CN109441057A - Prefabrication type artistic floors - Google Patents
Prefabrication type artistic floors Download PDFInfo
- Publication number
- CN109441057A CN109441057A CN201811572583.XA CN201811572583A CN109441057A CN 109441057 A CN109441057 A CN 109441057A CN 201811572583 A CN201811572583 A CN 201811572583A CN 109441057 A CN109441057 A CN 109441057A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- byk
- weight
- prefabrication type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of prefabrication type artistic floors comprising bottom base and the artistic layer in base, the art layer includes the coating being mixed by component A and B component by weight 5:1；Wherein component A is raw materials used by weight are as follows: 100-110 parts of E-51 epoxy resin, 30-40 parts of epoxy propane butyl ether, 1-5 parts of cyclohexanol, 60-80 parts of heavy calcium carbonate, 10-20 parts of magnesium carbonate, 15-20 parts of mill base, 5-7 parts of nbr carboxyl terminal, 0.09-0.1 parts of BYK-307,0.1-0.6 parts of BYK-088,1-1.5 parts of BYK-2155；B component is raw materials used by weight are as follows: aliphatic cyclic amine 40-50 parts, 2-3 parts of benzylalcohol modified.Prefabrication type artistic floors of the present invention can Fast Installation at the construction field (site), it is significant to shorten the construction time, and the problem of environmental pollution that may cause when traditional construction polishing can be solved.
Description
Technical field
The invention belongs to building engineering fields, and in particular to a kind of prefabrication type artistic floors.
Background technique
The preparation of terrace at present often uses field polish, mats formation, and can generate a large amount of dust in the process, and then to environment
It pollutes.Meanwhile if construction area is larger, cost of labor is higher, and the construction time is long, can seriously affect the duration.
Summary of the invention
The purpose of the present invention is to provide a kind of prefabrication type artistic floors, can Fast Installation at the construction field (site), it is significant to contract
The short construction time, and can solve the problems, such as generate a large amount of dust when traditional construction polishing, cause environmental pollution.
To achieve the above object, the present invention adopts the following technical scheme:
A kind of prefabrication type artistic floors, the artistic layer including bottom base and in base, wherein it is described art layer include by
The coating that component A and B component are mixed by weight 5:1；
In component A it is raw materials used by weight are as follows: 100-110 parts of E-51 epoxy resin, 30-40 parts of epoxy propane butyl ether,
1-5 parts of cyclohexanol, 60-80 parts of heavy calcium carbonate, 10-20 parts of magnesium carbonate, 15-20 parts of mill base, nbr carboxyl terminal 5-7
Part, 0.09-0.1 parts of BYK-307,0.1-0.6 parts of BYK-088,1-1.5 parts of BYK-2155；
In B component it is raw materials used by weight are as follows: modified 40-50 parts of aliphatic cyclic amine DG7627,2-3 parts of benzylalcohol.
The preparation step of the bottom base is as follows:
1) 80 ~ 150 cm × 80 ~ cm of 150 cm × 1.2 template is made, and in the setting one of template bottom with a thickness of 0.5-1 cm
Bottom plate；
2) casting cement inside template, and press to form bumps on surface with wire netting when cement is not dry, it is pasted with increasing
When adhesive force, after its drying after demould, the bottom base is made.
The application method of the prefabrication type artistic floors includes the following steps:
1) land clearing is clean；
2) one layer of binding material is brushed on the ground handled well by the way of roller coating or spraying；
3) the prefabrication type artistic floors are laid on the ground for being painted with binding material, and equal again on prefabrication type artistic floors
Even steamed bun applies one layer of binding material, so that prefabrication type artistic floors be made firmly to combine on the ground；
4) stream to be bonded is flat, solidify to get.
Wherein, the binding material is to be mixed by component C and D component by weight 5:1；
In component C it is raw materials used by weight are as follows: 100-110 parts of E-51 epoxy resin, 30-40 parts of epoxy propane butyl ether,
1-5 parts of cyclohexanol, 60-80 parts of heavy calcium carbonate, 10-20 parts of magnesium carbonate, 5-7 parts of nbr carboxyl terminal, BYK-307
0.09-0.1 parts, 0.1-0.6 parts of BYK-088,1-1.5 parts of BYK-2155；
In D component it is raw materials used by weight are as follows: modified 40-50 parts of aliphatic cyclic amine DG7627,2-3 parts of benzylalcohol.
Of the invention is particularly advantageous in that:
(1) the artistic layer on prefabrication type artistic floors of the present invention has good wear-resisting, anti-scratch, resistant to pressure, chemical resistance, heat-resisting
Property and antifouling property, and its rate of expanding with heat and contract with cold is low.
(2) product anti-yellowing property can be improved in the use of modified aliphatic cyclic amine in the present invention, and artistic layer coating is glued with used
The composition of raw materials of ramming material is almost the same, therefore the two compatibility is good, is firmly bonded, and the wear-resisting property of product can be improved, and can prevent
Pattern removing, so as to play the effect for extending terrace service life jointly.
(3) prefabrication type artistic floors provided by the invention can Fast Installation at the construction field (site), it is significant to shorten the construction time, and
It can solve the problems, such as generate a large amount of dust when traditional construction polishing, cause environmental pollution.
(4) prefabrication type artistic floors of the present invention can also be used for the decorated wall surfaces such as production television background wall.
Specific embodiment
A kind of prefabrication type artistic floors, the artistic layer including bottom base and in base, wherein the art layer packet
Include the coating being mixed by component A and B component by weight 5:1；
In component A it is raw materials used by weight are as follows: 100-110 parts of E-51 epoxy resin, 30-40 parts of epoxy propane butyl ether,
1-5 parts of cyclohexanol, 60-80 parts of heavy calcium carbonate, 10-20 parts of magnesium carbonate, 15-20 parts of mill base, nbr carboxyl terminal 5-7
Part, 0.09-0.1 parts of BYK-307,0.1-0.6 parts of BYK-088,1-1.5 parts of BYK-2155；
In B component it is raw materials used by weight are as follows: modified 40-50 parts of aliphatic cyclic amine DG7627,2-3 parts of benzylalcohol.
One of the preparation method of the art layer is to form the coating with artistic feeling by the allotment of different mill bases；
The two of the preparation method of the art layer are on the coating made of A, B component by drawing, the side for pasting or transferring
Formula is covered with a layer pattern, then steamed bun applies one layer of binding material and is made on it.
The preparation step of the bottom base is as follows:
1) 80 ~ 150 cm × 80 ~ cm of 150 cm × 1.2 template is made, and in the setting one of template bottom with a thickness of 0.5-1 cm
Bottom plate；
2) casting cement inside template, and press to form bumps on surface with wire netting when cement is not dry, to increase attachment
Power demoulds after its drying, the bottom base is made.
The application method of the prefabrication type artistic floors includes the following steps:
1) land clearing is clean；
2) one layer of binding material is brushed on the ground handled well by the way of roller coating or spraying；
3) the prefabrication type artistic floors are laid on the ground for being painted with binding material, and equal again on prefabrication type artistic floors
Even steamed bun applies one layer of binding material, so that prefabrication type artistic floors be made firmly to combine on the ground；
4) stream to be bonded is flat, solidify to get.
Wherein, the binding material is to be mixed by component C and D component by weight 5:1；
In component C it is raw materials used by weight are as follows: 100-110 parts of E-51 epoxy resin, 30-40 parts of epoxy propane butyl ether,
1-5 parts of cyclohexanol, 60-80 parts of heavy calcium carbonate, 10-20 parts of magnesium carbonate, 5-7 parts of nbr carboxyl terminal, BYK-307
0.09-0.1 parts, 0.1-0.6 parts of BYK-088,1-1.5 parts of BYK-2155；
In D component it is raw materials used by weight are as follows: modified 40-50 parts of aliphatic cyclic amine DG7627,2-3 parts of benzylalcohol.
In order to make content of the present invention easily facilitate understanding, With reference to embodiment to of the present invention
Technical solution is described further, but the present invention is not limited only to this.
Embodiment 1
A kind of prefabrication type artistic floors, preparation method include the following steps:
1) template of the cm × 1.2 of 80 cm × 80 cm is made, and in template bottom setting one with a thickness of the bottom plate of 0.5 cm；
2) casting cement inside template, and press to form bumps on surface with wire netting when cement is not dry, to increase attachment
Power demoulds after its drying, the bottom base is made；
3) A, B component are prepared respectively by material rate, rear steamed bun is then mixed and is applied in the bottom base；
4) it after solidification to be coated, draws a design on it；
5) after pattern parches, then steamed bun applies one layer of binding material thereon, forms artistic layer；
6) stream to be bonded is put down, is polished after solidification to get the prefabrication type artistic floors.
The weight ratio of component A and B component is 5:1 in artistic layer；In component A it is raw materials used by weight are as follows: E-51 ring
100 parts of oxygen resin, 40 parts of epoxy propane butyl ether, 1 part of cyclohexanol, 60 parts of heavy calcium carbonate, 20 parts of magnesium carbonate, mill base 20
Part, 7 parts of nbr carboxyl terminal, 0.09 part of BYK-307,0.6 part of BYK-088,1 part of BYK-2155；Original used in B component
Material is by weight are as follows: modified 40 parts of aliphatic cyclic amine DG7627,3 parts of benzylalcohol.
The binding material is mixed by component C and D component by weight 5:1；In component C it is raw materials used by weight
Are as follows: 100 parts of E-51 epoxy resin, 40 parts of epoxy propane butyl ether, 1 part of cyclohexanol, 60 parts of heavy calcium carbonate, magnesium carbonate 20
Part, 7 parts of nbr carboxyl terminal, 0.09 part of BYK-307,0.6 part of BYK-088,1 part of BYK-2155；Original used in D component
Material is by weight are as follows: modified 40 parts of aliphatic cyclic amine DG7627,3 parts of benzylalcohol.
Embodiment 2
Component A is raw materials used by weight in artistic layer are as follows: 105 parts of E-51 epoxy resin, 35 parts of epoxy propane butyl ether, ring
3 parts of hexanol, 70 parts of heavy calcium carbonate, 15 parts of magnesium carbonate, 16 parts of mill base, 6 parts of nbr carboxyl terminal, 0.1 part of BYK-307,
0.1 part of BYK-088,1.5 parts of BYK-2155；B component is raw materials used by weight are as follows: modified 45 parts of aliphatic cyclic amine DG7627,
2 parts of benzylalcohol.
Component C is raw materials used by weight in binding material are as follows: 105 parts of E-51 epoxy resin, epoxy propane butyl ether 35
Part, 3 parts of cyclohexanol, 70 parts of heavy calcium carbonate, 15 parts of magnesium carbonate, 6 parts of nbr carboxyl terminal, 0.1 part of BYK-307, BYK-
088 0.1 parts, 1.5 parts of BYK-2155；B component is raw materials used by weight are as follows: modified 45 parts of aliphatic cyclic amine DG7627, benzylalcohol
2 parts.
Remaining step is the same as embodiment 1.
Embodiment 3
Component A is raw materials used by weight in artistic layer are as follows: 110 parts of E-51 epoxy resin, 30 parts of epoxy propane butyl ether, ring
5 parts of hexanol, 80 parts of heavy calcium carbonate, 10 parts of magnesium carbonate, 15 parts of mill base, 5 parts of nbr carboxyl terminal, 0.1 part of BYK-307,
0.2 part of BYK-088,1.2 parts of BYK-2155；B component is raw materials used by weight are as follows: modified 50 parts of aliphatic cyclic amine DG7627,
2 parts of benzylalcohol.
Component C is raw materials used by weight in binding material are as follows: 110 parts of E-51 epoxy resin, epoxy propane butyl ether 30
Part, 5 parts of cyclohexanol, 80 parts of heavy calcium carbonate, 10 parts of magnesium carbonate, 5 parts of nbr carboxyl terminal, 0.1 part of BYK-307, BYK-
088 0.2 parts, 1.2 parts of BYK-2155；B component is raw materials used by weight are as follows: modified 50 parts of aliphatic cyclic amine DG7627, benzylalcohol
2 parts.
Remaining step is the same as embodiment 1.
The performance indicator of terrace sample obtained by embodiment 1-3 is shown in Table 1.
Table 1
The foregoing is merely presently preferred embodiments of the present invention, all equivalent changes done according to scope of the present invention patent with repair
Decorations, are all covered by the present invention.
Claims (4)
1. a kind of prefabrication type artistic floors, the artistic layer including bottom base and in base, it is characterised in that: the art
Layer includes the coating being mixed by component A and B component by weight 5:1；
In component A it is raw materials used by weight are as follows: 100-110 parts of E-51 epoxy resin, 30-40 parts of epoxy propane butyl ether,
1-5 parts of cyclohexanol, 60-80 parts of heavy calcium carbonate, 10-20 parts of magnesium carbonate, 15-20 parts of mill base, nbr carboxyl terminal 5-7
Part, 0.09-0.1 parts of BYK-307,0.1-0.6 parts of BYK-088,1-1.5 parts of BYK-2155；
In B component it is raw materials used by weight are as follows: modified aliphatic cyclic amine 40-50 parts, 2-3 parts of benzylalcohol.
2. prefabrication type artistic floors according to claim 1, it is characterised in that: the preparation step of the bottom base is such as
Under:
1) 80 ~ 150 cm × 80 ~ cm of 150 cm × 1.2 template is made, and in the setting one of template bottom with a thickness of 0.5-1 cm
Bottom plate；
2) casting cement inside template, and press to form bumps on surface with wire netting when cement is not dry, after its drying
Demoulding, is made the bottom base.
3. prefabrication type artistic floors according to claim 1, it is characterised in that: its application method includes the following steps:
1) land clearing is clean；
2) one layer of binding material is brushed on the ground handled well by the way of roller coating or spraying；
3) the prefabrication type artistic floors are laid on the ground for being painted with binding material, and equal again on prefabrication type artistic floors
Even steamed bun applies one layer of binding material, so that prefabrication type artistic floors be made firmly to combine on the ground；
4) stream to be bonded is flat, solidify to get.
4. prefabrication type artistic floors according to claim 3, it is characterised in that: the binding material is pressed by component C and D component
Weight ratio 5:1 is mixed；
In component C it is raw materials used by weight are as follows: 100-110 parts of E-51 epoxy resin, 30-40 parts of epoxy propane butyl ether,
1-5 parts of cyclohexanol, 60-80 parts of heavy calcium carbonate, 10-20 parts of magnesium carbonate, 5-7 parts of nbr carboxyl terminal, BYK-307
0.09-0.1 parts, 0.1-0.6 parts of BYK-088,1-1.5 parts of BYK-2155；
In D component it is raw materials used by weight are as follows: modified aliphatic cyclic amine 40-50 parts, 2-3 parts of benzylalcohol.