CN109666214A - 一种低能耗epp阻燃颗粒 - Google Patents
一种低能耗epp阻燃颗粒 Download PDFInfo
- Publication number
- CN109666214A CN109666214A CN201811442081.5A CN201811442081A CN109666214A CN 109666214 A CN109666214 A CN 109666214A CN 201811442081 A CN201811442081 A CN 201811442081A CN 109666214 A CN109666214 A CN 109666214A
- Authority
- CN
- China
- Prior art keywords
- parts
- fire
- retardant
- agent
- crosslinking agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种低能耗EPP阻燃颗粒，包括以下重量份的原料：聚丙烯树脂130‑150份、乙烯类弹性体20‑40份、苯烯类弹性体3‑5份、尼龙树脂10‑15份、交联剂1‑3份、助交联剂0.5‑1份、相容剂2‑4份、光稳定剂1‑3份、抗氧剂1‑3份、增强剂3‑8份、耐磨剂1‑3份、阻燃剂3‑5份、阻燃助剂3‑5份、聚乙烯蜡润滑剂0.5‑1.5份、阻燃协效剂3‑5份、碳黑颜料3‑20份。本发明设计巧妙，成分合理，阻燃效果好，适合推广使用。
Description
技术领域
本发明涉及阻燃颗粒技术领域，尤其涉及一种低能耗EPP阻燃颗粒。
背景技术
阻燃剂，赋予易燃聚合物难燃性的功能性助剂，主要是针对高分子材料的阻燃设计的；阻燃剂有多种类型，按使用方法分为添加型阻燃剂和反应型阻燃剂。
添加型阻燃剂是通过机械混合方法加入到聚合物中，使聚合物具有阻燃性的，目前添加型阻燃剂主要有有机阻燃剂和无机阻燃剂，卤系阻燃剂（有机氯化物和有机溴化物）和非卤。有机是以溴系、磷氮系、氮系和红磷及化合物为代表的一些阻燃剂，无机主要是三氧化二锑、氢氧化镁、氢氧化铝，硅系等阻燃体系。
现有的阻燃剂阻燃时间短，不能持久阻燃，阻燃效果也不是很好，为此，本发明提出一种低能耗EPP阻燃颗粒。
发明内容
本发明的目的是为了解决现有技术中存在的缺点，而提出的一种低能耗EPP阻燃颗粒。
为了实现上述目的，本发明采用了如下技术方案：
一种低能耗EPP阻燃颗粒，包括以下重量份的原料：聚丙烯树脂130-150份、乙烯类弹性体20-40份、苯烯类弹性体3-5份、尼龙树脂10-15份、交联剂1-3份、助交联剂0.5-1份、相容剂2-4份、光稳定剂1-3份、抗氧剂1-3份、增强剂3-8份、耐磨剂1-3份、阻燃剂3-5份、阻燃助剂3-5份、聚乙烯蜡润滑剂0.5-1.5份、阻燃协效剂3-5份、碳黑颜料3-20份。
优选的，包括以下重量份的原料：聚丙烯树脂135-145份、乙烯类弹性体25-35份、苯烯类弹性体3.5-4.5份、尼龙树脂11-14份、交联剂1.5-2.5份、助交联剂0.6-0.9份、相容剂2.5-3.5份、光稳定剂1.5-2.5份、抗氧剂1.5-2.5份、增强剂4-7份、耐磨剂1.5-2.5份、阻燃剂3.5-4.5份、阻燃助剂3.5-4.5份、聚乙烯蜡润滑剂0.7-1.3份、阻燃协效剂3.5-4.5份、碳黑颜料5-18份。
优选的，包括以下重量份的原料：聚丙烯树脂140份、乙烯类弹性体30份、苯烯类弹性体4份、尼龙树脂12.5份、交联剂2份、助交联剂0.75份、相容剂3份、光稳定剂2份、抗氧剂2份、增强剂5.5份、耐磨剂2份、阻燃剂4份、阻燃助剂4份、聚乙烯蜡润滑剂1份、阻燃协效剂4份、碳黑颜料13份。
优选的，所述阻燃剂为有机硅酮阻燃剂；阻燃助剂为硬脂酸镁、聚磷酸铵、氢氧化铝和氢氧化镁中的一种或几种。
优选的，所述阻燃协效剂为硫酸钡、纳米氢氧化铝、纳米碳酸钙、纳米蒙脱土、 滑石粉中的任一种。
优选的，包括以下制备步骤，
S1，将相应重量份的聚丙烯树脂、乙烯类弹性体、苯烯类弹性体和尼龙树脂用混合机混合，在30℃的温度下，以300r/min的速度搅拌30min，搅拌完毕后的混合物放置在25℃的温度下存放，得到混合物A备用；
S2，将得到的混合物A和交联剂、助交联剂、相容剂、光稳定剂、抗氧剂、增强剂、耐磨剂、阻燃剂、阻燃助剂、聚乙烯蜡润滑剂、阻燃协效剂、碳黑颜料加入到高速混合机中在80℃状态下混合100min，随后在双螺杆挤出机上熔融挤出造粒；
S3，得到的颗粒进行交联成型，得到阻燃颗粒。
本发明提出的一种低能耗EPP阻燃颗粒，将相应重量份的聚丙烯树脂、乙烯类弹性体、苯烯类弹性体和尼龙树脂用混合机混合，在30℃的温度下，以300r/min的速度搅拌30min，搅拌完毕后的混合物放置在25℃的温度下存放，得到混合物A备用，颗粒进行交联成型，得到阻燃颗粒，制备方法消耗的能源较低，因此成本低，通过阻燃助剂、聚乙烯蜡润滑剂和阻燃协效剂的添加，可以提高本阻燃颗粒的阻燃效果，延长本阻燃颗粒的阻燃时间，本发明设计巧妙，成分合理，阻燃效果好，适合推广使用。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。
实施例一
本发明提出的一种低能耗EPP阻燃颗粒，包括以下重量份的原料：聚丙烯树脂130份、乙烯类弹性体20份、苯烯类弹性体3份、尼龙树脂10份、交联剂1份、助交联剂0.5份、相容剂2份、光稳定剂1份、抗氧剂1份、增强剂3-8份、耐磨剂1份、阻燃剂3份、阻燃助剂3份、聚乙烯蜡润滑剂0.5份、阻燃协效剂3份、碳黑颜料3份。
本发明提出的一种低能耗EPP阻燃颗粒，包括以下制备步骤，
S1，将相应重量份的聚丙烯树脂、乙烯类弹性体、苯烯类弹性体和尼龙树脂用混合机混合，在30℃的温度下，以300r/min的速度搅拌30min，搅拌完毕后的混合物放置在25℃的温度下存放，得到混合物A备用；
S2，将得到的混合物A和交联剂、助交联剂、相容剂、光稳定剂、抗氧剂、增强剂、耐磨剂、阻燃剂、阻燃助剂、聚乙烯蜡润滑剂、阻燃协效剂、碳黑颜料加入到高速混合机中在80℃状态下混合100min，随后在双螺杆挤出机上熔融挤出造粒；
S3，得到的颗粒进行交联成型，得到阻燃颗粒。
实施例二
本发明提出的一种低能耗EPP阻燃颗粒，包括以下重量份的原料：聚丙烯树脂140份、乙烯类弹性体30份、苯烯类弹性体4份、尼龙树脂12.5份、交联剂2份、助交联剂0.75份、相容剂3份、光稳定剂2份、抗氧剂2份、增强剂5.5份、耐磨剂2份、阻燃剂4份、阻燃助剂4份、聚乙烯蜡润滑剂1份、阻燃协效剂4份、碳黑颜料13份。
本发明提出的一种低能耗EPP阻燃颗粒，包括以下制备步骤，
S1，将相应重量份的聚丙烯树脂、乙烯类弹性体、苯烯类弹性体和尼龙树脂用混合机混合，在30℃的温度下，以300r/min的速度搅拌30min，搅拌完毕后的混合物放置在25℃的温度下存放，得到混合物A备用；
S2，将得到的混合物A和交联剂、助交联剂、相容剂、光稳定剂、抗氧剂、增强剂、耐磨剂、阻燃剂、阻燃助剂、聚乙烯蜡润滑剂、阻燃协效剂、碳黑颜料加入到高速混合机中在80℃状态下混合100min，随后在双螺杆挤出机上熔融挤出造粒；
S3，得到的颗粒进行交联成型，得到阻燃颗粒。
实施例三
本发明提出的一种低能耗EPP阻燃颗粒，包括以下重量份的原料：聚丙烯树脂150份、乙烯类弹性体40份、苯烯类弹性体5份、尼龙树脂15份、交联剂3份、助交联剂1份、相容剂4份、光稳定剂3份、抗氧剂3份、增强剂8份、耐磨剂3份、阻燃剂5份、阻燃助剂5份、聚乙烯蜡润滑剂1.5份、阻燃协效剂5份、碳黑颜料20份。
本发明提出的一种低能耗EPP阻燃颗粒，包括以下制备步骤，
S1，将相应重量份的聚丙烯树脂、乙烯类弹性体、苯烯类弹性体和尼龙树脂用混合机混合，在30℃的温度下，以300r/min的速度搅拌30min，搅拌完毕后的混合物放置在25℃的温度下存放，得到混合物A备用；
S2，将得到的混合物A和交联剂、助交联剂、相容剂、光稳定剂、抗氧剂、增强剂、耐磨剂、阻燃剂、阻燃助剂、聚乙烯蜡润滑剂、阻燃协效剂、碳黑颜料加入到高速混合机中在80℃状态下混合100min，随后在双螺杆挤出机上熔融挤出造粒；
S3，得到的颗粒进行交联成型，得到阻燃颗粒。
本发明提出的一种低能耗EPP阻燃颗粒，将相应重量份的聚丙烯树脂、乙烯类弹性体、苯烯类弹性体和尼龙树脂用混合机混合，在30℃的温度下，以300r/min的速度搅拌30min，搅拌完毕后的混合物放置在25℃的温度下存放，得到混合物A备用，颗粒进行交联成型，得到阻燃颗粒，制备方法消耗的能源较低，因此成本低，通过阻燃助剂、聚乙烯蜡润滑剂和阻燃协效剂的添加，可以提高本阻燃颗粒的阻燃效果，延长本阻燃颗粒的阻燃时间，本发明设计巧妙，成分合理，阻燃效果好，适合推广使用。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (6)
1.一种低能耗EPP阻燃颗粒，其特征在于，包括以下重量份的原料：聚丙烯树脂130-150份、乙烯类弹性体20-40份、苯烯类弹性体3-5份、尼龙树脂10-15份、交联剂1-3份、助交联剂0.5-1份、相容剂2-4份、光稳定剂1-3份、抗氧剂1-3份、增强剂3-8份、耐磨剂1-3份、阻燃剂3-5份、阻燃助剂3-5份、聚乙烯蜡润滑剂0.5-1.5份、阻燃协效剂3-5份、碳黑颜料3-20份。
2.根据权利要求1所述的一种低能耗EPP阻燃颗粒，其特征在于，包括以下重量份的原料：聚丙烯树脂135-145份、乙烯类弹性体25-35份、苯烯类弹性体3.5-4.5份、尼龙树脂11-14份、交联剂1.5-2.5份、助交联剂0.6-0.9份、相容剂2.5-3.5份、光稳定剂1.5-2.5份、抗氧剂1.5-2.5份、增强剂4-7份、耐磨剂1.5-2.5份、阻燃剂3.5-4.5份、阻燃助剂3.5-4.5份、聚乙烯蜡润滑剂0.7-1.3份、阻燃协效剂3.5-4.5份、碳黑颜料5-18份。
3.根据权利要求1所述的一种低能耗EPP阻燃颗粒，其特征在于，包括以下重量份的原料：聚丙烯树脂140份、乙烯类弹性体30份、苯烯类弹性体4份、尼龙树脂12.5份、交联剂2份、助交联剂0.75份、相容剂3份、光稳定剂2份、抗氧剂2份、增强剂5.5份、耐磨剂2份、阻燃剂4份、阻燃助剂4份、聚乙烯蜡润滑剂1份、阻燃协效剂4份、碳黑颜料13份。
4.根据权利要求1所述的一种低能耗EPP阻燃颗粒，其特征在于，所述阻燃剂为有机硅酮阻燃剂；阻燃助剂为硬脂酸镁、聚磷酸铵、氢氧化铝和氢氧化镁中的一种或几种。
5.根据权利要求1所述的一种低能耗EPP阻燃颗粒，其特征在于，所述阻燃协效剂为硫酸钡、纳米氢氧化铝、纳米碳酸钙、纳米蒙脱土、 滑石粉中的任一种。
6.根据权利要求1所述的一种低能耗EPP阻燃颗粒，其特征在于，包括以下制备步骤，
S1，将相应重量份的聚丙烯树脂、乙烯类弹性体、苯烯类弹性体和尼龙树脂用混合机混合，在30℃的温度下，以300r/min的速度搅拌30min，搅拌完毕后的混合物放置在25℃的温度下存放，得到混合物A备用；
S2，将得到的混合物A和交联剂、助交联剂、相容剂、光稳定剂、抗氧剂、增强剂、耐磨剂、阻燃剂、阻燃助剂、聚乙烯蜡润滑剂、阻燃协效剂、碳黑颜料加入到高速混合机中在80℃状态下混合100min，随后在双螺杆挤出机上熔融挤出造粒；
S3，得到的颗粒进行交联成型，得到阻燃颗粒。