CN109628834A - 一种重型变速器轴齿零件用高镍含铌高强度渗碳钢材料 - Google Patents
一种重型变速器轴齿零件用高镍含铌高强度渗碳钢材料 Download PDFInfo
- Publication number
- CN109628834A CN109628834A CN201811640629.7A CN201811640629A CN109628834A CN 109628834 A CN109628834 A CN 109628834A CN 201811640629 A CN201811640629 A CN 201811640629A CN 109628834 A CN109628834 A CN 109628834A
- Authority
- CN
- China
- Prior art keywords
- nickelic
- niobium
- heavy
- transmission axis
- tooth part
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种重型变速器轴齿零件用高镍含铌高强度渗碳钢材料,其特征在于:高镍含铌高强度渗碳钢材料,包括C、Si、Mn、P、S、Cr、Mo、Ni、Nb、Fe化学元素,各元素质量百分比为C:0.15‑0.20%,Si:0.15‑0.35%,Mn:0.60‑0.90%,P≤0.025%,S:≤0.030%,Ni:1.40‑1.70%,Cr:0.85‑1.35%,Mo:0.25‑0.35%,Nb:0.015‑0.030%,其余为Fe和不可避免杂质。能够满足重型变速器轴齿零件高强度、高韧性、高抗冲击性和良好的切削加工性等综合要求。
Description
技术领域
本发明涉及一种重型变速器轴齿零件用高镍含铌高强度渗碳钢材料,属汽车高强度材料技术领域。
背景技术
齿轮钢是汽车材料中用量较大,要求较高的关键材料之一。不仅影响车辆寿命、能耗等技术经济指标,而且对于满足安全、环保及舒适性要求也是至关重要的。
我国轻、微、轿、中型变速器齿轮钢牌号较多,基本满足使用要求。而重型变速器齿轮用钢,尚有待开发和生产。
发明内容
本发明的目的是提供一种重型变速器轴齿零件用高镍含铌高强度渗碳钢材料,该材料具有高强度、高韧性和抗冲击性等优点,同时,该材料亦可作为高温渗碳钢,采用高温渗碳工艺,缩短渗碳时间,环保节能,提高生产效率,具有良好的应用前景。
本发明的技术方案是这样实现的:一种重型变速器轴齿零件用高镍含铌高强度渗碳钢材料,其特征在于:高镍含铌高强度渗碳钢材料,包括C、Si、Mn、P、S、Cr、Mo、Ni、Nb、Fe化学元素,各元素质量百分比为C:0.15-0.20%,Si:0.15-0.35%,Mn:0.60-0.90%,P≤0.025%,S: ≤0.030%,Ni:1.40-1.70%,Cr:0.85-1.35%, Mo:0.25-0.35%,Nb:0.015-0.030%,其余为Fe和不可避免杂质。
该渗碳齿轮钢的力学性能数据要求:
Rm≥1200MPa; RP0.2≥800 MPa;δ≥7%;ψ≥30%;冲击韧性值ak≥41 J/cm2。
本发明积极效果是能够满足重型变速器轴齿零件高强度、高韧性、高抗冲击性和良好的切削加工性等综合要求。
具体实施方式
下面结合实施例对本发明做进一步说明:
实施例1
一种重型变速器轴齿零件用高镍含铌高强度渗碳钢材料,其特征在于:高镍含铌高强度渗碳钢材料,包括C、Si、Mn、P、S、Cr、Mo、Ni、Nb、Fe化学元素,各元素质量百分比为C:0.15%,Si:0.15%,Mn:0.60%,P≤0.025%,S: ≤0.030%,Ni:1.40%,Cr:0.85%, Mo:0.25%,Nb:0.015%,其余为Fe和不可避免杂质。
该渗碳齿轮钢的力学性能数据要求:
Rm≥1200MPa; RP0.2≥800 MPa;δ≥7%;ψ≥30%;冲击韧性值ak≥41 J/cm2。
实施例2
一种重型变速器轴齿零件用高镍含铌高强度渗碳钢材料,其特征在于:高镍含铌高强度渗碳钢材料,包括C、Si、Mn、P、S、Cr、Mo、Ni、Nb、Fe化学元素,各元素质量百分比为C:0.20%,Si: 0.35%,Mn: 0.90%,P≤0.025%,S: ≤0.030%,Ni: 1.70%,Cr: 1.35%, Mo:0.35%,Nb: 0.030%,其余为Fe和不可避免杂质。
该渗碳齿轮钢的力学性能数据要求:
Rm≥1200MPa; RP0.2≥800 MPa;δ≥7%;ψ≥30%;冲击韧性值ak≥41 J/cm2。
实施例3
一种重型变速器轴齿零件用高镍含铌高强度渗碳钢材料,其特征在于:高镍含铌高强度渗碳钢材料,包括C、Si、Mn、P、S、Cr、Mo、Ni、Nb、Fe化学元素,各元素质量百分比为C:0.18%,Si:0.25%,Mn:0.70%,P≤0.025%,S: ≤0.030%,Ni:1.5%,Cr: 1.00%, Mo:0.30%,Nb:0.020%,其余为Fe和不可避免杂质。
该渗碳齿轮钢的力学性能数据要求:
Rm≥1200MPa; RP0.2≥800 MPa;δ≥7%;ψ≥30%;冲击韧性值ak≥41 J/cm2。
Claims (1)
1.一种重型变速器轴齿零件用高镍含铌高强度渗碳钢材料,其特征在于:高镍含铌高强度渗碳钢材料,包括C、Si、Mn、P、S、Cr、Mo、Ni、Nb、Fe化学元素,各元素质量百分比为C:0.15-0.20%,Si:0.15-0.35%,Mn:0.60-0.90%,P≤0.025%,S: ≤0.030%,Ni:1.40-1.70%,Cr:0.85-1.35%, Mo:0.25-0.35%,Nb:0.015-0.030%,其余为Fe和不可避免杂质。