CN109483666A - The industrialization preparation method of three layers of orthogonal integrated plate and the orthogonal circuit board of preparation - Google Patents
The industrialization preparation method of three layers of orthogonal integrated plate and the orthogonal circuit board of preparation Download PDFInfo
- Publication number
- CN109483666A CN109483666A CN201811587633.1A CN201811587633A CN109483666A CN 109483666 A CN109483666 A CN 109483666A CN 201811587633 A CN201811587633 A CN 201811587633A CN 109483666 A CN109483666 A CN 109483666A
- Authority
- CN
- China
- Prior art keywords
- plate
- thickness
- length
- orthogonal
- standard
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of industrialization preparation methods of three layers of orthogonal integrated plate, the preparation method first prepares isometric wide grade strip side, again by the upper gluing in grade strip side longitudinal direction, it is superimposed and suppresses so that the fixed standard integrated timber of length and width is made, the thickness of the standard integrated timber is equal to the width of grade strip side, standard integrated timber through-thickness is cut as intermediate products, take three pieces of intermediate products, wherein two pieces of thickness are identical using as dash board, interior thickness is equal to the sum of dash board thickness using as intermediate plate, it is orthogonally located after three blocks of intermediate products gluings, apply positive pressure, orthogonal integrated plate finished product is made.Preparation method of the invention and orthogonal circuit board want can have enough intensity and non-deformability, and are suitble to the large scale preparation of industrialization.
Description
Technical field
The present invention relates to composite material preparations, are related specifically to a kind of industrialization preparation side of three layers of orthogonal integrated plate
Method and the orthogonal circuit board of preparation.
Background technique
Orthogonal laminated wood (Cross-laminated timber, CLT) is that one kind is at least answered by 3 layers of solid sawn lumber or structure
The orthogonal assembly of plywood material.Its using structural adhesive compacting made of rectangle, straight line, flat sheet form prefabrication engineering
Wood products.The composite sheet structure used includes laminated veneer lumber, batten orientation laminated timber, oriented shaving square bar and oriented wood chipboard
Deng.Type of attachment has glue connection and nail connection etc. between sawn timber or between sawn timber and composite sheet structure in CLT product, due to using
CLT product mechanical property with higher made of structural adhesive compacting, so general CLT product mostly uses greatly structure glue glutinous
Agent is suppressed.
About the preparation of orthogonal glued board, raw material and working condition are presently limited to, use traditional production technology substantially.
A kind of as disclosed in Chinese patent CN201610127930 to intersect laminated timber and its manufacturing method point out, this method first handles original
Timber, to be dried or batten is made again after drying, the batten being made into is carried out referring to again and be connect, and then is spliced and become finger-jointed plate, finally again
The pressing of finger-jointed plate group embryo is become into the hardened structure of cross-level product.Above-mentioned is strictly the general procedure of laminated timber production, is produced
Intersecting laminated timber is also conventional structure, the identical deficiency that also there is certainly: 1. raw material are processed as requiring and be added with log
Work starting point then is dried and is dried by being truncated and beat circle processing, and sawing sheet refers to connect and is combined into big plate, then to big plate lamination group
It closes, is suitble to small-scale timber plant produced to operate, capability of industrialization is significantly insufficient；2. cannot still overcome in this method product at
The later bending of type and alice problem, although having issued stress slot and release stress, still when finger connects and compresses with plain splice
Meeting accumulated pressure is limited to the limitation of production technology and production process in spite of the effect of glue, and can not thoroughly form limitation
The resulting structure of deformation, therefore be difficult to thoroughly change the predicament of existing laminated board.
Summary of the invention
It is an object of the present invention to overcome above-mentioned prior art Shortcomings, a kind of three layers of new orthogonal circuit board are provided
The industrialization preparation method of material and the orthogonal integrated plate prepared using this method.Preparation method of the invention and orthogonal integrated
Plate wants can have enough intensity and non-deformability, and is suitble to the large scale preparation of industrialization.
In order to achieve the above object of the invention, the technical solution that the invention patent provides is as follows:
A kind of industrialization preparation method of three layers of orthogonal integrated plate, which is characterized in that the preparation method first prepares isometric
Wide grade strip side, then by the upper gluing in grade strip side longitudinal direction, superposition and suppress so that the fixed mark of length and width is made
Quasi- integrated timber, the thickness of the standard integrated timber are equal to the width of grade strip side, standard integrated timber through-thickness are cut into
For intermediate products, three pieces of intermediate products are taken, wherein two pieces of thickness are identical using as dash board, centrally located and thickness is not less than
Dash board thickness is orthogonally located after three blocks of intermediate products gluings using as intermediate plate, applies positive pressure, orthogonal integrated plate is made
Finished product.
In the industrialization preparation method of three layers of orthogonal integrated plate of the invention, which includes following step in detail
It is rapid:
The plank of solid wood S4S of drying is become wide isometric grade strip side, the grade strip side by the first step
Thickness it is identical or different, length direction is whole and is made or is referred to by more and connect be made in succession；
The layer-by-layer gluing in manufactured grade strip side is superimposed, superimposed grade strip side by second step on the operational platform
It is put on plate joggling apparatus, standard integrated timber is formed with grade strip side after being superimposed, the length of the standard integrated timber is grade strip
The length of side, with a thickness of the width of grade strip side；
Third step is 10- from positive and side to pressure, positive pressure limit is applied respectively after plate joggling apparatus starting
16MPa, lateral pressure limit are 1-5MPa, and maintaining the time range of above-mentioned pressure is 0.5-1 hours, unclamp plate joggling apparatus, will
Manufactured standard integrated timber is removed and stands 24 hours in the room of workshop；
Standard integrated timber is laid flat on horizontal plane saw, plate is cut from thickness direction, formed multiple by the 4th step
The length and width of two plate of standard, two plate of standard is identical as the length and width of standard integrated timber, carries out sand to two plate of standard
Light processing；
5th step takes three blocks of two plates of standard, and two pieces of thickness are identical in three blocks of two plates of standard, and one piece of thickness is not less than in addition
Two pieces of thickness, and two plate of standard of two pieces of same thickness is respectively as upper and lower two dash boards, one block of intermediate two plate of standard
As intermediate plate, intermediate plate is unlocked from middle part so that dash board and intermediate plate are placed into just by its length equal to the width of dash board
To on press so that the direction of two pieces of dash boards it is identical and with intermediate plate direction it is perpendicular, formed dash board it is orthogonal with intermediate plate
State, when placing, in the position that is in contact, gluing is bonded and fixed at integrally formed assembly respectively；
6th step continues the assembly for putting other multiple dash boards and intermediate plate on the same positive press, starts institute
The assembly through-thickness that multiple-layer stacked is stacked is applied and continues 1-4 hours by the positive press stated；
7th step unclamps the positive press, respectively removes the orthogonal integrated plate that compacting is completed, and in workshop
24 hours are stood, four sides deburring simultaneously forms orthogonal integrated plate finished product after carrying out sanding surface.
In the industrialization preparation method of three layers of orthogonal integrated plate of the invention, the length of the standard integrated timber is
2400mm, width 1200mm unlock the intermediate plate for two boards from middle part, and the length for unlocking back plate is equal to the width of dash board
Degree, the sum of two boards width placed side by side and in the same direction are equal to the length of upper dash board and lower dash board.
In the industrialization preparation method of three layers of orthogonal integrated plate of the invention, the length of the standard integrated timber is
2440mm, width 600mm unlock the intermediate plate for two boards from middle part, and the length for unlocking back plate is equal to the width of dash board
Degree, the sum of four pieces of board widths placed side by side and in the same direction are equal to the length of upper dash board and lower dash board.
In the industrialization preparation method of three layers of orthogonal integrated plate of the invention, the length of the standard integrated timber is
2400mm, width 300mm unlock the intermediate plate for two boards from middle part, and the length for unlocking back plate is equal to the width of dash board
Degree, the sum of eight pieces of board widths placed side by side and in the same direction are equal to the length of upper dash board and lower dash board.
In the industrialization preparation method of three layers of orthogonal integrated plate of the invention, include on the orthogonal integrated plate construction
There are three layers, respectively upper epidermis plate, intermediate plate and following table laminate, the upper epidermis plate, intermediate plate and following table laminate are by on-gauge plate
Item Founder cuts and is made to bonding, compacting and lateral plane, and the length and width of the grade strip side is all the same；Positioned at two sides
Following table laminate it is identical as the placement direction of upper epidermis plate, be located in the middle intermediate plate placement direction and upper epidermis plate, layer
Plate orthogonal vertical is fixed between the upper epidermis plate and intermediate plate, between intermediate plate and following table laminate by adhesive bonds；It is described
Following table laminate is identical as the thickness of upper epidermis plate, and the thickness of intermediate plate is not less than the thickness of upper epidermis plate and following table laminate.
In the industrialization preparation method of three layers of orthogonal integrated plate of the invention, the width and length of the grade strip side
Spend identical, thickness can be identical or can also be different, and length direction is that whole drying long slab side is made or is referred to by more short slab sides
It connects and is made in succession.
The grade strip side is superimposed bonding in a thickness direction, and half item side of standard in the direction of the width saw by layered plane
It is split into as upper epidermis plate, intermediate plate and following table laminate.
Based on foregoing invention content, the industrialization preparation method of three layers of orthogonal integrated plate of the present invention and prepare orthogonal
Circuit board has following technological merit:
1. the industrialization preparation method of the invention patent from plank of solid wood as production starting point, by earlier processing steps and
Standardising process front end, these plank of solid wood can profession production product, be also possible to remaining side in other process
These plank of solid wood are supported grade strip side by corner material, as the operation important step of the invention patent method, standardize ability
Industrialization is brought, meets subsequent diversity requirement, and the product of most important the invention patent method preparation is width 1.22
Rice, the standard plate that length is 2.44 meters, naturally it is also possible to produce 1.22 meters of width and length is more than 3 meters of plate.
2. the core ideas of the industrialization preparation method of the invention patent is, after grade strip side is made, utilize
Standard integrated timber is made in superposition bonding on grade strip side's thickness direction, recycles horizontal plane plane along the thickness of standard integrated timber
Direction higher slice is splitted as two plate of standard, and the thickness direction of standard integrated timber is then just at the width direction of grade strip side,
Two plate plane of standard made of in this way is that have the thickness direction tight bond of multiple grade strip sides to be bonded, and is also just mentioned significantly
The high tightness and stability of two plate of standard, and clean mark is clear, greatly mentions while reducing single inherent strain
High stability.
3. another vital point of industrialization preparation method of the invention is, orthogonal integrated by multiple two plates of standard
It is orthogonal set into plate, two plate of standard come will be produced on the same standard integrated timber, divide into dash board, lower dash board and intermediate plate
It is combined, and requires upper dash board identical with the thickness of lower dash board, and be not more than the thickness of intermediate plate.In this way in upper dash board
When design identical with following table plate thickness is so that surface is deformed because of external force or endogenetic process, it can lead mutually up and down
System, and since intermediate plate and upper and lower dash board orthogonal design make more have holdback force, increase stability.In order to further mention
High non-deformability, the thickness that intermediate plate thickness is greater than dash board has also been devised in we, so that deformability is further pressed down
System.
4. being also a kind of completely new product based on the orthogonal integrated timber that the method for the present invention obtains, it is believed that the final products
The superposition bonding of grade strip side in a thickness direction is utilized, then is formed the thickness direction after being adhesively fixed as plane,
That is the thickness in the width direction of grade strip side as standard integrated timber recycles standard integrated timber to be made into standard two
Plate, same plate carry out orthogonal integrated again, also ensure that the indeformable of plate, realize other existing plates and be difficult to reach
Structural stability.
Detailed description of the invention
Fig. 1 is the production procedure schematic diagram of the industrialization preparation method of three layers of orthogonal integrated plate of the invention.
Fig. 2 is that the structure of the grade strip side of the preparation of the industrialization preparation method of three layers of orthogonal integrated plate of the invention is shown
It is intended to.
Fig. 3 is that the structure of the standard integrated timber of the preparation of the industrialization preparation method of three layers of orthogonal integrated plate of the invention is shown
It is intended to.
Fig. 4 is the structural representation of two plate of standard of the preparation of the industrialization preparation method of three layers of orthogonal integrated plate of the invention
Figure.
Fig. 5 is the structure group of the orthogonal integrated timber of the preparation of the industrialization preparation method of three layers of orthogonal integrated plate of the invention
At schematic diagram.
Specific embodiment
We come in conjunction with attached drawing and specific embodiment to a kind of industrialization of three layers of orthogonal integrated plate of the invention below
Preparation method and the orthogonal integrated timber of preparation are described in further detail, but cannot be used as a limitation protection model of the invention
It encloses.
As shown in Figure 1, the present invention is a kind of industrialization preparation method of three layers of orthogonal integrated plate, which is first made
Standby isometric wide grade strip side, then longitudinally above gluing, superposition and compacting are consolidated so that length and width is made by grade strip side
Fixed standard integrated timber, the thickness of the standard integrated timber is equal to the width of grade strip side, by standard integrated timber through-thickness
Cutting becomes intermediate products, takes three pieces of intermediate products, wherein two pieces of thickness are identical using as dash board, centrally located and thickness
It is orthogonally located after three blocks of intermediate products gluings not less than dash board thickness using as intermediate plate, apply positive pressure, orthogonal set is made
At plate finished product.
In the industrialization preparation method of three layers of orthogonal integrated plate of the invention, which includes following step in detail
It is rapid:
The plank of solid wood S4S of drying is become wide isometric grade strip side 1 by the first step, as shown in Fig. 2, should
The thickness of grade strip side 1 is identical or different, and length direction is made for whole or refers to connect in succession by more and is made.The step is from reality
Wood lath is as production starting point, and by earlier processing steps and standardising process front end, these plank of solid wood professional can be made
Product, be also possible to remaining leftover pieces in other process, by these plank of solid wood support grade strip side.As this
The operation important step of patent of invention method, standardization can just bring industrialization, meet subsequent diversity requirement, and most important
The product of the invention patent method preparation be 1.22 meters of width, length is 2.44 meters of standard plate, naturally it is also possible to be produced
1.22 meters of width and length are more than 3 meters of plate.
The layer-by-layer gluing in manufactured grade strip side is superimposed, superimposed grade strip side 1 by second step on the operational platform
It is put on plate joggling apparatus, standard integrated timber 2 is formed with grade strip side after being superimposed, as shown in figure 3, the length of the standard integrated timber 2
Degree is the length of grade strip side 1, with a thickness of the width of grade strip side 1.After grade strip side is made, on-gauge plate is utilized
Standard integrated timber is made in superposition bonding on item side's thickness direction, recycles horizontal plane plane from the thickness direction of standard integrated timber
Layering is splitted as two plate of standard, and the thickness direction of standard integrated timber is then just at the width direction of grade strip side, in this way system
At two plate plane of standard be to there is the thickness direction tight bond of multiple grade strip sides to be bonded, be also considerably improved mark
The tightness and stability of quasi- two plates, and clean mark is clear, greatly increases while reducing single inherent strain steady
It is qualitative.
Third step is 10- from positive and side to pressure, positive pressure limit is applied respectively after plate joggling apparatus starting
16MPa, lateral pressure limit are 1-5MPa, and maintaining the time range of above-mentioned pressure is 0.5-1 hours, unclamp plate joggling apparatus, will
Manufactured standard integrated timber is removed and stands 24 hours in the room of workshop；Here compacting may include hot pressing and cold pressing, if adopting
With cold pressing, is then carried out using cold glue, hot melt adhesive is used to carry out if hot pressing.
Standard integrated timber is laid flat on horizontal plane saw, plate is cut from thickness direction, formed multiple by the 4th step
Two plate 3 of standard, as shown in Figure 4.The length and width of two plate 3 of standard is identical as the length and width of standard integrated timber, to mark
Quasi- two plates 3 carry out sanding processing.Become orthogonal circuit board by multiple two plate orthogonal sets of standard, it will be on the same standard integrated timber
Two plate of standard come is produced, dash board, lower dash board and intermediate plate is divided into and is combined, and requires upper dash board and lower dash board
Thickness is identical, and is not more than the thickness of intermediate plate.
5th step takes three pieces of standards, two plate 3, and two pieces of thickness are identical in three pieces of standards, two plate 3, and one piece of thickness is not less than another
Outer two pieces of thickness, and two plate of standard of two pieces of same thickness is respectively as upper and lower two dash boards, one piece of intermediate standard two
Plate 3 is used as intermediate plate, and intermediate plate is unlocked from middle part so that dash board and intermediate plate are placed by its length equal to the width of dash board
On positive press so that the direction of two pieces of dash boards it is identical and with intermediate plate direction it is perpendicular, forming dash board and intermediate plate just
Friendship state, when placing, in the position that is in contact, gluing is bonded and fixed at integrally formed assembly respectively, is made for orthogonal circuit board
Material 4, structure is as shown in Figure 5.In this way upper dash board and following table plate thickness it is identical design so that surface because external force or in
When power effect is deformed, it can check and balance up and down, and since intermediate plate and upper and lower dash board orthogonal design more to lead
Power processed, increases stability.In order to further improve non-deformability, intermediate plate thickness is had also been devised greater than dash board in we
Thickness, so that deformability is further inhibited.
6th step continues the assembly for putting other multiple dash boards and intermediate plate on the same positive press, starts institute
The assembly through-thickness that multiple-layer stacked is stacked is applied and continues 1-4 hours by the positive press stated；
7th step unclamps the positive press, respectively removes the orthogonal integrated plate that compacting is completed, and in workshop
24 hours are stood, four sides deburring simultaneously forms orthogonal integrated plate finished product after carrying out sanding surface.
In the industrialization preparation method of three layers of orthogonal integrated plate of the invention, as the most common situation, the mark
The length of quasi- integrated timber is 2440mm, width 1220mm, and the intermediate plate is unlocked from middle part as two boards, back plate is unlocked
Length is equal to the width of dash board, and the sum of two boards width placed side by side and in the same direction is equal to the length of upper dash board and lower dash board.
In the industrialization preparation method of three layers of orthogonal integrated plate of the invention, as another common situation, institute
The length for stating standard integrated timber is 2440mm, width 610mm, the intermediate plate is unlocked from middle part as two boards, after unlocking
The length of plate is equal to the width of dash board, and the sum of four pieces of board widths placed side by side and in the same direction are equal to the length of upper dash board and lower dash board
Degree.
In the industrialization preparation method of three layers of orthogonal integrated plate of the invention, as another common situation, institute
The length for stating standard integrated timber is 2440mm, width 305mm, the intermediate plate is unlocked from middle part as two boards, after unlocking
The length of plate is equal to the width of dash board, and the sum of eight pieces of board widths placed side by side and in the same direction are equal to the length of upper dash board and lower dash board
Degree.
In the industrialization preparation method of three layers of orthogonal integrated plate of the invention, as manufactured final products, this is just
Intersection is at including three layers on plate construction, respectively upper epidermis plate, intermediate plate and following table laminate, the upper epidermis plate, intermediate plate
It is cut and is made from grade strip Founder to bonding, compacting and lateral plane with following table laminate, the length of the grade strip side
It is all the same with width；Following table laminate positioned at two sides is identical as the placement direction of upper epidermis plate, is located in the middle intermediate plate placement
Direction and upper epidermis plate, following table laminate orthogonal vertical, between the upper epidermis plate and intermediate plate, between intermediate plate and following table laminate
It is fixed by adhesive bonds；The following table laminate is identical as the thickness of upper epidermis plate, and the thickness of intermediate plate is not less than upper epidermis
The thickness of plate and following table laminate.
As core of the invention point, the width of above-mentioned standard lath side is identical with length, and thickness can be identical or can also
With difference, length direction is made for whole drying long slab side or refers to connect in succession by more short slab sides and is made.The grade strip
Superposition bonds in a thickness direction for side, and layered plane is cut as upper epidermis plate, intermediate plate half item side of standard in the direction of the width
With following table laminate.
It is also a kind of completely new product based on the orthogonal integrated timber that the method for the present invention obtains, it is believed that final products benefit
It is bonded with the superposition of grade strip side in a thickness direction, then is formed the thickness direction after being adhesively fixed as plane,
That is the thickness in the width direction of grade strip side as standard integrated timber, recycles standard integrated timber to be made into standard two
Plate, same plate carry out orthogonal integrated again, also ensure that the indeformable of plate, realize other existing plates and be difficult to reach
Structural stability.
Unquestionably, several concrete cases of the above only present patent application, in addition to this, present patent application
It further include other concrete implementation process and structure forms.To sum up, protection scope of the present invention is also and in other for this
It obviously converts and substitutes for the technical staff of field.
Claims (8)
1. a kind of industrialization preparation method of three layers of orthogonal integrated plate, which is characterized in that the preparation method first prepares isometric etc.
Wide grade strip side, then by the upper gluing in grade strip side longitudinal direction, superposition and suppress so that the fixed standard of length and width is made
Integrated timber, the thickness of the standard integrated timber are equal to the width of grade strip side, and standard integrated timber through-thickness, which is cut, to be become
Intermediate products take three pieces of intermediate products, wherein two pieces of thickness are identical using as dash board, centrally located and thickness is not less than table
Plate thickness is orthogonally located after three blocks of intermediate products gluings using as intermediate plate, applies positive pressure, be made orthogonal integrated plate at
Product.
2. a kind of industrialization preparation method of three layers of orthogonal integrated plate according to claim 1, which is characterized in that the system
Preparation Method includes following detailed step:
The plank of solid wood S4S of drying is become wide isometric grade strip side, the thickness of the grade strip side by the first step
Spend identical or different, length direction is whole and is made or is referred to by more and connect be made in succession；
The layer-by-layer gluing in manufactured grade strip side is superimposed by second step on the operational platform, and superimposed grade strip side is put into
On plate joggling apparatus, standard integrated timber is formed with grade strip side after being superimposed, the length of the standard integrated timber is grade strip side
Length, with a thickness of the width of grade strip side；
Third step is 10-16MPa from positive and side to pressure, positive pressure limit is applied respectively after plate joggling apparatus starting,
Lateral pressure limit is 1-5MPa, and maintaining the time range of above-mentioned pressure is 0.5-1 hours, unclamps plate joggling apparatus, will be manufactured
Standard integrated timber is removed and stands 24 hours in the room of workshop；
Standard integrated timber is laid flat on horizontal plane saw, plate is cut from thickness direction, forms multiple standards by the 4th step
The length and width of two plates, two plate of standard is identical as the length and width of standard integrated timber, carries out at sanding to two plate of standard
Reason；
5th step takes three blocks of two plates of standard, and two pieces of thickness are identical in three blocks of two plates of standard, and one piece of thickness is not less than other two pieces
Thickness, and two plate of standard of two pieces of same thickness is respectively as upper and lower two dash boards, intermediate one piece of standard, two plate conduct
Intermediate plate unlocks intermediate plate so that dash board and intermediate plate are placed into positive pressure equal to the width of dash board by its length from middle part
On machine so that the direction of two pieces of dash boards it is identical and with intermediate plate direction it is perpendicular, formed dash board and intermediate plate quadrature,
When placing, in the position that is in contact, gluing is bonded and fixed at integrally formed assembly respectively；
6th step continues the assembly that other multiple dash boards and intermediate plate are put on the same positive press, starts described
The assembly through-thickness that multiple-layer stacked is stacked is applied and continues 1-4 hours by positive press；
7th step unclamps the positive press, respectively removes the orthogonal integrated plate that compacting is completed, and stand in workshop
24 hours, four sides deburring simultaneously formed orthogonal integrated plate finished product after carrying out sanding surface.
3. a kind of industrialization preparation method of three layers of orthogonal integrated plate according to claim 2, which is characterized in that described
The length of standard integrated timber is 2440mm, width 1220mm, and the intermediate plate is unlocked from middle part as two boards, back plate is unlocked
Length be equal to dash board width, the sum of two boards width placed side by side and in the same direction be equal to upper dash board and lower dash board length.
4. a kind of industrialization preparation method of three layers of orthogonal integrated plate according to claim 2, which is characterized in that described
The length of standard integrated timber is 2440mm, width 610mm, and the intermediate plate is unlocked from middle part as two boards, back plate is unlocked
Length be equal to dash board width, the sum of four pieces of board widths placed side by side and in the same direction be equal to upper dash board and lower dash board length.
5. a kind of industrialization preparation method of three layers of orthogonal integrated plate according to claim 2, which is characterized in that described
The length of standard integrated timber is 2440mm, width 305mm, and the intermediate plate is unlocked from middle part as two boards, back plate is unlocked
Length be equal to dash board width, the sum of eight pieces of board widths placed side by side and in the same direction be equal to upper dash board and lower dash board length.
6. the orthogonal circuit board prepared using the industrialization preparation method of three layers of one kind orthogonal integrated plate as claimed in claim 2
Material, which is characterized in that it include three layers on the orthogonal integrated plate construction, respectively upper epidermis plate, intermediate plate and following table laminate,
The upper epidermis plate, intermediate plate and following table laminate are cut and are made from grade strip Founder to bonding, compacting and lateral plane, described
The length and width of grade strip side is all the same；
Upper epidermis plate positioned at two sides is identical as following table laminate placement direction, is located in the middle intermediate plate placement direction and upper epidermis
Plate, following table laminate orthogonal vertical, between the upper epidermis plate and intermediate plate, between intermediate plate and following table laminate by adhesive bonds
It is fixed；
The following table laminate is identical as the thickness of upper epidermis plate, and the thickness of intermediate plate is not less than upper epidermis plate and following table laminate
Thickness.
7. orthogonal integrated plate according to claim 6, which is characterized in that the width and length phase of the grade strip side
Together, thickness can be identical or can also be different, and length direction is that whole drying long slab side is made or is referred in succession by more short slab sides
It connects and is made.
8. orthogonal integrated plate according to claim 6, which is characterized in that the grade strip side is in a thickness direction
Superposition bonding, layered plane is cut as upper epidermis plate, intermediate plate and following table laminate half item side of standard in the direction of the width.