CN109371535A - A kind of high resiliency combing worsted spinning and preparation method thereof - Google Patents
A kind of high resiliency combing worsted spinning and preparation method thereof Download PDFInfo
- Publication number
- CN109371535A CN109371535A CN201811637387.6A CN201811637387A CN109371535A CN 109371535 A CN109371535 A CN 109371535A CN 201811637387 A CN201811637387 A CN 201811637387A CN 109371535 A CN109371535 A CN 109371535A
- Authority
- CN
- China
- Prior art keywords
- yarn
- fabric
- spinning
- preparation
- high resiliency
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation methods of high resiliency combing worsted spinning, comprising the following steps: prepares warp thread, use is spinning, by mass percentage by 30% wool and 70% blend polyester, obtains the warp thread that metric count is 70/2;Prepare weft yarn, use is spinning, by mass percentage by 25% wool, 55.5% terylene and 14.5% polyvinyl it is blended, obtain the yarn of metric count 60/2, and will be blended after yarn and spandex spun core-spun yarn, the plying twist uses 200 viscosity coefficients;The warp thread and the weft yarn are organized into fabric;Fabric is post-processed, successively carries out that fabric sizing, open washing boil, braying, dye vat move back dimension, even boil, dry, singe, even boil, be formed, obtain fabric after soft, tank steams to fabric.The product that the application is finally prepared has many advantages, such as super-elastic property, has crease-resistant, machine washable, soft, the suitable high-end business wear of production.
Description
Technical field
The present invention relates to worsted fabric fields, and in particular to a kind of high resiliency combing worsted spinning and preparation method thereof.
Background technique
With the continuous improvement of textile science being constantly progressive and consumer requires properties of textile, people are to clothes
Elasticity, fabric hand feel and easy care performance propose higher requirement, it is especially elastic, almost arrived the journey of " no bullet not cloth "
Degree.
Currently, in the prior art, the elasticity of worsted fabric has one with cotton products and chemical fiber plus material ratio generally 10~20%
Determine gap, it can be by the more loose so that elasticity reaches 20~30%, still of the structure setting of fabric generally for elasticity is improved
In this fabric since structure is more loose, often elasticity restore it is poor, cause practicability inadequate, the above problem be this field urgently
Problem to be solved.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of high resiliency combing wools for combining elasticity and elasticity and restoring
The preparation method of fabric.
In order to solve the above technical problem, the present invention provides scheme be: a kind of preparation side of high resiliency combing worsted spinning
Method, comprising the following steps:
S101, warp thread is prepared, use is spinning, by mass percentage by 30% wool and 70% blend polyester, obtains
The warp thread that metric count is 70/2;
S102, weft yarn is prepared, use is spinning, by mass percentage by 25% wool, 55.5% terylene and 14.5%
Polyvinyl is blended, obtains the yarn of metric count 60/2, and will be blended after yarn and spandex spun core-spun yarn, the plying twist uses
200 viscosity coefficients;
S103, the warp thread and the weft yarn are organized into fabric;
S201, fabric is post-processed, successively carries out that fabric sizing, open washing boil, braying, dye vat move back dimension, even to fabric
It boils, dry, singing, even boil, be formed, soft, tank obtains fabric after steaming.
Further, blended in the step S101 successively comprise the following steps that:
Silver mixing, scalp acupuncture, two needles, three needles, four needles, head be thick, two thick, fine sand, yarn steamings, white winder, doubling, double twisting, yarn steaming,
It is blended in the step S102 to comprise the following steps that:
Silver mixing, scalp acupuncture, two needles, three needles, four needles, head be thick, two thick, fine sand, yarn steamings, white winder, doubling, double twisting, yarn steaming.
Further, the polyvinyl is added during the scalp acupuncture in the step S102.
Further, being covered during yarn steaming to the polyvinyl twice in the step S102.
Further, the polyvinyl is the polyvinyl that fusing point is 70 DEG C.
Further, the thread count of the fabric is 312 × 274/10cm.
Further, the technological parameter that the dye vat pushes away dimension is, 90 DEG C of temperature, time 20min.
The application further provides a kind of high resiliency combing worsted spinning prepared according to the above method.
Beneficial effects of the present invention: the application is cooperated by the way that soluble polyvinylalcohol and spandex is added, and is carried out by above-mentioned equivalent
Proportion, polyvinyl dissolves leaving gap after blended and post-processing, so that the texture and certain elasticity of the application softness are assigned,
And twist factor is combineeed using 200 superelevation, so that the product that the application is prepared finally has super-elastic property, have anti-
Wrinkle, machine washable, it is soft the advantages that, be suitble to the high-end business wear of production.
Specific embodiment
The present invention is further explained in the light of specific embodiments, so that those skilled in the art can be preferably
Understand the present invention and can be practiced, but illustrated embodiment is not as a limitation of the invention.
A kind of preparation method of high resiliency combing worsted spinning, comprising the following steps:
S1, spinning, use is spinning, prepares warp thread and weft yarn respectively, and warp thread and weft yarn is oblique using 2/1 by institutional framework
Line, tissue obtain fabric.
Wherein, in spinning process, raw material is matched by following mass percent:
Warp thread: wool 30%, terylene 70%;
Weft yarn: wool 25%, terylene 55.5%, polyvinyl 14.5%, spandex 5%;
Wherein, yarn count (Nm) twist factor presses following parameter designing:
Warp thread: 70/2, single thread 89, payment to a porter 130;
Weft yarn: 60/2, single thread 89, payment to a porter 200.
Wherein, thread count presses 312 × 274/10cm;
Wherein, when preparing above-mentioned warp thread and weft yarn, progress is blended specifically to comprise the following steps that process:
Silver mixing, scalp acupuncture, two needles, three needles, four needles, head be thick, two thick, fine sand, yarn steamings, white winder, doubling, double twisting, yarn steaming.
Wherein, crude oil, antistatic agent are summed it up during silver mixing.
The white polyvinyl item of 15% 70 DEG C of dissolutions is added when preparing weft yarn in the application during scalp acupuncture, specifically,
Polyvinyl selects 20 × 75mm of toray company production, the polyvinyl item of 70 DEG C of dissolutions.
Polyvinyl is covered during fine sand and yarn steaming by white Nylon cloth, can be prevented water drop contact yarn, be prevented yarn
Line melting, wherein the parameter of the technique of yarn steaming is preferably 90 DEG C × 60min, and is vacuumized.
S2, following technique passed sequentially through to the fabric being prepared post-process, obtain finished product:
Wherein, post-processing the following steps are included:
Fabric sizing, open washing are boiled, braying, dye vat move back dimension, even boil, dry, singing, even boil, be formed, after soft, tank steams
To fabric.
Wherein every technological parameter is as follows:
Fabric sizing: 175 DEG C of temperature, speed 35m/min, overfeeding 4%, upper gate width 168cm;
Open washing boils: 85 DEG C of temperature, time 2min, speed 35m/min;
Braying: 40 DEG C of temperature, time 45min, speed 300m/min, 1loop=60m;
Dye vat removes PVA: 90 DEG C of temperature, time 20min;
Company boils: 85 DEG C of temperature, time 2min, speed 35m/min, wet door width 150cm;
Drying: 130 DEG C of temperature, time 0.3min, speed 35m/min, overfeeding 8%, upper gate width 150cm;
It singes: vertical burning, air pressure 8pa, speed 90m/min;
Company boils: 90 DEG C of temperature, time 3min, speed 20m/min, wet door width 11. 40cm
Drying: 130 DEG C of temperature, time 0.3min, speed 35m/min, overfeeding 8%, upper gate width 150cm
Sizing: 190 DEG C of temperature, time 1min, speed 15m/min, overfeeding 8%, upper gate width 150cm
Soft: softness scrapes 4g/L, 130 DEG C of temperature, time 0.3min, speed 35m/min, overfeeding 8%, upper gate width
150cm;
Tank steaming: cold 3min TMT pressure 1.5bar, first outer steaming 3min, again interior steaming 3min, is taken out again, finished door width 145cm is left
It is right.
The application is cooperated by the way that soluble polyvinylalcohol and spandex is added, and is matched by above-mentioned equivalent, polyvinyl blended and
Leaving gap is dissolved after post-processing, to assign the texture and certain elasticity of the application softness, and is closed using 200 superelevation
Stock twist factor has crease-resistant, machine washable, soft so that the product that the application is prepared finally has super-elastic property
The advantages that, it is suitble to the high-end business wear of production.
Properties test is carried out to the finished product that the application is prepared, it is shown that specifically test result is as follows:
The application polyvinyl is not incorporated in item dye recombing technique, is adjusted to be incorporated in spinning process, in preceding spinning
It after silver mixing adds grease, is added in scalp acupuncture technique, to can avoid polyvinyl contact wetting, and then avoids operating due to machine
Slight fever in the process causes polyvinyl to meet water and melts, adhesion caused, in addition, the application can also have preferable yarn evenness.
The application is in preparing weft yarn step, and polyvinyl covers yarn steaming using calico in secondary yarn steaming, to prevent water steam
Return condensate, suitable yarn can be steamed and prevent handle and yarn contacts moisture, cause polyvinyl contact wetting dissolve.
Weft yarn is designed using ultrahigh twist, and spinning weaving yarn generally combines twist factor 130~160, and the application uses
The 200 superelevation twist factors twisted, can assign the good elasticity of fabric and elasticity is restored, and by special raw material proportioning to assign
Fabric machine washability energy.
In aftertreatment technology, first braying, then dye vat move back dimension, the sky left in fabric after polyvinyl can be made full use of to dissolve
Gap can allow fabric to have the feel of fluffy softness.
During dye vat moves back dimension, the application uses fusing point for 70 DEG C of polyvinyl, and dye vat temperature setting is 90 DEG C, and is kept
On the one hand 20min can fully be dissolved polyvinyl, on the other hand can be retained again by above-mentioned technological parameter.
It is steamed in technique in tank, using small stepping tension, big vapor pressure conditions, so as to effectively improve the application system
The wrinkle resistance of standby finished product.
Embodiment described above is only to absolutely prove preferred embodiment that is of the invention and being lifted, protection model of the invention
It encloses without being limited thereto.Those skilled in the art's made equivalent substitute or transformation on the basis of the present invention, in the present invention
Protection scope within.Protection scope of the present invention is subject to claims.
Claims (8)
1. a kind of preparation method of high resiliency combing worsted spinning, which comprises the following steps:
S101, warp thread is prepared, use is spinning, by mass percentage by 30% wool and 70% blend polyester, obtains metric system
The warp thread that number is 70/2;
S102, weft yarn is prepared, use is spinning, by mass percentage by 25% wool, 55.5% terylene and 14.5% polyvinyl
It is blended, obtain the yarn of metric count 60/2, and will be blended after yarn and spandex spun core-spun yarn, the plying twist is viscous using 200
Spend coefficient;
S103, the warp thread and the weft yarn are organized into fabric;
S201, fabric is post-processed, fabric sizing successively is carried out to fabric, open washing boils, braying, dye vat moves back dimension, company boils, dries
It does, singe, even boil, be formed, soft, tank obtains fabric after steaming.
2. the preparation method of high resiliency combing worsted spinning as described in claim 1, which is characterized in that mixed in the step S101
Spinning successively comprises the following steps that:
Silver mixing, scalp acupuncture, two needles, three needles, four needles, head be thick, two thick, fine sand, yarn steamings, white winder, doubling, double twisting, yarn steaming,
It is blended in the step S102 successively to comprise the following steps that:
Silver mixing, scalp acupuncture, two needles, three needles, four needles, head be thick, two thick, fine sand, yarn steamings, white winder, doubling, double twisting, yarn steaming.
3. the preparation method of high resiliency combing worsted spinning as claimed in claim 2, which is characterized in that in the step S102,
The polyvinyl is added during the scalp acupuncture.
4. the preparation method of high resiliency combing worsted spinning as claimed in claim 2, which is characterized in that in the step S102,
The polyvinyl is covered during yarn steaming twice.
5. the preparation method of high resiliency combing worsted spinning as claimed in claim 2, which is characterized in that the polyvinyl is that fusing point is
70 DEG C of polyvinyl.
6. the preparation method of high resiliency combing worsted spinning as described in claim 1, which is characterized in that the weft density of the fabric
Degree is 312 × 274/10cm.
7. the preparation method of high resiliency combing worsted spinning as described in claim 1, which is characterized in that the dye vat pushes away the work of dimension
Skill parameter is 90 DEG C of temperature, time 20min.
8. a kind of high resiliency combing worsted spinning of preparation according to claim 1~any one of 7.