CN109402858A - One-pass molding one-way wet-guide two-needle bar warp-knitted face fabric and preparation method thereof - Google Patents
One-pass molding one-way wet-guide two-needle bar warp-knitted face fabric and preparation method thereof Download PDFInfo
- Publication number
- CN109402858A CN109402858A CN201811634058.6A CN201811634058A CN109402858A CN 109402858 A CN109402858 A CN 109402858A CN 201811634058 A CN201811634058 A CN 201811634058A CN 109402858 A CN109402858 A CN 109402858A
- Authority
- CN
- China
- Prior art keywords
- fiber yarn
- fabric
- water
- knitted
- guide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses one-pass molding one-way wet-guide two-needle bar warp-knitted face fabric and preparation method thereof, fabric is using the woven three-layer mesh fabric structure of double rib warp loom, including water blocking layer, conducting shell, water absorption layer;Water blocking layer is knitted to form using water preventing ability chemical synthetic fiber yarn and profiled-cross-section moisture absorption hydrofuge chemical synthetic fiber yarn using preceding needle bed sley bar;Conducting shell uses transmissibility chemical synthetic fiber yarn, carries out front and back braiding using intermediate sley bar and forms water blocking layer and water absorption layer progress effectively connection;Water absorption layer uses profiled-cross-section moisture absorption hydrofuge chemical synthetic fiber yarn, is knitted to form with rear needle bed sley bar.There is the fabric product that one-pass molding one-way wet-guide two-needle bar warp-knitted face fabric of the present invention and preparation method thereof obtains extremely good one-way wet-guide to perspire effect, and good permeability, and quality is soft so, affine human body.
Description
Technical field
The present invention relates to one-pass molding one-way wet-guide two-needle bar warp-knitted face fabrics and preparation method thereof.
Background technique
Nowadays people are higher and higher to a kind of personal moisture absorbing and sweat releasing requirement for taking product such as nightwear, pillow.With baby children
For youngster's pillow products, infant perspires during sleep, and quickly sweat is absorbed and shifted if pillow can not be realized, sweat
Pillow surface will be accumulated in, sweat evaporation is with infant's shell temperature, thus the case where inducing treating baby's cold.
Existing pillow fabric is to reach good moisture absorbing and sweat releasing effect, frequently with the different face of compound various moisture pick-up properties
Addition water repellent or the mode of the coating of water suction in the mode or fabric of material.Regardless of that will necessarily be brought using which kind of above-mentioned mode
Following problems: 1, non-natural chemical component (including compound glue or coating material), one side mentioned component are introduced
It is possible that being harmful to the human body, on the other hand repeatedly above-mentioned chemical component easily loses to influence fabric function after washing;2, compound
Or the complex process of coating will also increase compound or coating process flow, product other than the weaving process of fabric body
Itself can not one-pass molding, it is with high costs;3, compound or coating mode will change the wearability of fabric, not be able to satisfy soft
It is soft, the requirement of affine human body;4, on the effect of obtaining moisture absorbing and sweat releasing product by the way of compound or coating from moisture absorbing and sweat releasing simultaneously
It is undesirable, also continue the space for improving effect.5, it produces to be formed using one-pass molding, shortens production process, improve production effect
Rate saves production cost.
Summary of the invention
The purpose of the present invention is to provide one-pass molding one-way wet-guide two-needle bar warp-knitted face fabrics, it is intended to solve the above problems.
To achieve the goals above, the technical scheme is to design one-pass molding one-way wet-guide two-needle bar warp knit faces
Material, the one-pass molding one-way wet-guide two-needle bar warp-knitted face fabric are using the woven three layers of warp-knitted face fabric knot of double rib warp loom
Structure, including water blocking layer, conducting shell, water absorption layer;The water blocking layer (includes: water preventing ability using water preventing ability chemical synthetic fiber yarn
Polyester fiber yarn, polyethylene fibre yarn, polypropylene fibre yarn) with profiled-cross-section (include: "●" "+", "×", " Y ",
" C ", " W " cross-section) conjunction of moisture absorption hydrofuge chemical synthesis polyester fibers knot, it is knitted to form and is blocked water using preceding needle bed sley bar
Layer;And water preventing ability chemical synthetic fiber yarn proportion range 5%~50% in fabric in water blocking layer, profiled-cross-section moisture absorption row
Wet chemical synthetic polyester fibers yarn proportion range 5%~50% in fabric;The conducting shell is using transmissibility chemistry
Synthetic yarns (including: transmissibility polyester fiber yarn, Fypro yarn) carry out front and back braiding using intermediate sley bar
Water blocking layer and water absorption layer are subjected to effectively connection and form conducting shell;And transmissibility chemical synthetic fiber yarn institute's accounting in fabric
Example range 10%~80%;The water absorption layer is inhaled using profiled-cross-section (including: "●" "+", "×", " Y ", " C ", " W " cross-section)
Wet hydrofuge chemical synthesis polyester fiber yarn is knitted to form water absorption layer with rear needle bed sley bar.And profiled-cross-section is inhaled in water absorption layer
Wet hydrofuge chemical synthesis polyester fiber yarn proportion range 5%~60% in fabric.
Further, the water blocking layer uses 50D~600D water preventing ability chemical synthetic fiber and 50D~600D profiled-cross-section
Moisture absorption hydrofuge chemical synthesis polyester fiber yarn;The conducting shell uses 50D~600D transmissibility chemical synthetic fiber yarn;
The water absorption layer uses 50D~600D profiled-cross-section moisture absorption hydrofuge chemical synthesis polyester fiber yarn.
The preparation method of one-pass molding one-way wet-guide two-needle bar warp-knitted face fabric, comprising the following steps:
Step 1: machine choice in production process: warping apparatus is automatic stop computer copy function warping machine of taking pictures;Fabric manufacture equipment is
Double rib warp loom, setting selection RD series tricot machine model according to product purpose includes: common double rib warp loom, EL electronics
Traversing double rib warp loom, PJ computer jacquard double rib warp loom, machine range: E=16~28 needles, sley bar number range: 4~8 combs
Comb or PJ computer jacquard comb;
Step 2: warping, sets warping head part according to fabric breadth, according to raw material specification D number setting speed range: 50 revs/min
Clock~1000 rev/min;Yarn tension range 1CN~10CN is set according to raw material specification D number and speed;It is set according to material performance
Surely oil stick numberical range 1~8;
Step 3: weaving, selects double rib warp loom establishment;Wherein preceding needle bed sley bar is knitted to form water blocking layer;It is combed using centre
Comb carries out front and back braiding and water blocking layer and water absorption layer progress effectively connection is formed conducting shell;Needle bed sley bar is knitted to form water suction afterwards
Layer;
Step 4: post-processing, fabric turn over cloth;Fabric sizing: setting temperature control is at 100 DEG C~200 DEG C, 15 yard/minute of speed
~60 yards/minute, 8~10 section of shaping baking oven joint number;It is handled into cylinder: 40 DEG C~130 DEG C of temperature, 20 minutes~60 points of total time
Clock is added in chemical fibre and removes oil assistant 1%~20%, cools down at 0 DEG C~60 DEG C, and hydrophilic additive 1%~20% is added, divides in carry out 5
Clock~40 minute processing;Dehydration;Removing the work;Finished product sizing: temperature control is at 100 DEG C~200 DEG C, speed: 15 yard/minute~60
Code/minute, 8~10 section of shaping baking oven joint number;Clot packaging.
The advantages and beneficial effects of the present invention are: a kind of molding one-way wet-guide warp-knitted face fabric of the present invention has following spy
Point, 1, water droplet fall on web surface, web surface water will not horizontal proliferation, moment, which absorbs water, simultaneously shifts water quickly through conducting shell
To water absorption layer;2, good gas permeability, fabric are Sandwich screen-cloth structure, and fabric overall structure is made of mesh, are had good
Gas permeability, it is also not sultry when having water;3, fabric is soft, and skin-friendly is good;4, no using compound using warp knitting technology one-pass molding
Etc. techniques, it is nontoxic without the ingredients such as glue, it is non-stimulated.
Detailed description of the invention
Fig. 1 is schematic diagram of the invention.
Fig. 2 is the principle of the present invention figure.
Wherein, water blocking layer 1, conducting shell 2, water absorption layer 3.
Specific embodiment
With reference to the accompanying drawings and examples, further description of the specific embodiments of the present invention.Following embodiment is only
For clearly illustrating technical solution of the present invention, and not intended to limit the protection scope of the present invention.
Embodiment 1:
The selection of equipment:
1, warping apparatus is using automatic stop computer copy function warping machine of taking pictures;
2, fabric manufacture equipment uses RD series EL electronics horizontal movement electronic warp feeding double rib warp loom, and machine number: 22 needles, 6 weave sley bar.
Weaving is selected: needle bed sley bar GB1 and GB2 are knitted to form water blocking layer before wherein;Using intermediate sley bar GB3 and GB4, into
Water blocking layer and water absorption layer are carried out effectively connection and form conducting shell by the braiding of row front and back;Needle bed sley bar GB5 and GB6 are knitted to form suction afterwards
Water layer.
Water blocking layer (wire side): 75D water preventing ability polyester fiber yarn, DTY are used, and accounts for fabric ratio 10%;75D is special-shaped
"+" section polyester fiber yarn, DTY, and account for fabric ratio 10%;
Technique: GB1, GB2:1222 2,333 3,444 4,544 4,333 3,222 2,111 1000;
Conducting shell (centre connection): 75D transmissibility polyester fiber yarn is used, and accounts for fabric ratio 60%;
Technique: GB3, GB4:1012 2312;
Water absorption layer (bottom surface): 75D abnormal shape "+" section polyester fiber yarn, DTY, and account for fabric ratio 20%;
Technique: GB5:1000 1222;GB6:1222 1000;
Final finishing is selected: fabric turns over cloth;Fabric sizing: setting temperature control is at 190 DEG C, 40 yard/minute of speed, shaping baking oven section
10 section of number;Into cylinder processing: 80 DEG C of temperature, 50 minutes total times being added in chemical fibre and remove oil assistant 10%, cool down at 40 DEG C, be added
Hydrophilic additive 5% handle within 10 minutes;Dehydration;Removing the work;Finished product sizing: temperature control is at 190 DEG C, speed: 45 yards/point
Clock, 10 section of shaping baking oven joint number;Clot packaging.
Embodiment 2:
The selection of equipment:
1, warping apparatus is using automatic stop computer copy function warping machine of taking pictures;
2, fabric manufacture equipment is using the common double rib warp loom of RD series, and machine number: 24 needles, 7 weave sley bar.
Weaving is selected: needle bed sley bar GB1 and GB2 are knitted to form water blocking layer before wherein;Using intermediate sley bar GB3 and GB4, into
Water blocking layer and water absorption layer are carried out effectively connection and form conducting shell by the braiding of row front and back;Needle bed sley bar GB5, GB6, GB7 tri- is volume afterwards
It knits to form water absorption layer.
Water blocking layer (wire side): 100D water preventing ability polyethylene fibre yarn, FDY are used, and accounts for fabric ratio 15%;100D is different
The section type " w " polyester fiber yarn, FDY, and account for fabric ratio 15%;
Technique: GB1:(4555 5444) × 2 group of 4,555 4,333 3,222 2111 (1,000 0111) × 2 group 1,000 1222
2333 3444;GB2:(1000 0111) × 2 group of 1,000 1,222 2,333 3444 (4,555 5444) × 2 group 4,555 4333
3222 2111 ;
Conducting shell (centre connection): 70D transmissibility Fypro yarn, FDY are used, and accounts for fabric ratio 50%;
Technique: GB3:1012 2312;GB4:2312 1012;
Water absorption layer (bottom surface): 75D abnormal shape section " w " polyester fiber yarn, DTY, and account for fabric ratio 20%;
Technique: GB5:1000 0111;GB6:1000 1222;GB7:1222 1000;
Final finishing is selected: fabric turns over cloth;Fabric sizing: setting temperature control is at 120 DEG C, 45 yard/minute of speed, shaping baking oven section
10 section of number;Into cylinder processing: 100 DEG C of temperature, 60 minutes total times being added in chemical fibre and remove oil assistant 15%, cool down at 40 DEG C, add
Enter hydrophilic additive 10%, handle within 15 minutes;Dehydration;Removing the work;Finished product sizing: temperature control is at 120 DEG C, speed: 50 yards/
Minute, 10 section of shaping baking oven joint number;Clot packaging.
Embodiment 3:
The selection of equipment:
1, warping apparatus is using automatic stop computer copy function warping machine of taking pictures;
2, fabric manufacture equipment uses RD Series P J double rib warp loom, machine number: 22 needles, the braiding of PJ computer jacquard sley bar.
Weaving is selected: needle bed sley bar is that PJ computer jacquard sley bar PJ1 and PJ2 are knitted to form water blocking layer before wherein;In
Between sley bar GB3 and GB4, carry out front and back braiding water blocking layer and water absorption layer be subjected to effectively connection to form conducting shell;Needle bed sley bar afterwards
GB5, GB6 are knitted to form water absorption layer.
Water blocking layer (wire side): 1500D water preventing ability polypropylene fibre yarn, DTY are used, and accounts for fabric ratio 18%;150D
Special-shaped section " Y " polyester fiber yarn, DTY, and account for fabric ratio 18%;
Technique: PJ1 and PJ2 jacquard weave comb comb technique for computer jacquard and design completion technique flower pattern, this reality on special-purpose software CAD
It can not be shown in example
Conducting shell (centre connection): 85D transmissibility transmissibility polyester fiber yarn, FDY are used, and accounts for fabric ratio 35%;
Technique: GB3:1012 2312;GB4:2312 1012;
Water absorption layer (bottom surface): 150D abnormal shape section " Y " polyester fiber yarn, DTY, and account for fabric ratio 29%;
Technique: GB5:1000 0111;GB6:1000 1222;
Final finishing is selected: fabric turns over cloth;Fabric sizing: setting temperature control is at 130 DEG C, 45 yard/minute of speed, shaping baking oven section
8 section of number;Into cylinder processing: 80 DEG C of temperature, 45 minutes total times being added in chemical fibre and remove oil assistant 10%, cool down at 45 DEG C, be added
Hydrophilic additive 10% handle within 15 minutes;Dehydration;Removing the work;Finished product sizing: temperature control is at 130 DEG C, speed: 45 yards/point
Clock, 8 section of shaping baking oven joint number;Clot packaging.
If Fig. 2 is the principle of the present invention schematic diagram
Arrow represents the direction of water droplet flowing in figure, and water droplet first is dropped in web surface, and web surface is water blocking layer 1, drippage
Water droplet to web surface will not only be spread around in water blocking layer 1, along the mesh on 1 surface of water blocking layer after assembling instead
Infiltration downwards, then the lower water droplet seeped of accumulation is transmitted via conducting shell 2 reaches water absorption layer 3, and water absorption layer 3 absorbs water, and water droplet laterally expands
It dissipates.To sum up, this fabric upper surface is after touching water droplet, the upper surface of fabric, i.e., water blocking layer 1 is the shape continued drying out
State, and the lower surface of fabric, i.e. water absorption layer 3 are in moist state after absorbing moisture.The dress-goods prepared using this fabric, pillow
Head etc., it is only necessary to the upper surface of fabric is bonded human skin, following table faces outwardly, it will be able to realize the effect that good absorbing sweat perspires
Fruit.
The above is only a preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, without departing from the technical principles of the invention, several improvements and modifications can also be made, these improvements and modifications
Also it should be regarded as protection scope of the present invention.
Claims (6)
1. one-pass molding one-way wet-guide two-needle bar warp-knitted face fabric, it is characterised in that: the one-pass molding one-way wet-guide two-needle bar warp
Weaving fabric is using the woven three layers of warp-knitted face fabric structure of double rib warp loom, including water blocking layer, conducting shell, water absorption layer;It is described
Water blocking layer uses water preventing ability chemical synthetic fiber yarn and profiled-cross-section moisture absorption hydrofuge chemical synthesis polyester fiber yarn, and benefit
Be knitted to form with preceding needle bed sley bar, and in water blocking layer water preventing ability chemical synthetic fiber yarn in fabric proportion range 5%~
50%, profiled-cross-section moisture absorption hydrofuge chemical synthesis polyester fiber yarn proportion range 5%~50% in fabric;The biography
Conducting shell uses transmissibility chemical synthetic fiber yarn, and carrying out front and back braiding using intermediate sley bar has water blocking layer and water absorption layer
Effect connection forms conducting shell;And transmissibility chemical synthetic fiber proportion range 10%~80% in fabric;The water absorption layer
Using profiled-cross-section moisture absorption hydrofuge chemical synthesis polyester fiber yarn, it is knitted to form water absorption layer using rear needle bed sley bar, and inhale
Profiled-cross-section moisture absorption hydrofuge chemical synthesis polyester fiber yarn proportion range 5%~60% in fabric in water layer.
2. one-pass molding one-way wet-guide two-needle bar warp-knitted face fabric according to claim 1, it is characterised in that: the water preventing ability
Chemical synthetic fiber yarn includes water preventing ability polyester fiber yarn, polyethylene fibre yarn, polypropylene fibre yarn one kind or more
Kind.
3. one-pass molding one-way wet-guide two-needle bar warp-knitted face fabric according to claim 1, it is characterised in that: described special-shaped section
The section of face moisture absorption hydrofuge chemical synthesis polyester fiber yarn is "●" "+", "×", " Y ", " C ", " W ".
4. one-pass molding one-way wet-guide two-needle bar warp-knitted face fabric according to claim 1, it is characterised in that: the transmissibility
Chemical synthetic fiber yarn includes one of transmissibility polyester fiber yarn, Fypro yarn or a variety of.
5. one-pass molding one-way wet-guide two-needle bar warp-knitted face fabric according to claim 1, it is characterised in that: the water blocking layer
Using 50D~600D water preventing ability chemical synthetic fiber yarn and 50D~600D profiled-cross-section moisture absorption hydrofuge chemical synthetic fiber
Yarn;The conducting shell uses 50D~600D transmissibility chemical synthetic fiber yarn;The water absorption layer is different using 50D~600D
Type section moisture absorption hydrofuge chemical synthesis polyester fiber yarn.
6. the preparation method of one-pass molding one-way wet-guide two-needle bar warp-knitted face fabric according to claim 1, which is characterized in that
The following steps are included:
Step 1: machine choice in production process: warping apparatus is automatic stop computer copy function warping machine of taking pictures;Fabric manufacture equipment is
Double rib warp loom, setting selection RD series tricot machine model according to product purpose includes: common double rib warp loom, EL electronics
Traversing double rib warp loom, PJ computer jacquard double rib warp loom, machine range: E=16~28 needles, sley bar number range: 4~8 combs
Comb or PJ computer jacquard comb;
Step 2: warping, sets warping head part according to fabric breadth, according to raw material specification D number setting speed range: 50 revs/min
Clock~1000 rev/min;Yarn tension range 1CN~10CN is set according to raw material specification D number and speed;It is set according to material performance
Surely oil stick numberical range 1~8;
Step 3: weaving, selects double rib warp loom establishment;Wherein preceding needle bed sley bar is knitted to form water blocking layer;It is combed using centre
Comb carries out front and back braiding and water blocking layer and water absorption layer progress effectively connection is formed conducting shell;Needle bed sley bar is knitted to form water suction afterwards
Layer;
Step 4: post-processing, fabric turn over cloth;Fabric sizing: setting temperature control is at 100 DEG C~200 DEG C, 15 yard/minute of speed
~60 yards/minute, 8~10 section of shaping baking oven joint number;It is handled into cylinder: 40 DEG C~130 DEG C of temperature, 20 minutes~60 points of total time
Clock is added in chemical fibre and removes oil assistant 1%~20%, cools down at 0 DEG C~60 DEG C, and hydrophilic additive 1%~20% is added, divides in carry out 5
Clock~40 minute processing;Dehydration;Removing the work;Finished product sizing: temperature control is at 100 DEG C~200 DEG C, speed: 15 yard/minute~60
Code/minute, 8~10 section of shaping baking oven joint number;Clot packaging.