CN109456603A - 一种可塑蜡及其应用 - Google Patents
一种可塑蜡及其应用 Download PDFInfo
- Publication number
- CN109456603A CN109456603A CN201811099226.6A CN201811099226A CN109456603A CN 109456603 A CN109456603 A CN 109456603A CN 201811099226 A CN201811099226 A CN 201811099226A CN 109456603 A CN109456603 A CN 109456603A
- Authority
- CN
- China
- Prior art keywords
- wax
- paraffin
- plastic
- microwax
- plastic wax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种可塑蜡，包含以下重量百分含量的组分：石蜡10～85％、微晶蜡0～85％、矿物蜡和/或植物蜡0～20％、增粘树脂0～30％、油脂或凡士林4～20％、高分子聚合物0～10％和相溶剂0.25～5％。所述可塑蜡原料安全无副作用，制得的可塑蜡可塑性强，可做任意形状，具有玩味性，可以随使用部位的需要任意变换成不同形状使用。可塑蜡中可以添加作用于皮肤表面的物质，无需使用专业设备加热即可直接使用，安全方便，且可以起到缓释的效果，使这些物质长期有效，让广大人群都可轻松享用蜡疗，且用于皮肤时，可以打开毛孔，促进皮肤对这些物质的吸收。本发明还公开了可塑蜡在美容、保健、香薰中的应用。
Description
技术领域
本发明涉及一种蜡，具体涉及一种可塑蜡及其应用。
背景技术
市面上蜡需要蜡疗机加热融化后才可使用，存在使用不方便的问题，一般只能在美容院、理疗馆或医院才能使用，加热后有烫伤皮肤的可能，存在安全隐患。蜡水易于洒落在地面或衣服上，存在不易清洗的问题。顾客在使用蜡的时候，蜡没有带来的好看、好闻、好玩、好用的赏心悦目的感觉，且不可以变形随意贴于身体的不同部位，限制了人们对蜡的使用。因此上述缺陷对于让***普遍使用蜡疗产品，享受它的好处是不可能的，如何克服上述缺陷，为广大用户提供一种随时随地、于身体不同部位又可反复使用的品质优良的固体可塑蜡，是人们急需解决的问题。
发明内容
本发明的目的在于克服现有技术存在的不足之处而提供一种可塑蜡及其应用。
为实现上述目的，本发明采取的技术方案为：一种可塑蜡，包含以下重量百分含量的组分：石蜡10～85％、微晶蜡0～85％、矿物蜡、动物蜡和植物蜡的至少一种0～50％、增粘树脂0～20％、油脂或凡士林4～10％、高分子聚合物0～10％和相溶剂0.25～1％。
可塑蜡在蜡的使用历史中，是从来没有的。采用上述配方可以制备成可塑蜡，原料安全无副作用，制得的可塑蜡可塑性强，造型百变，如橡皮泥，可做任意形状，具有玩味性，可以随使用部位的需要任意变换成不同形状使用。可塑蜡中可以添加作用于皮肤表面的物质，诸如药物、护肤成分和植物精油等成分，无需使用专业设备加热即可在原料中直接添加，方便使用。可塑蜡中也可以添加香薰物质，作为香薰用途。且可塑蜡作为这些作用于皮肤表面的物质或香薰物质的载体时，可以起到缓释的效果，使这些物质长期有效，让广大人群都可享用蜡疗，且用于皮肤时，可以打开毛孔，促进皮肤对这些物质的吸收。
优选地，所述可塑蜡包含以下重量百分含量的组分：石蜡0～35％、微晶蜡55～85％、增粘树脂0～20％、矿物蜡和/或植物蜡0～20％、油脂或凡士林4～10％、高分子聚合物0～10％和相溶剂0.25～1％。
优选地，所述可塑蜡包括以下重量百分含量的组分：石蜡30～65％、微晶蜡25～60％、增粘树脂0～20％、矿物蜡和/或植物蜡0～20％、油脂或凡士林4～10％、高分子聚合物0～10％和相溶剂0.25～1％。
优选地，所述可塑蜡包括以下重量百分含量的组分：石蜡60～85％、微晶蜡0～25％、增粘树脂0～20％、矿物蜡和/或植物蜡0～20％、油脂或凡士林4～10％、高分子聚合物0～10％和相溶剂0.25～1％。
所述可塑蜡优选采用上述三种配方，制备的可塑蜡的韧性更高，可塑性更强，且可操作性更高。
优选地，所述微晶蜡为70#微晶蜡、80#微晶蜡、64#微晶蜡、美国微晶蜡W445、韩国微晶蜡160s、170s软蜡，沙索微晶蜡1365、沙索微晶蜡2528、沙索微晶蜡3971和壳牌软蜡中的至少一种。70#微晶蜡、80#微晶蜡、64#微晶蜡可以购自中国石油化工股份有限公司、荆门分公司、济南分公司、南阳石蜡精细化工厂等厂家。上述微晶蜡的分子结构比较细腻，柔韧性好，更适合制作可塑蜡。
优选地，所述微晶蜡为美国微晶蜡W445、韩国微晶蜡160s、170s软蜡，沙索微晶蜡1365、沙索微晶蜡2528、沙索微晶蜡3971和壳牌软蜡中的至少一种。当微晶蜡为上述进口微晶软蜡时，更适合用作可塑蜡的制备，制作更方便。
优选地，所述微晶蜡为70#微晶蜡、80#微晶蜡和64#微晶蜡中的至少一种，所述微晶蜡在所述可塑蜡中的重量百分含量为10～50％。当微晶蜡为上述熔点的微晶蜡时，微晶蜡添加量为10～50％时更有利于可塑蜡的制备，韧性更好。
优选地，所述石蜡为46#石蜡、48#石蜡、50#石蜡、52#石蜡、54#石蜡、56#石蜡、58#石蜡、60#石蜡、62#石蜡、64#石蜡、66#石蜡、68#石蜡、70#石蜡、全精炼石蜡和食品级石蜡中的至少一种。所述石蜡选择化妆品级及食品级石蜡，可以为中石化和中石油各分公司的产品，比如大连石化、茂名石化、荊门石化、荊门维利、上海石化、大庆石化、抚顺石化、南阳石化等。
优选地，所述石蜡为46#石蜡、48#石蜡、50#石蜡、52#石蜡和54#石蜡中至少一种。当石蜡为上述低熔点石蜡时，更适合用作可塑蜡的制备，制作更方便。
当石蜡为56#石蜡、58#石蜡、60#石蜡、62#石蜡、64#石蜡、66#石蜡、68#石蜡、70#石蜡等高熔点蜡时，优选在可塑蜡中的重量百分含量为10～50％。
优选地，所述油和凡士林的混合物中，所述油脂为化妆品级油脂或食品级油脂。所述凡士林为化妆品级或医药级凡士林。油和凡士林可以用于包裹植物和中药精油等功效成分，有利于滋润肌肤，更容易渗透和吸收。
更优选地，所述油脂为杏仁油、椰子油、橄榄油、角沙烷、白矿油、芦荟油、玫瑰果油和荷荷巴油中的至少一种。
优选地，所述高分子聚合物包含聚异丁烯、氢化石油树脂、、乙烯-醋酸乙烯共聚物、乙丙橡胶、乙烯-丙烯共聚物、乙烯-辛烯嵌段共聚物、AFFINITY聚烯烃塑性树脂、低分子聚丙烯、聚乙烯辛烯共弹性体和压敏胶中的至少一种。其中，所述低分子聚丙烯优选为无规聚丙烯，分子量为3000～10000。
优选地，所述相溶剂为马来酸酐接枝类聚合物中的至少一种，所述相溶剂热变形温度范围为50～130℃。在该温度范围内的马来酸酐接枝类聚合物容易熔化，相溶性好。
优选地，所述矿物蜡为费托蜡；所述植物蜡为木蜡、大豆蜡、米糠蜡和玉米蜡中的至少一种。所述费托蜡的熔点为45～70℃，所述植物蜡的滴熔点优选为48～64℃。
优选地，所述可塑蜡还包括助剂，所述助剂包含渗透剂、抗氧剂、流平剂、增亮增透剂、紫外线吸收剂和颜色添加剂；优选地，所述助剂的各成分在所述可塑蜡中的重量百分含量为：渗透剂0.1～0.3％、抗氧剂0.1～0.6％、流平剂0.01～0.05％、增亮增透剂0.1～0.5％、紫外线吸收剂0.1～0.6％和颜色添加剂0～0.5％。
优选地，所述渗透剂为氮酮。氮酮有助于促进功效成分渗透入皮肤中。
优选地，所述抗氧剂为抗氧化剂1010、抗氧化剂168、抗氧化剂B225和抗氧化剂644中的至少一种。
优选地，所述流平剂为流平剂950。
优选地，所述增亮增透剂为增亮增透剂400D。
优选地，所述紫外线吸收剂为紫外线吸收剂UV-531、紫外线吸收剂UV-9、紫外线吸收剂3030和紫外线吸收剂770中的至少一种。所述紫外线吸收剂可以选择一些常用的紫外线吸收剂，优选为上述紫外线吸收剂。
优选地，所述颜色添加剂为天然食用色粉、色膏和色母中的至少一种。可以根据不同的色彩需要加入相应的天然食用色粉、色膏、色母，比如说玫瑰红、粉色、果绿色、黄色等五颜六色。
优选地，所述可塑蜡还包括以下重量百分含量的组分：中药药粉0～40％、中药提取物0～40％、植物精油0～10％和香薰精油0～10％，各组分的下限不同时为0。
所述可塑蜡中可以根据不同功效的需要加入相应的中药药粉或中药提取物单方或复方，比如说通筋活络约、活血化瘀的、镇定安神的、提神醒脑的。可以根据不同功效和味道的需要加入相应的植物精油或香薰精油单方或复方，比如说镇定安神的、提神醒脑的、令人欢快愉悦的植物精油或香薰精油。
优选地，所述增粘树脂为固体增粘树脂和/或液体型增粘树脂；所述固体增粘树脂的环球软化点范围为80～130℃。该环球软化点范围的固体增粘树脂，容易熔化，加入可塑蜡中后，韧性相对更好。
更优选地，所述固体增粘树脂为氢化松香甘油酯、ESCOrez5600增粘树脂、氢化石油树脂、氢化松香树脂、水白松香树脂和氢化的食品级或化妆品级的树脂中的至少一种。
氢化松香甘油酯优选为美国Pinova，ESCOrez5600增粘树脂的型号为埃克森美孚公司5600/5400，氢化石油树脂的型号为韩国可隆SU-100)，氢化松香树脂购买自广东科茂林产化工股份有限公司。
本发明的另一目的还在于提供所述可塑蜡在美容、保健、香薰、洁肤、护肤、玩具、工艺装饰品中的应用。
所述可塑蜡可以作为药物、护肤成分、植物精油、香薰精油等的载体，也可以替代橡皮泥作为小孩子的可变型玩具，也可以作为工艺装饰品。
本发明制得的可塑蜡可塑性强，发明人历经十多年做过无数试验，所做的可塑蜡因为要求和原料的配方不一样，有的似橡皮泥，有的似拉面，有的韧性强力度大，可制作各种软的、硬的、软硬程度适中的可塑蜡。
本发明的有益效果在于：本发明提供了一种可塑蜡，所述可塑蜡原料安全无副作用，制得的可塑蜡可塑性强，造型百变，如橡皮泥，可做任意形状，具有玩味性，可以随使用部位的需要任意变换成不同形状使用。可塑蜡中可以添加作用于皮肤表面的物质，诸如药物、护肤成分、香薰精油和植物精油等成分，无需使用专业设备加热即可直接使用，安全方便。且可塑蜡作为这些作用于皮肤表面的物质或香薰成分等物质的载体时，可以起到缓释的效果，使这些物质长期有效，让广大人群都可轻松享用蜡疗，且用于皮肤时，可以打开毛孔，促进皮肤对这些物质的吸收。本发明还提供了可塑蜡在美容、保健、香薰中的应用。
具体实施方式
为更好的说明本发明的目的、技术方案和优点，下面将结合具体实施例对本发明作进一步说明。
实施例1
本发明所述可塑蜡的一种实施例，本实施例所述可塑蜡包含以下重量百分含量的组分：
其中，所述香薰精油包含以下重量百分含量的组分：玫瑰精油40％、檀香精油20％、乳香精油20％和橙花精油20％。本实施例所述可塑蜡可以提神醒脑。
实施例2
本发明所述可塑蜡的一种实施例，本实施例所述可塑蜡包含以下重量百分含量的组分：
其中，所述香薰精油包含以下重量百分含量的组分：檀香精油50％、玫瑰花精油25％和洋甘菊精油25％。本实施例所述可塑蜡可以促进血液循环、改善皱纹。
实施例3
本发明所述可塑蜡的一种实施例，本实施例所述可塑蜡包含以下重量百分含量的组分：
其中，所述中药植物精油包含以下重量百分含量的组分：黄连15％、黄芩17％、黄柏17％、生大黄17％、蚤休17％和苦参17％。本实施例所述可塑蜡对皮肤有一定的消毒作用，能改善脓疱。
实施例4
本发明所述可塑蜡的一种实施例，本实施例所述可塑蜡包含以下重量百分含量的组分：
其中，所述中药植物精油包含以下重量百分含量的组分：朱砂10％、全蝎10％、白鲜皮20％、防风20％、皂角刺20％和制首乌20％。本实施例所述可塑蜡有通经活络的作用。
实施例5
本发明所述可塑蜡的一种实施例，本实施例所述可塑蜡包含以下重量百分含量的组分：
其中，所述香薰精油包含以下重量百分含量的组分：甜橙精油50％和玫瑰精油50％。本实施例所述可塑蜡可以提神醒脑。
实施例6
本发明所述可塑蜡的一种实施例，本实施例所述可塑蜡包含以下重量百分含量的组分：
其中，所述香薰精油包含以下重量百分含量的组分：柠檬精油50％、迷迭香精油50％。本实施例所述可塑蜡提神、愉悦身心。
实施例7
本发明所述可塑蜡的一种实施例，本实施例所述可塑蜡包含以下重量百分含量的组分：
其中，所述中药药粉包含以下重量百分含量的组分：透骨草1.6％、没药16.4％、大黄16.4％、杜仲16.4％、川断16.4％、僵蚕16.4％、白芷16.4％。本实施例所述可塑蜡可以通经活络。
实施例8
本发明所述可塑蜡的一种实施例，本实施例所述可塑蜡包含以下重量百分含量的组分：
其中，所述香薰精油包含以下重量百分含量的组分：茶树精油50％、薰衣草精油25％和尤加利精油25％。本实施例所述可塑蜡可以改善鼻塞。
实施例9
本发明所述可塑蜡的一种实施例，本实施例所述可塑蜡包含以下重量百分含量的组分：
其中，所述香薰精油包含以下重量百分含量的组分：柠檬精油50％、天竺葵精油25％和茉莉花精油25％。本实施例所述可塑蜡可以改善忧郁、使心情愉悦。
实施例10
本发明所述可塑蜡的一种实施例，本实施例所述可塑蜡包含以下重量百分含量的组分：
其中，所述香薰精油包含以下重量百分含量的组分：柠檬精油50％、甜橙精油33％和迷迭香精油17％。本实施例所述可塑蜡有助于提神醒脑。
实施例11
本发明所述可塑蜡的一种实施例，本实施例所述可塑蜡包含以下重量百分含量的组分：
其中，所述香薰精油包含以下重量百分含量的组分：薰衣草精油20％、没药精油20％、檀香精油30％、依兰精油20％和百合精油10％。本实施例所述可塑蜡有助于放松舒缓。
实施例12
测试各实施例的熔点、含油量、针入度、粘度等性能指标，测试结果见表1和表2。
表1实施例1～7所述可塑蜡理化性能测试结果
表2实施例8～11理化性能测试结果
最后所应当说明的是，以上实施例仅用以说明本发明的技术方案而非对本发明保护范围的限制，尽管参照较佳实施例对本发明作了详细说明，本领域的普通技术人员应当理解，可以对本发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的实质和范围。
Claims (10)
1.一种可塑蜡，其特征在于，包含以下重量百分含量的组分：石蜡10～85％、微晶蜡0～85％、矿物蜡和/或植物蜡0～20％、增粘树脂0～20％、油脂或凡士林4～10％、高分子聚合物0～10％和相溶剂0.25～1％。
2.如权利要求1所述可塑蜡，其特征在于，所述可塑蜡包含以下重量百分含量的组分：石蜡0～35％、微晶蜡55～85％、增粘树脂0～20％、矿物蜡和/或植物蜡0～20％、油脂或凡士林4～10％、高分子聚合物0～10％和相溶剂0.25～1％。
3.如权利要求1所述可塑蜡，其特征在于，所述可塑蜡包括以下重量百分含量的组分：石蜡30～65％、微晶蜡25～60％、增粘树脂0～20％、矿物蜡和/或植物蜡0～20％、油脂或凡士林4～10％、高分子聚合物0～10％和相溶剂0.25～1％。
4.如权利要求1所述可塑蜡，其特征在于，所述可塑蜡包括以下重量百分含量的组分：石蜡60～85％、微晶蜡0～25％、增粘树脂0～20％、矿物蜡和/或植物蜡0～20％、油脂或凡士林4～10％、高分子聚合物0～10％和相溶剂0.25～1％。
5.如权利要求1～4中任一项所述可塑蜡，其特征在于，所述微晶蜡为70#微晶蜡、80#微晶蜡、64#微晶蜡、美国微晶蜡W445、韩国微晶蜡160s、170s软蜡，沙索微晶蜡1365、沙索微晶蜡2528、沙索微晶蜡3971和壳牌软蜡中的至少一种。
6.如权利要求1～4中任一项所述可塑蜡，其特征在于，所述石蜡为46#石蜡、48#石蜡、50#石蜡、52#石蜡、54#石蜡、56#石蜡、58#石蜡、60#石蜡、62#石蜡、64#石蜡、66#石蜡、68#石蜡、70#石蜡、全精炼石蜡和食品级石蜡中的至少一种。
7.如权利要求1～4中任一项所述可塑蜡，其特征在于，所述矿物蜡为费托蜡；所述植物蜡为木蜡、大豆蜡、米糠蜡和玉米蜡中的至少一种。
8.如权利要求1所述可塑蜡，其特征在于，所述可塑蜡还包括助剂，所述助剂包含渗透剂、抗氧剂、流平剂、增亮增透剂、紫外线吸收剂和颜色添加剂；优选地，所述助剂的各成分在所述可塑蜡中的重量百分含量为：渗透剂0.1～0.3％、抗氧剂0.1～0.6％、流平剂0.01～0.05％、增亮增透剂0.1～0.5％、紫外线吸收剂0.1～0.6％和颜色添加剂0～0.5％。
9.如权利要求1所述可塑蜡，其特征在于，所述可塑蜡还包括以下重量百分含量的组分：中药药粉0～40％、中药提取物0～40％、植物精油0～10％和香薰精油0～10％，各组分的下限不同时为0。
10.如权利要求1～9中任一项所述可塑蜡在美容、保健、香薰、洁肤、护肤、玩具和工艺装饰品中的应用。