CN109394032A - Wood-plastic composite chopping board with drainage channels - Google Patents
Wood-plastic composite chopping board with drainage channels Download PDFInfo
- Publication number
- CN109394032A CN109394032A CN201811401365.XA CN201811401365A CN109394032A CN 109394032 A CN109394032 A CN 109394032A CN 201811401365 A CN201811401365 A CN 201811401365A CN 109394032 A CN109394032 A CN 109394032A
- Authority
- CN
- China
- Prior art keywords
- powder
- chopping board
- parts
- wood
- board ontology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of Wood-plastic composite chopping board with drainage channels, box body including chopping board ontology and opening upwards, the chopping board ontology is set in box body in a manner of detachable connection, and there are spaces between the chopping board body edges and box side wall, form rhone；The box portion bottom wall is equipped with taper type protrusion, while the chopping board body bottom portion is equipped with the mounting groove with the taper type protrusion form-fit；By foring a circle rhone around chopping board ontology, water flows everywhere when solving the problems, such as to cut the dish；And it is arranged to the mode that taper type protrusion is connected with mounting groove, facilitate the installation and removal of chopping board ontology and box body；Meanwhile chopping board ontology is prepared using new material, the chopping board ontology with excellent comprehensive mechanical property and excellent antibacterial and mouldproof performance can be prepared.
Description
Technical field
The present invention relates to kitchen utensils fields, and in particular to a kind of Wood-plastic composite chopping board with drainage channels.
Background technique
Chopping board, that is, chopping block is one of necessity of daily life.Currently, chopping board be generally it is wooden, due to wooden dish
Plate has piece or borehole, germ easy to breed, so soup is often scrubbed or pour boiling water on, to keep chopping board sanitation and hygiene.
But wooden chopping board is easy to happen loss, and by long-time, using can all generate on chopping board surface, scratch is even tiny to be split
Seam, and can be mouldy without good maintenance, this is that chopping board made of any wood materials is all inevitable.And plastics dish
Plate is easily-deformable because expanding with heat and contract with cold, and chopping board is easy sliding on the table, dangerous.
In addition, now widely used chopping board is mostly plane, and when cutting high-moisture dish or meat, the juice of dish or meat
Water can flow on table top from the different place of chopping board at random, clean get up it is time-consuming and laborious, it is not satisfactory.
Therefore, to solve the above-mentioned problems, need to develop a kind of Wood-plastic composite chopping board with drainage channels, overcome because of wood
Material intensity is low, variability is big, easily loss, easily use limitation caused by mouldy and low, mutability of elasticity of plastics modulus etc., simultaneously
Water sinuous flow when solving the problem of to cut the dish.
Summary of the invention
In view of this, the present invention provides a kind of Wood-plastic composite chopping board with drainage channels, it is able to solve when cutting the dish, water sinuous flow
The problem of, and have the characteristics that water-fast moisture resistance is good, plasticity is strong, the feature of environmental protection is good, the service life is long and to be not easy raw bacterium mouldy, it does not open
Split, do not expand, it is indeformable and without maintenance, convenient for cleaning.
Wood-plastic composite chopping board with drainage channels provided by the invention, the box body including chopping board ontology and opening upwards, institute
It states chopping board ontology to be set in box body in a manner of detachable connection, and is stayed between the chopping board body edges and box side wall
There is space, forms rhone；The box portion bottom wall is equipped with taper type protrusion, while the chopping board body bottom portion is equipped with and the frustum
The mounting groove of shape protrusion form-fit；
The raw material of the chopping board ontology includes following component by weight: 50-55 parts of polyethylene, 15-20 parts of polypropylene,
15-20 parts of ABS resin, 12-15 parts of TPU, 40-45 parts of wood powder, 15-17 parts of nanometer jade powder, 15-17 parts of talcum powder, boron nitride
4-6 parts, 2-3 parts of Folium Artemisiae Argyi powder, 1-2 parts of garlic powder, 1-2 parts of onion powder, 0.3-0.5 parts of vinyl trimethylsilane, zinc stearate
0.2-0.3 parts.
Further, the box body bottom is equipped with non-slip mat.
Further, the raw material of the chopping board ontology includes following component by weight: 52 parts of polyethylene, 18 parts of polypropylene,
18 parts of ABS resin, 13 parts of TPU, 16 parts of 42 part, nanometer jade powder of wood powder, 15 parts of talcum powder, 5 parts of boron nitride, 2 parts of Folium Artemisiae Argyi powder,
2 parts of garlic powder, 1 part of onion powder, 0.4 part of vinyl trimethylsilane, 0.2 part of zinc stearate.
Further, the granularity of the wood powder is 80-100 mesh；The granularity of the talcum powder is 800-1250 mesh；The nitridation
The granularity of boron is 800-1250 mesh；The Folium Artemisiae Argyi powder, garlic powder, onion powder are micro mist of the partial size less than 100 mesh.
Further, the TPU is polyether thermoplastic polyurethane.
Further, the box body is made of polypropylene material.
Further, the preparation method of the chopping board ontology includes the following steps:
(1) take polyethylene, polypropylene, ABS resin, TPU and zinc stearate, vinyl trimethylsilane that blender is added
In, be warming up to 150 DEG C, 12-15min be mixed with the revolving speed of 300r/min, be then added wood powder, Folium Artemisiae Argyi powder, garlic powder and
Onion powder, adjustment revolving speed are 600r/min, are warming up to 160 DEG C, continue to stir 12-15min, are eventually adding a nanometer jade powder, cunning
Mountain flour and boron nitride, adjustment revolving speed are 1000r/min, continue to stir 20-25min；
(2) mixture obtained in step (1) is added in pelletizer and is granulated；
(3) particle obtained in step (2) is sent into press machine, is 5-6MPa in pressure, temperature is at 200-210 DEG C
Template is struck out, forms finished product after cooled to room temperature.
Beneficial effects of the present invention:
Wood-plastic composite chopping board with drainage channels provided by the invention, passes through the detachable company of chopping board ontology and box body
It connects, a circle rhone is formd around chopping board ontology, the water generated when cutting the dish can be stored in rhone, be solved
The problem of water flows everywhere when cutting the dish；And be arranged to the mode that taper type protrusion is connected with mounting groove, facilitate chopping board ontology with
The installation and removal of box body can separately clean them after cutting the dish, and clear up more convenient；Meanwhile it being set in box body bottom
Non-slip mat is set, can be slided on table top to avoid chopping board when cutting the dish.
Chopping board ontology provided by the invention prepares using new Wood-plastic material, is equipped with conjunction by using suitable component
The dosage of reason promotes each raw material component to realize mutual association during preparing chopping board ontology in conjunction with preferably preparation method
Same and mutual cooperation, greatly increases the comprehensive performance of chopping board ontology, prepares the dual excellent spy for having timber and plastics concurrently
Property chopping board ontology, solve the problems, such as existing wooden chopping board be easily lost, be easy to crack, easily mouldy, easy raw bacterium, make dish obtained
Plate ontology has excellent comprehensive mechanical property and antibacterial and mouldproof performance, is not afraid of and damages by worms, mildewproof bacterium, do not absorb moisture, uses
Service life is long, stability is good, intensity is high, plasticity is strong, the feature of environmental protection is good, do not crack, do not expand, it is indeformable and without maintenance, be convenient for
Cleaning.
Chopping board ontology of the invention is by the way that using polyethylene, polypropylene and ABS resin as complex matrix, then addition is appropriate
Polyether-type TPU, zinc stearate, vinyl trimethylsilane, then add suitable wood powder, jade powder, talcum powder, boron nitride into
Row mixing, can greatly improve the mechanical property, stability and intensity of chopping board ontology, can be realized between each raw material component non-
Often good mutual synergistic effect, the polyether-type TPU of such as addition can not only play its excellent oil resistant, water-fast, resistance to mould, anti-tear
Fragility, weatherability and wearability etc., additionally it is possible to improve between polyethylene, polypropylene and ABS resin, plastic substrate and wood powder, jade
Mountain flour, talcum powder, the compatibility between boron nitride, improve the comprehensive mechanical property of material；Plastic substrate can be with wood powder, jade
Powder, talcum powder, boron nitride mutually act synergistically, and improve stability, intensity and corrosion resistance of material, etc..Meanwhile this hair
Bright Folium Artemisiae Argyi powder, garlic powder, onion powder by addition cooperates with jade powder, is able to suppress the breeding of bacterium and microorganism, has excellent
Different antibacterial effect prevents chopping board ontology mouldy raw bacterium in use or placement process.
Detailed description of the invention
The invention will be further described with reference to the accompanying drawings and examples:
Fig. 1 is the top view of Wood-plastic composite chopping board provided by the invention；
Fig. 2 is the front sectional view of Wood-plastic composite chopping board provided by the invention；
In figure:
1, chopping board ontology, 2, box body, 3, rhone, 4, taper type protrusion, 5, non-slip mat.
Specific embodiment
Embodiment one
Wood-plastic composite chopping board with drainage channels provided in this embodiment, the box body including chopping board ontology 1 and opening upwards
2, the chopping board ontology 1 is set in box body 2 in a manner of detachable connection, and 1 edge of chopping board ontology and 2 side of box body
There are spaces between wall, form rhone 3；2 bottom wall of box body is equipped with taper type protrusion 4, while 1 bottom of chopping board ontology
Equipped with the mounting groove with raised 4 form-fits of the taper type；2 bottom of box body is equipped with non-slip mat 5, and the non-slip mat is rubber
Non-slip mat.
In the present embodiment, the raw material of the chopping board ontology includes following component by weight: 50 parts of polyethylene, polypropylene 20
Part, 18 parts of ABS resin, 15 parts of TPU, 17 parts of wood powder (80 mesh) 40 part, nanometer jade powder, 15 parts of talcum powder (1250 mesh), nitridation
6 parts of boron (800 mesh), 2 parts of Folium Artemisiae Argyi powder, 1 part of garlic powder, 2 parts of onion powder, 0.3 part of vinyl trimethylsilane, zinc stearate 0.2
Part；The box body is made of polypropylene material.
In the present embodiment, the preparation method of the chopping board ontology includes the following steps:
(1) take polyethylene, polypropylene, ABS resin, TPU and zinc stearate, vinyl trimethylsilane that blender is added
In, 150 DEG C are warming up to, 13min is mixed with the revolving speed of 300r/min, wood powder, Folium Artemisiae Argyi powder, garlic powder and onion is then added
Powder, adjustment revolving speed are 600r/min, are warming up to 160 DEG C, continue to stir 13min, are eventually adding a nanometer jade powder, talcum powder and nitrogen
Change boron, adjustment revolving speed is 1000r/min, continues to stir 22min；
(2) mixture obtained in step (1) is added in pelletizer and is granulated；
(3) particle obtained in step (2) is sent into press machine, is 5MPa in pressure, temperature is to strike out at 200 DEG C
Template forms finished product after cooled to room temperature.
Through detecting, the fracture load by bending of chopping board ontology obtained is 2910N, fracture load by bending under the conditions of 60 DEG C
Conservation rate is 87%, i.e., mechanical property is able to maintain higher level in normal conditions of use；Room temperature soaks in removing tap water
Bubble is wiped dry after 24 hours, weighing obtains weight gain as 0.37%, and water absorption rate is low, has high waterproof performance.
In the present embodiment, the TPU is polyether thermoplastic polyurethane；The Folium Artemisiae Argyi powder, garlic powder, onion powder are grain
Micro mist of the diameter less than 100 mesh.
Embodiment two
Wood-plastic composite chopping board with drainage channels provided in this embodiment, structure is the same as embodiment one.
In the present embodiment, the raw material of the chopping board ontology includes following component by weight: 52 parts of polyethylene, polypropylene 18
Part, 18 parts of ABS resin, 13 parts of TPU, 16 parts of wood powder (80 mesh) 42 part, nanometer jade powder, 15 parts of talcum powder (800 mesh), nitridation
5 parts of boron (1250 mesh), 2 parts of Folium Artemisiae Argyi powder, 2 parts of garlic powder, 1 part of onion powder, 0.4 part of vinyl trimethylsilane, zinc stearate 0.2
Part；The box body is made of polypropylene material.
In the present embodiment, the preparation method of the chopping board ontology includes the following steps:
(1) take polyethylene, polypropylene, ABS resin, TPU and zinc stearate, vinyl trimethylsilane that blender is added
In, 150 DEG C are warming up to, 13min is mixed with the revolving speed of 300r/min, wood powder, Folium Artemisiae Argyi powder, garlic powder and onion is then added
Powder, adjustment revolving speed are 600r/min, are warming up to 160 DEG C, continue to stir 14min, are eventually adding a nanometer jade powder, talcum powder and nitrogen
Change boron, adjustment revolving speed is 1000r/min, continues to stir 23min；
(2) mixture obtained in step (1) is added in pelletizer and is granulated；
(3) particle obtained in step (2) is sent into press machine, is 5MPa in pressure, temperature is to strike out at 210 DEG C
Template forms finished product after cooled to room temperature.
Through detecting, the fracture load by bending of chopping board ontology obtained is 3029N, fracture load by bending under the conditions of 60 DEG C
Conservation rate is 84%, i.e., mechanical property is able to maintain higher level in normal conditions of use；Room temperature soaks in removing tap water
Bubble is wiped dry after 24 hours, weighing obtains weight gain as 0.45%, and water absorption rate is low, has high waterproof performance.
In the present embodiment, the TPU is polyether thermoplastic polyurethane；The Folium Artemisiae Argyi powder, garlic powder, onion powder are grain
Micro mist of the diameter less than 100 mesh.
Embodiment three
Wood-plastic composite chopping board with drainage channels provided in this embodiment, structure is the same as embodiment one.
In the present embodiment, the raw material of the chopping board ontology includes following component by weight: 55 parts of polyethylene, polypropylene 20
Part, 20 parts of ABS resin, 15 parts of TPU, 17 parts of wood powder (100 mesh) 45 part, nanometer jade powder, 17 parts of talcum powder (1250 mesh), nitrogen
Change 6 parts of boron (1250 mesh), 3 parts of Folium Artemisiae Argyi powder, 2 parts of garlic powder, 2 parts of onion powder, 0.3 part of vinyl trimethylsilane, zinc stearate
0.3 part；The box body is made of polypropylene material.
In the present embodiment, the preparation method of the chopping board ontology includes the following steps:
(1) take polyethylene, polypropylene, ABS resin, TPU and zinc stearate, vinyl trimethylsilane that blender is added
In, 150 DEG C are warming up to, 15min is mixed with the revolving speed of 300r/min, wood powder, Folium Artemisiae Argyi powder, garlic powder and onion is then added
Powder, adjustment revolving speed are 600r/min, are warming up to 160 DEG C, continue to stir 15min, are eventually adding a nanometer jade powder, talcum powder and nitrogen
Change boron, adjustment revolving speed is 1000r/min, continues to stir 25min；
(2) mixture obtained in step (1) is added in pelletizer and is granulated；
(3) particle obtained in step (2) is sent into press machine, is 6MPa in pressure, temperature is to strike out at 210 DEG C
Template forms finished product after cooled to room temperature.
Through detecting, the fracture load by bending of chopping board ontology obtained is 3085N, fracture load by bending under the conditions of 60 DEG C
Conservation rate is 87%, i.e., mechanical property is able to maintain higher level in normal conditions of use；Room temperature soaks in removing tap water
Bubble is wiped dry after 24 hours, weighing obtains weight gain as 0.39%, and water absorption rate is low, has high waterproof performance.
In the present embodiment, the TPU is polyether thermoplastic polyurethane；The Folium Artemisiae Argyi powder, garlic powder, onion powder are grain
Micro mist of the diameter less than 100 mesh.
Example IV
Wood-plastic composite chopping board with drainage channels provided in this embodiment, structure is the same as embodiment one.
In the present embodiment, the raw material of the chopping board ontology includes following component by weight: 55 parts of polyethylene, polypropylene 15
Part, 20 parts of ABS resin, 12 parts of TPU, 15 parts of wood powder (100 mesh) 45 part, nanometer jade powder, 17 parts of talcum powder (1250 mesh), nitrogen
Change 4 parts of boron (800 mesh), 3 parts of Folium Artemisiae Argyi powder, 1 part of garlic powder, 1 part of onion powder, 0.4 part of vinyl trimethylsilane, zinc stearate
0.3 part；The box body is made of polypropylene material.
In the present embodiment, the preparation method of the chopping board ontology includes the following steps:
(1) take polyethylene, polypropylene, ABS resin, TPU and zinc stearate, vinyl trimethylsilane that blender is added
In, 150 DEG C are warming up to, 14min is mixed with the revolving speed of 300r/min, wood powder, Folium Artemisiae Argyi powder, garlic powder and onion is then added
Powder, adjustment revolving speed are 600r/min, are warming up to 160 DEG C, continue to stir 12min, are eventually adding a nanometer jade powder, talcum powder and nitrogen
Change boron, adjustment revolving speed is 1000r/min, continues to stir 20min；
(2) mixture obtained in step (1) is added in pelletizer and is granulated；
(3) particle obtained in step (2) is sent into press machine, is 6MPa in pressure, temperature is to strike out at 210 DEG C
Template forms finished product after cooled to room temperature.
Through detecting, the fracture load by bending of chopping board ontology obtained is 2977N, fracture load by bending under the conditions of 60 DEG C
Conservation rate is 85%, i.e., mechanical property is able to maintain higher level in normal conditions of use；Room temperature soaks in removing tap water
Bubble is wiped dry after 24 hours, weighing obtains weight gain as 0.42%, and water absorption rate is low, has high waterproof performance.
In the present embodiment, the TPU is polyether thermoplastic polyurethane；The Folium Artemisiae Argyi powder, garlic powder, onion powder are grain
Micro mist of the diameter less than 100 mesh.
Embodiment five
Wood-plastic composite chopping board with drainage channels provided in this embodiment, structure is the same as embodiment one.
In the present embodiment, the raw material of the chopping board ontology includes following component by weight: 50 parts of polyethylene, polypropylene 15
Part, 15 parts of ABS resin, 12 parts of TPU, 15 parts of wood powder (80 mesh) 40 part, nanometer jade powder, 15 parts of talcum powder (800 mesh), nitridation
4 parts of boron (800 mesh), 2 parts of Folium Artemisiae Argyi powder, 1 part of garlic powder, 1 part of onion powder, 0.5 part of vinyl trimethylsilane, zinc stearate 0.2
Part；The box body is made of polypropylene material.
In the present embodiment, the preparation method of the chopping board ontology includes the following steps:
(1) take polyethylene, polypropylene, ABS resin, TPU and zinc stearate, vinyl trimethylsilane that blender is added
In, 150 DEG C are warming up to, 12min is mixed with the revolving speed of 300r/min, wood powder, Folium Artemisiae Argyi powder, garlic powder and onion is then added
Powder, adjustment revolving speed are 600r/min, are warming up to 160 DEG C, continue to stir 12min, are eventually adding a nanometer jade powder, talcum powder and nitrogen
Change boron, adjustment revolving speed is 1000r/min, continues to stir 20min；
(2) mixture obtained in step (1) is added in pelletizer and is granulated；
(3) particle obtained in step (2) is sent into press machine, is 5MPa in pressure, temperature is to strike out at 200 DEG C
Template forms finished product after cooled to room temperature.
Through detecting, the fracture load by bending of chopping board ontology obtained is 2867N, fracture load by bending under the conditions of 60 DEG C
Conservation rate is 82%, i.e., mechanical property is able to maintain higher level in normal conditions of use；Room temperature soaks in removing tap water
Bubble is wiped dry after 24 hours, weighing obtains weight gain as 0.51%, and water absorption rate is low, has high waterproof performance.
In the present embodiment, the TPU is polyether thermoplastic polyurethane；The Folium Artemisiae Argyi powder, garlic powder, onion powder are grain
Micro mist of the diameter less than 100 mesh.
Each raw material component can be bought by market and be obtained in above-described embodiment.
Anti-microbial property test is carried out to chopping board ontology prepared by one~embodiment of above-described embodiment five, referring to QB/
T2591-2003 standard, measures the anti-microbial property of chopping board ontology made from each embodiment and Anti-mildew capability (selects golden yellow Portugal
Grape coccus, Escherichia coli, aspergillus niger are tested), it the results are shown in Table 1.
Table 1
As known from Table 1, chopping board ontology made from above-described embodiment has excellent antibacterial and mouldproof performance, can effectively press down
Mildew making and bacterial growth.
Finally, it is stated that the above examples are only used to illustrate the technical scheme of the present invention and are not limiting, although referring to compared with
Good embodiment describes the invention in detail, those skilled in the art should understand that, it can be to skill of the invention
Art scheme is modified or replaced equivalently, and without departing from the objective and range of technical solution of the present invention, should all be covered at this
In the scope of the claims of invention.
Claims (7)
1. a kind of Wood-plastic composite chopping board with drainage channels, it is characterised in that: the box body including chopping board ontology and opening upwards, institute
It states chopping board ontology to be set in box body in a manner of detachable connection, and is stayed between the chopping board body edges and box side wall
There is space, forms rhone；The box portion bottom wall is equipped with taper type protrusion, while the chopping board body bottom portion is equipped with and the frustum
The mounting groove of shape protrusion form-fit；
The raw material of the chopping board ontology includes following component by weight: 50-55 parts of polyethylene, 15-20 parts of polypropylene, ABS tree
15-20 parts of rouge, 12-15 parts of TPU, 40-45 parts of wood powder, 15-17 parts of nanometer jade powder, 15-17 parts of talcum powder, boron nitride 4-6
Part, 2-3 parts of Folium Artemisiae Argyi powder, 1-2 parts of garlic powder, 1-2 parts of onion powder, 0.3-0.5 parts of vinyl trimethylsilane, zinc stearate 0.2-
0.3 part.
2. Wood-plastic composite chopping board with drainage channels according to claim 1, it is characterised in that: the box body bottom is equipped with
Non-slip mat.
3. Wood-plastic composite chopping board with drainage channels according to claim 1, it is characterised in that: the original of the chopping board ontology
Material includes following component by weight: 52 parts of polyethylene, 18 parts of ABS resin, 13 parts of TPU, 42 parts of wood powder, is received 18 parts of polypropylene
Rice 16 parts of jade powder, 15 parts of talcum powder, 5 parts of boron nitride, 2 parts of Folium Artemisiae Argyi powder, 2 parts of garlic powder, 1 part of onion powder, vinyl trimethyl
0.4 part of silane, 0.2 part of zinc stearate.
4. Wood-plastic composite chopping board with drainage channels according to claim 1, it is characterised in that: the granularity of the wood powder is
80-100 mesh；The granularity of the talcum powder is 800-1250 mesh；The granularity of the boron nitride is 800-1250 mesh；The folium artemisiae argyi
Powder, garlic powder, onion powder are micro mist of the partial size less than 100 mesh.
5. Wood-plastic composite chopping board with drainage channels according to claim 1, it is characterised in that: the TPU is polyether-type
Thermoplastic polyurethane.
6. Wood-plastic composite chopping board with drainage channels according to claim 1, it is characterised in that: the box body uses poly- third
Alkene material is made.
7. Wood-plastic composite chopping board with drainage channels according to claim 1, it is characterised in that: the system of the chopping board ontology
Preparation Method includes the following steps:
(1) it takes polyethylene, polypropylene, ABS resin, TPU and zinc stearate, vinyl trimethylsilane to be added in blender, rises
12-15min is mixed to 150 DEG C, with the revolving speed of 300r/min in temperature, and wood powder, Folium Artemisiae Argyi powder, garlic powder and onion is then added
Powder, adjustment revolving speed are 600r/min, are warming up to 160 DEG C, continue to stir 12-15min, are eventually adding a nanometer jade powder, talcum powder
And boron nitride, adjustment revolving speed are 1000r/min, continue to stir 20-25min；
(2) mixture obtained in step (1) is added in pelletizer and is granulated；
(3) particle obtained in step (2) is sent into press machine, is 5-6MPa in pressure, temperature is punching press at 200-210 DEG C
At template, finished product is formed after cooled to room temperature.