CN109627515A - A kind of bonding anti-dropout rubber compounding - Google Patents
A kind of bonding anti-dropout rubber compounding Download PDFInfo
- Publication number
- CN109627515A CN109627515A CN201811295115.2A CN201811295115A CN109627515A CN 109627515 A CN109627515 A CN 109627515A CN 201811295115 A CN201811295115 A CN 201811295115A CN 109627515 A CN109627515 A CN 109627515A
- Authority
- CN
- China
- Prior art keywords
- parts
- carbon black
- rubber
- dropout
- bonding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of bonding anti-dropout rubber compoundings, are made of raw material from the following weight: 4155:100 parts of nitrile rubber, activated magnesia MgO150:5 ~ 10 part, anti-aging agent RD: 1 ~ 2 part, stearic acid: 1 ~ 2 part, DBU formates: 1 ~ 2 part, carbon black N550:35 ~ 50 part, carbon black N774:10 ~ 25 part, silicon powder 750:15 ~ 30 part, plasticizer RS107:10 ~ 20 part, sulphur S-80GE:1 ~ 2 part, accelerant CZ: 1 ~ 2 part, altax: 0.5 ~ 1.0 part.The invention has the following advantages: this kind maintains the excellent properties of nitrile rubber using nitrile rubber as the formula of base-material, and adhesive strength >=3.0N/mm with fluororesin THV 815, solve the technical issues of rubber compounding will appear delamination when bonding with fluororesin in the prior art.
Description
Technical field
The present invention relates to a kind of rubber compounding, specifically a kind of bonding anti-dropout rubber compounding.
Background technique
Due to the severization of national environmental standard, the piping material of automotive fuel oil system also requires to upgrade, the following Fuel System
Performance needs of the road under the overall leadership in terms of resistance to infiltration are greatly enhanced, complete to the year two thousand twenty with the gradually implementation of six regulation of state
Automobile, which requires, within the scope of state meets six emission regulation standard of state.Vehicle emission amount includes: hydrocarbon, oxynitrides,
Oxygen sulfur compound, and with automobile fuel oil pipeline it is closely bound up be hydrocarbon discharge.Hydrocarbon is arranged in fuel system
Putting source is mainly infiltration leakage, traditional NBR/PVC(nitrile rubber, polyvinyl chloride alloy rubber), FKM (fluorubber)+ECO
(chlorohydrin rubber) structure sebific duct can no longer meet harsh six emission request of state.Nitrile rubber (NBR) is as a kind of oil resistant, resistance to
The preferable synthetic rubber of aging, the composite construction (NBR/THV/NBR/CSM) with fluororesin (THV) is added as vehicle fuel
The direction of note pipe and canister evaporation tube.
Fluororesin be tetrafluoroethene (TFE), vinylidene (VDA), hexafluoroethylene (HFP) constituent, have it is excellent
Oil resistivity, osmotic-pressure-tolerant, anti-flammability and leakproofness, but due in its internal composition the bond energy of fluorine atom and carbon atom it is very high,
And the radius very little of fluorine atom, enables fluorine atom to be closely spaced around carbon atom, forms the protective barrier of C-C key, this
Sample just imparts the higher chemical inertness of fluororesin.Nitrile rubber is to be formed by butadiene and acrylonitrile through emulsion polymerization, usually
In the case of vulcanized using sulphur system, therefore, when producing nitrile rubber and fluororesin product, due to the chemical inertness of fluororesin
With the difference of vulcanization characteristics, common rubber compounding will appear delamination when bonding with fluororesin, be unable to reach industrialization
Purpose.In order to enable rubber and fluororesin to reach enough adhesive strengths, by lot of experiment validation, DBU formic acid is found
Salt can promote the adhesive force of the two, and DBU formates is a kind of bicyclic amidine compound, can generate the work of nitrogen at high temperature
Free love base, allows fluororesin to connect with nitrile rubber by way of bridge formation, achievees the purpose that chemical crosslinking.The present invention is logical
It crosses and nitrile rubber is cooperated using adhesive DBU formates, while keeping nitrile rubber excellent properties, solve fourth
The delamination problems of nitrile rubber and fluororesin make nitrile rubber and the product of fluororesin structure can be realized industrialization, and this group
Structure cost performance with higher is closed, for the material selection for meeting six emission regulation vehicle fuel filler pipe of state and canister evaporation tube
Good basis is established.
For this purpose, applicant proposed a kind of new technical solutions, and provide a kind of and excellent fourth of fluororesin adhesiveness
Nitrile rubber formula.
Summary of the invention
Technical problem to be solved by the invention is to provide a kind of bonding anti-dropout rubber compoundings.
In order to solve the above technical problems, the technical scheme is that a kind of bonding anti-dropout rubber compounding, by following heavy
The raw material of amount part is made: 4155:100 parts of nitrile rubber, activated magnesia MgO150:5 ~ 10 part, anti-aging agent RD: 1 ~ 2 part, tristearin
Acid: 1 ~ 2 part, DBU formates: 1 ~ 2 part, carbon black N550:35 ~ 50 part, carbon black N774:10 ~ 25 part, silicon powder 750:15 ~ 30 part, increasing
Mould agent RS107:10 ~ 20 part, sulphur S-80GE:1 ~ 2 part, accelerant CZ: 1 ~ 2 part, altax: 0.5 ~ 1.0 part.
Further, a kind of bonding anti-dropout rubber compounding, is made of raw material from the following weight: nitrile rubber 4155:
100 parts, activated magnesia MgO150:8 ~ 10 part, anti-aging agent RD: 1 ~ 1.5 part, stearic acid: 1 ~ 1.5 part, DBU formates: 1.5 ~ 2
Part, carbon black N550:45 ~ 50 part, carbon black N774:20 ~ 25 part, silicon powder 750:15 ~ 30 part, plasticizer RS107:18 ~ 20 part, sulphur
S-80GE:1 ~ 1.5 part, accelerant CZ: 1 ~ 1.5 part, altax: 0.5 ~ 1.0 part.
Preferably, a kind of bonding anti-dropout rubber compounding, is made of raw material from the following weight: nitrile rubber
4155:100 parts, MgO150:10 parts of activated magnesia, anti-aging agent RD: 1.5 parts, stearic acid: 1.5 parts, DBU formates: 2 parts, charcoal
N550:50 parts black, N774:25 parts of carbon black, RS107:20 parts of plasticizer, S-80GE:1.8 parts of sulphur, promotes 750:30 parts of silicon powder
CZ:1.5 parts of agent, altax: 1.0 parts.
Preferably, the weight part ratio of the nitrile rubber 4155 and DBU formates is 50:1.
Preferably, the carbon black N550 and carbon black N774 weight part ratio are 2:1.
Preferably, accelerant CZ and altax weight part ratio are 3:2.
Further, for the rubber and fluorine resin film of formula preparation using molding vulcanization, temperature is 160 DEG C, the time
25min, pressure 10Mpa.
Wherein above-mentioned raw material to be as follows:
Nitrile rubber 4155, German A Langxin section;
Activated magnesia MgO150, Nippon Union K. K;
Anti-aging agent RD, accelerant CZ, altax, Shandong Cao County this pass your company;
Stearic acid, Shandong Jin Dashuan roc group;
Carbon black N550, N774, Cabot Co., Ltd, the U.S.;
Silicon powder 750, Fuyang Li Pu chemical company;
Plasticizer RS107, Japanese ADEKA;
Sulphur S-80GE, Ningbo flowers of sulfur;
By adopting the above-described technical solution, a kind of bonding anti-dropout rubber compounding, is made: butyronitrile rubber of following raw material
4155:100 parts of glue, activated magnesia MgO150:5 ~ 10 part, anti-aging agent RD: 1 ~ 2 part, stearic acid: 1 ~ 2 part, DBU formates: 1 ~
2 parts, carbon black N550:35 ~ 50 part, carbon black N774:10 ~ 25 part, silicon powder 750:15 ~ 30 part, plasticizer RS107:10 ~ 20 part, sulphur
Sulphur S-80GE:1 ~ 2 part, accelerant CZ: 1 ~ 2 part, altax: 0.5 ~ 1.0 part;The invention has the following advantages: should
Kind maintains the excellent properties of nitrile rubber using nitrile rubber as the formula of base-material, and strong with the bonding of fluororesin THV 815
Degree >=3.0N/mm solves the technical issues of rubber compounding will appear delamination when bonding with fluororesin in the prior art;And
The sizing material processing performance is good, excellent storage stability.
Specific embodiment
The present invention is described further combined with specific embodiments below.
A kind of bonding anti-dropout rubber compounding of embodiment 1, is made of following raw material:
Serial number | Component | Dosage/part |
1 | Nitrile rubber 4155 | 100 |
2 | Activated magnesia MgO150 | 5 |
3 | Anti-aging agent RD | 1 |
4 | Stearic acid | 1 |
5 | DBU formates | 1 |
6 | Carbon black N550 | 45 |
7 | Carbon black N774 | 15 |
8 | Silicon powder 750 | 20 |
9 | Plasticizer RS107 | 16 |
10 | Sulphur S-80GE | 1.5 |
11 | Accelerant CZ | 1 |
12 | Altax | 0.5 |
The rubber performance of formula preparation:
Test result: the adhesive strength of fluorubber and fluororesin THV 815 are 4.8N/mm.
A kind of bonding anti-dropout rubber compounding of embodiment 2, is made of following raw material:
Serial number | Component | Dosage/part |
1 | Nitrile rubber 4155 | 100 |
2 | Activated magnesia MgO150 | 8 |
3 | Anti-aging agent RD | 1.5 |
4 | Stearic acid | 1 |
5 | DBU formates | 1.5 |
6 | Carbon black N550 | 45 |
7 | Carbon black N774 | 20 |
8 | Silicon powder 750 | 15 |
9 | Plasticizer RS107 | 18 |
10 | Sulphur S-80GE | 1.8 |
11 | Accelerant CZ | 1 |
12 | Altax | 0.5 |
The rubber performance of formula preparation:
Test result: the adhesive strength of fluorubber and fluororesin THV 815 are 5.6N/mm.
A kind of bonding anti-dropout rubber compounding of embodiment 3, is made of following raw material:
Serial number | Component | Dosage/part |
1 | Nitrile rubber 4155 | 100 |
2 | Activated magnesia MgO150 | 10 |
3 | Anti-aging agent RD | 1 |
4 | Stearic acid | 1 |
5 | DBU formates | 2 |
6 | Carbon black N550 | 50 |
7 | Carbon black N774 | 20 |
8 | Silicon powder 750 | 20 |
9 | Plasticizer RS107 | 18 |
10 | Sulphur S-80GE | 2 |
11 | Accelerant CZ | 1 |
12 | Altax | 0.8 |
The rubber performance of formula preparation:
Test result: the adhesive strength of fluorubber and fluororesin THV 815 are 5.8N/mm.
A kind of bonding anti-dropout rubber compounding of embodiment 4, is made of following raw material:
Serial number | Component | Dosage/part |
1 | Nitrile rubber 4155 | 100 |
2 | Activated magnesia MgO150 | 10 |
3 | Anti-aging agent RD | 1.5 |
4 | Stearic acid | 1.5 |
5 | DBU formates | 2 |
6 | Carbon black N550 | 50 |
7 | Carbon black N774 | 25 |
8 | Silicon powder 750 | 30 |
9 | Plasticizer RS107 | 20 |
10 | Sulphur S-80GE | 1.8 |
11 | Accelerant CZ | 1.5 |
12 | Altax | 1 |
The rubber performance of formula preparation:
Test result: the adhesive strength of fluorubber and fluororesin THV 815 are 5.9N/mm.
A kind of bonding anti-dropout rubber compounding of embodiment 5, is made of following raw material:
Serial number | Component | Dosage/part |
1 | Nitrile rubber 4155 | 100 |
2 | Activated magnesia MgO150 | 10 |
3 | Anti-aging agent RD | 2 |
4 | Stearic acid | 2 |
5 | DBU formates | 2 |
6 | Carbon black N550 | 50 |
7 | Carbon black N774 | 25 |
8 | Silicon powder 750 | 30 |
9 | Plasticizer RS107 | 20 |
10 | Sulphur S-80GE | 2 |
11 | Accelerant CZ | 2 |
12 | Altax | 1 |
The rubber performance of formula preparation:
Test result: the adhesive strength of fluorubber and fluororesin THV 815 are 4.1N/mm.
The foregoing is merely the schematical specific embodiment of the present invention, the range being not intended to limit the invention.It is any
Those skilled in the art, made equivalent changes and modifications under the premise of not departing from design and the principle of the present invention,
It should belong to the scope of protection of the invention.
Claims (7)
1. a kind of bonding anti-dropout rubber compounding, which is characterized in that be made of raw material from the following weight: nitrile rubber 4155:
100 parts, activated magnesia MgO150:5 ~ 10 part, anti-aging agent RD: 1 ~ 2 part, stearic acid: 1 ~ 2 part, DBU formates: 1 ~ 2 part, charcoal
Black N550:35 ~ 50 part, carbon black N774:10 ~ 25 part, silicon powder 750:15 ~ 30 part, plasticizer RS107:10 ~ 20 part, sulphur S-
80GE:1 ~ 2 part, accelerant CZ: 1 ~ 2 part, altax: 0.5 ~ 1.0 part.
2. a kind of bonding anti-dropout rubber compounding according to claim 1, which is characterized in that by the raw material of following parts by weight
It is made: 4155:100 parts of nitrile rubber, activated magnesia MgO150:8 ~ 10 part, anti-aging agent RD: 1 ~ 1.5 part, stearic acid: 1 ~ 1.5
Part, DBU formates: 1.5 ~ 2 parts, carbon black N550:45 ~ 50 part, carbon black N774:20 ~ 25 part, silicon powder 750:15 ~ 30 part, plasticizer
RS107:18 ~ 20 part, sulphur S-80GE:1 ~ 1.5 part, accelerant CZ: 1 ~ 1.5 part, altax: 0.5 ~ 1.0 part.
3. a kind of bonding anti-dropout rubber compounding according to claim 1 or 2, which is characterized in that by following parts by weight
Raw material is made: 4155:100 parts of nitrile rubber, MgO150:10 parts of activated magnesia, anti-aging agent RD: 1.5 parts, stearic acid: 1.5
Part, DBU formates: 2 parts, N550:50 parts of carbon black, N774:25 parts of carbon black, 750:30 parts of silicon powder, RS107:20 parts of plasticizer, sulphur
S-80GE:1.8 parts of sulphur, accelerant CZ: 1.5 parts, altax: 1.0 parts.
4. a kind of bonding anti-dropout rubber compounding according to claim 1 or 2, it is characterised in that: nitrile rubber 4155 with
The weight part ratio of DBU formates is 50:1.
5. a kind of bonding anti-dropout rubber compounding according to claim 1 or 2, it is characterised in that: the carbon black N550 with
Carbon black N774 weight part ratio is 2:1.
6. a kind of bonding anti-dropout rubber compounding according to claim 1 or 2, it is characterised in that: accelerant CZ and promotion
Agent DM weight part ratio is 3:2.
7. a kind of bonding anti-dropout rubber compounding as claimed in claim 1 or 2, it is characterised in that: the rubber of formula preparation
With fluorine resin film using molding vulcanization, temperature is 160 DEG C, time 25min, pressure 10Mpa.