CN109401519B - 一种沥青路面修复材料 - Google Patents
一种沥青路面修复材料 Download PDFInfo
- Publication number
- CN109401519B CN109401519B CN201811529638.9A CN201811529638A CN109401519B CN 109401519 B CN109401519 B CN 109401519B CN 201811529638 A CN201811529638 A CN 201811529638A CN 109401519 B CN109401519 B CN 109401519B
- Authority
- CN
- China
- Prior art keywords
- parts
- prepolymer
- thermosetting
- accelerator
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种沥青路面修复材料,其属于工程材料领域,该沥青路面修复材料包括包括热固性聚合物的单体和/或热固性聚合物的预聚体20‑60份,抗氧化剂2‑8份,促进剂1‑8份,掺合料10‑30份,热塑性聚合物5‑60份,引发剂10‑40份,增强剂10‑20份,稀释剂1‑60份,集料10‑40份。本发明提供的沥青路面修复材料具有凝结速度快,30min内即可修复路面恢复交通,强度高,高密水性,耐磨性以及施工简易等优点。通过该沥青路面修复材料修复的路面抗压强度可达100MPa,湿轮磨耗值小于800 g·m‑2,负荷车轮粘附砂量浸水1d小于450 g·m‑2。
Description
技术领域
本发明涉及工程材料技术领域,特别涉及一种沥青路面修复材料。
背景技术
我国已建成的高速公路80%左右为沥青路面,受交通量迅速增长、车辆大型化、重载化及极端气候条件影响,沥青路面出现不同程度的裂缝、车辙、表面松散、坑槽等早期损坏,降低了路面使用性能,严重的甚至引起路面结构破坏。为了保持路面良好的使用性能,延长使用寿命,在路面寿命周期的各个不同阶段需要采用不同的养护维修措施。
目前,沥青路面的养护维修作业主要分为预防性养护、修复性养护、路面翻修和路面重建四类。预防性养护是在路面状况良好的情况下,通过道路检测手段,使用各项技术指标评价道路现有状况,通过科学的、有针对性的、预防性的养护技术手段,能够保持高速公路的良好使用品质,提高道路的使用寿命。因此,预防性养护是一种有计划的基于费用-效益分析的道路养护策略,能够延长路面使用寿命、改善路面使用性能以及降低路面总体养护费用。正是由于预防性养护的巨大经济和社会效益,使这一技术得到了迅速发展。
目前,广泛应用的预防性养护技术主要有混合料罩面和涂刷沥青路面防护涂料两种方式。其中,混合罩面具有密实耐久、抗滑耐磨、抗疲劳、抗高温车辙和减少低温开裂等特点,但由于造价偏高,应用范围受限。而现有技术中的沥青路面防护涂料虽然能够缓解路面的硬化脆裂程度,增强路面的防水性能,但不能改善路面的抗磨性能和强度。
发明内容
本发明的目的在于提供一种硬化后具有高强度、高耐磨和密水性的沥青路面修复材料。
本发明解决技术问题所采用的技术方案是:一种沥青路面修复材料,其特征在于,由A类组分和B类组分组成,所述A类组分按质量份数包括:
热固性聚合物的单体和/或热固性聚合物的预聚体 1-80份;
掺合料 5-40份;
所述B类组分按质量份数包括:
热塑性聚合物 1-80份;
所述热固性聚合物的单体和/或热固性聚合物的预聚体聚合得到热固性聚合物;所述热固性聚合物的预聚体包含热固性聚氨酯预聚体、热固性酚醛树脂预聚体、不饱和聚酯预聚体、呋喃树脂预聚体、液体聚硫橡胶预聚体、环氧树脂预聚体、聚脲预聚体、热固性三聚氰胺甲醛树脂、热固性丙烯酸树脂中的一种或多种;
所述热固性聚合物的单体是具可反应性的单官能单体、双官能单体、三官能单体和多官能单体中的一种或多种;优选为含有多官能丙烯酸系单体(如三羟甲基丙烷三丙烯酸酯)或其他多官能烯类单体(如二乙烯基苯)中的一种或多种。
所述热塑性聚合物包含天然橡胶、丁苯橡胶、丁腈橡胶、丁二烯橡胶、乙丙橡胶、氯丁橡胶、苯乙烯-丁二烯热塑性弹性体、热塑性聚氨酯弹性体、聚丙二醇以及道路沥青中的一种或多种。
该方案配制的沥青路面修复材料仅由热固性聚合物的单体和/或热固性聚合物的预聚体、掺合料和热塑性聚合物三种组份组成,得到的路面修复材料涂层较薄,用于路面的养护及快速修复损伤较小的路面。
对于损坏严重,需要高强度和耐磨性修复材料的路面,本发明提供以下技术方案的沥青路面修复材料:
一种沥青路面修复材料,包括A类组分和B类组分,所述A类组分按质量份数包括:
热固性聚合物的单体和/或热固性聚合物的预聚体 20-60份;
抗氧化剂 2-8份;
促进剂 1-8份;
掺合料 10-30份;
B类组分按质量份数包括:
热塑性聚合物 5-60份;
引发剂 10-40份;
增强剂 10-20份;
稀释剂 1-60份;
集料 10-40份。
通过该质量配比得到的沥青路面修复材料厚度较厚,具有更高的强度,更好的密水性和耐磨性。
所述热固性聚合物的单体和/或热固性聚合物的预聚体聚合得到热固性聚合物,所述热固性聚合物包含热固性酚醛树脂、热固性脲醛树脂、热固性丙烯酸树脂、热固性环氧树脂、热固性聚氨酯、热固性不饱和聚酯、热固性聚脲和热固性可硫化橡胶中的一种或多种。
所述热固性酚醛树脂是具有热固性的松香改性酚醛树脂、醇类醚化酚醛树脂、环氧改性酚醛树脂和醇酸改性酚醛树脂中的一种或多种;
所述热固性氨基树脂是具有的热固性的脲醛树脂、三聚氰胺甲醛树脂、聚酰胺多胺环氧氯丙烷中的一种或多种;
所述热固性丙烯酸树脂是含有活性羟基官能团或者羧基官能团的丙烯酸树脂中的的一种或多种,其能够与氨基树脂通过烷氧基反应固化或者与多异氰酸酯交联;所述含有活性羟基官能团或者羧基官能团的丙烯酸树脂可具体为丙烯羟乙酯、甲基丙烯羟乙酯、丙烯酸羟丙酯、甲基丙烯酸羟丙酯、丙烯酸、甲基丙烯酸中的一种或多种。
所述热固性环氧树脂是具有的热固性的缩水甘油醚类环氧树脂、缩水甘油酯类环氧树脂、缩水甘油胺类环氧树脂、脂肪族环氧树脂、脂环族环氧树脂、双酚A环氧树脂、双酚S环氧树脂、双酚S环氧乙烯基树脂和双酚S环硫树脂中的一种或多种;
所述热固性聚氨酯是由脂肪族异氰酸酯、脂环族异氰酸酯、芳香族异氰酸酯、聚酯多元醇和聚醚多元醇中的一种或多种聚合得到。
所述热固性不饱和聚酯是具有的热固性的邻苯型不饱和聚酯、间苯型不饱和聚酯、对苯型不饱和聚酯、双酚A型不饱和聚酯和乙烯基酯型不饱和聚酯中的一种或多种;
所述热固性聚脲是由异佛尔酮二异氰酸酯、二苯基甲烷二异氰酸酯或甲苯二异氰酸酯与乙二胺、间苯二胺、二氨基二苯甲烷或端氨基聚醚聚合得到的热固性聚脲中的一种或多种;
所述热固性可硫化橡胶是具有热固性的天然橡胶、丁苯橡胶、异戊橡胶、顺丁橡胶、三元乙丙橡胶、丁基橡胶、氯丁橡胶、羧基橡胶、丁腈橡胶、氯磺化聚乙烯橡胶、硅橡胶、氟橡胶和聚硫橡胶中的一种或多种。
所述热塑性聚合物包含具有热塑性的聚甲基丙烯酸、聚甲基丙烯酸甲酯、ABS树脂、丁腈橡胶、聚硫橡胶、丁苯橡胶、天然橡胶、顺丁橡胶、异戊橡胶、乙丙橡胶、聚乙烯醇、聚乙烯醇缩丁醛、聚乙烯醇缩甲醛、硝化纤维素、醋酸纤维素、三醋酸纤维素、羟甲基纤维素、羟丙基纤维素、聚氯乙烯、聚偏氟乙烯、聚丙烯腈、聚苯乙烯、聚芳砜、聚醚砜、聚芳酰胺、聚苯醚、聚苯硫醚、芳香聚酰胺、芳香聚酰胺肼、聚苯砜—对苯二甲酰、聚醚酰亚胺、聚醚砜酮、聚苯并咪唑酮、聚苯并咪唑、聚醚酮、聚醚醚酮、聚哌嗪酰胺、聚氨酯、聚碳酸酯、聚对苯二甲酸乙二醇酯、聚甲醛、苯乙烯类热塑性弹性体、嵌段聚醚酰胺弹性体、聚烯烃热塑性弹性体、聚氨酯热塑性弹性体、聚氯乙烯热塑性弹性体、聚酯热塑性弹性体、二烯类热塑性弹性体和沥青中的一种或多种。
所述掺合料包含石英粉、粉煤灰、高炉矿渣粉、石灰石粉、滑石粉、橡胶粉、钢渣粉和尾矿砂中的一种或多种
所述掺合料的粒径在80μm以下。
所述引发剂包含过氧化物类引发剂、偶氮类引发剂、过硫酸盐类引发剂、脂肪族多胺类引发剂、芳香族多胺类引发剂、咪唑类引发剂、改性胺类引发剂、有机酸酐类引发剂和三氟化硼类引发剂、橡胶硫化剂中的一种或多种。
所述增强剂包含炭黑、白炭黑、碳纤维、碳纳米管、石墨烯、碳酸钙粉、陶土、滑石、硅藻土、云母粉、石棉、金属粉、金属氧化物、热固性树脂中空球、木粉、粉末纤维素、硅烷偶联剂中的一种或多种。
所述集料的粒径为80μm以上。
所述抗氧化剂包含胺类抗氧化剂、酚类抗氧化剂、硫代酯、亚磷酸酯和金属离子钝化剂中的一种或多种。
本发明提供的沥青路面修复材料,包括热固性聚合物的单体和/或热固性聚合物的预聚体,其质量份数为1-80份,优选为20-60份,更优选为30-50份。本发明对热固性聚合物的单体和/或热固性聚合物的预聚体的种类没有特殊的限定,采用本领域技术人员熟知的热固性聚合物的单体和/或热固性聚合物的预聚体能够聚合得到热固性聚合物即可。热固性聚合物优选包含热固性酚醛树脂及其衍生物、热固性脲醛树脂及其衍生物、热固性丙烯酸树脂及其衍生物、热固性环氧树脂及其衍生物、热固性聚氨酯及其衍生物、不饱和聚酯及其衍生物、热固性聚脲及其衍生物和可硫化橡胶及其衍生物中的一种或多种。热固性聚合物的单体和/或热固性聚合物的预聚体优选为能够聚合得到上述热固性聚合物中的任意一种或多种的单体和/或预聚体。
在本发明中,所述热固性酚醛树脂及其衍生物优选包含松香改性酚醛树脂、醇类醚化酚醛树脂、环氧改性酚醛树脂和醇酸改性酚醛树脂中的一种或多种。热固性酚醛树脂的单体优选是酚类单体和醛类单体;酚类单体优选是苯酚、甲酚、二甲酚、烷基酚和双酚A中的一种或多种;醛类单体优选是甲醛、乙二醛、丙醛、丙烯醛、戊醛和苯甲醛中的一种或多种。热固性酚醛树脂衍生物的单体优选是双酚S、双酚C、二氮杂萘酮(DHPZ)、4-氯苯酚、乙酰间苯三酚、环糊精醛、三卤丁醛、丙烯醛和三氯乙醛中的一种或多种。
在本发明中,所述热固性氨基树脂及其衍生物,是由含有氨基的化合物与甲醛经缩聚而成的树脂的总称,包含但不局限于脲醛树脂(UF)、三聚氰胺甲醛树脂(MF)、聚酰胺多胺环氧氯丙烷(PAE)中的一种或多种。热固性氨基树脂及其衍生物的氨类单体优选是含有氨基并能够与甲醛和醇类共聚的化合物,更优选地,是尿素、硫脲、三聚氰胺、磺甲基化三聚氰胺、低级醇醚化三聚氰胺(甲醇醚化三聚氰胺、丁醇醚化三聚氰胺等)、醇胺醚化三聚氰胺、苯代三聚氰胺、聚氨酯、双氰胺、磺酰胺和苯胺中的一种或多种。热固性氨基树脂及其衍生物的醛类单体优选是甲醛、丙醛、乙二醛、糠醛和苯甲醛中的一种或多种。
在本发明中,所述热固性丙烯酸树脂及其衍生物是具有热固性的聚甲基丙烯酸甲酯、聚三羟甲基丙烷三丙烯酸酯和聚甲基丙烯酸中的一种或多种。热固性丙烯酸树脂及其衍生物的单体优选是丙烯酸酯和/或其衍生物,最优选为烷基丙烯酸酯。热固性丙烯酸树脂的单体可具体为甲基丙烯酸甲酯、三羟甲基丙烷三丙烯酸酯和甲基丙烯酸中的一种或多种。
在本发明中,所述热固性环氧树脂衍生物优选包含缩水甘油醚类环氧树脂、缩水甘油酯类环氧树脂、缩水甘油胺类环氧树脂、脂肪族环氧树脂、脂环族环氧树脂、双酚S环氧树脂、双酚S环氧乙烯基树脂和双酚S环硫树脂中的一种或多种。热固性环氧树脂的单体优选为但不局限于双酚A、双酚S、间苯二酚、羟甲基双酚A、氢化双酚A、环氧氯丙烷、环氧乙烷和环氧丙烷中的至少两种。热固性环氧树脂的单体可具体为双酚A和环氧氯丙烷。
在本发明中,所述热固性聚氨酯树脂的单体优选为脂肪族异氰酸酯、脂环族异氰酸酯、芳香族异氰酸酯、聚酯多元醇和聚醚多元醇(聚醚的预聚体)中的一种或多种。脂肪族异氰酸酯优选是六亚甲基二异氰酸酯(HDI),脂环族异氰酸酯优选是异佛尔酮二异氰酸酯(IPDI)和/或甲基环己基二异氰酸酯(HTDI);芳香族异氰酸酯优选为甲苯二异氰酸酯(TDI)、二苯基甲烷二异氰酸酯(MDI)、聚甲撑聚苯基氰酸酯(PAPI)、二苯基甲烷二异氰酸酯(PPDI)、1,5-萘二异氰酸酯(NDI)中的一种或多种;聚酯多元醇优选为脂肪链聚酯多元醇、己内酯型聚酯多元醇和聚碳酸酯型聚酯多元醇中的一种或多种;聚醚多元醇优选为环氧丙烷聚醚多元醇、四氢呋喃聚醚多元醇、端氨基聚醚中的一种或多种。
在本发明中,所述不饱和聚酯优选包含邻苯型不饱和聚酯、间苯型不饱和聚酯、对苯型不饱和聚酯、双酚A型不饱和聚酯和乙烯基酯型不饱和聚酯中的一种或多种。热固性不饱和聚酯的单体优选为但不局限于顺丁烯二酸(马来酸)、顺丁烯二酸酐(马来酸酐)、反丁烯二酸、氯化马来酸、衣康酸、柠康酸、乙二醇、丙二醇、一缩二乙二醇、一缩二丙二醇和新戊二醇中的多种。
在本发明中,所述热固性聚脲及其衍生物的单体优选为但不局限于异佛尔酮二异氰酸酯(IPDI)、二苯基甲烷二异氰酸酯(MDI)、甲苯二异氰酸酯(TDI)、乙二胺、间苯二胺、二氨基二苯甲烷和端氨基聚醚中的多种。
在本发明中,所述可硫化橡胶及其衍生物优选为但不局限于具有热固性的天然橡胶、丁苯橡胶、异戊橡胶、顺丁橡胶、三元乙丙橡胶、丁基橡胶、氯丁橡胶、羧基橡胶(丙烯酸橡胶)、丁腈橡胶、氯磺化聚乙烯橡胶、硅橡胶、氟橡胶和聚硫橡胶中的一种或多种。
在本发明中,所述热固性聚合物的预聚体包含热固性聚氨酯预聚体、热固性酚醛树脂预聚体、不饱和聚酯预聚体、呋喃树脂预聚体、液体聚硫橡胶预聚体、环氧树脂预聚体、聚脲预聚体、热固性三聚氰胺甲醛树脂、热固性丙烯酸树脂中的一种或多种。优选地,热固性聚合物的预聚体可具体为不饱和聚酯预聚体(191型、196型)、呋喃树脂预聚体、液体聚硫橡胶预聚体(JLY-115、JYL-121、JYL-124、JLY-125、JLY-155、JYL-1225)、环氧树脂预聚体(E02、E12、E20、E21、E31、E42、E44、 E51)、MDI异氰酸酯预聚体、IPDI异氰酸酯预聚体、TDI异氰酸酯预聚体、聚脲预聚体、氰基丙烯酸酯、三聚氰胺甲醛树脂、热固性酚醛树脂预聚体中的一种或几种。
本发明提供的沥青路面修复材料包括抗氧化剂,其质量份数为0-10份,优选为2-8份,更优选为4-6份。优选地,该抗氧化剂包含胺类抗氧化剂、酚类抗氧化剂、硫代酯、亚磷酸酯和金属离子钝化剂中的一种或多种。该抗氧化剂能够阻止氧气不良影响,能帮助捕获并中和自由基。
在本发明中,所述胺类抗氧化剂优选包含但不局限于N,N-二仲丁基对苯二胺、4,4一二甲氧基二苯胺、二辛基对苯二胺和二异丁基对苯二胺中的一种或多种。酚类抗氧化剂优选包含对苯二酚、2,4-二甲基-6-叔丁基苯酚、叔丁基对苯二酚、丁基羟基茴香醚、2,6-二叔丁基对甲苯酚和2,5-二特戊基对苯二酚中的一种或多种。硫代酯优选包含棓酸丙酯、硫代二丙酸月桂醇酯和硫代二丙酸十八碳醇酯中的一种或多种。亚磷酸酯优选为亚磷酸二苯基辛己酯和/或亚磷酸三酯。金属离子钝化剂优选包含三聚氰胺、丙苯***、8-羟基喹啉和腙中的一种或多种。
本发明提供的沥青路面修复材料包括促进剂,其质量份数为0-10份,优选为1-8份,更优选为2-5份。促进剂优选包含环氧树脂用促进剂、聚氨酯用促进剂、酚醛树脂用促进剂、不饱和聚酯树脂用促进剂、丙烯酸树脂用促进剂、厌氧胶用促进剂、橡胶及橡胶型胶黏剂用促进剂中的一种或多种。优选地,促进剂的种类根据热固性聚合物的单体和热固性聚合物的预聚体的种类进行选择。促进剂可以催化热固性聚合物的单体和热固性聚合物的预聚体的交联聚合反应,提高反应速率,缩短沥青路面修复材料的固化时间。
本发明对环氧树脂用促进剂的种类没有特殊的限定,采用本领域技术人员熟知的环氧树脂用促进剂即可。优选地,环氧树脂用促进剂包含但不局限于三乙醇胺、二甲基苯胺、三-2-乙基己酸盐、咪唑、咪唑盐类和过渡金属有机化合物中的一种或多种。过渡金属有机化合物优选为过渡金属羧酸盐,更优选地,包含锰、钴、钙和锌的金属羧酸盐中的一种或多种。
本发明对所述聚氨酯用促进剂的种类没有特殊的限定,采用本领域技术人员熟知的聚氨酯用促进剂即可。优选地,聚氨酯用促进剂包含但不局限于N,N-二甲基环己胺、三乙胺、N,N-二甲基苄胺、N-甲基吗啉、三乙醇胺、二乙基甲苯二胺、N,N’-二甲基吡啶和二丁基锡二月桂酸酯中的一种或多种。
本发明对酚醛树脂用促进剂的种类没有特殊的限定,采用本领域技术人员熟知的酚醛树脂用促进剂即可。优选地,酚醛树脂用促进剂包含但不局限于氢氧化钠、氢氧化钾、氢氧化锂、氨水、三乙胺、氢氧化钡、氧化镁、醋酸锌、氯化亚锡、三氯化铁和对氯代苯甲酸中的一种或多种。
本发明对不饱和聚酯树脂用促进剂的种类没有特殊的限定,采用本领域技术人员熟知的不饱和聚酯树脂用促进剂即可。优选地,不饱和聚酯树脂用促进剂包含环烷酸钴、异辛酸钴、二甲基苯胺、二乙基苯胺、十二烷基硫醇和磷酸钒中的一种或多种。
本发明对丙烯酸树脂用促进剂的种类没有特殊的限定,采用本领域技术人员熟知的丙烯酸树脂用促进剂即可。优选地,丙烯酸树脂用促进剂包含但不局限于异锌酸矾、四甲基硫脲、乙酰丙酮钒、乙酰丙酮、三苯基膦、正丁醛-苯胺缩合物和苄基二甲胺中的一种或多种。
本发明对厌氧胶用促进剂的种类没有特殊的限定,采用本领域技术人员熟知的厌氧胶用促进剂即可。优选地,厌氧胶用促进剂包含但不局限于N,N-二甲基对甲基苯胺、三乙胺、氢喹啉、8-羟基喹啉、糖精、二茂铁和三乙酰丙酮铝中的一种或多种。
本发明对所述橡胶及橡胶型胶黏剂用促进剂的种类没有特殊的限定,采用本领域技术人员熟知的橡胶及橡胶型胶黏剂用促进剂即可。优选地,橡胶及橡胶型胶黏剂用促进剂包含但不局限于二氧化锰、二氧化铅、氧化镁、过氧化锌、过氧化二苯甲酰、过氧化二异丙苯、过氧化二叔丁烷、2,5-二甲基-2,5-双(叔丁基过氧基)己烷(双二五硫化剂)、二苯胍、2-硫醇基苯并噻唑、二硫化四甲基秋兰姆和二甲基二硫代氨基甲酸锌、己二胺、三乙撑四胺、二肉桂叉己二胺、双呋喃甲叉己二胺、烷基酚醛树脂、卤化羟甲基酚醛树脂、醌类(对醌而肟)、马来酰亚胺类(双马来酰亚胺)、异氰酸酯类中的一种或多种。
本发明提供的沥青路面修复材料包括掺合料,其质量份数为5-40份,优选为10-30份,更优选为15-25份。优选地,掺合料包含滑石粉、石英粉、粉煤灰、高炉矿渣粉、石灰石粉、橡胶粉、钢渣粉和尾矿砂中的一种或多种。掺合料的粒径优选为80μm以下,更优选为10-60μm,最优选为30-40μm。掺合料可以提高沥青路面修复材料的表面磨耗抗蚀性能。
本发明提供的沥青路面修复材料包括热塑性聚合物,其质量份数为1-80份,优选为5-60份,更优选为30-50份。热塑性聚合物优选包含具有热塑性的聚甲基丙烯酸、聚甲基丙烯酸甲酯、ABS树脂、丁腈橡胶、聚硫橡胶、丁苯橡胶、天然橡胶、顺丁橡胶、异戊橡胶、乙丙橡胶、明胶、聚乙烯醇、聚乙烯醇缩丁醛、聚乙烯醇缩甲醛、硝化纤维素、醋酸纤维素、三醋酸纤维素、羟甲基纤维素、羟丙基纤维素、聚氯乙烯、聚偏氟乙烯、聚丙烯腈、聚苯乙烯、聚(芳)砜、聚醚砜、聚(芳)酰胺、聚苯醚、聚苯硫醚、芳香聚酰胺、芳香聚酰胺肼、聚苯砜—对苯二甲酰、聚醚酰亚胺、聚醚砜酮、聚苯并咪唑酮、聚苯并咪唑、聚醚酮、聚醚醚酮、聚哌嗪酰胺、聚氨酯热塑性弹性体、聚酯(醇酸树脂)、聚碳酸酯、聚对苯二甲酸乙二醇酯、聚甲醛、苯乙烯类热塑性弹性体、嵌段聚醚酰胺弹性体、聚烯烃热塑性弹性体、聚氨酯热塑性弹性体、聚氯乙烯热塑性弹性体、聚酯热塑性弹性体、二烯类热塑性弹性体和沥青中的一种或多种。热塑性聚合物可具体为ABS树脂和丁腈橡胶的组合,或聚硫橡胶和聚乙烯醇缩丁醛的组合。ABS树脂和丁腈橡胶的质量比优选为1:0.5-1:3,更优选为1:1-1:2;聚硫橡胶和聚乙烯醇缩丁醛的质量比优选为1:0.4-1:1,更优选为1:0.6-1:0.8。热塑性聚合物具有受热软化、冷却硬化的性能,能够提高固化后修复材料的柔韧性。
本发明提供的沥青路面修复材料包括引发剂,其质量份数为0-60份,优选为10-40份,更优选为20-30份。优选地,引发剂包含过氧化物类引发剂、偶氮类引发剂、过硫酸盐类引发剂、脂肪族多胺类引发剂、芳香族多胺类引发剂、咪唑类引发剂、改性胺类引发剂、有机酸酐类引发剂、三氟化硼及其衍生物类引发剂和橡胶硫化剂中的一种或多种。在本发明中,引发剂用于引发热固性聚合物的单体和/或热固性聚合物的预聚体的交联聚合反应,同时具有固化剂的作用,本领域中也将其称为固化剂,可调节沥青路面修复材料的固化时间。
热固性聚合物及其衍生物特别是本领域所熟知的多组分热固性聚合物的预聚体,已经包含热固性聚合物固化所需的组分,如热固性环氧树脂预聚体中含有的双酚A型环氧树脂和聚酰胺环氧树脂;又如热固性聚氨酯预聚体中的TDI异氰酸酯预聚体及聚醚预聚体均属于固化剂的要求范畴,在此对固化剂不做特别说明。
本发明对过氧化物类引发剂没有特殊的限定,采用本领域技术人员熟知的过氧化物类引发剂即可。优选地,过氧化物类引发剂是无机过氧化物和有机过氧化物中的一种或多种。无机过氧化物优选为过氧化氢、过硫酸钾、过硫酸铵等。有机过氧化物优选为但不局限于异丙苯过氧化氢、过氧化苯甲酰、过氧化苯甲酰叔丁酯、过氧化二苯甲酮、过氧化甲乙酮和过氧化环己酮中的一种或多种。
本发明对偶氮类引发剂没有特殊的限定,采用本领域技术人员熟知的偶氮类引发剂即可。优选地,偶氮类引发剂是偶氮二异丁腈和/或偶氮二异庚腈。
本发明对所述过硫酸盐类引发剂没有特殊的限定,采用本领域技术人员熟知的过硫酸盐即可。过硫酸盐类引发剂优选为过硫酸钠、过硫酸钾和过硫酸铵中的一种或多种。
本发明对所述脂肪族多胺类引发剂没有特殊的限定,采用本领域技术人员熟知的脂肪族多胺即可。脂肪族多胺类引发剂优选为但不局限于乙二胺、己二胺、三甲基己二胺、二乙烯三胺、三乙烯四胺、六亚甲基四胺、三亚乙基四胺、三乙烯二胺、四乙烯五胺、二丙烯三胺和三甲基六亚甲基二胺中的一种或多种。
本发明对芳香族多胺类引发剂没有特殊的限定,采用本领域技术人员熟知的芳香族多胺即可。芳香族多胺类引发剂优选为但不局限于间苯二胺、间苯二甲胺、二氨基二苯基甲烷、间氨基甲胺和联苯胺中的一种或多种。
本发明对所述咪唑类引发剂的种类没有特殊的限定,采用本领域技术人员熟知的咪唑类化合物即可。咪唑类引发剂优选为但不局限于2-乙基-4-甲基咪唑、l,3二氮杂环戊二烯、2-甲基咪唑和2-乙基咪唑中的一种或多种。
本发明对改性胺类引发剂的种类没有特殊的限定,采用本领域技术人员熟知的改性胺类化合物即可。改性胺类化合物优选为曼尼希型酚醛改性胺引发剂、环氧树脂胺加成物、缩水甘油醚胺加成物、环氧烷胺加成物和多元胺与烯双键加成改性胺引发剂中的一种或多种。
本发明对有机酸酐类引发剂的种类没有特殊的限定,采用本领域技术人员熟知的有机酸酐即可。有机酸酐类引发剂优选为但不局限于包括均苯四甲酸酐、邻苯二甲酸酐、二苯酮四羧基二酸酐和十二烷基代顺丁烯二酸酐中的一种或多种。
本发明对橡胶硫化剂的种类没有特殊的限定,采用本领域技术人员熟知的橡胶硫化剂即可。优选地,橡胶硫化剂包含但不局限于包括硫磺、氧化锌、氧化铅、二氧化锰、四氧化三铅、烷基酚醛树脂、叔丁基苯醛甲醛树脂、叔辛基苯酚甲醛树脂、二硫化四甲基秋兰姆等中的一种或多种。
本发明提供的沥青路面修复材料包括增强剂,其质量份数为0-30份,优选为10-20份,更优选为12-16份。优选地,增强剂包含但不局限于白炭黑、碳纤维、碳纳米管、石墨烯、碳酸钙粉、陶土、滑石、硅藻土、云母粉、石棉、金属粉、金属氧化物、热固性树脂中空球、木粉、粉末纤维素以及硅烷偶联剂中的一种或多种。金属粉优选为铁粉、铝粉和锌粉中的一种或多种。金属氧化物优选为氧化亚铁、三氧化二铁、氧化铝、氧化锌和氧化镁中的一种或多种。增强剂的粒径优选为80μm以下,更优选为10-60μm,最优选为30-40μm。在本发明中,增强剂可以与掺合料配合,进一步提高沥青路面修复材料的抗磨耐蚀性能。
本发明提供的沥青路面修复材料包括稀释剂,其质量份数为0-80份,优选为1-60份,更优选为20-40份。本发明对稀释剂的种类没有特殊的限定,采用本领域技术人员熟知的稀释剂即可。稀释剂优选为但不局限于二甲基硅油、丙烯酸、脂肪酸、四氢呋喃、酯类溶剂、酮类溶剂、醇类溶剂、芳香类溶剂、酰胺类溶剂和砜类溶剂中的一种或多种。稀释剂可以提高沥青路面修复材料的流平性,改善可施工性。
所述酯类溶剂优选为但不局限于乙酸乙酯、邻苯二甲酸二乙酯和邻苯二甲酸二丁酯中的一种或多种。酮类溶剂优选为但不局限于丙酮、甲乙酮、环己酮和N-甲基吡咯烷酮中的一种或多种。醇类溶剂优选为但不局限于乙醇、乙二醇和正丁醇中的一种或多种。芳香类溶剂优选为但不局限于苯、甲苯、二甲苯和苯乙烯中的一种或多种。酰胺类溶剂优选为但不局限于甲酰胺、二甲基甲酰胺和二甲基乙酰胺中的一种或多种。亚砜类溶剂优选为但不局限于二甲基亚砜和/或环丁砜。
本发明提供的沥青路面修复材料包括集料,其质量份数为0-60份,优选为10-40份,更优选为20-30份。集料的粒径优选为80μm以上,更优选为100-400μm,最优选为200-300μm。本发明对集料的种类没有特殊的限定,采用本领域技术人员熟知的集料即可。优选地,集料包含橡胶颗粒、石英砂、碎石和卵石中的一种或多种。
在本发明中,沥青路面修复材料在常温下的凝固时间优选为10min-24h,更优选为1-20h,最优选为5-10h。沥青路面修复材料固化后的密度优选为1.6-2.0g/cm3,更优选为1.7-1.9g/cm3;固化后的抗压强度10-100MPa,更优选为70-90MPa;固化后的抗弯拉强度优选为10-70MPa,更优选为20-40MPa;固化后的抗剪强度优选为20-50MPa,更优选为30-40MPa;弹性模量优选为8-15GPa,更优选为10-13GPa;固化后的泊松比优选为0.20-0.35。
本发明对沥青路面修复材料的制备方法没有特殊的限制,采用本领域技术人员熟知的制备组合物的制备方法即可。该沥青路面修复材料的制备方法优选为:将热固性聚合物的单体和/或热固性聚合物的预聚体、热塑性聚合物、掺合料、引发剂、促进剂、增强剂、稀释剂、集料和抗氧化剂混合,得到沥青路面修复材料。
在本发明中,热固性聚合物的单体和/或热固性聚合物的预聚体和引发剂需分别封装避光存储。
本发明对所述沥青路面修复材料的使用方法没有特殊的限定,采用本领域技术人员熟知的涂料涂覆方式即可。该沥青路面修复材料的涂覆方法优选为人工涂刷或机械喷涂。
在本发明的技术方案相比于现有技术具有以下优点:
本发明提供一种沥青路面修复材料,该材料仅由热固性聚合物的单体和/或热固性聚合物的预聚体、掺合料和热缩型性聚合物三种组份组成,得到的路面修复材料涂层较薄,用于路面的养护及快速修复损伤较小的路面。本发明提供另一种沥青路面修复材料,该材料包括热固性聚合物的单体和/或热固性聚合物的预聚体,掺合料,热塑性聚合物三种主要涂覆原料,热固性聚合物的单体和/或热固性聚合物的预聚体具有活性反应官能团,能够进行交联聚合反应,固化后形成不溶解、不熔融的网状分子结构的热固性聚合物,提高路面的强度。热固性聚合物的单体和/或热固性聚合物的预聚体交联聚合过程中,通过物理、化学作用将热塑性聚合物均匀的分布在热固性聚合物的网状分子结构中,形成软硬适当的聚合物层,提高了修复材料的柔韧性和密水性,掺合料均匀的混入热固性聚合物和热塑性聚合物形成的聚合物分子中,进一步提高了修复材料的表面磨耗抗蚀性能。该交联聚合反应常温下即可进行,无需额外热源,使得路面修复更加简单,方便。
在所述的沥青路面修复材料中添加引发剂,用于引发热固性聚合物的单体和/或热固性聚合物的预聚体的交联聚合反应,提高交联聚合反应的速率,引发剂同时具有固化剂的作用,进一步调节沥青路面修复材料的固化时间,缩短该沥青路面修复材料道路修复的时间。
在所述的沥青路面修复材料中添加增强剂,增强剂增强不同原料之间的粘结力,与掺合料配合进一步提高该沥青路面修复材料的抗磨耐蚀性能。
在所述的沥青路面修复材料中添加促进剂,促进剂的种类根据热固性聚合物的单体和热固性聚合物的预聚体的种类进行选择。促进剂可以催化热固性聚合物的单体和热固性聚合物的预聚体的交联聚合反应,提高反应速率,缩短沥青路面修复材料的固化时间。
在所述的沥青路面修复材料中添加抗氧化剂,该抗氧化剂能够阻止氧气不良影响,能帮助捕获并中和自由基,减少氧气对于热固性聚合物的单体和/或热固性聚合物的预聚体的活性反应官能团的破坏,增强该材料的强度。
在所述的沥青路面修复材料中添加稀释剂和集料。稀释剂可以提高沥青路面修复材料的流平性,改善可施工性。集料主要用于减小材料在固化过程中的体积变化。
本发明提供的沥青路面修复材料制备方法简单,无需加热,常温下将原料简单混合即可,克服了其它路面修复材料需要高温加热的缺点,很大程度上简化了路面的养护及修复,节省时间的同时减少了因道路修复造成的交通拥堵。
该沥青路面修复材料凝结速度快,在常温下的凝固时间为10min-24h,其固化后的密度为1.6-2.0g/cm3,抗压强度为10-100MPa,抗弯拉强度为10-70MPa,抗剪强度为20-50MPa,弹性模量为8-15GPa,泊松比0.20-0.35。该沥青路面修复材料30min内即可修复路面恢复交通,强度高、施工简易等优点。修复的路面抗压强度可达100MPa,湿轮磨耗值<800g·m-2,负荷车轮粘附砂量浸水1d<450 g·m-2。
下面结合实施例对本发明提供的沥青路面修复材料进行详细地描述,但不能将它们理解为对本发明保护范围的限定。
集料分为粗集料和细集料(或者称为粗骨料和细骨料)细集料是指粒径小于4.75mm的一般多称之为砂(限定集料的粒径为80μm以上,80μm以下的多称为粉或者泥);而大于4.75mm的称为石,一般指的是碎石或者卵石。在以下实施例中如无特殊规定的,粗集料和细集料的规格适用该规定。
实施例1:
热固性聚合物的预聚体:TDI异氰酸酯预聚体和热固性酚醛树脂预聚体;
热塑性聚合物:90#道路沥青;
引发剂:聚醚预聚体和三乙烯二胺;
促进剂:二月桂酸二丁基锡;
掺合料:橡胶粉和石英砂;
稀释剂:二甲基硅油;
材料的配制质量份数分别为:TDI异氰酸酯预聚体50份,热固性酚醛树脂预聚体10份,聚醚预聚体30份,三乙烯二胺5份,二甲基硅油6份,二月桂酸二丁基锡3份,90#道路沥青11份,橡胶粉8份,石英砂20份,根据施工需要复配碎石作为粗骨料。
为包装方便,将TDI异氰酸酯预聚体、热固性酚醛树脂预聚体和90#道路沥青混合包装作为A组分;聚醚预聚体、二甲基硅油、三乙烯二胺、二月桂酸二丁基锡混合包装作为B组分;橡胶粉和石英砂混合包装作为C组分;施工时将A、B、C三组分混合均匀后即可采用人工涂刷或机械喷涂施工。
本实施例提供的沥青路面修复材料用于路面修复时的凝结时间为30min;凝结30min的黏结力为3.0 N·m,湿轮磨耗值为512 g·m-2,负荷车轮粘附砂量浸水1d为320 g·m-2。
实施例2:
热固性聚合物的单体:甲基丙烯酸甲酯、甲基丙烯酸、三羟甲基丙烷三丙烯酸酯;
热塑性聚合物:ABS树脂和丁腈橡胶;
引发剂:异丙苯过氧化氢;
促进剂:六亚甲基四胺、异辛酸钒;
抗氧化剂:对苯二酚
掺合料:一级粉煤灰;
稀释剂:乙二醇;
材料配制的质量份数分别为:甲基丙烯酸甲酯45份,甲基丙烯酸12份,三羟甲基丙烷三丙烯酸酯5份,对苯二酚0.6份,乙二醇5份,ABS树脂7份,丁腈橡胶10份,异丙苯过氧化氢4份,六亚甲基四胺3份,异辛酸钒0.3份,一级粉煤灰8份,根据施工需要复配碎石作为粗骨料。
为包装方便,将甲基丙烯酸甲酯、甲基丙烯酸、三羟甲基丙烷三丙烯酸酯、对苯二酚、乙二醇、ABS树脂、异丙苯过氧化氢混合包装作为A1组分;对苯二酚、丁腈橡胶、六亚甲基四胺、异辛酸钒、粉煤灰混合包装作为B1组份;使用时将A1、B1组份混合均匀后即可采用人工涂刷或机械喷涂施工。
本实施例提供的沥青路面修复材料用于路面修复时的凝结时间20min;凝结30min的黏结力为3.5 N·m,湿轮磨耗值为470 g·m-2,负荷车轮粘附砂量浸水1d 为358 g·m-2。
实施例3:
热固性聚合物的预聚体:热固性环氧树脂预聚体(双酚A型树脂601);
热塑性聚合物:聚硫橡胶、聚乙烯醇缩丁醛;
引发剂:聚酰胺环氧树脂引发剂;
促进剂:三乙醇胺;
抗氧化剂:亚磷酸酯;
掺合料:矿粉S95;
稀释剂:甲苯、丙酮;
材料配制的质量份数分别为:热固性环氧树脂预聚体(双酚A型树脂601) 35份,聚酰胺环氧树脂引发剂14份,亚磷酸酯1份,甲苯6份,丙酮6份,聚硫橡胶10份,聚乙烯醇缩丁醛6份,三乙醇胺4份,矿粉S95 16份,根据施工需要复配碎石作为粗骨料。
为包装方便,将热固性环氧树脂预聚体(双酚A型树脂601)、聚硫橡胶、三乙醇胺、甲苯、混合包装作为A2组分;聚酰胺环氧树脂固化剂、亚磷酸酯、聚乙烯醇缩丁醛、丙酮、矿粉S95混合包装作为B2组份;使用时将A2、B2组份混合均匀后即可采用人工涂刷或机械喷涂施工。
本实施例提供的沥青路面修复材料用于路面修复时的凝结时间25min;凝结30min的黏结力为4.6 N·m,湿轮磨耗值为437 g·m-2,负荷车轮粘附砂量浸水1d 为321 g·m-2。
实施例4:
热固性聚合物的预聚体:三聚氰胺甲醛树脂;
热塑性聚合物:苯乙烯-丁二烯热塑性弹性体;
引发剂:三亚乙基四胺;
促进剂:过氧化二异丙苯;
抗氧化剂:二丁基羟基甲苯;
增强剂:滑石粉;
稀释剂:邻苯二甲酸二甲酯;
材料的配制质量份数分别为:三聚氰胺甲醛树脂53.5份,苯乙烯-丁二烯热塑性弹性体15份,二丁基羟基甲苯0.5份,邻苯二甲酸二甲酯6份,三亚乙基四胺12份,过氧化二异丙苯3份,滑石粉10份,根据施工需要复配碎石作为粗骨料。
为包装方便,将三聚氰胺甲醛树脂、二丁基羟基甲苯、过氧化二异丙苯混合包装作为A3组分;苯乙烯-丁二烯热塑性弹性体、邻苯二甲酸二甲酯、三亚乙基四胺、滑石粉混合包装作为B3组份;使用时将A3、B3乙组份混合均匀后即可采用人工涂刷或机械喷涂施工。
本实施例提供的沥青路面修复材料用于路面修复时的凝结时间20min;凝结30min的黏结力为3.1 N·m,湿轮磨耗值为572 g·m-2,负荷车轮粘附砂量浸水1d 为307 g·m-2。
实施例5:
热固性聚合物的预聚体和热固性聚合物单体:热固性环氧树脂预聚体E51和氰基丙烯酸酯;
热塑性聚合物:热塑性聚氨酯(黑料);
掺合料:石英粉;
增强剂:无;
引发剂:无;
促进剂:无;
抗氧化剂:无;
稀释剂:无;
材料的配制质量份数分别为:热固性环氧树脂预聚体E51为40份,氰基丙烯酸酯10份,聚氨酯预聚体(黑料)40份,石英粉10份,根据施工需要复配碎石作为粗骨料。
为包装方便将热固性环氧树脂预聚体(E51)和氰基丙烯酸酯混合包装作为A4组分;聚氨酯预聚体(黑料)40粉、石英粉混合包装作为B4组份;使用时将A4、B4组份混合均匀后即可采用人工涂刷或机械喷涂施工。
本实施例提供的沥青路面修复材料用于路面修复时的凝结时间25min;凝结30min的黏结力为2.7 N·m,湿轮磨耗值为637 g·m-2,负荷车轮粘附砂量浸水1d 为403 g·m-2。
实施例6:
热固性聚合物的预聚体:MDI异氰酸酯预聚体;
热塑性聚合物:聚氯乙烯;
引发剂:聚醚多元醇(N220)和端胺基聚醚(Jefamine T-5000)
促进剂:二乙基甲苯二胺;
抗氧化剂:N-苯基-2-萘胺;
掺合料:石灰石粉;
稀释剂:乙酸乙酯;
材料的配制质量份数分别为:MDI异氰酸酯预聚体44份,聚氯乙烯8份;乙酸乙酯12份,N-苯基-2-萘胺1份,聚醚多元醇(N220)为15份,二乙基甲苯二胺2份,端胺基聚醚(Jefamine T-5000) 10份,石灰石粉8份,根据施工需要复配碎石作为粗骨料。
为包装方便,将MDI异氰酸酯预聚体、石灰石粉混合包装作为A5组分;将聚氯乙烯于乙酸乙酯中溶解后与对苯二酚、聚醚多元醇N220、端胺基聚醚、二乙基甲苯二胺混合包装作为B5组份;使用时将A5、B5组份混合均匀后即可采用人工涂刷或机械喷涂施工。
本实施例提供的沥青路面修复材料用于路面修复时的凝结时间20min;凝结30min的黏结力为3.7 N·m,湿轮磨耗值为434 g·m-2;负荷车轮粘附砂量浸水1d 为327 g·m-2。
实施例7:
热固性聚合物的预聚体:液体聚硫橡胶预聚体(JYL-124)和环氧树脂预聚体(E44);
热塑性聚合物:聚丙烯腈;
引发剂:二氧化锰;
促进剂:三乙烯四胺;
抗氧化剂:叔丁基对苯二酚;
增强剂:白炭黑;
稀释剂:二甲基亚砜;
材料的配制质量份数分别为:液体聚硫橡胶预聚体(JYL-124)为50份,聚丙烯腈6份;二甲基亚砜12份,叔丁基对苯二酚1份,环氧树脂预聚体(E44)9份,三乙烯四胺4份,二氧化锰6份,白炭黑12份,根据施工需要复配碎石作为粗骨料。
为包装方便,将液体聚硫橡胶和三乙烯四胺混合包装作为A6组分;将聚丙烯腈溶于二甲基亚砜中溶解后与叔丁基对苯二酚、环氧树脂、二氧化锰、白炭黑混合包装作为B6组份;使用时将A6、B6组份混合均匀后即可采用人工涂刷或机械喷涂施工。
本实施例提供的沥青路面修复材料用于路面修复时的凝结时间25min;凝结30min的黏结力为3.4 N·m,湿轮磨耗值为534 g·m-2,负荷车轮粘附砂量浸水1d 为348 g·m-2。
实施例8:
热固性聚合物的预聚体:不饱和聚酯预聚体(191型)和呋喃树脂预聚体
热塑性聚合物:聚醚砜;
引发剂:过氧化苯甲酰;
促进剂:N,N-二甲基苯胺;
抗氧化剂:丁基羟基茴香醚;
增强剂:云母粉;
稀释剂:四氢呋喃;
材料的配制质量份数分别为:不饱和聚酯预聚体(191型)为50份,呋喃树脂预聚体20份,聚醚砜5份,四氢呋喃8份,过氧化苯甲酰 3份,N,N-二甲基苯胺1.4份,丁基羟基茴香醚0.6份,云母粉15份,根据施工需要复配碎石作为粗骨料。
将不饱和聚酯(191型)和N,N-二甲基苯胺混合包装作为A7组分;将聚醚砜溶于四氢呋喃中溶解后与过氧化苯甲酰、呋喃树脂、丁基羟基茴香醚、云母粉混合包装作为B7组份;使用时将A7、B7组份混合均匀后即可采用人工涂刷或机械喷涂施工。
本实施例提供的沥青路面修复材料用于路面修复时的凝结时间25min;凝结30min的黏结力3.8 N·m,湿轮磨耗值为324 g·m-2,负荷车轮粘附砂量浸水1d 为243 g·m-2。
实施例9:
热固性聚合物的预聚体:双酚S双丙烯基醚、环糊精醛和IPDI异氰酸酯预聚体
热塑性聚合物:硝化纤维素;
掺合料:高炉矿渣粉;
引发剂:过氧化甲乙酮;
促进剂:二月桂酸二丁基锡;
抗氧化剂:二辛基对苯二胺;
增强剂:碳酸钙粉;
稀释剂:苯乙烯;
集料:100μm的碎石和卵石;
材料的配制质量份数分别为:双酚S双丙烯基醚20份,环糊精醛17.5份,IPDI异氰酸酯预聚体25份,硝化纤维素20份,苯乙烯6份,过氧化甲乙酮5份,二辛基对苯二胺2.3份,碳酸钙粉12份,高炉矿渣粉15份,100μm碎石粉10份,100μm卵石粉10份,根据施工需要复配碎石骨料作为粗骨料。
材料的配制过程和喷涂方法参照实施例8。
本实施例提供的沥青路面修复材料用于路面修复时的凝结时间25min;凝结30min的黏结力3.2 N·m,湿轮磨耗值为618g·m-2,负荷车轮粘附砂量浸水1d 为357g·m-2。
实施例10:
热固性聚合物的预聚体:糠醛、甲醇醚化三聚氰胺
热塑性聚合物:聚醚酮;
掺合料:滑石粉
引发剂:对甲苯磺酸;
促进剂:磷酸正丁酯;
抗氧化剂:叔丁基对苯二酚;
增强剂:硅藻土和氧化镁粉末;
稀释剂:二甲基乙酰胺;
集料:100μm的石英砂;
材料的配制质量份数分别为:糠醛为20份,甲醇醚化三聚氰胺30份,聚醚酮10份,二甲基乙酰胺10份,对甲苯磺酸6份,磷酸正丁酯1份,叔丁基对苯二酚1份,滑石粉20份,硅藻土5份,氧化镁粉末5份,100μm的石英砂10份,根据施工需要复配碎石作为粗骨料。
材料的配制过程和喷涂方法参照实施例8。
本实施例提供的沥青路面修复材料用于路面修复时的凝结时间25min;凝结30min的黏结力3.9N·m,湿轮磨耗值为512 g·m-2,负荷车轮粘附砂量浸水1d 为379g·m-2。
实施例11:
热固性聚合物的预聚体:三羟甲基丙烷三丙烯酸酯和聚脲预聚体
热塑性聚合物:聚甲基丙烯酸甲酯;
掺合料:钢渣粉;
引发剂:过氧化苯甲酰;
促进剂:辛酸亚锡;
抗氧化剂:硫代二丙酸月桂醇酯;
增强剂:石墨烯;
稀释剂:四氢呋喃;
集料:200μm的橡胶颗粒;
材料的配制质量份数分别为:三羟甲基丙烷三丙烯酸酯为40份,聚脲预聚体20份,聚甲基丙烯酸甲酯30份,四氢呋喃20份,过氧化苯甲酰2.5份,辛酸亚锡0.5份,硫代二丙酸月桂醇酯2份,钢渣粉30份,石墨烯10份,200μm的橡胶颗粒30份,根据施工需要复配碎石作为粗骨料。
材料的配制过程和喷涂方法参照实施例8。
本实施例提供的沥青路面修复材料用于路面修复时的凝结时间25min;凝结30min的黏结力3.4N·m,湿轮磨耗值为417g·m-2,负荷车轮粘附砂量浸水1d 为 347 g·m-2。
实施例12:
热固性聚合物的预聚体:环氧树脂预聚体E42和IPDI异氰酸酯预聚体
热塑性聚合物:芳香聚酰胺肼;
掺合料:石英粉;
引发剂:二丙烯三胺;
促进剂:过氧化锌;
抗氧化剂:亚磷酸二苯基辛己酯;
增强剂:白炭黑;
稀释剂:邻苯二甲酸二丁酯;
集料:300μm的碎石;
材料的配制质量份数分别为:环氧树脂预聚体E42为25份,IPDI异氰酸酯预聚体25份,芳香聚酰胺肼35份,邻苯二甲酸二丁酯35份,二丙烯三胺10份,过氧化锌8份,亚磷酸二苯基辛己酯2份,石英粉28份,白炭黑13.5份,300μm的碎石10份,根据施工需要复配碎石作为粗骨料。
材料的配制过程和喷涂方法参照实施例8。
本实施例提供的沥青路面修复材料用于路面修复时的凝结时间25min;凝结30min的黏结力3.8 N·m,湿轮磨耗值为346 g·m-2,负荷车轮粘附砂量浸水1d 为413 g·m-2。
实施例13:
热固性聚合物的预聚体:六亚甲基二异氰酸酯(HDI)预聚体和二苯基甲烷二异氰酸酯(MDI)预聚体
热塑性聚合物:聚烯烃热缩性弹性体;
掺合料:石灰石粉;
引发剂:端氨基聚醚;
促进剂:氢氧化钡;
抗氧化剂:二辛基对苯二胺;
增强剂:400μm的陶土;
稀释剂:环丁砜;
集料:碎石;
材料的配制质量份数分别为:六亚甲基二异氰酸酯(HDI)预聚体为13份,二苯基甲烷二异氰酸酯(MDI)预聚体17份,聚烯烃热缩性弹性体50份,环丁砜1份,端氨基聚醚3.5份,氢氧化钡1.3份,二辛基对苯二胺1.4份,石灰石粉23份,陶土17份,400μm的碎石40份,根据施工需要复配碎石作为粗骨料。
材料的配制过程和喷涂方法参照实施例8。
本实施例提供的沥青路面修复材料用于路面修复时的凝结时间25min;凝结30min的黏结力4.6N·m,湿轮磨耗值为621g·m-2,负荷车轮粘附砂量浸水1d 为 374g·m-2。
实施例14:
热固性聚合物的预聚体:不饱和聚酯预聚体(191型)和呋喃树脂预聚体
热塑性聚合物:聚氨酯热缩性弹性体;
掺合料:橡胶粉;
引发剂:偶氮二异丁腈;
促进剂:甲乙酮;
抗氧化剂:叔丁基对苯二酚;
增强剂:木粉和粉末纤维素;
稀释剂:二甲基乙酰胺;
集料:350μm的石英砂;
材料的配制质量份数分别为:不饱和聚酯预聚体(191型)为15份,呋喃树脂预聚体5份,聚氨酯热缩性弹性体60份,二甲基乙酰胺15.5份,偶氮二异丁腈1.7份,甲乙酮1.2份,叔丁基对苯二酚0.8份,橡胶粉10份,木粉13份和粉末纤维素7份,350μm的石英砂25份,根据施工需要复配碎石作为粗骨料。
材料的配制过程和喷涂方法参照实施例8。
本实施例提供的沥青路面修复材料用于路面修复时的凝结时间25min;凝结30min的黏结力4.8 N·m,湿轮磨耗值为504 g·m-2,负荷车轮粘附砂量浸水1d 为 313g·m-2。
实施例15:
热固性聚合物的预聚体:热固性酚醛树脂预聚体;
热塑性聚合物:嵌段聚醚酰胺弹性体;
掺合料:钢渣粉;
引发剂:碳酸丙烯酯;
促进剂:乙酰丙酮;
抗氧化剂:棓酸丙酯;
增强剂:铁粉和三氧化二铁粉末;
稀释剂:正丁醇;
集料:200μm的石英砂;
材料的配制质量份数分别为:热固性酚醛树脂预聚体55份,嵌段聚醚酰胺弹性体8份,正丁醇22份,碳酸丙烯酯3份,乙酰丙酮2份,棓酸丙酯2份,钢渣粉17份,铁粉7份,三氧化二铁粉末8份,200μm的石英砂27份,根据施工需要复配碎石作为粗骨料。
材料的配制过程和喷涂方法参照实施例8。
本实施例提供的沥青路面修复材料用于路面修复时的凝结时间25min;凝结30min的黏结力2.9N·m,湿轮磨耗值为537g·m-2,负荷车轮粘附砂量浸水1d 为 378g·m-2。
实施例16:
热固性聚合物的预聚体:氰基丙烯酸酯和液体聚硫橡胶预聚体
热塑性聚合物:聚苯醚;
掺合料:粉煤灰;
引发剂:二氧化锰;
促进剂:二乙基苯胺;
抗氧化剂:丁基羟基茴香醚;
增强剂:硅藻土;
稀释剂:乙酸乙酯;
集料:300μm的石英砂;
材料的配制质量份数分别为:氰基丙烯酸酯25份,液体聚硫橡胶预聚体20份,聚苯醚45份,乙酸乙酯33份,二氧化锰5份,二乙基苯胺1.5份,丁基羟基茴香醚3.5份,粉煤灰30份,硅藻土11份,300μm的石英砂17份,根据施工需要复配碎石作为粗骨料。
材料的配制过程和喷涂方法参照实施例8。
本实施例提供的沥青路面修复材料用于路面修复时的凝结时间25min;凝结30min的黏结力3.8N·m,湿轮磨耗值为617g·m-2,负荷车轮粘附砂量浸水1d 为 369 g·m-2。
本发明的其它实施例用表格1和表格2的形式给出原料组分的质量配比,其中表格1所述实施例不含抗氧化剂、促进剂、引发剂、增强剂、稀释剂、集料,表格2所述实施例中抗氧化剂、促进剂、引发剂、增强剂、稀释剂、集料的选取及质量份数按照说明书给出的具体物质和用量进行选取,材料的包装和配制方法参照实施例8;
表格1
表格2
以上实施例是本发明的优选实施方式,并非对本发明作任何形式上的限制。应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (2)
1.一种沥青路面修复材料,其特征在于,选自材料1-11中的一种,材料1-11按质量分数包含下列组分组成:
材料1:
热固性聚合物的预聚体:TDI异氰酸酯预聚体50份,热固性酚醛树脂预聚体10份;
热塑性聚合物:90#道路沥青11份;
固化剂:聚醚预聚体30份,三乙烯二胺5份;
促进剂:二月桂酸二丁基锡3份;
掺合料:橡胶粉8份,石英砂20份;
稀释剂:二甲基硅油6份;
材料2:
热固性聚合物的单体:甲基丙烯酸甲酯45份,甲基丙烯酸12份,三羟甲基丙烷三丙烯酸酯5份;
热塑性聚合物:ABS树脂7份,丁腈橡胶10份;
引发剂:异丙苯过氧化氢4份;
促进剂:六亚甲基四胺3份,异辛酸钒0.3份;
抗氧化剂:对苯二酚0.6份;
掺合料:一级粉煤灰8份;
稀释剂:乙二醇5份;
材料3:
热固性聚合物的预聚体:双酚A型树脂601 35份;
热塑性聚合物:聚硫橡胶10份,聚乙烯醇缩丁醛6份;
固化剂:聚酰胺环氧树脂引发剂14份;
促进剂:三乙醇胺4份;
抗氧化剂:亚磷酸酯1份;
掺合料:矿粉S9516份;
稀释剂:甲苯6份,丙酮6份;
材料4:
热固性聚合物的预聚体:三聚氰胺甲醛树脂53.5份;
热塑性聚合物:苯乙烯-丁二烯热塑性弹性体15份;
固化剂:三亚乙基四胺12份;
促进剂:过氧化二异丙苯3份;
抗氧化剂:二丁基羟基甲苯0.5份;
增强剂:滑石粉10份;
稀释剂:邻苯二甲酸二甲酯6份;
材料5:
热固性聚合物的预聚体:MDI异氰酸酯预聚体44份;
热塑性聚合物:聚氯乙烯8份;
固化剂:聚醚多元醇N220 15份,端胺基聚醚Jefamine T-5000 10份;
促进剂:二乙基甲苯二胺 2份;
抗氧化剂:N-苯基-2-萘胺 1份;
掺合料:石灰石粉 8份;
稀释剂:乙酸乙酯 12份;
材料6:
热固性聚合物的预聚体:液体聚硫橡胶预聚体JYL-124 50份,环氧树脂预聚体E44 9份
热塑性聚合物:聚丙烯腈 6份;
固化剂:二氧化锰 6份;
促进剂:三乙烯四胺 4份;
抗氧化剂:叔丁基对苯二酚 1份;
增强剂:白炭黑 12份;
稀释剂:二甲基亚砜 12份;
材料7:
热固性聚合物的预聚体:不饱和聚酯预聚体191型 50份,呋喃树脂预聚体 20份;
热塑性聚合物:聚醚砜 5份;
引发剂:过氧化苯甲酰 3份;
促进剂:N,N-二甲基苯胺 1.4份;
抗氧化剂:丁基羟基茴香醚 0.6份;
增强剂:云母粉 15份;
稀释剂:四氢呋喃 8份;
材料8:
热固性聚合物的预聚体:糠醛20份,甲醇醚化三聚氰胺30份;
热塑性聚合物:聚醚酮 10份;
掺合料:滑石粉 20份;
固化剂:对甲苯磺酸 6份;
促进剂:磷酸正丁酯 1份;
抗氧化剂:叔丁基对苯二酚 1份;
增强剂:硅藻土5份,氧化镁粉末5份 ;
稀释剂:二甲基乙酰胺10份;
集料:100μm的石英砂10份;
材料9:
热固性聚合物的预聚体:三羟甲基丙烷三丙烯酸酯40份,聚脲预聚体20份;
热塑性聚合物:聚甲基丙烯酸甲酯30份;
掺合料:钢渣粉30份;
引发剂:过氧化苯甲酰2.5份;
促进剂:辛酸亚锡0.5份;
抗氧化剂:硫代二丙酸月桂醇酯2份;
增强剂:石墨烯10份;
稀释剂:四氢呋喃20份;
集料:200μm的橡胶颗粒30份;
材料10:
热固性聚合物的预聚体:环氧树脂预聚体E42 25份,IPDI异氰酸酯预聚体25份;
热塑性聚合物:芳香聚酰胺肼35份;
掺合料:石英粉28份;
固化剂:二丙烯三胺10份;
促进剂:过氧化锌8份;
抗氧化剂:亚磷酸二苯基辛己酯2份;
增强剂:白炭黑13.5份;
稀释剂:邻苯二甲酸二丁酯35份;
集料:300μm的碎石10份;
材料11:
热固性聚合物的预聚体:热固性酚醛树脂预聚体55份;
热塑性聚合物:嵌段聚醚酰胺弹性体8份;
掺合料:钢渣粉17份;
固化剂:碳酸丙烯酯3份;
促进剂:乙酰丙酮2份;
抗氧化剂:棓酸丙酯2份;
增强剂:铁粉7份,三氧化二铁粉8份;
稀释剂:正丁醇22份;
集料:200μm的石英砂27份。
2.根据权利要求1所述的沥青路面修复材料,其特征在于,所述掺合料的粒径在80μm以下。