CN109535907A - 一种水性丙烯酸环氧氨基烘烤白色底漆的制备方法 - Google Patents

一种水性丙烯酸环氧氨基烘烤白色底漆的制备方法 Download PDF

Info

Publication number
CN109535907A
CN109535907A CN201811466560.0A CN201811466560A CN109535907A CN 109535907 A CN109535907 A CN 109535907A CN 201811466560 A CN201811466560 A CN 201811466560A CN 109535907 A CN109535907 A CN 109535907A
Authority
CN
China
Prior art keywords
time
period
water
grams
added
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201811466560.0A
Other languages
English (en)
Inventor
陈有权
康伦国
姚东生
阳京辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shaoguan Union Chemical Co Ltd
Union Foshan Chemical Co Ltd
Original Assignee
Shaoguan Union Chemical Co Ltd
Union Foshan Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shaoguan Union Chemical Co Ltd, Union Foshan Chemical Co Ltd filed Critical Shaoguan Union Chemical Co Ltd
Priority to CN201811466560.0A priority Critical patent/CN109535907A/zh
Publication of CN109535907A publication Critical patent/CN109535907A/zh
Withdrawn legal-status Critical Current

Abstract

本发明涉及一种水性丙烯酸环氧氨基烘烤白色底漆的制备方法，包括以下步骤：先合成一种水性羟基丙烯酸树脂WR.步骤为：加参加聚合的单体和引发剂入滴加罐，搅拌混合均匀，加溶剂入反应釜，开搅拌，通入氮气，加热到反应温度，滴加滴加罐的混合物，在一定时间内滴完，保温一段时间，补加引发剂,一定时间内滴完，保温一段时间，降温,出料。把水性羟基丙烯酸树脂WR投入配漆缸，加入中和剂和水，高速搅拌一段时间，调整PH值，再按照一定的比例在高速搅拌下分别加氨基树脂，环氧树脂，白色浆，消泡剂，流平剂，湿润剂，分散剂入配漆缸，高速搅拌一段时间，再加入溶剂和水，高速搅拌一段时间，取样检测细度和粘度合格后，包装。

Description

一种水性丙烯酸环氧氨基烘烤白色底漆的制备方法
技术领域
本发明涉及一种水性丙烯酸环氧氨基烘烤白色底漆的制备方法， 属于高分子有机化合物的合成技术领域。
技术背景
水性漆优点：第一以水作溶剂，节省大量资源；消除了施工时火灾危险性；降低了对大气污染；仅采用少量低毒性醇醚类有机溶剂，改善了作业环境条件。一般的水性涂料有机溶剂(占涂料)在15%～15%之间，第二水性涂料在湿表面和潮湿环境中可以直接涂覆施工；对材质表面适应性好，涂层附着力强。第三涂装工具可用水清洗，大大减少清洗溶剂的消耗。所以水性漆的用量越来越大，其中最为突出的是水性丙烯酸氨基烤漆，其用量越来越大，主要用于涂装卷材，铁桶，电动车，摩托车，汽车，汽车油箱，机械设备，不锈钢门，铝合金门和窗，塑料部件和钢构部件等等。
水性丙烯酸氨基烤漆的耐水性和耐盐雾性远远优于水性醇酸氨基烤漆和水性聚酯氨基烤漆，目前市场上能加入较多水的水性丙烯酸氨基烘烤底漆干燥速度慢，干燥速度快的水性丙烯酸氨基烘烤底漆能加入的水量少，达不到国家环保的要求。本发明配制的水性丙烯酸环氧氨基烘烤白色底漆使用了自己合成的水性丙烯酸树脂，不但能加入很多水，而且干燥速度快。
本发明涉及一种水性丙烯酸环氧氨基烘烤白色底漆的制备方法, 包括以下步骤：
(1) 先合成一种水性羟基丙烯酸树脂WR, 步骤为：加参加聚合的单体和引发剂入滴加罐，搅拌混合均匀，加溶剂入反应釜，开搅拌，通入氮气，加热到反应温度，滴加滴加罐的混合物，在一定时间内滴完，保温一段时间，补加引发剂, 一定时间内滴完，保温一段时间，降温, 出料得到水性羟基丙烯酸树脂WR。
（2）把水性羟基丙烯酸树脂WR投入配漆缸，加入中和剂和少量水，调整PH值，高速搅拌一段时间。
（3）按照一定的比例在高速搅拌下分别加氨基树脂，环氧树脂，白色浆，消泡剂，流平剂，湿润剂，分散剂入配漆缸，高速搅拌一段时间，再加入溶剂和水，高速搅拌一段时间。
（4）取样检测细度和粘度合格后，包装。
优选的，所述步骤（1）中水性羟基丙烯酸树脂WR的固体含量为60%至70%，粘度为8000-10000厘泊/25度（转动粘度计），羟值为30-50mgKOH/g。
优选的，所述步骤（3）中的环氧树脂为E-44。
具体实施方式
下面结合实施例对本发明的一种水性丙烯酸环氧氨基烘烤白色底漆的制备方法做进一步的描述。可以理解的是，此处所描述的具体实施例仅仅用于解释相关发明，而非对该发明的限定。
实施例1
（1）先合成一种水性羟基丙烯酸树脂WR，步骤为：先把5克丙烯酸，2克甲基丙烯酸，30克丙烯酸羟丙酯，18克苯乙烯，15克丙烯酸丁酯，28克甲基丙烯酸丁酯，6克过氧化二苯甲酰加入滴加罐，搅拌混合均匀。加15克异丁醇和35克入乙二醇单丁醚入反应釜，开搅拌，通入氮气，加热到90-93度，滴加滴加罐的混合物，4小时滴完，在90-93度保温3小时，补加2克过氧化二苯甲酰, 在90-93度保温5小时，降温, 出料。
（2）把60克水性羟基丙烯酸树脂WR投入配漆缸，开高速搅拌，加入5克二甲基乙醇胺和1克水，调整PH值为8.5-8.8，继续高速搅拌30分钟。
（3）加13克含固量为80%的氨基树脂氰特325，0.3克迪高270，0.2克迪高902W，0.2克迪高450，0.2克迪高755, 3克E-44环氧树脂和12克水性白色浆入配漆缸，高速搅拌0.5小时，再加5克DBE和80克水入配漆缸，高速搅拌1小时.
（4）取样检测细度小于50微米，用水调节粘度为1800-2300厘泊/25度后，包装。
实施例2
（1）先合成一种水性羟基丙烯酸树脂WR，步骤为：先把7克丙烯酸，8克醋酸乙烯，17克甲基丙烯酸甲酯，18克丙烯酸羟丙酯，17克丙烯酸丁酯，25克甲基丙烯酸丁酯，6克过氧化苯甲酸戊丁酯加入滴加罐，搅拌混合均匀。加8克异丁醇和42克入乙二醇单丁醚入反应釜，开搅拌，通入氮气，加热到110-115度，滴加滴加罐的混合物，6小时滴完，在110-115度保温2小时，补加0.5克过氧化苯甲酸叔丁酯，在110-115度保温6小时，降温, 出料。
（2）把65克水性羟基丙烯酸树脂WR投入配漆缸，加入5克三乙胺和0.5克水，调整PH值为7.6-7.8，高速搅拌30分钟。
（3）加15克含固量为80%的氨基树脂三木5717，0.3克迪高270，0.3克迪高902W，0.2克迪高450，0.2克迪高755, 4克E-44环氧树脂和13克水性白色浆入配漆缸，高速搅拌0.5小时，再加8克DBE和75克水入配漆缸，高速搅拌1小时.
（4）取样检测细度小于50微米，用水调节粘度为1800-2300厘泊/25度后，包装。
实施例3
（1）先合成一种水性羟基丙烯酸树脂WR，步骤为：先把6克丙烯酸，25克甲基丙烯酸甲酯，22克丙烯酸羟丙酯，16克丙烯酸丁酯，20克甲基丙烯酸丁酯，7克过氧化苯甲酸叔丁酯加入滴加罐，搅拌混合均匀。加40克入乙二醇单丁醚入反应釜，开搅拌，通入氮气，加热到110-115度，滴加滴加罐的混合物，5小时滴完，在110-115度保温4小时，补加0.5克过氧化苯甲酸叔丁酯，在110-115度保温6小时，降温, 出料。
（2）把62克水性羟基丙烯酸树脂WR投入配漆缸，加入5克三乙胺和0.5克水，调整PH值为7.6-7.8，高速搅拌30分钟。
（3）加14克含固量为80%的氨基树脂三木5717，0.3克迪高270，0.3克迪高902W，0.2克迪高450，0.2克迪高755, 4.5克E-44环氧树脂和11克水性白色浆入配漆缸，高速搅拌0.5小时，加8克乙二醇单甲醚和75克水入配漆缸，高速搅拌1小时.
（4）取样检测细度小于50微米，用水调节粘度为1800-2300厘泊/25度后，包装。
实施例4
（1）先合成一种水性羟基丙烯酸树脂WR，步骤为：先把2克丙烯酸，4克甲基丙烯酸，15克甲基丙烯酸冰片酯，5克甲基丙烯酸甲酯，18克丙烯酸羟乙酯，21克丙烯酸丁酯，30克甲基丙烯酸丁酯，8克过氧化苯甲酸叔丁酯加入滴加罐，搅拌混合均匀。加45克入丙二醇单丁醚入反应釜，开搅拌，通入氮气，加热到145-150度，滴加滴加罐的混合物，4小时滴完，在145-150度保温2小时，补加0.5克过氧化苯甲酸叔丁酯，在130-135度保温6小时，降温, 出料。
（2）把65克水性羟基丙烯酸树脂WR投入配漆缸，加入5.5克三乙胺和0.5克水，调整PH值为7.8-8.3，高速搅拌30分钟。
（3）加15克含固量为80%的氨基树脂三木5717，0.2克迪高270，0.2克迪高902W，0.2克迪高450，0.3克迪高755, 4克E-44环氧树脂和12克水性白色浆入配漆缸，高速搅拌0.5小时，加8克乙二醇单甲醚和75克水入配漆缸，高速搅拌1小时。
（4）取样检测细度小于50微米，用水调节粘度为1800-2300厘泊/25度后，包装。
4个实例烤漆的性能（烘烤温度95度，30分钟，漆膜厚度20微米）
烤漆编号 实例1 实例2 实例3 实例4
硬度 2H 2H 2H 2H
光泽（60度光泽仪 56-58 57-59 54-57 55-58
丰满度 可 可 可 可
水泡240小时 不起泡，不脱落 不起泡，不脱落 不起泡，不脱落 不起泡，不脱落
附着力（百格法） 通过 通过 通过 通过
反冲击 50厘米公斤 通过 通过 通过 通过
柔韧性 0级 0级 0级 0级
尽管本发明已作了详细说明并引证了实施例，但对于本领域的普通技术人员，显然可以按照上述说明而做出的各种方案、修改和改动，都应该包括在权利要求的范围之内。

Claims (4)

1.本发明涉及一种水性丙烯酸环氧氨基烘烤白色底漆的制备方法, 包括以下步骤：
（1）先合成一种水性羟基丙烯酸树脂WR, 步骤为：加参加聚合的单体和引发剂入滴加罐，搅拌混合均匀，加溶剂入反应釜，开搅拌，通入氮气，加热到反应温度，滴加滴加罐的混合物，在一定时间内滴完，保温一段时间，补加引发剂, 一定时间内滴完，保温一段时间，降温, 出料；
（2）把水性羟基丙烯酸树脂WR投入配漆缸，加入中和剂和少量水，调整PH值，高速搅拌一段时间；
（3）按照一定的比例在高速搅拌下分别加氨基树脂，环氧树脂，白色浆，消泡剂，流平剂，湿润剂，分散剂入配漆缸，高速搅拌一段时间，再加入溶剂和水，高速搅拌一段时间；
（4）取样检测细度和粘度合格后，包装。
2.根据权利1所述的制备方法，其特征在于，所述步骤（1）中水性羟基丙烯酸树脂WR的固体含量为60%至70%，粘度为8000-10000厘泊/25度（转动粘度计），羟值为30-50mgKOH/g。
3.根据权利1所述的制备方法，其特征在于，所述步骤（3）中的环氧树脂为E-44。
4.权利要求1至3任意一项所述的制备方法制备得到的水性丙烯酸环氧氨基烘烤白色底漆。
CN201811466560.0A 2018-12-03 2018-12-03 一种水性丙烯酸环氧氨基烘烤白色底漆的制备方法 Withdrawn CN109535907A (zh)