CN109485346A - A kind of ceramic tile marble adhesive and preparation method thereof - Google Patents
A kind of ceramic tile marble adhesive and preparation method thereof Download PDFInfo
- Publication number
- CN109485346A CN109485346A CN201811586973.2A CN201811586973A CN109485346A CN 109485346 A CN109485346 A CN 109485346A CN 201811586973 A CN201811586973 A CN 201811586973A CN 109485346 A CN109485346 A CN 109485346A
- Authority
- CN
- China
- Prior art keywords
- parts
- ceramic tile
- raw material
- tile marble
- marble adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of ceramic tile marble adhesives, prepare in raw material and contain: portland cement, quartz sand, coarse whiting, talcum powder, hydroxymethyl starch ether, lignosulfonate salt, polymer, early strength agent.By reasonably combined and its content the reasonably adjusting of the production raw material to ceramic tile marble adhesive in the present invention, obtained ceramic tile marble adhesives power is strong, and construction effect is good, and raw material cost is low, and production method is simple, is convenient for large-scale promotion.
Description
Technical field
The present invention relates to a kind of ceramic tile marble adhesives and preparation method thereof.
Background technique
Tile adhesives, also known as glue for tile, ceramic tile bond or ceramic tile viscose glue mud, be mainly used for paste ceramic tile, face brick,
The ornament materials such as brick are widely used in the facing decoration places of the buildings such as inside and outside metope, ground, bathroom, kitchen.
Traditional tile bonding system is substantially simple silicate cement cement mortar, since the moisture in mortar can be very
It is adsorbed fastly by base material or ceramic tile, because cement aquation is insufficient, only part of cement really plays hydration, greatly
The intensity and cohesive force of mortar are affected greatly, furthermore slurry dehydration is too fast, so that mortar can generate bending before interface hardening
Stress just generates removing when this stress is greater than cohesive force, so can not obtain using simple silicate cement cement mortar
Good bond effect.
With the development of technology, occur many novel tile adhesives at present.For example CN108570287A is such as magnificent
In disclose a kind of tile adhesives, the raw material including following parts by weight: 0.5-2 parts of emulsifier, 0.5-2 parts of acrylic acid, propylene
10-25 parts of acid butyl ester, 10-20 parts of styrene, 10-25 parts of acrylic acid isooctyl, 0.4-1 parts of catalyst, firmness is more when use
By force, adhesive force is more preferably.CN108751848A discloses a kind of high-strength water-resistance tile adhesives and preparation method thereof, by following
The raw material of parts by weight is made: 50-60 parts of ordinary portland cement, 20-30 parts of bunt gypsum, 28-34 parts of slate, beidellite 22-28
Part, 15-20 parts of diabase, magnesium is powder 10-15 parts strong, 5-10 parts of torispherical glass powder, 8-16 parts of lithium magnesium silicate, vinyl acetate-uncle
Ethylene carbonate -4-8 parts of butyl acrylate ternary polymerization latex powder, 3-6 parts of edible seaweed powder, 2-5 parts of ghatti gum, the chloro- N- of 4- are (hard
Acyl amine methyl) 1-2 parts of pyridine, 0.5-1.5 parts of rosin acid calcium soap, 0.5-1.5 parts of zirconium stearate.Although these binders can take
Preferable bond effect, but the cost of manufacture in binder are unfavorable for large-scale promotion.
Summary of the invention
The purpose of the present invention is to provide a kind of ceramic tile marble adhesives and preparation method thereof.
The technical solution used in the present invention is:
A kind of ceramic tile marble adhesive, prepares in raw material and contains: portland cement, quartz sand, coarse whiting, talcum powder, hydroxyl
Methyl starch ether, lignosulfonate salt, polymer, early strength agent.
Further, it in terms of mass fraction, prepares in raw material and contains: 300~500 parts of portland cement, quartz sand 200~
350 parts, 50~70 parts of coarse whiting, 30~50 parts of talcum powder, 20~35 parts of hydroxymethyl starch ether, 8~22 parts of polymer, sulfonation it is wooden
0.1~1 part of plain salt, 1~10 part of early strength agent.
Further, it in terms of mass fraction, prepares in raw material and contains: 300~400 parts of portland cement, quartz sand 200~
300 parts, 50~60 parts of coarse whiting, 30~40 parts of talcum powder, 20~30 parts of hydroxymethyl starch ether, 8~15 parts of polymer, sulfonation it is wooden
0.1~0.5 part of plain salt, 1~4 part of early strength agent.
Further, it in terms of mass fraction, prepares in raw material and contains: 300 parts of portland cement, 250 parts of quartz sand, coarse whiting
50 parts, 35 parts of talcum powder, 30 parts of hydroxymethyl starch ether, 9 parts of polymer, 0.3 part of lignosulfonate salt, 2 parts of early strength agent.
Further, polymer is vinyl acetate/ethylene/copolymer, hydroxypropyl methyl cellulose.
Further, according to the mass fraction, containing 5~12 parts of vinyl acetate/ethylene/copolymer, hydroxypropyl methyl fiber
3~10 parts of element;
Further, according to the mass fraction, containing 5~10 parts of vinyl acetate/ethylene/copolymer, hydroxypropyl methyl fiber
3~5 parts of element.
Further, according to the mass fraction, containing 5 parts of vinyl acetate/ethylene/copolymer, hydroxypropyl methyl cellulose 4
Part.
Further, early strength agent is calcium formate.
The preparation method of above-mentioned ceramic tile marble adhesive, it is characterised in that: mixed after weighing raw material by mass fraction
Uniformly.
The beneficial effects of the present invention are:
Pass through reasonably combined and its content the reasonable tune of the production raw material to ceramic tile marble adhesive in the present invention
Whole, obtained ceramic tile marble adhesives power is strong, and construction effect is good, and raw material cost is low, and production method is simple, just
In large-scale promotion.
Specific embodiment
Enumerate embodiment further below with the present invention will be described in detail.It will similarly be understood that following embodiment is served only for this
Invention is further described, and should not be understood as limiting the scope of the invention, those skilled in the art are according to the present invention
Some nonessential modifications and adaptations that the principle of elaboration is made all belong to the scope of protection of the present invention.Following specific works of example
Skill parameter etc. is also only an example in OK range, i.e. those skilled in the art can do suitable model by the explanation of this paper
Interior selection is enclosed, and does not really want to be defined in hereafter exemplary specific data.
Embodiment 1
A kind of ceramic tile marble adhesive is prepared in raw material and is contained in terms of mass fraction: 300 parts of portland cement, quartz
200 parts of sand, 50 parts of coarse whiting, 30 parts of talcum powder, 20 parts of hydroxymethyl starch ether, 5 parts of vinyl acetate/ethylene/copolymer, hydroxypropyl
3 parts of methylcellulose, 0.1 part of lignosulfonate salt, 1 part of calcium formate.
Embodiment 2
A kind of ceramic tile marble adhesive is prepared in raw material and is contained in terms of mass fraction: 500 parts of portland cement, quartz
350 parts of sand, 70 parts of coarse whiting, 50 parts of talcum powder, 35 parts of hydroxymethyl starch ether, 2 parts of vinyl acetate/ethylene/copolymer 1, hydroxypropyl
10 parts of methylcellulose, 1 part of lignosulfonate salt, 10 parts of calcium formate.
Embodiment 3
A kind of ceramic tile marble adhesive is prepared in raw material and is contained in terms of mass fraction: 400 parts of portland cement, quartz
300 parts of sand, 60 parts of coarse whiting, 40 parts of talcum powder, 30 parts of hydroxymethyl starch ether, 0 part of vinyl acetate/ethylene/copolymer 1, hydroxypropyl
5 parts of methylcellulose, 0.5 part of lignosulfonate salt, 4 parts of calcium formate.
Embodiment 4
A kind of ceramic tile marble adhesive is prepared in raw material and is contained in terms of mass fraction: 300 parts of portland cement, quartz
250 parts of sand, 50 parts of coarse whiting, 35 parts of talcum powder, 30 parts of hydroxymethyl starch ether, 5 parts of vinyl acetate/ethylene/copolymer, hydroxypropyl
4 parts of methylcellulose, 0.3 part of lignosulfonate salt, 2 parts of calcium formate.
The preparation method of ceramic tile marble binder in Examples 1 to 4: it is uniformly mixed i.e. after weighing raw material by mass fraction
It can.
Performance detection is carried out to the product of above-described embodiment, testing result is as shown in the table:
Claims (10)
1. a kind of ceramic tile marble adhesive, it is characterised in that: prepare in raw material and contain: portland cement, quartz sand, coarse whiting,
Talcum powder, hydroxymethyl starch ether, lignosulfonate salt, polymer, early strength agent.
2. ceramic tile marble adhesive according to claim 1, it is characterised in that: in terms of mass fraction, prepare in raw material
Contain: 300~500 parts of portland cement, 200~350 parts of quartz sand, 50~70 parts of coarse whiting, 30~50 parts of talcum powder, methylol
20~35 parts of starch ether, 8~22 parts of polymer, 0.1~1 part of lignosulfonate salt, 1~10 part of early strength agent.
3. ceramic tile marble adhesive according to claim 2, it is characterised in that: in terms of mass fraction, prepare in raw material
Contain: 300~400 parts of portland cement, 200~300 parts of quartz sand, 50~60 parts of coarse whiting, 30~40 parts of talcum powder, methylol
20~30 parts of starch ether, 8~15 parts of polymer, 0.1~0.5 part of lignosulfonate salt, 1~4 part of early strength agent.
4. ceramic tile marble adhesive according to claim 3, it is characterised in that: in terms of mass fraction, prepare in raw material
Contain: 300 parts of portland cement, 250 parts of quartz sand, 50 parts of coarse whiting, 35 parts of talcum powder, 30 parts of hydroxymethyl starch ether, polymer 9
Part, 0.3 part of lignosulfonate salt, 2 parts of early strength agent.
5. ceramic tile marble adhesive according to claim 1, it is characterised in that: polymer is vinyl acetate/ethylene/
Copolymer, hydroxypropyl methyl cellulose.
6. ceramic tile marble adhesive according to claim 5, it is characterised in that: according to the mass fraction, contain acetic acid second
5~12 parts of enester/ethylene copolymer, 3~10 parts of hydroxypropyl methyl cellulose;
7. ceramic tile marble adhesive according to claim 6, it is characterised in that: according to the mass fraction, contain acetic acid second
5~10 parts of enester/ethylene copolymer, 3~5 parts of hydroxypropyl methyl cellulose.
8. ceramic tile marble adhesive according to claim 7, it is characterised in that: according to the mass fraction, contain acetic acid second
5 parts of enester/ethylene copolymer, 4 parts of hydroxypropyl methyl cellulose.
9. described in any item ceramic tile marble adhesives according to claim 1~8, it is characterised in that: early strength agent is calcium formate.
10. the preparation method of ceramic tile marble adhesive according to any one of claims 1 to 9, it is characterised in that: press mass parts
Number is uniformly mixed after weighing raw material.