CN109610155A - A kind of fiber opening process of modal knitted fabric peach face - Google Patents
A kind of fiber opening process of modal knitted fabric peach face Download PDFInfo
- Publication number
- CN109610155A CN109610155A CN201811421551.XA CN201811421551A CN109610155A CN 109610155 A CN109610155 A CN 109610155A CN 201811421551 A CN201811421551 A CN 201811421551A CN 109610155 A CN109610155 A CN 109610155A
- Authority
- CN
- China
- Prior art keywords
- knitted fabric
- fibrillation
- opening process
- modal
- fiber opening
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of fiber opening process of modal knitted fabric peach face, are related to Modal fibrillation technical field, it is intended to solve the problems, such as to lack modal knitted fabric fiber opening process in the prior art, the fiber opening process is the following steps are included: S1, washing pad；S2, washing drying；S3, receipts are smooth；S4, fibrillation；S5, water outlet is neutralized.The present invention passes through the mechanism of air flow dyeing machine high-speed flow, and yam surface fiber bundle-like fiber is made to scatter, and cooperates the microetch role of organic acid fibrillation agent, while guaranteeing to be knitted fabric blank fibrillation effect, obtains peach face cloth cover, improves final product quality.
Description
Technical field
The present invention relates to Modal fibrillation technical field more particularly to a kind of fibrillation works of modal knitted fabric peach face
Skill.
Background technique
Modal fibre is a kind of is made by wooden slurries through special spinning technique, with good flexibility
It is harmless due to all natural materials of its raw material with excellent hygroscopic man-made cellulose fibers, and can divide naturally
Solution, environmental sound, and be used widely in the textile industry；And in the prior art, when handling embryo cloth, often deposit
The shortcomings that removal of cloth cover filoplume is not clean in fibrillation, and fibrillation effect and uniformity are poor, cloth cover Boardy Feeling, no flannelette.
To solve the above-mentioned problems, currently, the Chinese invention patent of notification number CN103952917B discloses a kind of not generation
That shuttle-woven fabric fiber opening process, comprises the following steps that: fabric is handled with enzyme, desizing agent, scouring agent and bleeding agent cold dome, and
Through washing and pre-setting；It carries out spraying processing in machine cylinder by treated cloth, selects water level control in 3.5-4.5
Between ton, bath raio 1:15-20；The secondary cylinder of sulfuric acid addition is diluted and stirred evenly, machine cylinder mentioned above is then slowly added into
In, heating, and keep the temperature carry out pickling；Cloth after pickling is washed again, and is neutralized with soda ash, after fibrillation can be obtained
Cloth.
Although this energy Modal shuttle-woven fabric fiber opening process can remove the impurity woollen on cloth cover filoplume completely,
It is that the shuttle-woven fabric that this fiber opening process is directed to Modal is designed, due to the knitting side of shuttle-woven fabric and knitting fabric
The difference of formula, leads to the fabric construction of the fabric of knitting forming difference, and knitted fabric has good compared to woven
Gas, elasticity and extensibility, when being handled using the fiber opening method of existing shuttle-woven fabric knitting fabric, it may appear that fibrillation
Excessive phenomenon, and make Modal fibre excessive damage, and then destroy the physical mechanical property of fabric, so that finished textile product quality
It is poor；Therefore, a kind of fiber opening process of modal knitted fabric is needed.
Summary of the invention
In view of the deficiencies of the prior art, the present invention provides a kind of fibrillation works of modal knitted fabric peach face
Skill has the advantages that fibrillation is stable, fabric quality is excellent.
To realize the above-mentioned technical purpose, the fiber opening process of a kind of modal knitted fabric peach face provided by the invention, packet
Include following steps:
S1: washing is padded, and the knitting fabric that Modal fibre is made into is washed, at 85-90 DEG C, then washing temperature controls
Material is padded, and steams 1-2min in 85-90 DEG C of gas；
S2: washing drying, gas steam after knitting fabric blank washed again, temperature control at 80-90 DEG C, and using drying cylinder into
Row drying；
S3: receiving smooth, receive to the knitting fabric blank after drying smooth, temperature is controlled at 185-190 DEG C；
S4: knitting fabric blank of the receipts after smooth is put into air flow dyeing machine by fibrillation, and bath raio is (1:3-1:5), revolving speed control
In 400-500m/min, after fibrillation agent is added in room temperature, it is warming up to 90-110 DEG C, heating rate is controlled in 1.5-2 DEG C/min, and
Temperature persistently handles 50-70min after reaching 90-110 DEG C again；
S5: neutralizing water outlet, and drain after the pH value of solution is neutralized to 7 using sodium carbonate can carry out following process.
By adopting the above technical scheme, it has the advantages that one, by washing de-sizing operation, it is former to remove knitting fabric
Slurry on base, avoids residual slurry on fiber, and influences the wetability of knitting fabric blank, hinders chemical contact fine
Dimension；Two, after desizing, the knitting fabric blank after desizing is cleaned using hot water, avoids slurries from being adhered to knitting fabric again former
Desizing effect is influenced on base；Three, by the mechanical shock of the high-speed flow of air flow dyeing machine, keep yam surface fibre bundle fine
Dimension is scattered, so that knitting fabric blank long fibre under the biological microetch of fibrillation agent is cut off, forms one in fiber surface
The fine and close short flannel of layer, and then obtain special peach face cloth cover effect；Knitting fabric blank walk cloth speed is controlled by revolving speed, is matched
Run the microetch role of fine agent at high temperature jointly, the control microetch time assigns while guaranteeing the fibrillation effect of knitting fabric blank
Fabric surface peach face effect is given, final product quality is improved.
In some embodiments, in S1, the material that rolls includes degreaser, hydrogen peroxide and caustic soda, and the density of each component is
Degreaser 2-3g/L, hydrogen peroxide 4-6g/L and caustic soda 2-3g/L.
By adopting the above technical scheme, the degreaser of 2-3g/L is added in rolling material, peel adhesion is in knitting fabric blank
Cured matter, oil and dirt, and there is wetting, emulsification, washing and dispersibility, effectively avoid recontamination；And hydrogen peroxide is strong oxygen
Agent, can be broken degradation slurry macromolecular, make slurry be easy to be detached from knitting fabric blank, and soda bath can be swollen it is all kinds of
Slurry, and the dissolubility of slurry is improved, collaboration hydrogen peroxide removes the slurry in knitting fabric blank jointly, after avoiding it from influencing
Processing effect.
In some embodiments, the degreaser is degreaser 1001 or degreaser 1085.
By adopting the above technical scheme, use 1001 or 1085 as degreaser, since its foam is extremely low, strong applicability, no
Impurity can only be removed, moreover it is possible to assist hydrogen peroxide and caustic soda to remove slurry, and assign the knitting preferable capillary effect of fabric blank, together
When, property is mild, will not damage limit.
In some embodiments, in S2, washing time is controlled in 25-35min.
By adopting the above technical scheme, it when cleaning knitted side material blank using hot water, controls and cleans the time, guaranteeing to clean
While effect, cleaning efficiency is improved, reduces energy consumption.
In some embodiments, in S4, the fibrillation agent selects fibrillation agent M-1100A.
By adopting the above technical scheme, fibrillation agent M-1100A has highly stable, sufficient fibrillation effect, feel after fibrillation
It is soft, plentiful, sliding glutinous；It and being capable of good control fibrillation rate, it is ensured that product color fastness and dyeing colo r light stability；And into
One step can guarantee the fabric quality of fibrillation and avoid fibre damage, be conducive to rear road sanding and obtain fine and closely woven plentiful, uniform height
Mass effect.
In some embodiments, the fibrillation agent dosage is the 2-4% for being knitted fabric grey cloth weight.
By adopting the above technical scheme, the additive amount of fibrillation agent is selected according to the type of the weight of knitting fabric and fibrillation agent,
To while guaranteeing fibrillation efficiency, guarantee that knitting fabric blank can obtain good fibrillation effect.
In some embodiments, in S4, the number of the knitting fabric blank is 30-40.
By adopting the above technical scheme, the number of control knitting fabric blank is in 30-40 branch, so that the fineness of yarn is controlled,
To stablize fibrillation effect when heating.
In some embodiments, in S5, the density 2-4g/L of sodium carbonate.
By adopting the above technical scheme, by the addition of alkaline carbonic acid sodium, the acidity in solution is constantly neutralized, thus by solution
PH value be adjusted to neutrality to avoid knitting the excessive fibrillation of fabric blank and damage fiber, influence finished textile product Physical Mechanical
Energy.
In conclusion compared with prior art, the present invention having the advantage that
1. passing through the mechanism of air flow dyeing machine high-speed flow, yam surface fiber bundle-like fiber is made to scatter, cooperates organic acid
The microetch role of class fibrillation agent obtains peach face cloth cover while guaranteeing to be knitted fabric blank fibrillation effect, improves into quality
Amount；
2. degreaser, hydrogen peroxide and caustic soda are used cooperatively, while the greasy dirt, impurity and slurries for removing fiber surface, make
Fiber surface tentatively obtains capillary effect, is beneficial to subsequent fibrillation agent processing knitting fabric, obtains more regular, fine and close short flannel,
Improve finished product cloth cloth cover feel.
Specific embodiment
Embodiment 1:
This embodiment discloses herein a kind of fiber opening process of modal knitted fabric peach face, and the modal knitted fabric is by Modal
30 are knitted comprising following steps:
S1: washing is padded, and the knitting fabric that Modal fibre is made into is washed, and washing temperature is controlled at 85 DEG C, is then soaked
Roll material, wherein the degreaser in material including 2g/L, the hydrogen peroxide of 4g/L and the caustic soda of 2g/L are rolled, to utilize degreaser, dioxygen
The synergistic effect of water and caustic soda forms densification in fiber surface while the greasy dirt, impurity and slurries for removing fiber surface
Capillary effect structure, then gas steams 1min at 85 DEG C.
Wherein degreaser agent selects 1001 or 1085, and manufacturer is Hangzhou Mei Gao Chemical Co., Ltd..
S2: washing drying, the knitting fabric blank after gas steams are washed again, and temperature washes 25min at 80 DEG C, and adopts
It is dried with drying cylinder.
S3: receiving smooth, receive to the knitting fabric blank machine after drying smooth, temperature is controlled at 185 DEG C.
S4: knitting fabric blank of the receipts after smooth is put into air flow dyeing machine, bath raio 1:1 by fibrillation, and revolving speed control exists
500m/min after the fibrillation agent M-1100A that cloth weighs 2% is added in room temperature, is warming up to 90 DEG C, and heating rate is controlled in 1.5 DEG C/min,
And 50min is persistently handled again after temperature reaches 90 DEG C, thus by the mechanical effect of air flow dyeing machine high-speed flow, cooperation
The biological microetch role cutting of fibrillation agent is long fine, and further in-depth forms compound with regular structure, distribution on the basis of the capillary effect that S1 is formed
Fine and close short flannel, and then while guaranteeing fibrillation effect, obtain excellent finished surface structure.Wherein fibrillation agent M-1100A
Manufacturer is Hangzhou Mei Gao Chemical Co., Ltd..
S5: neutralizing water outlet, and drain after the pH value of solution is neutralized to 7 using the sodium carbonate of 2g/L can carry out subsequent add
Work.
The fibrillation that the present embodiment obtains finishes knitting fabric blank after subsequent machining technology is handled, and it is special that finished product has
Peach face cloth cover effect, sense of touch is soft, good hand feeling.
Embodiment 2:
This embodiment discloses herein a kind of fiber opening process of modal knitted fabric peach face, and the modal knitted fabric is by Modal
40 are knitted comprising following steps:
S1: washing is padded, and the knitting fabric that Modal fibre is made into is washed, and washing temperature is controlled at 87 DEG C, is then soaked
Roll material, wherein roll include in material 2.5g/L degreaser, the hydrogen peroxide of 5g/L and the caustic soda of 2.5g/L, thus using degreaser,
The synergistic effect of hydrogen peroxide and caustic soda is formed in fiber surface and is caused while the greasy dirt, impurity and slurries for removing fiber surface
Close capillary effect structure, then gas steams 1.5min at 87 DEG C.
Wherein degreaser agent selects 1001 or 1085, and manufacturer is Hangzhou Mei Gao Chemical Co., Ltd..
S2: washing drying, the knitting fabric blank after gas steams are washed again, and temperature washes 30min at 85 DEG C, and adopts
It is dried with drying cylinder.
S3: receiving smooth, receive to the knitting fabric blank machine after drying smooth, temperature is controlled at 187 DEG C.
S4: knitting fabric blank of the receipts after smooth is put into air flow dyeing machine, bath raio 1:4 by fibrillation, and revolving speed control exists
450m/min after the fibrillation agent M-1100A that cloth weighs 3% is added in room temperature, is warming up to 100 DEG C, and heating rate is controlled in 1.7 DEG C/min,
And 60min is persistently handled again after temperature reaches 100 DEG C, to be matched by the mechanical effect of air flow dyeing machine high-speed flow
The biological microetch role for running fine agent jointly cuts off long fibre, and further in-depth forms compound with regular structure, divides on the basis of the capillary effect that S1 is formed
The short flannel of cloth densification, and then while guaranteeing fibrillation effect, obtain excellent finished surface structure.Wherein fibrillation agent M-
1100A manufacturer is Hangzhou Mei Gao Chemical Co., Ltd..
S5: neutralizing water outlet, and drain after the pH value of solution is neutralized to 7 using the sodium carbonate of 3g/L can carry out subsequent add
Work.
The fibrillation that the present embodiment obtains finishes knitting fabric blank after subsequent machining technology is handled, and it is special that finished product has
Peach face cloth cover effect, sense of touch is soft, good hand feeling.
Embodiment 3:
This embodiment discloses herein a kind of fiber opening process of modal knitted fabric peach face, and the modal knitted fabric is by Modal
50 are knitted comprising following steps:
S1: washing is padded, and the knitting fabric that Modal fibre is made into is washed, and washing temperature is controlled at 90 DEG C, is then soaked
Roll material, wherein the degreaser in material including 3g/L, the hydrogen peroxide of 6g/L and the caustic soda of 3g/L are rolled, to utilize degreaser, dioxygen
The synergistic effect of water and caustic soda forms densification in fiber surface while the greasy dirt, impurity and slurries for removing fiber surface
Capillary effect structure, then gas steams 2min at 90 DEG C.
Wherein degreaser agent selects 1001 or 1085, and manufacturer is Hangzhou Mei Gao Chemical Co., Ltd..
S2: washing drying, the knitting fabric blank after gas steams are washed again, and temperature washes 35min at 90 DEG C, and adopts
It is dried with drying cylinder.
S3: receiving smooth, receive to the knitting fabric blank machine after drying smooth, temperature is controlled at 190 DEG C.
S4: knitting fabric blank of the receipts after smooth is put into air flow dyeing machine, bath raio 1:5 by fibrillation, and revolving speed control exists
400m/min after the fibrillation agent M-1100A that cloth weighs 4% is added in room temperature, is warming up to 110 DEG C, and heating rate is controlled in 2 DEG C/min, and
70min is persistently handled again after temperature reaches 100 DEG C, thus by the mechanical effect of air flow dyeing machine high-speed flow, cooperation
The biological microetch role cutting of fibrillation agent is long fine, and further in-depth forms compound with regular structure, distribution on the basis of the capillary effect that S1 is formed
Fine and close short flannel, and then while guaranteeing fibrillation effect, obtain excellent finished surface structure.Wherein fibrillation agent M-1100A
Manufacturer is Hangzhou Mei Gao Chemical Co., Ltd..
S5: neutralizing water outlet, and drain after the pH value of solution is neutralized to 7 using the sodium carbonate of 4g/L can carry out subsequent add
Work.
The fibrillation that the present embodiment obtains finishes knitting fabric blank after subsequent machining technology is handled, and it is special that finished product has
Peach face cloth cover effect, sense of touch is soft, good hand feeling.
Following items are directed to respectively according to the resulting modal knitted fabric with peach face of embodiment 1-3 to be examined
It surveys, including elongation at break and fibrillation rate, examination criteria are respectively GB/T3923.1-2013 and GB/T 35266-2017, detection
The results are shown in Table 1:
Table 1
| Detection project | Embodiment 1 | Embodiment 2 | Embodiment 3 |
| Elongation at break/% | 35% | 30% | 25% |
| Fibrillation rate/% | 2%-3% | 3%-4% | 4%-5% |
In conclusion the resulting modal knitted fabric of embodiment 1-3 not only has excellent peach face surface effect, fibrillation
Effect is also relatively stable, and physical mechanical property is still able to satisfy fabric service performance under secondary microetch, wherein with 2 institute of embodiment
The peach face texture of the modal knitted fabric obtained is the most regular, and sense of touch is soft, good hand feeling, meanwhile, with optimal
Physical mechanical property.
The above is only a preferred embodiment of the present invention, protection scope of the present invention is not limited merely to above-mentioned implementation
Example, all technical solutions belonged under thinking of the present invention all belong to the scope of protection of the present invention.It should be pointed out that for the art
Those of ordinary skill for, several improvements and modifications without departing from the principles of the present invention, these improvements and modifications
It should be regarded as protection scope of the present invention.
Claims (8)
1. a kind of fiber opening process of modal knitted fabric peach face, which comprises the following steps:
S1: washing is padded, and the knitting fabric that Modal fibre is made into is washed, then washing temperature is controlled at 85-90 DEG C
Material is padded, and steams 1-2min in 85-90 DEG C of gas；
S2: washing drying, gas steam after knitting fabric blank washed again, temperature control at 80-90 DEG C, and using drying cylinder into
Row drying；
S3: receiving smooth, receive to the knitting fabric blank after drying smooth, temperature is controlled at 185-190 DEG C；
S4: knitting fabric blank of the receipts after smooth is put into air flow dyeing machine, bath raio 1:3-1:5 by fibrillation), revolving speed control
In 400-500m/min, after fibrillation agent is added in room temperature, it is warming up to 90-110 DEG C, heating rate is controlled in 1.5-2 DEG C/min, and
Temperature persistently handles 50-70min after reaching 90-110 DEG C again；
S5: neutralizing water outlet, and drain after the pH value of solution is neutralized to 7 using sodium carbonate can carry out following process.
2. a kind of fiber opening process of modal knitted fabric peach face according to claim 1, which is characterized in that in S1,
The material that rolls includes degreaser, hydrogen peroxide and caustic soda, and the density of each component is degreaser 2-3g/L, hydrogen peroxide 4-6g/L and caustic soda
2-3g/L。
3. a kind of fiber opening process of modal knitted fabric peach face according to claim 2, which is characterized in that described to remove
Finish is degreaser 1001 or degreaser 1085.
4. a kind of fiber opening process of modal knitted fabric peach face according to claim 1, which is characterized in that in S2,
Washing time is controlled in 25-35min.
5. a kind of fiber opening process of modal knitted fabric peach face according to claim 1, which is characterized in that in S4,
The fibrillation agent selects fibrillation agent M-1100A.
6. a kind of fiber opening process of modal knitted fabric peach face according to claim 5, which is characterized in that described to open
Fine agent dosage is the 2-4% for being knitted fabric grey cloth weight.
7. a kind of fiber opening process of modal knitted fabric peach face according to claim 1, which is characterized in that in S4,
The number of the knitting fabric blank is 30-40.
8. a kind of fiber opening process of modal knitted fabric peach face according to claim 1, which is characterized in that in S5,
The density 2-4g/L of sodium carbonate.