CN109486310A - A kind of aqueous stone-like coating and its manufacturing method - Google Patents
A kind of aqueous stone-like coating and its manufacturing method Download PDFInfo
- Publication number
- CN109486310A CN109486310A CN201811524668.0A CN201811524668A CN109486310A CN 109486310 A CN109486310 A CN 109486310A CN 201811524668 A CN201811524668 A CN 201811524668A CN 109486310 A CN109486310 A CN 109486310A
- Authority
- CN
- China
- Prior art keywords
- coating
- thickener
- cosolvent
- aqueous stone
- defoaming agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
It includes that the group of following weight percentage is grouped as that the invention, which is related to a kind of aqueous stone-like coating and its manufacturing method, the coating: the water of colored lacquer particle 15-30%, acrylic resin modified 10-30%, coalescing agent 5-10%, thickener 5-10%, cosolvent 3-15%, sedimentary rock diatomite 3.5-10%, defoaming agent 3-6% and surplus；The aqueous stone-like coating is with acrylic resin modified for substrate, it is equipped with a variety of coalescing agents, thickener, cosolvent, sedimentary rock diatomite and defoaming agent, has that fire-retardant, waterproof, alkaline-resisting, adhesive force is strong, fidelity is high, is easy to the advantages that repairing damaged external wall.
Description
[technical field]
The invention is related to technical field of coatings, especially a kind of aqueous stone-like coating and its manufacturing method.
[background technique]
Existing structure exterior wall finishing needs to paste by cement mortar or the modes such as cladding mainly based on stone slice
It constructs, decoration cost is high；Exterior walls of buildings is exposed to outer, solarization wind and weather for a long time, stone material be easy to appear it is damaged or
Obscission, later period need to replace full wafer stone material when repairing, and not only difficulty of construction is big, but also is easy to appear two tone colour,
It influences beautiful, therefore develops a exterior wall finishing cost, particularly important convenient for the coating of exterior wall breakage reparation of can reduce.
[summary of the invention]
To solve the above problems, the invention provides a kind of aqueous stone-like coating and its manufacturing method, it can be effective
It reduces exterior wall finishing cost, repaired convenient for damaged.
To achieve the above object, the invention provides the following technical solutions:
A kind of aqueous stone-like coating, the coating include that the group of following weight percentage is grouped as: colored lacquer particle
15-30%, acrylic resin modified 10-30%, coalescing agent 5-10%, thickener 5-10%, cosolvent 3-15%, sedimentary rock
The water of diatomite 3.5-10%, defoaming agent 3-6% and surplus.
Preferably, it is further defined in that the coating includes that the group of following weight percentage is grouped as: color
Color lacquer particle 20-30%, acrylic resin modified 10-25%, coalescing agent 5-10%, thickener 5-10%, cosolvent
The water of 5-15%, sedimentary rock diatomite 5-10%, defoaming agent 4-6% and surplus.
Preferably, it is further defined in that the coating includes that the group of following weight percentage is grouped as: color
Color lacquer particle 20-25%, acrylic resin modified 15-25%, coalescing agent 5-8%, thickener 5-8%, cosolvent 5-
10%, the water of sedimentary rock diatomite 5-8%, defoaming agent 5% and surplus.
Preferably, it is further defined in that the coalescing agent is selected from glycol monoethyl ether, ethylene glycol list second
One of ether, ethylene glycol monobutyl ether, propylene glycol monomethyl ether or tripropylene glycol butyl ether or a variety of mixtures.
Preferably, it is further defined in that the thickener is selected from hydroxyethyl cellulose, carboxymethyl cellulose
Or the mixture of one or both of polyurethane.
Preferably, it is further defined in that the cosolvent is selected from ethylene glycol ether acetate or its mixing
Object.
Preferably, it is further defined in that the defoaming agent is selected from organic siliconresin class defoaming agent or it is mixed
Close object.
Preferably, the diameter for being further defined in that the colored lacquer particle is 0.5-5mm.
A method of above-mentioned aqueous stone-like coating is prepared, is included the following steps:
(a) each component is weighed by the weight percentage；
(b) weighed colored lacquer particle, acrylic resin modified, coalescing agent, sedimentary rock diatomite and water are thrown
Enter in blender and stir, room temperature, 800-1000r/min revolving speed under stir 20-30min；
(c) weighed thickener, cosolvent and defoaming agent are added in the blender in step (b), are warming up to 30-40
DEG C, 10-20min is stirred under the revolving speed of 1000-1200r/min, is cooled to room temperature, is filtered to get the aqueous stone-like coating.
The beneficial effect of the invention is: the invention with acrylic resin modified for substrate, be equipped with it is a variety of at
Film auxiliary agent, thickener, cosolvent, sedimentary rock diatomite and defoaming agent, have that fire-retardant, waterproof, alkaline-resisting, adhesive force is strong, fidelity
Height is easy to the advantages that repairing damaged external wall.
[specific embodiment]
Below in conjunction with specific embodiment, invention is further described in detail:
A kind of aqueous stone-like coating, the coating include that the group of following weight percentage is grouped as: colored lacquer particle
15-30%, acrylic resin modified 10-30%, coalescing agent 5-10%, thickener 5-10%, cosolvent 3-15%, sedimentary rock
The water of diatomite 3.5-10%, defoaming agent 3-6% and surplus.
In the present embodiment, the coalescing agent be selected from glycol monoethyl ether, ethylene glycol monoethyl ether, ethylene glycol monobutyl ether,
One of propylene glycol monomethyl ether or tripropylene glycol butyl ether or a variety of mixtures, coalescing agent can promote to form a film.More into one
Say that the coalescing agent is selected from Dow group (DOW) production, and the tripropylene glycol butyl ether of model TPnB plays in step ground
Promote the effect of film forming.
In the present embodiment, the thickener is selected from one of hydroxyethyl cellulose, carboxymethyl cellulose or polyurethane
Or two kinds of mixture.Furthermore, the thickener is selected from BASF AG (Badische Anilin-und-Soda-
Fabrik it) produces, the polyurethane thickener of model NLS300 can be improved product stability, application property and water resistance.Institute
It states cosolvent and is selected from or mixtures thereof ethylene glycol ether acetate, play the role of promoting dissolution.
In the present embodiment, the defoaming agent is selected from or mixtures thereof organic siliconresin class defoaming agent, furthermore,
The defoaming agent is selected from the production of Ming Jia company, and the organosilicon and mineral oil mixture product of model 7120 improve product paint
Film hydrophobicity, compactness, adhesive force and construction recoatability.The diameter of the colour lacquer particle is 0.5-5mm.Preferably
1-5mm, more preferably status 3-5mm.
A method of above-mentioned aqueous stone-like coating is prepared, is included the following steps:
(a) each component is weighed by the weight percentage；
(b) weighed colored lacquer particle, acrylic resin modified, coalescing agent, sedimentary rock diatomite and water are thrown
Enter in blender and stir, room temperature, 800-1000r/min revolving speed under stir 20-30min；
(c) weighed thickener, cosolvent and defoaming agent are added in the blender in step (b), are warming up to 30-40
DEG C, 10-20min is stirred under the revolving speed of 1000-1200r/min, is cooled to room temperature, is filtered to get the aqueous stone-like coating.
Embodiment 1
(a1) percentage composition weighs following material by weight: colored lacquer particle 15%, it is acrylic resin modified 30%,
Coalescing agent 5%, thickener 10%, cosolvent 15%, sedimentary rock diatomite 3.5%, defoaming agent 6% and surplus water.
(b1) weighed colored lacquer particle, acrylic resin modified, coalescing agent, sedimentary rock diatomite and water are thrown
Enter in blender and stir, room temperature, 800-1000r/min revolving speed under stir 20-30min；
(c1) weighed thickener, cosolvent and defoaming agent are added in the blender in step (b1), are warming up to 30-40
DEG C, 10-20min is stirred under the revolving speed of 1000-1200r/min, is cooled to room temperature, is filtered to get the aqueous stone-like coating.
Embodiment 2
(a2) percentage composition weighs following material by weight: colored lacquer particle 20%, it is acrylic resin modified 25%,
Coalescing agent 10%, thickener 5%, cosolvent 3%, sedimentary rock diatomite 10%, defoaming agent 6% and surplus water.
(b2) weighed colored lacquer particle, acrylic resin modified, coalescing agent, sedimentary rock diatomite and water are thrown
Enter in blender and stir, room temperature, 800-1000r/min revolving speed under stir 20-30min；
(c2) weighed thickener, cosolvent and defoaming agent are added in the blender in step (b2), are warming up to 30-40
DEG C, 10-20min is stirred under the revolving speed of 1000-1200r/min, is cooled to room temperature, is filtered to get the aqueous stone-like coating.
Embodiment 3
(a3) percentage composition weighs following material by weight: colored lacquer particle 25%, it is acrylic resin modified 20%,
Coalescing agent 8%, thickener 8%, cosolvent 8%, sedimentary rock diatomite 8%, defoaming agent 5% and surplus water.
(b3) weighed colored lacquer particle, acrylic resin modified, coalescing agent, sedimentary rock diatomite and water are thrown
Enter in blender and stir, room temperature, 800-1000r/min revolving speed under stir 20-30min；
(c3) weighed thickener, cosolvent and defoaming agent are added in the blender in step (b3), are warming up to 30-40
DEG C, 10-20min is stirred under the revolving speed of 1000-1200r/min, is cooled to room temperature, is filtered to get the aqueous stone-like coating.
Embodiment 4
(a4) percentage composition weighs following material by weight: colored lacquer particle 25%, it is acrylic resin modified 15%,
Coalescing agent 5%, thickener 10%, cosolvent 10%, sedimentary rock diatomite 8%, defoaming agent 5% and surplus water.
(b4) weighed colored lacquer particle, acrylic resin modified, coalescing agent, sedimentary rock diatomite and water are thrown
Enter in blender and stir, room temperature, 800-1000r/min revolving speed under stir 20-30min；
(c4) weighed thickener, cosolvent and defoaming agent are added in the blender in step (b4), are warming up to 30-40
DEG C, 10-20min is stirred under the revolving speed of 1000-1200r/min, is cooled to room temperature, is filtered to get the aqueous stone-like coating.
Embodiment 5
(a5) percentage composition weighs following material by weight: colored lacquer particle 30%, it is acrylic resin modified 10%,
Coalescing agent 10%, thickener 10%, cosolvent 5%, sedimentary rock diatomite 5%, defoaming agent 4% and surplus water.
(b5) weighed colored lacquer particle, acrylic resin modified, coalescing agent, sedimentary rock diatomite and water are thrown
Enter in blender and stir, room temperature, 800-1000r/min revolving speed under stir 20-30min；
(c5) weighed thickener, cosolvent and defoaming agent are added in the blender in step (b5), are warming up to 30-40
DEG C, 10-20min is stirred under the revolving speed of 1000-1200r/min, is cooled to room temperature, is filtered to get the aqueous stone-like coating.
Aqueous stone-like coating made from Examples 1 to 5 is painted on external wall respectively, after to be dried, is randomly selected
20 people of volunteer is compared the coating of Examples 1 to 5 using range estimation, with modes such as hand touches, as a result such as table 1
By table 1 it can be seen that the aqueous stone-like coating fidelity of the invention is high, all reached in terms of observing and touching
The effect of stone material is arrived.
Claims (9)
1. a kind of aqueous stone-like coating, it is characterised in that the coating includes that the group of following weight percentage is grouped as: colored true
Mineral varnish particle 15-30%, acrylic resin modified 10-30%, coalescing agent 5-10%, thickener 5-10%, cosolvent 3-
15%, the water of sedimentary rock diatomite 3.5-10%, defoaming agent 3-6% and surplus.
2. aqueous stone-like coating according to claim 1, it is characterised in that the coating includes following weight percentage
Group is grouped as: colored lacquer particle 20-30%, acrylic resin modified 10-25%, coalescing agent 5-10%, thickener 5-
10%, the water of cosolvent 5-15%, sedimentary rock diatomite 5-10%, defoaming agent 4-6% and surplus.
3. aqueous stone-like coating according to claim 1, it is characterised in that the coating includes following weight percentage
Group is grouped as: colored lacquer particle 20-25%, acrylic resin modified 15-25%, coalescing agent 5-8%, thickener 5-
8%, the water of cosolvent 5-10%, sedimentary rock diatomite 5-8%, defoaming agent 5% and surplus.
4. aqueous stone-like coating according to claim 1, it is characterised in that the coalescing agent be selected from glycol monoethyl ether,
One of ethylene glycol monoethyl ether, ethylene glycol monobutyl ether, propylene glycol monomethyl ether or tripropylene glycol butyl ether or a variety of mixtures.
5. aqueous stone-like coating according to claim 1, it is characterised in that the thickener is selected from hydroxyethyl cellulose, carboxylic
The mixture of one or both of methylcellulose or polyurethane.
6. aqueous stone-like coating according to claim 1, it is characterised in that the cosolvent is selected from ethylene glycol ethyl ether acetic acid
Or mixtures thereof ester.
7. aqueous stone-like coating according to claim 1, it is characterised in that the defoaming agent is selected from organic siliconresin class and disappears
Or mixtures thereof infusion.
8. aqueous stone-like coating according to claim 1, it is characterised in that the diameter of the colour lacquer particle is
0.5-5mm。
9. a kind of method for preparing the aqueous stone-like coating as described in claim 1-5 is any, which is characterized in that including walking as follows
It is rapid:
(a) each component is weighed by the weight percentage；
(b) weighed colored lacquer particle, acrylic resin modified, coalescing agent, sedimentary rock diatomite and water investment are stirred
Mix in machine and stir, room temperature, 800-1000r/min revolving speed under stir 20-30min；
(c) weighed thickener, cosolvent and defoaming agent are added in the blender in step (b), are warming up to 30-40 DEG C,
10-20min is stirred under the revolving speed of 1000-1200r/min, is cooled to room temperature, is filtered to get the aqueous stone-like coating.