CN109535949A - PE exempts from polish unsaturated polyester (UP) woodcare paint and its application method - Google Patents
PE exempts from polish unsaturated polyester (UP) woodcare paint and its application method Download PDFInfo
- Publication number
- CN109535949A CN109535949A CN201811399101.5A CN201811399101A CN109535949A CN 109535949 A CN109535949 A CN 109535949A CN 201811399101 A CN201811399101 A CN 201811399101A CN 109535949 A CN109535949 A CN 109535949A
- Authority
- CN
- China
- Prior art keywords
- unsaturated polyester
- polishing
- exempts
- paint
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of PE to exempt from polish unsaturated polyester (UP) woodcare paint and its application method, it is characterized in that, it is mainly mixed by four kinds of host agent, diluent, cobalt naphthenate and methyl ethyl ketone peroxide components, by weight, host agent: diluent: cobalt naphthenate: methyl ethyl ketone peroxide=100:30-35:1-2:1.2-2.5.PE provided by the invention exempts from unsaturated polyester (UP) woodcare paint of polishing, and there is paint film not need sanding polishing, and can directly construct polyurethane paint, and paint film interlayer has good adhesive force.It changes previous unsaturated polyester (UP) woodcare paint and needs abundant sanding polishing, could have the shortcomings that good adhesion with polyurethane paint.
Description
Technical field
The present invention relates to woodcare paint technical field, it is specifically related to a kind of unsaturated polyester (UP) woodcare paint and its application method.
Background technique
Woodcare paint refers to a kind of lacquer type organic coating on woodwork, there is polyester, polyurethane paint etc., can be divided into aqueous and oily
Property.Bloom, semi-matte, dumb light can be divided by gloss.Furniture lacquer, floor paint etc. can be divided by purposes.And PE woodcare paint, it is insatiable hunger
And Polyester Paint, it is mutually concocted by host agent, promotor, initiator three and carries out polymerization bridging reaction and solidify, solvent is benzene second
Alkene participates in reaction when film forming.The advantages of PE is painted is that have " 100% respond ", it means that liquid composition can draw
Under the action of sending out agent, no by-product releases and can be completely reformed into solid polymer.And solvent paint need it is a large amount of molten
After agent volatilization, paint film could be formed, such paint film is simultaneously hard not as resin solidification molding, and the volatilization of solvent causes
Certain environmental pollution, and the damage of health is also brought to construction personnel.In addition the good combination property of unsaturated polyester varnish: can
The thicker paint film of one-pass molding, bridging is good, and richness is high；It is wear-resisting, heat-resisting, corrosion-resistant, in terms of with PU paint phase
When；Hardness, richness, transparency, in terms of be better than other coating.But its shortcomings that is that abundant sanding is needed to beat
Mill, could have the shortcomings that good adhesion with polyurethane paint.
Summary of the invention
The object of the invention is to the one kind provided to solve the deficiency of the prior art, and there is paint film not need sanding
Polishing, can directly construct polyurethane paint, and there is paint film interlayer the PE of good adhesive force to exempt from unsaturated polyester (UP) of polishing
Woodcare paint.
It is a further object of the present invention to provide the application methods that a kind of PE exempts from polishing unsaturated polyester (UP) woodcare paint.
The present invention is to be attained in that a kind of PE exempts from unsaturated polyester (UP) woodenware of polishing using following technical solution
Paint, which is characterized in that it is mainly mixed by four kinds of host agent, diluent, cobalt naphthenate and methyl ethyl ketone peroxide components, by weight
Measure ratio, host agent: diluent: cobalt naphthenate: methyl ethyl ketone peroxide=100:30-35:1-2:1.2-2.5；
The host agent includes following weight percent composition:
As a further illustration of the above scheme, the unsaturated polyester resin is the BC9900# of Guangdong Bai Chuan chemical industry,
Acid value 25-35mgKOH/g, solid content 73-77%.
The titanium dioxide selects rutile type titanium white, using R895, Ning Taixin good fortune company of one hundred Li Lian company
NTR-606。
The anti-settling agent selects fumed silica or one kind of polyamide wax or more, rich using U.S.'s card
The 6900-20X of special company CAB-O-SIL fumed silica M-5 and DISPARLON company.
The dispersing agent uses the modified polyurethane wetting dispersing agent of Efka company: EFKA-4010.
The levelling agent uses the acrylate polymeric levelling agent of BYK company: BYK-358N.
The defoaming agent uses the modified polyorganosiloxane defoaming agent of this De Qian company of hamming: Defom5300.
The talcum powder uses the WF90-10-98Q/TZB of Guangxi Tian Ze superfine talcum powder company.
A kind of PE exempts from the application method of polishing unsaturated polyester (UP) woodcare paint, which is characterized in that it includes the following steps:
First host agent, diluent and cobalt naphthenate are mixed and stirred for uniformly, adding methyl ethyl ketone peroxide and stirring evenly,
Then using brushing, having gas or airless spraying to construct, the area of coating constructed every time is 0.18-0.2kg/ ㎡, recoating
Time 4-8 hour, drying condition are as follows: drying temperature: 10-40 DEG C, drying time 4-12 hour, drying means be spontaneously dry or
Person's heating drying.
The present invention is using the above-mentioned attainable beneficial effect of technical solution:
The present invention is using unsaturated polyester (UP) woodcare paint mainly by host agent, diluent, cobalt naphthenate and methyl ethyl ketone peroxide four
Kind component mixes, and PE provided by the invention exempts from unsaturated polyester (UP) woodcare paint of polishing, and there is paint film not need sanding polishing, can
With polyurethane paint of directly constructing, paint film interlayer has good adhesive force；Change previous unsaturated polyester (UP) woodcare paint
It needs abundant sanding to polish, could have the shortcomings that good adhesion with polyurethane paint.
Specific embodiment
The technical program is explained in detail below in conjunction with specific embodiment.
Embodiment 1
The unsaturated polyester resin is the BC9900# of Guangdong Bai Chuan chemical industry, acid value 25-35mgKOH/g, and solid content is
73-77%.Titanium dioxide selects rutile type titanium white, using the R895 of one hundred Li Lian company；Anti-settling agent selects fumed silica
Using Cabot Co., Ltd, U.S. CAB-O-SIL fumed silica M-5；Dispersing agent can be used: the modification of Efka company
Polyurethane wetting dispersing agent: EFKA-4010.Levelling agent uses the acrylate polymeric levelling agent of BYK company: BYK-358N disappears
Infusion uses the modified polyorganosiloxane defoaming agent of this De Qian company of hamming: Defom5300；Talcum powder uses the ultra-fine cunning of Guangxi Tian Ze
The WF90-10-98Q/TZB of mountain flour company；Trihydroxy methyl diallyl ether uses Japan great Cao DAISO.
In use, 90KG unsaturated polyester resin and 0.6KG dispersing agent 200 are added under stirring to stand
It rises in high speed disperser, 500-600 revs/min, stirs 5 minutes.1KG anti-settling agent and 40KG titanium dioxide, 1200-1500 is added
Revs/min high speed dispersion 10-15 minutes.Control fineness is 30-35um.50KG talcum powder, 1200-1500 revs/min of height is added
Speed dispersion 15-20 minutes.0.6KG levelling agent, 7.2KG butyl acetate and 10KG trihydroxy methyl diallyl ether, 800-100 is added
Revs/min high speed dispersion 10-15 minutes.
Styrene, butyl acetate and propylene glycol methyl ether acetate solvent weight share are put into 200 liter solvent cylinders,
It is uniform by gear pump circulation stirring, the clear bright diluent composition of water is made.
By host agent: diluent: cobalt naphthenate: methyl ethyl ketone peroxide is 100:35:1.5:1.8 (temperature: 25 by weight
DEG C, environment temperature: 75%), obtained PE exempts from unsaturated polyester varnish of polishing.
Construction material: closed medium-density plate has been done；
Construction method: rock field W-77,2.5mm bore manual spray gun, aerial spraying construction are selected；
Drying condition: room temperature spontaneously dries (20-30 DEG C).
It is detected using relevant criterion method, as a result as follows:
PE exempts from unsaturated polyester varnish host agent of polishing
| Project | Data | Detection method |
| Original paint appearance | Thick liquid, free from admixture | GB/T1721-1979 |
| Host agent solid content, % | 86 | GB/T1725-2007 |
| Gel time, min | 12 | GB/T7193-2008 |
| Surface drying time, min | 30 | GB/T1728-1979 |
| Paint film appearance | It is smooth | GB/T9761-1988 |
| Adhesive force, grade | 1 | GB/T9286-1998 |
| Covering power, g/ ㎡ | 150 | GB/T1725-1979 |
| Gloss (60 °) | 65 | GB/T4893-1985 |
Diluent
| Project | Data | Detection method |
| Appearance | Clearly, transparent, free from admixture | GB/T1721-1979 |
| Color | 1 | GB/T1721-1979 |
| Moisture | It is not muddy | GB/T1751-1992 |
Cobalt naphthenate
| Project | Data | Detection method |
| Appearance | Aubergine liquid | GB/T1721-1979 |
Methyl ethyl ketone peroxide
| Project | Data | Detection method |
| Appearance | It is colourless, transparent, clear liquid | GB/T1721-1979 |
PE exempts from polishing unsaturated polyester varnish and is sprayed on after plate face X hours, sprays PU Brilliant white paint；Experiment is white with PU light
Finishing coat: 82006PU ordor removing color inhibition spy's brilliant white finishing coat；12097PU ordor removing color inhibition light specially matches curing agent, and 10106PU is advanced
Finishing coat diluent
By host agent: curing agent: diluent by weight 1:0.8:0.6 (temperature: 25 DEG C, environment temperature: 75%)；Construction work
Tool: rock field W-71 spray gun, nozzle diameter: 1.5mm.
Embodiment 2
The unsaturated polyester resin is the BC9900# of Guangdong Bai Chuan chemical industry, acid value 25-35mgKOH/g, and solid content is
73-77%；Titanium dioxide selects rutile type titanium white, the NTR-606 of Ning Taixin good fortune company；Anti-settling agent selects polyamide wax
The 6900-20X of DISPARLON company；Dispersing agent can be used: the modified polyurethane wetting dispersing agent of Efka company: EFKA-
4010.Levelling agent uses the acrylate polymeric levelling agent of BYK company: BYK-358N；Defoaming agent uses the modest public affairs of this moral of hamming
The modified polyorganosiloxane defoaming agent of department: Defom5300；Talcum powder uses the WF90-10- of Guangxi Tian Ze superfine talcum powder company
98Q/TZB；Trihydroxy methyl diallyl ether uses Japan great Cao DAISO.
100KG unsaturated polyester resin and 0.4KG dispersing agent are added to 200 liter high speed dispersers under stirring
In, it 500-600 revs/min, stirs 5 minutes.1.6KG anti-settling agent and 40KG titanium dioxide, 1200-1500 revs/min of high speed is added
Dispersion 10-15 minutes.Control fineness is 30-35um.42KG talcum powder, 1200-1500 revs/min of high speed dispersion 15-20 is added
Minute.0.6KG levelling agent, 0.4KG defoaming agent, 7KG butyl acetate and 8KG trihydroxy methyl diallyl ether, 800-100 is added
Revs/min high speed dispersion 10-15 minutes.
Styrene, butyl acetate and propylene glycol methyl ether acetate solvent weight share are put into 200 liter solvent cylinders,
It is uniform by gear pump circulation stirring, the clear bright diluent composition of water is made.
By host agent: diluent: cobalt naphthenate: methyl ethyl ketone peroxide is 100:35:1.5:1.8 (temperature: 25 by weight
DEG C, environment temperature: 75%), obtained PE exempts from unsaturated polyester varnish of polishing.Construction material: closed medium-density plate has been done；Construction party
Method: rock field W-77,2.5mm bore manual spray gun, aerial spraying construction are selected；Drying condition: room temperature spontaneously dries (20-30
℃)。
It is detected using relevant criterion method, as a result as follows:
PE exempts from unsaturated polyester varnish host agent of polishing
| Project | Data | Detection method |
| Original paint appearance | Thick liquid, free from admixture | GB/T1721-1979 |
| Host agent solid content, % | 87 | GB/T1725-2007 |
| Gel time, min | 10 | GB/T7193-2008 |
| Surface drying time, min | 29 | GB/T1728-1979 |
| Paint film appearance | It is smooth | GB/T9761-1988 |
| Adhesive force, grade | 1 | GB/T9286-1998 |
| Covering power, g/ ㎡ | 150 | GB/T1725-1979 |
| Gloss (60 °) | 70 | GB/T4893-1985 |
Diluent
| Project | Data | Detection method |
| Appearance | Clearly, transparent, free from admixture | GB/T1721-1979 |
| Color | 1 | GB/T1721-1979 |
| Moisture | It is not muddy | GB/T1751-1992 |
Cobalt naphthenate
| Project | Data | Detection method |
| Appearance | Aubergine liquid | GB/T1721-1979 |
Methyl ethyl ketone peroxide
| Project | Data | Detection method |
| Appearance | It is colourless, transparent, clear liquid | GB/T1721-1979 |
PE exempts from polishing unsaturated polyester varnish and is sprayed on after plate face X hours, sprays PU Brilliant white paint, and experiment is white with PU light
Finishing coat: 82006PU ordor removing color inhibition spy's brilliant white finishing coat, 12097PU ordor removing color inhibition light specially match curing agent, and 10106PU is advanced
Finishing coat diluent；By host agent: curing agent: diluent by weight 1:0.8:0.6 (temperature: 26 DEG C, environment temperature: 74%)；It applies
Work tool: rock field W-71 spray gun, nozzle diameter: 1.5mm.
Embodiment 3
The unsaturated polyester resin is the BC9900# of Guangdong Bai Chuan chemical industry, acid value 25-35mgKOH/g, and solid content is
73-77%；Titanium dioxide selects rutile type titanium white, the NTR-606 of Ning Taixin good fortune company；Anti-settling agent selects polyamide wax
The 6900-20X of DISPARLON company；Dispersing agent can be used: the modified polyurethane wetting dispersing agent of Efka company: EFKA-
4010.Levelling agent uses the acrylate polymeric levelling agent of BYK company: BYK-358N；Defoaming agent uses the modest public affairs of this moral of hamming
The modified polyorganosiloxane defoaming agent of department: Defom5300；Talcum powder uses the WF90-10- of Guangxi Tian Ze superfine talcum powder company
98Q/TZB；Trihydroxy methyl diallyl ether uses Japan great Cao DAISO.
110KG unsaturated polyester resin and 0.4KG dispersing agent are added to 200 liter high speed dispersers under stirring
In, it 500-600 revs/min, stirs 5 minutes.1KG anti-settling agent and 40KG titanium dioxide, 1200-1500 revs/min of high speed point is added
It dissipates 10-15 minutes.Control fineness is 30-35um.34KG talcum powder is added, 1200-1500 revs/min of high speed dispersion 15-20 divides
Clock.0.6KG levelling agent, 0.4KG defoaming agent, 7.6KG butyl acetate and 8KG trihydroxy methyl diallyl ether, 800-100 is added
Revs/min high speed dispersion 10-15 minutes.
Styrene, butyl acetate and propylene glycol methyl ether acetate solvent weight share are put into 200 liter solvent cylinders,
It is uniform by gear pump circulation stirring, the clear bright diluent composition of water is made.
By host agent: diluent: cobalt naphthenate: methyl ethyl ketone peroxide is 100:35:1.5:1.8 (temperature: 27 by weight
DEG C, environment temperature: 78%), obtained PE exempts from unsaturated polyester varnish of polishing.Construction material: closed medium-density plate has been done；Construction party
Method: rock field W-77,2.5mm bore manual spray gun, aerial spraying construction are selected；Drying condition: room temperature spontaneously dries (20-30
℃)；First of PE exempts from unsaturated polyester varnish of polishing, and is detected using relevant criterion method, as a result as follows:
PE exempts from unsaturated polyester varnish host agent of polishing
| Project | Data | Detection method |
| Original paint appearance | Thick liquid, free from admixture | GB/T1721-1979 |
| Host agent solid content, % | 86 | GB/T1725-2007 |
| Gel time, min | 13 | GB/T7193-2008 |
| Surface drying time, min | 33 | GB/T1728-1979 |
| Paint film appearance | It is smooth | GB/T9761-1988 |
| Adhesive force, grade | 1 | GB/T9286-1998 |
| Covering power, g/ ㎡ | 150 | GB/T1725-1979 |
| Gloss (60 °) | 70 | GB/T4893-1985 |
Diluent
| Project | Data | Detection method |
| Appearance | Clearly, transparent, free from admixture | GB/T1721-1979 |
| Color | 1 | GB/T1721-1979 |
| Moisture | It is not muddy | GB/T1751-1992 |
Cobalt naphthenate
| Project | Data | Detection method |
| Appearance | Aubergine liquid | GB/T1721-1979 |
Methyl ethyl ketone peroxide
| Project | Data | Detection method |
| Appearance | It is colourless, transparent, clear liquid | GB/T1721-1979 |
After spraying PE exempts from polishing unsaturated polyester varnish air drying 4 hours, second PE is sprayed directly on its dry film and is exempted from
Polishing unsaturated polyester varnish, second PE are exempted from unsaturated polyester varnish of polishing, are detected using relevant criterion method, as a result such as
Under:
PE exempts from unsaturated polyester varnish host agent of polishing
| Project | Data | Detection method |
| Original paint appearance | Thick liquid, free from admixture | GB/T1721-1979 |
| Host agent solid content, % | 86 | GB/T1725-2007 |
| Gel time, min | 13 | GB/T7193-2008 |
| Surface drying time, min | 33 | GB/T1728-1979 |
| Paint film appearance | It is smooth | GB/T9761-1988 |
| Adhesive force, grade | 1 | GB/T9286-1998 |
| Covering power, g/ ㎡ | 150 | GB/T1725-1979 |
| Gloss (60 °) | 70 | GB/T4893-1985 |
| Adhesive force (draw compartment away from 2mm)/grade | 1 | GB/T9286-1998 |
PE exempts from polishing unsaturated polyester varnish and is sprayed on after plate face X hours, sprays PU Brilliant white paint, and experiment is white with PU light
Finishing coat: 82006PU ordor removing color inhibition spy's brilliant white finishing coat, 12097PU ordor removing color inhibition light specially match curing agent, and 10106PU is advanced
Finishing coat diluent.
By host agent: curing agent: diluent by weight 1:0.8:0.6 (temperature: 25 DEG C, environment temperature: 75%)；Construction work
Tool: rock field W-71 spray gun, nozzle diameter: 1.5mm.
Compared with prior art, the present invention using unsaturated polyester (UP) woodcare paint mainly by host agent, diluent, cobalt naphthenate and
Four kinds of components of methyl ethyl ketone peroxide mix, and PE provided by the invention exempts from unsaturated polyester (UP) woodcare paint of polishing, and have paint film not
Sanding is needed to polish, can directly construct polyurethane paint, and paint film interlayer has good adhesive force；It changes in the past not
Saturated polyester woodcare paint needs abundant sanding polishing, could have the shortcomings that good adhesion with polyurethane paint.
What has been described above is only a preferred embodiment of the present invention, it is noted that for those of ordinary skill in the art
For, without departing from the concept of the premise of the invention, various modifications and improvements can be made, these belong to the present invention
Protection scope.
Claims (9)
1. a kind of PE exempt from polish unsaturated polyester (UP) woodcare paint, which is characterized in that it mainly by host agent, diluent, cobalt naphthenate and
Four kinds of components of methyl ethyl ketone peroxide mix, by weight, host agent: diluent: cobalt naphthenate: methyl ethyl ketone peroxide=100:
30-35:1-2:1.2-2.5；
The host agent includes following weight percent composition:
2. PE according to claim 1 exempts from unsaturated polyester (UP) woodcare paint of polishing, which is characterized in that the unsaturated polyester (UP)
Resin is the BC9900#, acid value 25-35mgKOH/g, solid content 73-77% of Guangdong Bai Chuan chemical industry.
3. PE according to claim 1 exempts from unsaturated polyester (UP) woodcare paint of polishing, which is characterized in that the titanium dioxide is selected
Rutile type titanium white, using the NTR-606 of R895, Ning Taixin good fortune company of one hundred Li Lian company.
4. PE according to claim 1 exempts from unsaturated polyester (UP) woodcare paint of polishing, which is characterized in that the anti-settling agent is selected
Fumed silica or one kind of polyamide wax or more, using Cabot Co., Ltd, U.S. CAB-O-SIL gas phase dioxy
The 6900-20X of SiClx M-5 and DISPARLON company.
5. PE according to claim 1 exempts from unsaturated polyester (UP) woodcare paint of polishing, which is characterized in that the dispersing agent uses
The modified polyurethane wetting dispersing agent of Efka company: EFKA-4010.
6. PE according to claim 1 exempts from unsaturated polyester (UP) woodcare paint of polishing, which is characterized in that the levelling agent uses
The acrylate polymeric levelling agent of BYK company: BYK-358N.
7. PE according to claim 1 exempts from unsaturated polyester (UP) woodcare paint of polishing, which is characterized in that the defoaming agent uses
The modified polyorganosiloxane defoaming agent of this De Qian company of hamming: Defom5300.
8. PE according to claim 1 exempts from unsaturated polyester (UP) woodcare paint of polishing, which is characterized in that the talcum powder uses
The WF90-10-98Q/TZB of Guangxi Tian Ze superfine talcum powder company.
9. a kind of corresponding PE of unsaturated polyester (UP) woodcare paint of exempting from PE described in claim 1-8 any one to polish exempts from polishing not
The application method of saturated polyester woodcare paint, which is characterized in that it includes the following steps:
First host agent, diluent and cobalt naphthenate are mixed and stirred for uniformly, adding methyl ethyl ketone peroxide and stirring evenly, then
Using brushing, having gas or airless spraying to construct, the area of coating constructed every time is 0.18-0.2kg/ ㎡, repainting time
4-8 hours, drying condition are as follows: drying temperature: 10-40 DEG C, drying time 4-12 hour, drying means was to spontaneously dry or rise
Temperature is dry.