CN109609069A - One kind is for container bottom board bamboo mat bamboo curtain splint dipping new type resin adhesive - Google Patents
One kind is for container bottom board bamboo mat bamboo curtain splint dipping new type resin adhesive Download PDFInfo
- Publication number
- CN109609069A CN109609069A CN201811562696.1A CN201811562696A CN109609069A CN 109609069 A CN109609069 A CN 109609069A CN 201811562696 A CN201811562696 A CN 201811562696A CN 109609069 A CN109609069 A CN 109609069A
- Authority
- CN
- China
- Prior art keywords
- parts
- urea
- container bottom
- bottom board
- new type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses one kind to be used for container bottom board bamboo mat bamboo curtain splint dipping new type resin adhesive, and the formula of raw material by weight is as follows: 35-45 parts of polyurethane modified epoxy resin, 6-8 parts of silicon carbide, 18-22 parts of formaldehyde, 6-8 parts of urea, 5-7 parts of melamine, 0.8-1.2 parts of triethanolamine, 0.4-0.8 parts of phthalic anhydride, 0.4-0.8 parts of polyol crosslink agent, 0.4-0.8 parts of catalyst, 0.8-1.2 parts of mixed aid.The invention also discloses a kind of preparation methods for container bottom board bamboo mat bamboo curtain splint dipping new type resin adhesive.The present invention has the advantages that resistance to boiling water, weatherability, impact resistance, ageing-resistant and glued power are strong.
Description
Technical field
The present invention relates to adhesive preparation technical fields, more particularly to a kind of impregnate for container bottom board bamboo mat bamboo curtain splint to use
New type resin adhesive.
Background technique
In the multimodal transport logistics of world today's rapid development, the manufacture and outlet that China has ascended container are greatly
State, every year need to more than 165 ten thousand stere of container bottom board, and in the several years from now on, the production quantity of container there is still a need for
It increases substantially.
Container is manufactured, must just use container bottom board, it is the weight of container which, which belongs to structure load-bearing material,
One of construct, play a part of supporting cargo and protection cargo in case, and with the overall process of Container Transport.Therefore container
Bottom plate needs to have the properties such as good load-carrying, antidetonation, impact resistance, weatherability.Traditional container bottom board mainly uses
Clone's face side and hardwood veneer are formed through gluing hot-press gluing, and with the reduction for cloning the wooden import resource, country is to wildwood
It is comprehensive taboo cut down, hardwood resource will be reduced increasingly.Clone's wood is substituted with bamboo mat, has been mesh with bamboo curtain splint substitution hardwood veneer
The inevitable choice of preceding container bottom board manufacturing enterprise, and container bottom board is to water-fast, moisture resistance, weatherability and wet shape bonding strength
There is particular/special requirement, thus all bamboo mats, bamboo curtain splint impregnation use phenolic resin adhesive at present.And common melamine-urea
The modified adhesive of aldehyde cannot be used for container bottom board bamboo mat, bamboo curtain splint dipping.For this purpose, we have proposed one kind to be used for container bottom board
Bamboo mat bamboo curtain splint dipping new type resin adhesive.
Summary of the invention
The invention proposes one kind to be used for container bottom board bamboo mat bamboo curtain splint dipping new type resin adhesive, above-mentioned to solve
The problem of being proposed in background technique.
The invention proposes one kind to be used for container bottom board bamboo mat bamboo curtain splint dipping new type resin adhesive, and raw material is by weight
The formula of amount is as follows: 35-45 parts of polyurethane modified epoxy resin, 6-8 parts of silicon carbide, 18-22 parts of formaldehyde, 6-8 parts of urea, trimerization
5-7 parts of cyanamide, 0.8-1.2 parts of triethanolamine, 0.4-0.8 parts of phthalic anhydride, 0.4-0.8 parts of polyol crosslink agent, catalyst 0.4-0.8
Part, 0.8-1.2 parts of mixed aid.
Preferably, polyurethane modified epoxy resin, silicon carbide weight ratio be 38-42:6.5-7.5.
Preferably, formaldehyde, urea, melamine, triethanolamine, phthalic anhydride weight ratio be 19-21:6.5-7.5:5.5-
6.5:0.9-1.1:0.5-0.7.
Preferably, polyol crosslink agent, catalyst, mixed aid weight ratio be 0.5-0.7:0.5-0.7:0.9-1.1.
Preferably, the formula of raw material by weight is as follows:
38-42 parts of polyurethane modified epoxy resin, 6.5-7.5 parts of silicon carbide, 19-21 parts of formaldehyde, 6.5-7.5 parts of urea,
5.5-6.5 parts of melamine, 0.9-1.1 parts of triethanolamine, 0.5-0.7 parts of phthalic anhydride, 0.5-0.7 parts of polyol crosslink agent, catalysis
0.5-0.7 parts of agent, 0.9-1.1 parts of mixed aid.
Preferably, the optimization formula of raw material by weight is as follows:
40 parts of polyurethane modified epoxy resin, 7 parts of silicon carbide, 20 parts of formaldehyde, 7 parts of urea, 6 parts of melamine, three ethyl alcohol
1 part of amine, 0.6 part of phthalic anhydride, 0.6 part of polyol crosslink agent, 0.6 part of catalyst, 1 part of mixed aid.
The present invention also provides a kind of preparation works for container bottom board bamboo mat bamboo curtain splint dipping new type resin adhesive
Skill includes the following steps:
S1, each component is weighed by above-mentioned composition, and by control errors within 1%;
S2, the polyurethane modified epoxy resin of the parts by weight and silicon carbide stirring are warming up to 40-60 degrees Celsius, instead
120-200min is answered, A phase mixture is obtained;
S3, the formaldehyde measured and A phase mixture are all put into reaction kettle, start blender, open steam valve
First urea and melamine is added with sodium hydroxide tune reaction solution PH to 9.0-10 in heat temperature raising, after mixing, obtains
To reaction solution, this batch of urea is the 58%-62% of urea total amount, this batch of melamine is the 60%-62% of total amount;
S3, after the completion of S2, carry out heating treatment, when reacting liquid temperature rises to 75-80 degrees Celsius, be added second batch urine
Element, this batch of urea is the 38%-42% of urea total amount, while continuing to heat up, when reacting liquid temperature rises to 85-90 degrees Celsius,
Steam off valve starts to keep the temperature, and soaking time 70-80 minutes, 91-94 degrees Celsius of holding temperature;
S4, reaction solution pH value is adjusted, specific as follows:
Reacting liquid temperature is adjusted to 80-85 DEG C, with formic acid tune reaction solution PH to 5.2-5.8, is reacted 20-30 minutes;
With formic acid tune reaction solution PH to 5.0-5.5, react 15-20 minutes;
Again with formic acid tune reaction solution pH value to 4.1-4.5, the reaction was continued, and constantly takes a sample test reaction fluid viscosity, until 25 DEG C
When to apply 4 glasss of number of seconds be until 28-30 seconds;
After S5, viscosity are up to standard, with sodium hydroxide tune reaction solution pH value to 8.5-9.0, and reacting liquid temperature 85-90 is controlled
DEG C, second batch melamine is added, this batch of melamine is the 38%-40% of total amount, and checking and adjusting PH is 8.5-9.0, instead
83-85 DEG C of liquid temperature is answered, the reaction was continued 20-25 minutes;
S6, inspection simultaneously adjust PH as 7.0-7.5, whole triethanolamine and phthalic anhydride are added, reacting liquid temperature is controlled in 75-
80 DEG C, the reaction was continued 20-30 minutes;
S7, reaction solution is made to cool down, checking and adjusting PH is that 7.0-7.5 is obtained when reacting liquid temperature is down to 35-40 DEG C
Adhesive of the present invention.
Preferably, the mixed aid is specially the mixture of dispersing agent, defoaming agent, curing agent and anti-aging agent, and
Dispersing agent, defoaming agent, curing agent and anti-aging agent molal weight ratio be 1:0.2:1:0.5.
Beneficial effects of the present invention are as follows: by the addition of plurality of raw materials in the present invention, and with the different reaction time, no
With temperature, the mode of different pH values and fed batch makes the copolymerization of a variety of chemical raw materials together, produce one kind be different from it is general
The new type resin adhesive of the logical modified adhesive of melamine-urea formaldehyde -- container bottom board bamboo mat bamboo curtain splint, which impregnates, uses multiway tree
Rouge adhesive, it had both had the advantages that traditional phenolic resin adhesive: i.e. resistance to boiling water, weatherability, impact resistance, ageing-resistant, glued
Power is strong, and overcomes the inherent defect of phenolic resin adhesive.Free aldehyde≤0.1% of polynary resin cement of the invention is low
Poison ring is protected;And the manufacturing cost of polynary resin cement is only the 55% of phenolic resin adhesive manufacturing cost, and is beaten
Having broken the urea-formaldehyde-modified adhesive of common melamine-cannot be used for the confinement of container bottom board bamboo mat, bamboo curtain splint dipping, have weight
Big creative breakthrough.
Specific embodiment
It is next combined with specific embodiments below that the present invention will be further described.
Embodiment 1
The invention proposes one kind to be used for container bottom board bamboo mat bamboo curtain splint dipping new type resin adhesive, and raw material is by weight
The formula of amount is as follows: 35 parts of polyurethane modified epoxy resin, 6 parts of silicon carbide, 18 parts of formaldehyde, 6 parts of urea, 5 parts of melamine, three
0.8 part of ethanol amine, 0.4 part of phthalic anhydride, 0.4 part of polyol crosslink agent, 0.4 part of catalyst, 0.8 part of mixed aid.
The present invention also provides a kind of preparation works for container bottom board bamboo mat bamboo curtain splint dipping new type resin adhesive
Skill includes the following steps:
S1, each component is weighed by above-mentioned composition, and by control errors within 1%;
S2, the polyurethane modified epoxy resin of the parts by weight and silicon carbide stirring are warming up to 40-60 degrees Celsius, instead
120-200min is answered, A phase mixture is obtained;
S3, the formaldehyde measured and A phase mixture are all put into reaction kettle, start blender, open steam valve
First urea and melamine is added with sodium hydroxide tune reaction solution PH to 9.0-10 in heat temperature raising, after mixing, obtains
To reaction solution, this batch of urea is the 58%-62% of urea total amount, this batch of melamine is the 60%-62% of total amount;
S3, after the completion of S2, carry out heating treatment, when reacting liquid temperature rises to 75-80 degrees Celsius, be added second batch urine
Element, this batch of urea is the 38%-42% of urea total amount, while continuing to heat up, when reacting liquid temperature rises to 85-90 degrees Celsius,
Steam off valve starts to keep the temperature, and soaking time 70-80 minutes, 91-94 degrees Celsius of holding temperature;
S4, reaction solution pH value is adjusted, specific as follows:
Reacting liquid temperature is adjusted to 80-85 DEG C, with formic acid tune reaction solution PH to 5.2-5.8, is reacted 20-30 minutes;
With formic acid tune reaction solution PH to 5.0-5.5, react 15-20 minutes;
Again with formic acid tune reaction solution pH value to 4.1-4.5, the reaction was continued, and constantly takes a sample test reaction fluid viscosity, until 25 DEG C
When to apply 4 glasss of number of seconds be until 28-30 seconds;
After S5, viscosity are up to standard, with sodium hydroxide tune reaction solution pH value to 8.5-9.0, and reacting liquid temperature 85-90 is controlled
DEG C, second batch melamine is added, this batch of melamine is the 38%-40% of total amount, and checking and adjusting PH is 8.5-9.0, instead
83-85 DEG C of liquid temperature is answered, the reaction was continued 20-25 minutes;
S6, inspection simultaneously adjust PH as 7.0-7.5, whole triethanolamine and phthalic anhydride are added, reacting liquid temperature is controlled in 75-
80 DEG C, the reaction was continued 20-30 minutes;
S7, reaction solution is made to cool down, checking and adjusting PH is that 7.0-7.5 is obtained when reacting liquid temperature is down to 35-40 DEG C
Adhesive of the present invention.
The mixed aid is specially the mixture of dispersing agent, defoaming agent, curing agent and anti-aging agent, and dispersing agent,
The molal weight ratio of defoaming agent, curing agent and anti-aging agent is 1:0.2:1:0.5.
Embodiment 2
The invention proposes one kind to be used for container bottom board bamboo mat bamboo curtain splint dipping new type resin adhesive, and raw material is by weight
The formula of amount is as follows: 38 parts of polyurethane modified epoxy resin, 6.5 parts of silicon carbide, 19 parts of formaldehyde, 6.5 parts of urea, melamine
5.5 parts, 0.9 part of triethanolamine, 0.5 part of phthalic anhydride, 0.5 part of polyol crosslink agent, 0.5 part of catalyst, 0.9 part of mixed aid.
The present invention also provides a kind of preparation works for container bottom board bamboo mat bamboo curtain splint dipping new type resin adhesive
Skill includes the following steps:
S1, each component is weighed by above-mentioned composition, and by control errors within 1%;
S2, the polyurethane modified epoxy resin of the parts by weight and silicon carbide stirring are warming up to 40-60 degrees Celsius, instead
120-200min is answered, A phase mixture is obtained;
S3, the formaldehyde measured and A phase mixture are all put into reaction kettle, start blender, open steam valve
First urea and melamine is added with sodium hydroxide tune reaction solution PH to 9.0-10 in heat temperature raising, after mixing, obtains
To reaction solution, this batch of urea is the 58%-62% of urea total amount, this batch of melamine is the 60%-62% of total amount;
S3, after the completion of S2, carry out heating treatment, when reacting liquid temperature rises to 75-80 degrees Celsius, be added second batch urine
Element, this batch of urea is the 38%-42% of urea total amount, while continuing to heat up, when reacting liquid temperature rises to 85-90 degrees Celsius,
Steam off valve starts to keep the temperature, and soaking time 70-80 minutes, 91-94 degrees Celsius of holding temperature;
S4, reaction solution pH value is adjusted, specific as follows:
Reacting liquid temperature is adjusted to 80-85 DEG C, with formic acid tune reaction solution PH to 5.2-5.8, is reacted 20-30 minutes;
With formic acid tune reaction solution PH to 5.0-5.5, react 15-20 minutes;
Again with formic acid tune reaction solution pH value to 4.1-4.5, the reaction was continued, and constantly takes a sample test reaction fluid viscosity, until 25 DEG C
When to apply 4 glasss of number of seconds be until 28-30 seconds;
After S5, viscosity are up to standard, with sodium hydroxide tune reaction solution pH value to 8.5-9.0, and reacting liquid temperature 85-90 is controlled
DEG C, second batch melamine is added, this batch of melamine is the 38%-40% of total amount, and checking and adjusting PH is 8.5-9.0, instead
83-85 DEG C of liquid temperature is answered, the reaction was continued 20-25 minutes;
S6, inspection simultaneously adjust PH as 7.0-7.5, whole triethanolamine and phthalic anhydride are added, reacting liquid temperature is controlled in 75-
80 DEG C, the reaction was continued 20-30 minutes;
S7, reaction solution is made to cool down, checking and adjusting PH is that 7.0-7.5 is obtained when reacting liquid temperature is down to 35-40 DEG C
Adhesive of the present invention.
The mixed aid is specially the mixture of dispersing agent, defoaming agent, curing agent and anti-aging agent, and dispersing agent,
The molal weight ratio of defoaming agent, curing agent and anti-aging agent is 1:0.2:1:0.5.
Embodiment 3
The invention proposes one kind to be used for container bottom board bamboo mat bamboo curtain splint dipping new type resin adhesive, and raw material is by weight
The formula of amount is as follows: 40 parts of polyurethane modified epoxy resin, 7 parts of silicon carbide, 20 parts of formaldehyde, 7 parts of urea, 6 parts of melamine, three
1 part of ethanol amine, 0.6 part of phthalic anhydride, 0.6 part of polyol crosslink agent, 0.6 part of catalyst, 1 part of mixed aid.
The present invention also provides a kind of preparation works for container bottom board bamboo mat bamboo curtain splint dipping new type resin adhesive
Skill includes the following steps:
S1, each component is weighed by above-mentioned composition, and by control errors within 1%;
S2, the polyurethane modified epoxy resin of the parts by weight and silicon carbide stirring are warming up to 40-60 degrees Celsius, instead
120-200min is answered, A phase mixture is obtained;
S3, the formaldehyde measured and A phase mixture are all put into reaction kettle, start blender, open steam valve
First urea and melamine is added with sodium hydroxide tune reaction solution PH to 9.0-10 in heat temperature raising, after mixing, obtains
To reaction solution, this batch of urea is the 58%-62% of urea total amount, this batch of melamine is the 60%-62% of total amount;
S3, after the completion of S2, carry out heating treatment, when reacting liquid temperature rises to 75-80 degrees Celsius, be added second batch urine
Element, this batch of urea is the 38%-42% of urea total amount, while continuing to heat up, when reacting liquid temperature rises to 85-90 degrees Celsius,
Steam off valve starts to keep the temperature, and soaking time 70-80 minutes, 91-94 degrees Celsius of holding temperature;
S4, reaction solution pH value is adjusted, specific as follows:
Reacting liquid temperature is adjusted to 80-85 DEG C, with formic acid tune reaction solution PH to 5.2-5.8, is reacted 20-30 minutes;
With formic acid tune reaction solution PH to 5.0-5.5, react 15-20 minutes;
Again with formic acid tune reaction solution pH value to 4.1-4.5, the reaction was continued, and constantly takes a sample test reaction fluid viscosity, until 25 DEG C
When to apply 4 glasss of number of seconds be until 28-30 seconds;
After S5, viscosity are up to standard, with sodium hydroxide tune reaction solution pH value to 8.5-9.0, and reacting liquid temperature 85-90 is controlled
DEG C, second batch melamine is added, this batch of melamine is the 38%-40% of total amount, and checking and adjusting PH is 8.5-9.0, instead
83-85 DEG C of liquid temperature is answered, the reaction was continued 20-25 minutes;
S6, inspection simultaneously adjust PH as 7.0-7.5, whole triethanolamine and phthalic anhydride are added, reacting liquid temperature is controlled in 75-
80 DEG C, the reaction was continued 20-30 minutes;
S7, reaction solution is made to cool down, checking and adjusting PH is that 7.0-7.5 is obtained when reacting liquid temperature is down to 35-40 DEG C
Adhesive of the present invention.
The mixed aid is specially the mixture of dispersing agent, defoaming agent, curing agent and anti-aging agent, and dispersing agent,
The molal weight ratio of defoaming agent, curing agent and anti-aging agent is 1:0.2:1:0.5.
Embodiment 4
The invention proposes one kind to be used for container bottom board bamboo mat bamboo curtain splint dipping new type resin adhesive, and raw material is by weight
The formula of amount is as follows: 42 parts of polyurethane modified epoxy resin, 7.5 parts of silicon carbide, 21 parts of formaldehyde, 7.5 parts of urea, melamine
6.5 parts, 1.1 parts of triethanolamine, 0.7 part of phthalic anhydride, 0.7 part of polyol crosslink agent, 0.7 part of catalyst, 1.1 parts of mixed aid.
The present invention also provides a kind of preparation works for container bottom board bamboo mat bamboo curtain splint dipping new type resin adhesive
Skill includes the following steps:
S1, each component is weighed by above-mentioned composition, and by control errors within 1%;
S2, the polyurethane modified epoxy resin of the parts by weight and silicon carbide stirring are warming up to 40-60 degrees Celsius, instead
120-200min is answered, A phase mixture is obtained;
S3, the formaldehyde measured and A phase mixture are all put into reaction kettle, start blender, open steam valve
First urea and melamine is added with sodium hydroxide tune reaction solution PH to 9.0-10 in heat temperature raising, after mixing, obtains
To reaction solution, this batch of urea is the 58%-62% of urea total amount, this batch of melamine is the 60%-62% of total amount;
S3, after the completion of S2, carry out heating treatment, when reacting liquid temperature rises to 75-80 degrees Celsius, be added second batch urine
Element, this batch of urea is the 38%-42% of urea total amount, while continuing to heat up, when reacting liquid temperature rises to 85-90 degrees Celsius,
Steam off valve starts to keep the temperature, and soaking time 70-80 minutes, 91-94 degrees Celsius of holding temperature;
S4, reaction solution pH value is adjusted, specific as follows:
Reacting liquid temperature is adjusted to 80-85 DEG C, with formic acid tune reaction solution PH to 5.2-5.8, is reacted 20-30 minutes;
With formic acid tune reaction solution PH to 5.0-5.5, react 15-20 minutes;
Again with formic acid tune reaction solution pH value to 4.1-4.5, the reaction was continued, and constantly takes a sample test reaction fluid viscosity, until 25 DEG C
When to apply 4 glasss of number of seconds be until 28-30 seconds;
After S5, viscosity are up to standard, with sodium hydroxide tune reaction solution pH value to 8.5-9.0, and reacting liquid temperature 85-90 is controlled
DEG C, second batch melamine is added, this batch of melamine is the 38%-40% of total amount, and checking and adjusting PH is 8.5-9.0, instead
83-85 DEG C of liquid temperature is answered, the reaction was continued 20-25 minutes;
S6, inspection simultaneously adjust PH as 7.0-7.5, whole triethanolamine and phthalic anhydride are added, reacting liquid temperature is controlled in 75-
80 DEG C, the reaction was continued 20-30 minutes;
S7, reaction solution is made to cool down, checking and adjusting PH is that 7.0-7.5 is obtained when reacting liquid temperature is down to 35-40 DEG C
Adhesive of the present invention.
The mixed aid is specially the mixture of dispersing agent, defoaming agent, curing agent and anti-aging agent, and dispersing agent,
The molal weight ratio of defoaming agent, curing agent and anti-aging agent is 1:0.2:1:0.5.
Embodiment 5
The invention proposes one kind to be used for container bottom board bamboo mat bamboo curtain splint dipping new type resin adhesive, and raw material is by weight
The formula of amount is as follows: 45 parts of polyurethane modified epoxy resin, 8 parts of silicon carbide, 22 parts of formaldehyde, 8 parts of urea, 7 parts of melamine, three
1.2 parts of ethanol amine, 0.8 part of phthalic anhydride, 0.8 part of polyol crosslink agent, 0.8 part of catalyst, 1.2 parts of mixed aid.
The present invention also provides a kind of preparation works for container bottom board bamboo mat bamboo curtain splint dipping new type resin adhesive
Skill includes the following steps:
S1, each component is weighed by above-mentioned composition, and by control errors within 1%;
S2, the polyurethane modified epoxy resin of the parts by weight and silicon carbide stirring are warming up to 40-60 degrees Celsius, instead
120-200min is answered, A phase mixture is obtained;
S3, the formaldehyde measured and A phase mixture are all put into reaction kettle, start blender, open steam valve
First urea and melamine is added with sodium hydroxide tune reaction solution PH to 9.0-10 in heat temperature raising, after mixing, obtains
To reaction solution, this batch of urea is the 58%-62% of urea total amount, this batch of melamine is the 60%-62% of total amount;
S3, after the completion of S2, carry out heating treatment, when reacting liquid temperature rises to 75-80 degrees Celsius, be added second batch urine
Element, this batch of urea is the 38%-42% of urea total amount, while continuing to heat up, when reacting liquid temperature rises to 85-90 degrees Celsius,
Steam off valve starts to keep the temperature, and soaking time 70-80 minutes, 91-94 degrees Celsius of holding temperature;
S4, reaction solution pH value is adjusted, specific as follows:
Reacting liquid temperature is adjusted to 80-85 DEG C, with formic acid tune reaction solution PH to 5.2-5.8, is reacted 20-30 minutes;
With formic acid tune reaction solution PH to 5.0-5.5, react 15-20 minutes;
Again with formic acid tune reaction solution pH value to 4.1-4.5, the reaction was continued, and constantly takes a sample test reaction fluid viscosity, until 25 DEG C
When to apply 4 glasss of number of seconds be until 28-30 seconds;
After S5, viscosity are up to standard, with sodium hydroxide tune reaction solution pH value to 8.5-9.0, and reacting liquid temperature 85-90 is controlled
DEG C, second batch melamine is added, this batch of melamine is the 38%-40% of total amount, and checking and adjusting PH is 8.5-9.0, instead
83-85 DEG C of liquid temperature is answered, the reaction was continued 20-25 minutes;
S6, inspection simultaneously adjust PH as 7.0-7.5, whole triethanolamine and phthalic anhydride are added, reacting liquid temperature is controlled in 75-
80 DEG C, the reaction was continued 20-30 minutes;
S7, reaction solution is made to cool down, checking and adjusting PH is that 7.0-7.5 is obtained when reacting liquid temperature is down to 35-40 DEG C
Adhesive of the present invention.
The mixed aid is specially the mixture of dispersing agent, defoaming agent, curing agent and anti-aging agent, and dispersing agent,
The molal weight ratio of defoaming agent, curing agent and anti-aging agent is 1:0.2:1:0.5.
A kind of container bottom board bamboo mat bamboo curtain splint dipping new type resin adhesive major technique that is used for proposed by the present invention refers to
It marks as follows:
(1) appearance: colloidal liquid white or yellowish
(2) solid content: 53% -55%
(3) viscosity (25 DEG C): 26-33 seconds (applying 4 glasss)
(4) pH value: 7.0-7.5
(5) dissociate aldehyde :≤0.15%
With the bamboo mat of the polynary resin cement dipping of the present invention, the container bottom board of bamboo curtain splint production, through repeated detection, it is each
Item mechanics index of physics complies fully with standard GB/T/T19536-2015 requirement.
Following table is the inspection report of the container bottom board produced using bamboo mat, the bamboo curtain splint of the polynary resin cement dipping of the present invention
It accuses:
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (8)
1. one kind is for container bottom board bamboo mat bamboo curtain splint dipping new type resin adhesive, which is characterized in that its raw material is by weight
Formula it is as follows: 35-45 parts of polyurethane modified epoxy resin, 6-8 parts of silicon carbide, 18-22 parts of formaldehyde, 6-8 parts of urea, melamine
5-7 parts of amine, 0.8-1.2 parts of triethanolamine, 0.4-0.8 parts of phthalic anhydride, 0.4-0.8 parts of polyol crosslink agent, catalyst 0.4-0.8
Part, 0.8-1.2 parts of mixed aid.
2. according to claim 1 for container bottom board bamboo mat bamboo curtain splint dipping new type resin adhesive, feature exists
In the weight ratio of, polyurethane modified epoxy resin, silicon carbide be 38-42:6.5-7.5.
3. according to claim 1 for container bottom board bamboo mat bamboo curtain splint dipping new type resin adhesive, feature exists
In the weight ratio of, formaldehyde, urea, melamine, triethanolamine, phthalic anhydride be 19-21:6.5-7.5:5.5-6.5:0.9-1.1:
0.5-0.7。
4. according to claim 1 for container bottom board bamboo mat bamboo curtain splint dipping new type resin adhesive, feature exists
In the weight ratio of, polyol crosslink agent, catalyst, mixed aid be 0.5-0.7:0.5-0.7:0.9-1.1.
5. being used for container bottom board bamboo mat bamboo curtain splint dipping new type resin adhesive, feature according to claim 2-4
It is, the formula of raw material by weight is as follows:
38-42 parts of polyurethane modified epoxy resin, 6.5-7.5 parts of silicon carbide, 19-21 parts of formaldehyde, 6.5-7.5 parts of urea, trimerization
5.5-6.5 parts of cyanamide, 0.9-1.1 parts of triethanolamine, 0.5-0.7 parts of phthalic anhydride, 0.5-0.7 parts of polyol crosslink agent, catalyst
0.5-0.7 parts, 0.9-1.1 parts of mixed aid.
6. according to claim 1 for container bottom board bamboo mat bamboo curtain splint dipping new type resin adhesive, feature exists
In the optimization formula of raw material by weight is as follows:
40 parts of polyurethane modified epoxy resin, 7 parts of silicon carbide, 20 parts of formaldehyde, 7 parts of urea, 6 parts of melamine, triethanolamine 1
Part, 0.6 part of phthalic anhydride, 0.6 part of polyol crosslink agent, 0.6 part of catalyst, 1 part of mixed aid.
7. a kind of preparation according to claim 1 for using new type resin adhesive for container bottom board bamboo mat bamboo curtain splint dipping
Technique, which comprises the steps of:
S1, each component is weighed by above-mentioned composition, and by control errors within 1%;
S2, the polyurethane modified epoxy resin of the parts by weight and silicon carbide stirring are warming up to 40-60 degrees Celsius, reaction
120-200min obtains A phase mixture;
S3, the formaldehyde measured and A phase mixture are all put into reaction kettle, start blender, open steam valve heating
Heating, with sodium hydroxide tune reaction solution PH to 9.0-10, is added first urea and melamine, after mixing, obtains anti-
Liquid is answered, this batch of urea is the 58%-62% of urea total amount, this batch of melamine is the 60%-62% of total amount;
S3, after the completion of S2, carry out heating treatment, when reacting liquid temperature rises to 75-80 degrees Celsius, be added second batch urea,
This batch of urea is the 38%-42% of urea total amount, while continuing to heat up, and when reacting liquid temperature rises to 85-90 degrees Celsius, closes
Steam valve starts to keep the temperature, and soaking time 70-80 minutes, 91-94 degrees Celsius of holding temperature;
S4, reaction solution pH value is adjusted, specific as follows:
Reacting liquid temperature is adjusted to 80-85 DEG C, with formic acid tune reaction solution PH to 5.2-5.8, is reacted 20-30 minutes;
With formic acid tune reaction solution PH to 5.0-5.5, react 15-20 minutes;
Again with formic acid tune reaction solution pH value to 4.1-4.5, the reaction was continued, and constantly takes a sample test reaction fluid viscosity, applies 4 when 25 DEG C
Cup number of seconds is until 28-30 seconds;
After S5, viscosity are up to standard, with sodium hydroxide tune reaction solution pH value to 8.5-9.0, and 85-90 DEG C of reacting liquid temperature are controlled, added
Enter second batch melamine, this batch of melamine is the 38%-40% of total amount, and checking and adjusting PH is 8.5-9.0, reaction solution temperature
83-85 DEG C of degree, the reaction was continued 20-25 minutes;
S6, inspection simultaneously adjust PH as 7.0-7.5, whole triethanolamine and phthalic anhydride are added, reacting liquid temperature is controlled in 75-80
DEG C, the reaction was continued 20-30 minutes;
S7, reaction solution is made to cool down, checking and adjusting PH is that 7.0-7.5 obtains this hair when reacting liquid temperature is down to 35-40 DEG C
The bright adhesive.
8. the preparation work according to claim 7 for using new type resin adhesive for container bottom board bamboo mat bamboo curtain splint dipping
Skill, which is characterized in that the mixed aid is specially the mixture of dispersing agent, defoaming agent, curing agent and anti-aging agent, and point
Powder, defoaming agent, curing agent and anti-aging agent molal weight ratio be 1:0.2:1:0.5.