CN109535789A - A kind of preparation method of interior wall multifunctional inorganic environmental protection coating material - Google Patents
A kind of preparation method of interior wall multifunctional inorganic environmental protection coating material Download PDFInfo
- Publication number
- CN109535789A CN109535789A CN201811357239.9A CN201811357239A CN109535789A CN 109535789 A CN109535789 A CN 109535789A CN 201811357239 A CN201811357239 A CN 201811357239A CN 109535789 A CN109535789 A CN 109535789A
- Authority
- CN
- China
- Prior art keywords
- diatomite
- solution
- agent
- interior wall
- lotion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of interior wall preparation methods of multifunctional inorganic environmental protection coating material.For the present invention mainly with alkaline silicate lithium, nano silica aqueous solution is main film forming matter, assists appropriate ordor removing lotion, titanium dioxide, coarse whiting, kaolin, diatomite is as pigments and fillers, with dispersing agent, defoaming agent, wetting agent, thickener etc. collectively constitute, the coating category ordor removing environment-friendly type coating, Diamond Search content, it is water-fast, mildew resistant moistureproof performance is good, there is certain fire resistance property, adding the diatomite with porous structure simultaneously has formaldehyde adsorption and other effects, is a kind of a kind of environment-friendly type coating of excellent combination property.
Description
Technical field
The present invention relates to inorganic fire, ordor removing interior wall coating, and the preparation of the multifunctional inorganic environmental protection coating material with adsorption function
Method.
Background technique
With the development of social economy and being constantly progressive for scientific level, raising of the people to environmental consciousness is increasingly infused
Weight indoor environmental quality
Inner wall surface ornament materials is mainly emulsion paint on the market at present, though environmental-protecting performance is being continuously improved, with inorganic painting
Material still has certain gap.It has excellent performance and the product price of epipodium guaranteed request is again more expensive.
Traditional interior wall inorganic coating, the feature of environmental protection and mildew resistance are preferable, but referring to GB/T9756-2009 " synthetic resin
Lotion interior wall coating " scrubbing resistance it is poor, and storage stability is not easy to control.
The characteristics of present invention incorporates traditional inorganic coatings provides preferable scrubbing resistance by using lithium metasilicate solution, resistance to
It is aqueous, fire protecting performance.The diatomite of porous structure is added, product has certain adsorption function and VOC content almost nil
Interior wall inorganic coating.
Summary of the invention
1, the present invention selects the ordor removing lotion of low film formation temperature, can not have to addition coalescing agent.
2, after ordor removing lotion is added, it is alkaline state that the system after lotion is added, which is adjusted, in addition potassium methyl silicate,
Prevention lotion is reacted with subsequent alkaline silicate potassium solution and nanosilica solution, it is ensured that the stability under storing, no
There is apparent rear thickening and flocculation phenomenon.
3, addition has the diatomite of porous structure, due to its special gap structure, has stronger suction-operated,
It can purify the air of a room.
4, nanosilica solution is added in the present invention, can preferably improves the storage stability of finished product paint.
Specific embodiment:
More detailed elaboration is carried out to the present invention below, in order to be understood by industry field technical staff, thus to the present invention
Protection scope be bound.
Embodiment one,
It is as follows for the preparation ratio of each section in the present invention:
Deionized water 20%
Dispersing agent 0.8%
Wetting agent 0.1%
Hydroxyethylmethylcellulose 0.3%
Defoaming agent 0.15%
Titanium dioxide 20%
Kaolin 5%
Diatomite 4%
Coarse whiting 5%
Ordor removing lotion 8%
Methane-siliconic acid potassium solution 0.3%
Nano silica 20%
Lithium metasilicate solution 15%
Defoaming agent 0.4%
Thickener 1%
Production explanation: 1, weighing deionized water, dispersing agent, wetting agent low speed and stir in advance 3 minutes, adds hydroxyethyl methyl fiber
Defoaming agent is added in element, stirring after five minutes.2, titanium dioxide, kaolin, diatomite and coarse whiting, high speed point are added under moderate-speed mixer
It dissipates 30-40 minutes.3, lotion is added, is alkaline state with methane-siliconic acid potassium solution regulation system.4, lithium metasilicate solution is added, is disappeared
Infusion, thickener.
Embodiment two,
It is as follows for the preparation ratio of each section in the present invention:
Deionized water 30%
Dispersing agent 0.4%
Wetting agent 0.3%
Hydroxyethylmethylcellulose 0.5%
Defoaming agent 0.4%
Titanium dioxide 10%
Kaolin 12%
Diatomite 5%
Coarse whiting 8%
Ordor removing lotion 3%
Methane-siliconic acid potassium solution 0.1%
Nano silica 20%
Lithium metasilicate solution 10%
Defoaming agent 0.1%
Thickener 0.2%
Production explanation: 1, weighing deionized water, dispersing agent, wetting agent low speed and stir in advance 3 minutes, adds hydroxyethyl methyl fiber
Defoaming agent is added in element, stirring after five minutes.2, titanium dioxide, kaolin, diatomite and coarse whiting, high speed point are added under moderate-speed mixer
It dissipates 30-40 minutes.3, lotion is added, is alkaline state with methane-siliconic acid potassium solution regulation system.4, lithium metasilicate solution is added, is disappeared
Infusion, thickener.
Embodiment three,
It is as follows for the preparation ratio of each section in the present invention:
Deionized water 25%
Dispersing agent 0.6%
Wetting agent 0.2%
Hydroxyethylmethylcellulose 0.4
Defoaming agent 0.25%
Titanium dioxide 12%
Kaolin 8%
Diatomite 8%
Coarse whiting 10%
Ordor removing lotion 5%
Methane-siliconic acid potassium solution 0.3%
Nano silica 10%
Lithium metasilicate solution 20%
Defoaming agent 0.3%
Thickener 0.7%
Production explanation: 1, weighing deionized water, dispersing agent, wetting agent low speed and stir in advance 3 minutes, adds hydroxyethyl methyl fiber
Defoaming agent is added in element, stirring after five minutes.2, titanium dioxide, kaolin, diatomite and coarse whiting, high speed point are added under moderate-speed mixer
It dissipates 30-40 minutes.3, lotion is added, is alkaline state with methane-siliconic acid potassium solution regulation system.4, lithium metasilicate solution is added, is disappeared
Infusion, thickener.
The present invention is not limited to the above embodiments, can be implemented described in the content of present invention and has the good result.
Claims (6)
1. a kind of interior wall preparation method of multifunctional inorganic environmental protection coating material
Deionized water 20-30%
Dispersing agent 0.4-0.8%
Wetting agent 0.1-0.3%
Hydroxyethylmethylcellulose 0.3-0.5%
Defoaming agent 0.15-0.4%
Titanium dioxide 10-20%
Kaolin 5-12%
Diatomite 4-8%
Coarse whiting 5-10%
Ordor removing lotion 3-8%
Methane-siliconic acid potassium solution 0.1-0.4%
Nanosilica solution 10-20%
Lithium metasilicate solution 10-20%
Defoaming agent 0.1-0.4%
Thickener 0.2-1%.
2. being free of APEO according to the method described in claim 1, the wetting agent has to comply with environmental requirement.
3. the ordor removing lotion that lotion selects minimum film formation temperature to be lower than 5 degrees Celsius.
4. lithium metasilicate solution produces according to the method described in claim 1, the nanosilica solution modulus is greater than 2.5
Modulus is greater than 2.6.
5. according to the method described in claim 1, the diatomite selects the diatomite with porous structure.
6. according to the method described in claim 1, ensure after addition methane-siliconic acid potassium solution slurry in alkaline state.