibre.
Waterproof polypropylene fibre contains the waterproofing agent of 7wt%;Waterproofing agent includes 22 parts of hydroxypropyl methyl cellulose-ethoxys
Cellulose-cellulose ether and 13 parts of polyoxyethylene ether trisiloxanes.
Uvioresistant layer includes the raw material of following parts by weight composition:
32 parts of polyacrylonitrile fibre;
5 parts of mint fibers;
Mint fibers further include the UV resistant agent of 5wt%;UV resistant agent includes 11 parts of Ti2AlC, 3~5 parts of metrafenones
With 3 parts of sulfated castor oils;
Absorbed layer includes the raw material of following parts by weight composition:
41 parts of cotton fiber;
25 parts of flax fiber;
4 parts of bamboo fibre;
Waterproof is placed on outermost layer, antibacterial to be placed on centre, and absorption is placed on most inner side, and three layers logical viscous by binder
It closes.
Comparative example 4:
A kind of waterproof uvioresistant fabrics, fabric include waterproof layer, uvioresistant layer and absorbed layer, and uvioresistant layer is prevented
Water layer and absorbed layer package;Waterproof layer is formed using the raw material hybrid woven of following parts by weight composition:
54 parts of Fypro;
22 parts of waterproof polypropylene fibre.
Waterproof polypropylene fibre contains the waterproofing agent of 7wt%;Waterproofing agent includes 22 parts of hydroxypropyl methyl cellulose-ethoxys
Cellulose-cellulose ether and 13 parts of polyoxyethylene ether trisiloxanes.
Uvioresistant layer includes the raw material of following parts by weight composition:
32 parts of polyacrylonitrile fibre;
24 parts of acid fiber by polylactic;
5 parts of mint fibers;
Mint fibers further include the UV resistant agent of 5wt%;UV resistant agent includes 11 parts of Ti2AlC, 3~5 parts of benzene bacterium
Ketone, 3 parts of hexamethylphosphoramide;
Absorbed layer includes the raw material of following parts by weight composition:
41 parts of cotton fiber;
25 parts of flax fiber;
Waterproof is placed on outermost layer, antibacterial to be placed on centre, and absorption is placed on most inner side, and three layers logical viscous by binder
It closes.
The performance test results of embodiment and comparative example are listed below:
It can be seen that by examples detailed above, the material obtained not only has excellent uvioresistant performance, and has good anti-
Aqueous energy.
Although the embodiments of the present invention have been disclosed as above, but its is not only in the description and the implementation listed
With it can be fully applied to various fields suitable for the present invention, for those skilled in the art, can be easily
Realize other modification, therefore without departing from the general concept defined in the claims and the equivalent scope, the present invention is simultaneously unlimited
In specific details.
Claims (10)
1. a kind of waterproof uvioresistant fabrics, which is characterized in that the fabric includes waterproof layer, uvioresistant layer and absorbed layer,
The uvioresistant layer is wrapped up by waterproof layer and absorbed layer;The waterproof layer uses the raw material hybrid woven of following parts by weight composition
It forms:
50~60 parts of Fypro;
20~30 parts of waterproof polypropylene fibre.
2. waterproof uvioresistant fabrics according to claim 1, which is characterized in that the waterproof polypropylene fibre contains 6
The waterproofing agent of~8wt%.
3. waterproof uvioresistant fabrics according to claim 2, which is characterized in that the waterproofing agent includes 20~25 parts of hydroxyls
Propyl methocel-hydroxyethyl cellulose-cellulose ether and 12~14 parts of polyoxyethylene ether trisiloxanes.
4. waterproof uvioresistant fabrics according to claim 2, which is characterized in that the uvioresistant layer includes following weight
Measure the raw material of part composition:
30~34 parts of polyacrylonitrile fibre;
20~25 parts of acid fiber by polylactic.
5. waterproof uvioresistant fabrics according to claim 4, which is characterized in that further include 4~6 parts of mint fibers.
6. waterproof uvioresistant fabrics according to claim 5, which is characterized in that the mint fibers further include 3~
The UV resistant agent of 7wt%.
7. waterproof uvioresistant fabrics according to claim 6, which is characterized in that the UV resistant agent includes 10~12
Part Ti2AlC, 3~5 parts of metrafenones, 2~4 parts of hexamethylphosphoramide and 2~4 parts of sulfated castor oils.
8. waterproof uvioresistant fabrics according to claim 1, which is characterized in that the absorbed layer includes following parts by weight
The raw material of composition:
40~42 parts of cotton fiber;
24~26 parts of flax fiber.
9. waterproof uvioresistant fabrics according to claim 8, which is characterized in that the absorbed layer further includes 3~5 parts
Bamboo fibre.
10. waterproof uvioresistant fabrics according to claim 1, which is characterized in that the waterproof is placed on outermost layer, suppression
Bacterium is placed on centre, and absorption is placed on most inner side, and three layers pass through the logical bonding of binder.