CN109453677A - The manufacturing method of two-sided hydrophilic film - Google Patents
The manufacturing method of two-sided hydrophilic film Download PDFInfo
- Publication number
- CN109453677A CN109453677A CN201811560106.1A CN201811560106A CN109453677A CN 109453677 A CN109453677 A CN 109453677A CN 201811560106 A CN201811560106 A CN 201811560106A CN 109453677 A CN109453677 A CN 109453677A
- Authority
- CN
- China
- Prior art keywords
- hydrophilic film
- film
- substrate
- lower layer
- coated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of manufacturing method of two-sided hydrophilic film, the two-sided hydrophilic film, including substrate, upper layer hydrophilic film is coated in the upper surface of substrate, it is compounded with upper layer PE film in the hydrophilic film of upper layer, is coated with lower layer's hydrophilic film in the lower surface of substrate, lower layer's PE film is compounded in lower layer's hydrophilic film;The manufacturing method of two-sided hydrophilic film includes the following steps: Step 1: be first coated with lower layer's hydrophilic film, Step 2: compound lower layer PE film after drying, Step 3: be coated upper layer hydrophilic film, Step 4: compound upper layer PE film after low temperature drying, Step 5: cutting.Two-sided hydrophilic film of the invention can greatly improve the blood diffusion of blood sugar test paper hydrophilic film, in favor of further increasing the detection accuracy of blood glucose target.
Description
Technical field
The present invention relates to a kind of manufacturing methods of two-sided hydrophilic film.
Background technique
In the detection of blood glucose quick diagnosis, blood sugar test paper has been widely used.In blood sugar test paper, detection accuracy is influenced
Other than oxidoreducing enzyme, conducting medium, there are also be exactly hydrophilic film.When tested blood sample drop is on blood sugar test paper, hydrophilic film energy
It is enough that drop of blood is quickly spread to and sucked electrode working zone, to ensure the progress of blood sugar test.
It, can only in the case where oxidoreducing enzyme, conducting medium have determined in order to improve the detection accuracy of blood sugar test paper
Improve the diffusion of hydrophilic film.The performance for how improving blood sugar test paper hydrophilic film, puts in face of those skilled in the art
One important topic.
Summary of the invention
The object of the present invention is to provide a kind of manufacturing methods of two-sided hydrophilic film, it can be ensured that the two-sided hydrophilic film can
Processing and manufacturing.The two-sided hydrophilic film produced can greatly improve the blood diffusion of blood sugar test paper hydrophilic film, in favor of into
The detection accuracy of one step raising blood glucose target.
To achieve the above object, the present invention adopts the following technical scheme:
A kind of manufacturing method of two-sided hydrophilic film, the two-sided hydrophilic film, including substrate are coated with upper layer in the upper surface of substrate
Hydrophilic film is coated with lower layer's hydrophilic film in the lower surface of substrate, upper layer PE film is compounded in the upper layer hydrophilic film, described
Lower layer's PE film is compounded in lower layer's hydrophilic film, the manufacturing method of the two-sided hydrophilic film includes the following steps:
Step 1: first it is coated with lower layer's hydrophilic film
Substrate is released from substrate coiled strip emptying roller, becomes horizontal transmission through guide roller guiding and its following table is face-up, lower layer
Hydrophilic film coating die head is above coated the lower surface of substrate;
Step 2: compound lower layer PE film after drying
The substrate for being coated with lower layer's hydrophilic film enters dry baking tunnel and is dried, after lower layer's hydrophilic film is dried, lower layer's PE film from
It is released on lower layer's hydrophilic film coiled strip emptying roller, it is compound to the substrate taken turns be coated with lower layer's hydrophilic film by the first compound rolling;
Step 3: it is coated upper layer hydrophilic film
It is coated with lower layer's hydrophilic film and the substrate for being compounded with lower layer's hydrophilic film is oriented to wheel through the first compound rolling, become horizontal biography
Give and its upper surface upward, upper layer hydrophilic film coating die head is above coated the upper surface of substrate;
Step 4: compound upper layer PE film after low temperature drying
The substrate for being coated with upper layer hydrophilic film enters low temperature drying channel and carries out low temperature drying, after upper layer hydrophilic film is dried, on
Layer PE film is released from the PE film roll material emptying roller of upper layer, by the second compound rolling to wheel and the substrate for being coated with upper layer hydrophilic film
It is compound;
Step 5: it cuts
The two-sided hydrophilic film of finished product is sent to cutter to wheel by the second compound rolling and cuts.
Compared with prior art the beneficial effects of the present invention are: the manufacturing method of the two-sided hydrophilic film of the present invention, it is ensured that on
Lower hydrophilic film, towards above, and avoids coating and is destroyed not with other component contacts before it is dried in coating.It is existing
Blood sugar test paper, be to be coated with hydrophilic substance in a surface (i.e. single side) of substrate, it is dry to pass through coating drying tunnel, hydrophilic substance
It adheres to substrate surface and constitutes hydrophilic film, then the compound PE film in hydrophilic film.Two-sided hydrophilic film of the invention, works as substrate
After coating and compound PE film are completed in upper surface, when in substrate lower surface, coating hydrophilic film enters drying tunnel drying, because of the dry temperature of drying tunnel
Degree is higher, can deform, blister, delamination after the PE film of upper surface is heated, in order to solve this problem, hydrophilic coating of the invention is molten
The agent spirit solvent easily dry using low temperature avoids the destruction to PE film this makes it possible to using cold drying drying.
Detailed description of the invention
Fig. 1 is structural schematic diagram of the invention;
Fig. 2 is the structural schematic diagram of coating system used in manufacturing method of the present invention.
Specific embodiment
In order to be more clear technical solution of the present invention, below in conjunction with attached Fig. 1 and 2, the present invention is described in detail.
It should be understood that specific embodiment described in this specification is not intended to limit just for the sake of explaining the present invention
Protection scope of the present invention.
The present invention is a kind of manufacturing method of two-sided hydrophilic film, the two-sided hydrophilic film, including substrate 1, in the upper of substrate 1
Surface is coated with upper layer hydrophilic film 2, is coated with lower layer's hydrophilic film 3 in the lower surface of substrate 1, multiple in the upper layer hydrophilic film 2
Conjunction has upper layer PE film 4, and lower layer's PE film 5 is compounded in lower layer's hydrophilic film 3, preferably, the upper layer hydrophilic film 2, under
Layer hydrophilic film 3 is to be dissolved in ethanol solution by fatty alcohol polyoxyethylene ether and then be made by the following method, the fat
In the ethanol solution of alcohol polyoxyethylene ether, the weight percent content of fatty alcohol polyoxyethylene ether is 1-3%, the substrate 1 by
PET material is made;The manufacturing method includes the following steps:
Step 1: first it is coated with lower layer's hydrophilic film.Substrate 1 is released from substrate coiled strip emptying roller 01, is become through guide roller guiding
Horizontal transmission and its following table is face-up, lower layer's hydrophilic film coating die head 07 is above coated the lower surface of substrate 1;
Step 2: compound lower layer PE film after drying.The substrate 1 for being coated with lower layer's hydrophilic film 3 is dried into dry baking tunnel 08,
Lower layer's hydrophilic film 3 by after drying, release from lower layer's hydrophilic film coiled strip emptying roller 03 by lower layer's PE film 5, passes through the first compound rolling
It is compound to wheel 04 and the substrate 1 that is coated with lower layer's hydrophilic film 3;
Step 3: it is coated upper layer hydrophilic film.It is coated with lower layer's hydrophilic film 3 and is compounded with the substrate 1 of lower layer's hydrophilic film 3 through first
Compound rolling is oriented to wheel 04, becomes horizontal transmission and its upper surface upward, upper layer hydrophilic film coating die head 06 is above to base
The upper surface of material 1 is coated;
Step 4: compound upper layer PE film after low temperature drying.The substrate 1 for being coated with upper layer hydrophilic film 2 enters low temperature drying channel 09
Low temperature drying is carried out, upper layer hydrophilic film 2 by after drying, release from upper layer PE film roll material emptying roller 02 by upper layer PE film 4, by the
Two compound rolling are compound to wheel 05 and the substrate 1 that is coated with upper layer hydrophilic film 2;
Step 5: it cuts.The two-sided hydrophilic film 6 of finished product is sent to cutter 011 to wheel 05 by the second compound rolling and cuts.
The coating system of above-mentioned two-sided hydrophilic film, including substrate coiled strip emptying roller 01,02 He of upper layer PE film roll material emptying roller
Lower layer's hydrophilic film coiled strip emptying roller 03, and play the first compound rolling rolling pair compound to wheel 04 and second of constant tension stretch
Wheel 05, for the upper layer hydrophilic film coating die head 06 and lower layer's hydrophilic film coating die head 07 of coating, dry baking tunnel 08 and low temperature are dry
Dry channel 09, substrate 1 are released from substrate coiled strip emptying roller 01, successively through guide roller, lower layer's hydrophilic film coating die head 07, dry
The compound rolling of dry drying tunnel 08, first is to wheel 04, upper layer hydrophilic film coating die head 06, low temperature drying channel 09, the second compound rolling
To wheel 05, it is transmitted in cutter 011, lower layer's PE film 5 is released from lower layer's hydrophilic film coiled strip emptying roller 03, passes through the first compound rolling
To press compound with the substrate 1 that is coated with lower layer's hydrophilic film 3 to wheel 04, upper layer PE film 4 is released from upper layer PE film roll material emptying roller 02,
It is compound to wheel 05 and the substrate 1 that is coated with upper layer hydrophilic film 2 by the second compound rolling.Preferably, the substrate 1 is through being oriented to
Idler wheel is directed to horizontal transmission and its following table is face-up, and lower layer's hydrophilic film coating die head 07 is located at the upper of 1 lower surface of substrate
Side;The substrate 1 is directed to horizontal transmission and its upper surface upward to wheel 04 through the first compound rolling, and the upper layer hydrophilic film applies
Cloth die head 06 is located at the top of 1 upper surface of substrate.
Claims (1)
1. a kind of manufacturing method of two-sided hydrophilic film, the two-sided hydrophilic film, including substrate (1) are applied in the upper surface of substrate (1)
Upper layer hydrophilic film (2) are furnished with, lower layer's hydrophilic film (3) are coated in the lower surface of substrate (1), on the upper layer hydrophilic film (2)
It is compounded with upper layer PE film (4), is compounded with lower layer's PE film (5) on lower layer's hydrophilic film (3), it is characterised in that including walking as follows
It is rapid:
Step 1: first it is coated with lower layer's hydrophilic film
Substrate (1) is released from substrate coiled strip emptying roller (01), becomes horizontal transmission and its lower surface court through guide roller guiding
On, lower layer's hydrophilic film coating die head (07) is above coated the lower surface of substrate (1);
Step 2: compound lower layer PE film after drying
The substrate (1) for being coated with lower layer's hydrophilic film (3) enters dry baking tunnel (08) and is dried, and lower layer's hydrophilic film (3) is dried
Afterwards, lower layer PE film (5) is released from lower layer's hydrophilic film coiled strip emptying roller (03), by the first compound rolling to wheel (04) and coating
There is the substrate (1) of lower layer's hydrophilic film (3) compound;
Step 3: it is coated upper layer hydrophilic film
It is coated with lower layer's hydrophilic film (3) and is compounded with the substrates (1) of lower layer's hydrophilic film (3) and wheel (04) is led through the first compound rolling
To, become horizontal transmission and its upper surface upward, upper layer hydrophilic film coating die head (06) above to the upper surface of substrate (1) into
Row coating;
Step 4: compound upper layer PE film after low temperature drying
The substrate (1) for being coated with upper layer hydrophilic film (2) enters low temperature drying channel (09) and carries out low temperature drying, upper layer hydrophilic film
(2) by after drying, upper layer PE film (4) is released from upper layer PE film roll material emptying roller (02), by the second compound rolling to wheel
(05) compound with the substrate (1) that is coated with upper layer hydrophilic film (2);
Step 5: it cuts
The two-sided hydrophilic film (6) of finished product is sent to cutter (011) to wheel (05) by the second compound rolling and cuts.