CN109370645B - 一种催化裂化汽油改质方法 - Google Patents
一种催化裂化汽油改质方法 Download PDFInfo
- Publication number
- CN109370645B CN109370645B CN201811346338.7A CN201811346338A CN109370645B CN 109370645 B CN109370645 B CN 109370645B CN 201811346338 A CN201811346338 A CN 201811346338A CN 109370645 B CN109370645 B CN 109370645B
- Authority
- CN
- China
- Prior art keywords
- catalyst
- gasoline
- oxide
- reaction
- nickel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
实施例/对比例 | 氧化锌 | 氧化镍 | ZSM-5 | 大孔氧化铝 | 铈锆固溶体 |
实施例1 | 37 | 17.3 | 23 | 17 | 5.7 |
实施例2 | 46 | 16 | 20 | 13 | 5.0 |
实施例3 | 29 | 20 | 33 | 13.5 | 4.5 |
实施例4 | 31 | 23 | 19 | 23.5 | 3.5 |
脱硫率/% | 辛烷值损失 | 穿透硫容/% | |
实施例1 | 98.9 | 0.3 | 29 |
实施例2 | 98.6 | 0.2 | 28 |
实施例3 | 99.8 | 0.2 | 30 |
实施例4 | 99.9 | 0.2 | 31 |
对比例1 | 98.2 | 2,4 | 28 |
对比例2 | 92.8 | 1.3 | 19 |
脱硫率/% | 辛烷值损失 | 穿透硫容/% | |
实施例1 | 98.8 | 0.3 | 29 |
实施例4 | 99.8 | 0.2 | 30 |
对比例1 | 94.1 | 2.6 | 25 |
对比例2 | 90.1 | 1.6 | 17 |
Claims (6)