CN109401630A - A kind of aluminium alloy anode oxide film mirror finish liquid and preparation method thereof - Google Patents
A kind of aluminium alloy anode oxide film mirror finish liquid and preparation method thereof Download PDFInfo
- Publication number
- CN109401630A CN109401630A CN201710711792.7A CN201710711792A CN109401630A CN 109401630 A CN109401630 A CN 109401630A CN 201710711792 A CN201710711792 A CN 201710711792A CN 109401630 A CN109401630 A CN 109401630A
- Authority
- CN
- China
- Prior art keywords
- aluminium alloy
- oxide film
- anode oxide
- alloy anode
- mirror
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of aluminium alloy anode oxide film mirror finish liquid and preparation method thereof, it is characterised in that it is prepared as a raw material by the alumina powder of high-purity, dispersing agent, wetting agent, surfactant, buffer, pure water.For the average grain diameter of alpha-type aluminum oxide micro mist used in the present invention between 0.5 ~ 2.0 μm, the aluminium alloy after anodic oxidation and dyeing can be polished out good mirror effect by polishing fluid within this range.
Description
Technical field
The present invention relates to a kind of for field of metal surface treatment technology more particularly to a kind of after anodized
Aluminum alloy surface mirror finish polishing fluid and preparation method thereof.
Background technique
Aluminium alloy is as alloying metal the most universal is applied, especially in electronic device industries such as computer, mobile phones
With quite extensively.Process for treating surface fundamentally can solve or improve protective, dicoration and the function of aluminium alloy
Property.
Aluminum alloy surface processing technique has: surface mechanical pretreatment, chemical pretreatment or chemical treatment, electrochemical treatments,
Physical treatment etc..It is existing to aluminium alloy do appearance processing technique in, anodized be using wide one of technique,
This technique can improve the hardness and corrosion resistance of aluminum alloy surface, while can obtain the production of different decorative effects by dyeing
Product so can largely widen the use scope of aluminium alloy.
Disclosure sets forth the preparation methods that the product after aluminium alloy anode oxide carries out the polishing fluid that automatically grinding uses.
Since the product surface of processing is non-planar in certain radian, product uses automatically grinding equipment, passes through cotton piece buff, polishing
Liquid and product obtain the product of mirror surface in the grinding-polishing of high speed.
Summary of the invention
The purpose of the present invention is provide a kind of aluminium alloy anode oxide film mirror surface throwing for the problems in above-mentioned prior art
Light liquid and preparation method thereof.
In order to achieve the above object, the technical solution of the present invention is as follows:
A kind of aluminium alloy anode oxide film mirror finish liquid, the matter of each raw material of the aluminium alloy anode oxide film mirror finish liquid
Measure percentage are as follows:
Alumina powder: 1~30%
Dispersing agent: 5~30%
Wetting agent: 0.1~10%
Surfactant: 0.1~5%
Buffer: 0.1~5%
Pure water: 20~93.7%.
Preferably, alumina powder is α type, and purity >=99.99%, average grain diameter is between 0.5 ~ 2.0 μm.
Preferably, the alumina powder passes through obtained after high-temperature calcination, crushing, purification, classification processing.
Preferably, dispersing agent is polyethylene glycol, in silica solution, sodium pyrophosphate, sodium carboxymethylcellulose, Sodium Polyacrylate
It is any one or any two or more.
Preferably, dispersing agent is sodium pyrophosphate, sodium carboxymethylcellulose and three kinds of Sodium Polyacrylate mixing, weight fraction ratio
Are as follows: 1:2:5.
Preferably, the wetting agent be polyethylene glycol, glycerol, stearic acid, sapn, in tween any one or it is any
Two or more compositions.
Preferably, the wetting agent be polyethylene glycol, two kinds of glycerol mix, weight fraction ratio 3:1.
Preferably, the surfactant is organic silicon defoamer, alkanolamide 6501, appointing in alkanolamide 6502
It anticipates a kind of or any two or more.
Preferably, the buffer be borax, it is boric acid, glycine, hydrochloric acid, barbital sodium, any in sodium hydroxide
It is two or more.
The preparation method comprises the following steps: S1: alumina powder being added in blender, pure water is then added, stirs evenly;S2: it uses
The nylon cloth of 200-800 mesh carries out vibration filtering, and filtered filtrate is put into another blender, and keeps persistently stirring
It mixes;S3: the buffer of borax, sodium hydroxide composition, stirring and dissolving is added;S4: silica solution, poly- second are sequentially added into filtrate again
Glycol, organic silicon defoamer;S5: lasting stirring, which is uniformly mixed system, can be obtained required polishing fluid.
Preferably, step S2: the nylon cloth used is 500 mesh.
The beneficial effects of the present invention are:
1) this polishing fluid is abrasive material by the alpha-type aluminum oxide micro mist that purity is 99.99% purity, the alpha-type aluminum oxide micro mist in polishing fluid
Mass percentage be 1 ~ 30%, if the content of alpha-type aluminum oxide micro mist is too low, the rate of polishing will be reduced, if α type
The content of alumina powder is too high, and polishing fluid system is not easy to disperse, and the mirror effect of polishing is bad, and wastes raw material.
2) particle diameter distribution of alpha-type aluminum oxide micro mist used in the present invention is between 0.5 ~ 2.0 μm, throwing within this range
Aluminium alloy after anodic oxidation and dyeing can be polished out good mirror effect by light liquid.Abrasive size is too small, polishing speed meeting
It reduces, partial size is too big then for leaving scratch on burnishing surface, influences product surface appearance.
3) abrasive material can be uniformly dispersed in by polishing fluid of the present invention in used dispersing agent in the case where low viscosity
In system, and be adhered on buff well again, polishing fluid is not easy to splash when high-speed rotation, it is ensured that the efficiency of polishing and
The usage amount of polishing fluid.
4) polishing fluid of the invention can be very good the rate of control polishing, can uniformly remove the table of anode oxide film
Layer, reaches the mirror effect of almost Perfect, while not will cause the locally heterochromatic feelings of the anodic oxidation film surface through dyeing processing
Condition.
Specific embodiment
Further illustrate a specific embodiment of the invention.
Example 1:
S1: the alpha-type aluminum oxide micro mist of 12g is added in blender, 145 g pure water are then added, stir evenly;
S2: vibration filtering is carried out using the nylon cloth of 500 mesh, filtered filtrate is put into another blender, and protects
Lasting stirring;
S3: the buffer of 1g borax, 0.05g sodium hydroxide composition, stirring and dissolving is added;
S4: the components such as 40g silica solution, 2g polyethylene glycol, 0.05g organic silicon defoamer are sequentially added into filtrate again;
S5: lasting stirring, which is uniformly mixed system, can be obtained required polishing fluid;
By the polishing fluid being prepared with DI water in polishing fluid: DI water ratio is to be sprayed at automatically grinding equipment after 1 ﹕ 2 ~ 3 dilutes
Cotton piece buff carry out automatically grinding, the revolving speed of rough polishing wheel positive and negative rotation is 1000 ~ 1100r/min, rough polishing time both forward and reverse directions each 30
Second, the revolving speed of precision polishing wheel positive and negative rotation is 900r/min, and essence is thrown the time positive and negative each 20 seconds.This polishing fluid is in alkalescent, is had very big
Grinding force, polishing time is short, high-efficient, polishing the anode oxide film through dyeing specular appearance effect can be obtained, not will cause
The non-uniform phenomenon of Film color.
Example 2:
S1: being added the alpha-type aluminum oxide micro mist of 320g in blender, and 3680g pure water is then added, stirs evenly;
S2: vibration filtering is carried out using the nylon cloth of 500 mesh, filtered filtrate is put into another blender, and protects
Lasting stirring;
S3: the buffer of 19g borax, 1g sodium hydroxide composition, stirring and dissolving is added;
S4: 800g silica solution, 30g polyethylene glycol, 20g alkanolamide 6501, the defoaming of 50g organosilicon are sequentially added into filtrate again
The components such as agent;
S5: lasting stirring, which is uniformly mixed system, can be obtained required polishing fluid;
By the polishing fluid being prepared with DI water in polishing fluid: DI water ratio is to be sprayed at automatically grinding equipment after 1 ﹕ 2 ~ 3 dilutes
Cotton piece buff carry out automatically grinding, the revolving speed of rough polishing wheel positive and negative rotation is 1000 ~ 1100r/min, rough polishing time both forward and reverse directions each 30
Second, the revolving speed of precision polishing wheel positive and negative rotation is 900r/min, and essence is thrown the time positive and negative each 20 seconds.This polishing fluid is in alkalescent, is had very big
Grinding force, polishing time is short, high-efficient, polishing the anode oxide film through dyeing specular appearance effect can be obtained, not will cause
The non-uniform phenomenon of Film color.
Example 3:
S1: being added the alpha-type aluminum oxide micro mist of 32g in blender, and 368g pure water is then added, stirs evenly;
S2: vibration filtering is carried out using the nylon cloth of 500 mesh, filtered filtrate is put into another blender, and protects
Lasting stirring;
S3: the buffer of 1.9g borax, 0.1g sodium hydroxide composition, stirring and dissolving is added;
S4: 90g silica solution, 3g glycerol, 1g alkanolamide 6502,0.2g sodium carboxymethylcellulose etc. are sequentially added into filtrate again
Component;
S5: lasting stirring, which is uniformly mixed system, can be obtained required polishing fluid;
By the polishing fluid being prepared with DI water in polishing fluid: DI water ratio is to be sprayed at automatically grinding equipment after 1 ﹕ 2 ~ 3 dilutes
Cotton piece buff carry out automatically grinding, the revolving speed of rough polishing wheel positive and negative rotation is 1100 ~ 1200r/min, rough polishing time both forward and reverse directions each 35
Second, the revolving speed of precision polishing wheel positive and negative rotation is 900r/min, and essence is thrown the time positive and negative each 20 seconds.This polishing fluid is in alkalescent, is had very big
Grinding force, polishing time is short, high-efficient, polishing the anode oxide film through dyeing specular appearance effect can be obtained, not will cause
The non-uniform phenomenon of Film color.
Example 4:
S1: being added the alpha-type aluminum oxide micro mist of 600g in blender, and 10kg pure water is then added, stirs evenly;
S2: vibration filtering is carried out using the nylon cloth of 500 mesh, filtered filtrate is put into another blender, and protects
Lasting stirring;
S3: the buffer of 53g borax, 2.7g sodium hydroxide composition, stirring and dissolving is added;
S4: 2.5kg silica solution, 100g glycerol, 30g alkanolamide 6502,5g carboxymethyl cellulose are sequentially added into filtrate again
The components such as sodium;
S5: lasting stirring, which is uniformly mixed system, can be obtained required polishing fluid;
By the polishing fluid being prepared with DI water in polishing fluid: DI water ratio is to be sprayed at automatically grinding equipment after 1 ﹕ 2 ~ 3 dilutes
Cotton piece buff carry out automatically grinding, the revolving speed of rough polishing wheel positive and negative rotation is 1100 ~ 1200r/min, rough polishing time both forward and reverse directions each 35
Second, the revolving speed of precision polishing wheel positive and negative rotation is 900r/min, and essence is thrown the time positive and negative each 20 seconds.This polishing fluid is in alkalescent, is had very big
Grinding force, polishing time is short, high-efficient, polishing the anode oxide film through dyeing specular appearance effect can be obtained, not will cause
The non-uniform phenomenon of Film color.
Example 5:
S1: being added the alpha-type aluminum oxide micro mist of 20kg in blender, and 200kg pure water is then added, stirs evenly;
S2: vibration filtering is carried out using the nylon cloth of 500 mesh, filtered filtrate is put into another blender, and protects
Lasting stirring;
S3: the buffer of 1.06kg borax, 54g sodium hydroxide composition, stirring and dissolving is added;
S4: it is fine that 63kg silica solution, 1.8kg glycerol, 0.5kg alkanolamide 6502,0.1kg carboxymethyl are sequentially added into filtrate again
Tie up the components such as plain sodium;
S5: lasting stirring, which is uniformly mixed system, can be obtained required polishing fluid;
By the polishing fluid being prepared with DI water in polishing fluid: DI water ratio is to be sprayed at automatically grinding equipment after 1 ﹕ 2 ~ 3 dilutes
Cotton piece buff carry out automatically grinding, the revolving speed of rough polishing wheel positive and negative rotation is 1100~1200r/min, rough polishing time both forward and reverse directions each 35
Second, the revolving speed of precision polishing wheel positive and negative rotation is 900r/min, and essence is thrown the time positive and negative each 20 seconds.This polishing fluid is in alkalescent, is had very big
Grinding force, polishing time is short, high-efficient, polishing the anode oxide film through dyeing specular appearance effect can be obtained, not will cause
The non-uniform phenomenon of Film color.
Example 6:
Obtained polishing fluid is matched by above example 1 to example 5, with DI water in polishing fluid: DI water ratio is to spray after 1 ﹕ 2 ~ 3 dilutes
The cotton piece buff for being applied to automatically grinding equipment carries out automatically grinding, and the revolving speed of rough polishing wheel positive and negative rotation is 1100~1300r/min, rough polishing
Time both forward and reverse directions each 30 ~ 40 seconds, the revolving speed of precision polishing wheel positive and negative rotation was 900 ~ 1000r/min, and essence throws the time positive and negative each 15 ~ 20
Second, do not carry out the anodized aluminum alloy product of dyeing processing, the available good mirror surface product of effect with the polishing of this condition.
The above is not intended to limit the scope of the present invention, and all technical spirits according to the present invention are to above
Any modification, equivalent variations and modification made by embodiment, in the range of still falling within technical solution of the present invention.
Claims (9)
1. a kind of aluminium alloy anode oxide film mirror-finishes liquid, it is characterised in that: the aluminium alloy anode oxide film mirror finish
The mass percent of each raw material of liquid are as follows:
Alumina powder: 1~30%
Dispersing agent: 5~30%
Wetting agent: 0.1~10%
Surfactant: 0.1~5%
Buffer: 0.1~5%
Pure water: 20~93.7%.
2. aluminium alloy anode oxide film according to claim 1 mirror-finishes liquid, it is characterised in that: alumina powder α
Type, purity >=99.99%, average grain diameter is between 0.5 ~ 2.0 μm.
3. aluminium alloy anode oxide film according to claim 1 mirror-finishes liquid, it is characterised in that: the alumina powder
By obtained after high-temperature calcination, crushing, purification, classification processing.
4. aluminium alloy anode oxide film according to claim 1 mirror-finishes liquid, it is characterised in that: dispersing agent is poly- second two
It is alcohol, silica solution, sodium pyrophosphate, sodium carboxymethylcellulose, any one or any two or more in Sodium Polyacrylate.
5. aluminium alloy anode oxide film according to claim 1 mirror-finishes liquid, it is characterised in that: the wetting agent is
Polyethylene glycol, glycerol, stearic acid, sapn, any one or any two or more compositions in tween.
6. aluminium alloy anode oxide film according to claim 1 mirror-finishes liquid, it is characterised in that: the surface-active
Agent is organic silicon defoamer, alkanolamide 6501, any one or any two or more in alkanolamide 6502.
7. aluminium alloy anode oxide film according to claim 6 mirror-finishes liquid, it is characterised in that: the buffer is
It is borax, boric acid, glycine, hydrochloric acid, barbital sodium, any two or more in sodium hydroxide.
8. aluminium alloy anode oxide film according to claim 1 mirror-finishes liquid, it is characterised in that: preparation method are as follows:
S1: alumina powder is added in blender, pure water is then added, stirs evenly;S2: carrying out vibration filtering using nylon cloth,
Filtered filtrate is put into another blender, and keeps lasting stirring;S3: borax is added, sodium hydroxide forms
Buffer, stirring and dissolving;S4: silica solution, polyethylene glycol, organic silicon defoamer are sequentially added into filtrate again;S5: lasting stirring
Being uniformly mixed system can be obtained required polishing fluid.
9. aluminium alloy anode oxide film according to claim 1 mirror-finishes liquid, it is characterised in that: step S2: use
Nylon cloth is 500 mesh.