CN109367175A - 一种拉丝膜复合材料以及包含其的包装材料和包装产品 - Google Patents

一种拉丝膜复合材料以及包含其的包装材料和包装产品 Download PDF

Info

Publication number
CN109367175A
CN109367175A CN201811177570.2A CN201811177570A CN109367175A CN 109367175 A CN109367175 A CN 109367175A CN 201811177570 A CN201811177570 A CN 201811177570A CN 109367175 A CN109367175 A CN 109367175A
Authority
CN
China
Prior art keywords
wire drawing
layer
drawing film
composite material
pet
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811177570.2A
Other languages
English (en)
Inventor
魏华友
代模
代平
刘彬
周建兵
周文强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHONGQING KEXIN PLASTIC Co Ltd
Original Assignee
CHONGQING KEXIN PLASTIC Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHONGQING KEXIN PLASTIC Co Ltd filed Critical CHONGQING KEXIN PLASTIC Co Ltd
Priority to CN201811177570.2A priority Critical patent/CN109367175A/zh
Publication of CN109367175A publication Critical patent/CN109367175A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种拉丝膜复合材料以及包含其的包装材料和包装产品。本发明所述拉丝膜复合材料依次包括：拉丝膜层，PET/VMPET阴阳膜层，牛皮纸层，以及聚丙烯层。本发明中，将具有金属质感的拉丝膜与具有磨砂质感的牛皮纸复合作为包装材料，所形成的复合材料不仅有金属光泽，同时还兼具牛皮纸质感，材料正反面差异化大，具有较好的装饰性。

Description

一种拉丝膜复合材料以及包含其的包装材料和包装产品
技术领域
本发明涉及材料领域，具体而言，涉及一种拉丝膜复合材料以及包含其的包装材料和包装产品。
背景技术
仿金属拉丝膜是近年来发展起来的一种新型装饰薄膜材料，主要作为产品表面装饰使用，由于仿金属拉丝膜具有和拉丝金属非常相似的外观和优越的成本优势，现已逐渐应用于日常生活的各个领域中，不仅能够作为电视机门板、冰箱门板、空调面板，以及电脑面板等各种家用电器的装饰材料，而且也能用于汽车、厨房设备，以及各类工业和建筑业的装饰中。
然而，目前对于拉丝膜的应用多仅限于装饰材料，对于应用领域的探索较少，而且，现有的拉丝材料结构较为简单固定，单纯的金属质感无法满足各类消费者和实际使用的需求。
有鉴于此，特提出本发明。
发明内容
本发明的第一目的在于提供一种拉丝膜复合材料，所述的拉丝膜复合材料将具有金属质感的拉丝膜与牛皮纸材料复合使用，具有装饰性强，质感好，感官差异化大等优点，同时还能够作为外包装材料使用。
本发明的第二目的在于提供一种包含本发明拉丝膜复合材料的包装材料。
本发明的第三目的在于提供一种包装产品。
为了实现本发明的上述目的，特采用以下技术方案：
一种拉丝膜复合材料，所述拉丝膜复合材料依次包括：拉丝膜层，PET/VMPET阴阳膜层，牛皮纸层，以及聚丙烯层。
优选的，本发明所述的拉丝膜复合材料中，所述拉丝膜层的厚度为：和/或，所述PET/VMPET膜层的厚度为：12μm；和/或，所述牛皮纸层的厚度为：35-120μm；和/或，所述聚丙烯层的厚度为：30-90μm。
优选的，本发明所述的拉丝膜复合材料中，所述拉丝膜层包括：PET拉丝薄膜；更优选的，所述PET拉丝薄膜为双向拉伸聚酯薄膜；进一步优选的，所述PET拉丝薄膜的厚度为10～100μm。
优选的，本发明所述的拉丝膜复合材料中，所述PET/VMPET阴阳膜层上还设置有附着力促进层以及真空镀铝层。
优选的，本发明所述的拉丝膜复合材料中，所述附着力促进层为改性丙烯酸树脂层。
优选的，本发明所述的拉丝膜复合材料中，所述丙烯酸树脂层主要由如下原料制备得到：丙烯酸单体，环氧树脂，乳化剂，以及交联剂。
优选的，本发明所述的拉丝膜复合材料中，所述PET拉丝薄膜的表面还设置有保护涂层。
优选的，本发明所述的拉丝膜复合材料中，所述保护涂层的主要原料包括：有机硅改性聚丙烯酸酯树脂，氟碳树脂，纯丙树脂，助剂，以及溶剂。
同时，本发明也提供了一种包装材料，所述包装材料包含本发明拉丝膜复合材料。
进一步的，本发明也提供了一种包装产品，所述包装产品的外包装结构中包含本发明包装材料。
与现有技术相比，本发明的有益效果为：
本发明中，将具有金属质感的拉丝膜与具有磨砂质感的牛皮纸复合作为包装材料，所形成的复合材料不仅有金属光泽，同时还兼具牛皮纸质感，材料正反面差异化大，具有较好的装饰性，同时在强光源照射下栩栩生辉，动感十足，成为抢手的卖点。
同时，本发明中，通过在复合材料拉丝膜层的PET薄膜表面设置防护涂层，也能够避免PET拉丝薄膜在使用中受损；胶粘层材料的选择和优化，也能够提高复合材料的整体性以及使用性能。
附图说明
为了更清楚地说明本发明实施例或现有技术中的技术方案，以下将对实施例或现有技术描述中所需要使用的附图作简单地介绍。
图1为本发明具体实施方式所提供的拉丝膜复合材料结构示意图；
图2为本发明具体实施方式所提供的拉丝膜层结构示意图；
图3为本发明具体实施方式所提供的PET/VMPET阴阳膜层结构示意图。
其中，图1中，1-拉丝膜层，2-PET/VMPET阴阳膜层，3-牛皮纸层，4-聚丙烯层。
图2中，101-PET拉丝薄膜，102-保护涂层。
图3中，201-PET/VMPET膜，202-附着力促进层，203-真空镀铝层。
具体实施方式
下面将结合实施例对本发明的实施方案进行详细描述，但是本领域技术人员将会理解，下列实施例仅用于说明本发明，而不应视为限制本发明的范围。实施例中未注明具体条件者，按照常规条件或制造商建议的条件进行。所用试剂或仪器未注明生产厂商者，均为可以通过市售购买获得的常规产品。
有鉴于现有仿金属拉丝膜在装饰性能以及应用领域探索等方面所存在的不足，本发明特提供了一种新型拉丝膜复合材料，以解决现有仿金属拉丝膜所存在的问题。
具体的，本发明所提供的拉丝膜复合材料，其由外至内依次包括：拉丝膜层，PET/VMPET阴阳膜层，牛皮纸层，以及聚丙烯层(在实际作为包装材料使用中，拉丝膜层在包装材料的最外层，与外部直接接触，而聚丙烯层则与包装内容物相接触)。
本发明中，创造性的将具有金属光泽的拉丝膜与具有磨砂感质地的牛皮纸复合，不仅能够作为具有优异性能的包装材料使用，同时还能够起到强烈的材质、质感的对比效果，从而达到良好的装饰作用。
同时，为了保证各层结构间能够紧密粘贴，本发明拉丝膜复合材料中，各层间还分别设置有粘合层。
即，优选的，本发明拉丝膜复合材料中，拉丝膜层的一侧通过第一粘结层与PET/VMPET阴阳膜层的一侧相粘结；PET/VMPET阴阳膜层的另一侧通过第二粘结层与牛皮纸层的一侧相粘结；牛皮纸层的另一侧通过第三粘结层与聚丙烯层的一侧相粘结；
其中，第一粘结层，第二粘结层，以及第三粘结层分别独立的为聚氨酯树脂层，聚丙烯酸树脂层，或者聚氨酯改性聚丙烯酸酯树脂层中的一种。
本发明拉丝膜复合材料中，拉丝膜层的厚度为：10-100μm，例如可以为，但不限于20、30、40、50、60、70、80，或者90μm；
PET/VMPET膜层的厚度为：12μm
牛皮纸层的厚度为：35-120μm，例如可以为，但不限于40、50、60、70、80、90、100，或者110μm；
聚丙烯层的厚度为：30-90μm，例如可以为，但不限于40、50、60、70，或者80μm。
同时，第一粘结层的厚度为0.1～5μm，例如可以为，但不限于0.5、1、1.5、2、2.5、3、3.5、4，或者4.5μm等；
第二粘结层的厚度为0.1～5μm，例如可以为，但不限于0.5、1、1.5、2、2.5、3、3.5、4，或者4.5μm等；
第三粘结层的厚度为0.1～5μm，例如可以为，但不限于0.5、1、1.5、2、2.5、3、3.5、4，或者4.5μm等。
作为拉丝膜复合材料最外层结构的拉丝膜，其为PET拉丝薄膜；
其中，PET拉丝薄膜为双向拉伸聚酯薄膜，其厚度为10～100μm，例如可以为，但不限于20、30、50、70，或者90μm等。
同时，为了避免作为最外层结构的PET拉丝薄膜在使用中被划伤影响其装饰性能，PET拉丝薄膜不与PET/VMPET阴阳膜层接触的一侧还设置有保护涂层。
进一步的，所述保护涂层由对应的涂料固化形成，用以制备涂料的原料为：有机硅改性聚丙烯酸酯树脂，氟碳树脂，纯丙树脂，助剂，以及溶剂；
其中，所述助剂包括：光引发剂、分散剂、消泡剂，以及流平剂；
所述光引发剂包括：过氧化二月桂酰；
所述溶剂包括：醋酸乙酯、醋酸丁酯。
保护涂层中各原料质量百分占比为：有机硅改性聚丙烯酸树脂10～30％，例如可以为，但不限于12、15、18、20、22、25，或者28％等；氟碳树脂25～45％，例如可以为，但不限于28、30、32、35、38、40，或者42％等；纯丙树脂：5～15％，例如可以为，但不限于8、10，或者12％等；光引发剂2～5％，分散剂0.5～1.5％，消泡剂0.5～1.5％，流平剂0.5～1.5％，溶剂10～30％，例如可以为，但不限于12、15、17、20、22、25，或者27％等。
如上所述用以形成保护涂层的涂料的制备方法可参照如下：
将树脂，溶剂，以及助剂在搅拌条件下混匀，即得到所述涂料。然后将所得涂料涂布于PET拉丝薄膜的表面，流平后光固化，即形成用于表面防护的保护涂层。
与拉丝膜层直接粘结复合的PET/VMPET膜层由外至内依次为：PET/VMPET膜，附着力促进层，以及真空镀铝层；
其中，附着力促进层的厚度为0.5～1.5μm，例如可以为，但不限于0.8、1，或者1.2μm等；
真空镀铝层的厚度为0.02～0.5μm，例如可以为，但不限于0.03、0.05、0.1、0.15、0.3、0.35、0.4，或者0.45μm等。
所述附着力促进层为改性丙烯酸树脂层，通过固化形成该材料层的改性丙烯酸胶粘剂由如下原料制备得到：丙烯酸单体，环氧树脂，乳化剂，以及交联剂；
进一步的，所述丙烯酸单体为：丙烯酸、丙烯酰胺、甲基丙烯酸、丙烯酸甲酯、丙烯酸乙酯、丙烯酸丁酯、甲基丙烯酸甲酯、丙烯酸羟乙酯、甲基丙烯酸羟乙酯、丙烯酸羟丙酯、甲基苯乙烯，以及苯乙烯中的一种或几种；
所述环氧树脂为：甲基丙烯酸环氧丙酯，水性环氧树脂中的一种或几种；
所述乳化剂为：阳离子乳化剂、非离子乳化剂，或其组合；
其中，阳离子乳化剂为：C12-C18的烷基季铵盐；非离子乳化剂为：烷基酚聚氧乙烯醚类，或者异构醇聚氧乙烯醚类中的一种或一种；
所述交联剂为：三烯丙基异三聚氰酸酯。
上述改性丙烯酸胶粘剂可以由如下方法制备得到：在高剪切分散条件下，将丙烯酸单体、环氧树脂、乳化剂，以及交联剂混合反应，即得到所述改性丙烯酸胶粘剂。
所制备的丙烯酸胶粘剂涂布于PET/VMPET膜的一侧后自然冷却，然后在所形成的改性丙烯酸树脂层上进行真空镀铝。
在PET/VMPET膜未与改性丙烯酸树脂层接触的一侧，以及在所形成真空镀铝层未与改性丙烯酸树脂层接触的一侧，分别涂布粘合剂，并与拉丝膜层、牛皮纸层，以及聚丙烯层复合，最终得到产品拉丝膜复合材料。
由如上方法所得到的拉丝膜复合材料不仅具有良好的装饰功能，同时还能够作为包装材料使用。因而，本发明也提供了一种以拉丝膜复合材料为主的包装材料，以及以该包装材料进行包装的包装产品。
实施例1
请参考图1，本发明所提供的拉丝膜复合材料由外至内料依次为：拉丝膜层1，PET阴阳膜层2，牛皮纸层3，以及聚丙烯层4；
其中，拉丝膜层1通过第一粘结层与PET阴阳膜层2相粘结，PET阴阳膜层2通过第二粘结层与牛皮纸层3相粘结，牛皮纸层3通过第三粘结层与聚丙烯层4相粘结。
进一步的，拉丝膜层1的厚度为50μm，PET阴阳膜层2的厚度为12μm，牛皮纸层3的厚度为100μm，聚丙烯层4的厚度为50μm。
实施例2
请参考图1，本发明所提供的拉丝膜复合材料由外至内料依次为：拉丝膜层1，VMPET阴阳膜层2，牛皮纸层3，以及聚丙烯层4；
其中，拉丝膜层1通过第一粘结层与VMPET阴阳膜层2相粘结，VMPET阴阳膜层2通过第二粘结层与牛皮纸层3相粘结，牛皮纸层3通过第三粘结层与聚丙烯层4相粘结。
进一步的，拉丝膜层1的厚度为20μm，VMPET阴阳膜层2的厚度为12μm，牛皮纸层3的厚度为50μm，聚丙烯层4的厚度为30μm。
实施例3
请参考图1以及图2，本发明所提供的拉丝复合模材料中，所述拉丝膜层为PET拉丝薄膜101；其中，PET拉丝薄膜101的厚度为80μm。
进一步的，PET拉丝薄膜101未与PET/VMPET阴阳膜层2接触的一侧还设置有保护涂层102。
实施例4
请参考图1以及图2，本发明所提供的拉丝复合模材料中，所述拉丝膜层1为PET拉丝薄膜101。
进一步的，PET拉丝薄膜101未与PET/VMPET阴阳膜层2接触的一侧还设置有保护涂层102；
其中，所述保护涂层102由涂料固化形成。
例如，可以以有机硅改性聚丙烯酸酯树脂，氟碳树脂，纯丙树脂，光引发剂、分散剂、消泡剂，以及流平剂，以及醋酸乙酯等为原料，通过搅拌混合，以得到涂料；
然后，将所得涂料涂布于PET拉丝薄膜101的一侧，固化后形成保护涂层102。
实施例5
请参考图1以及图3，本发明所提供的拉丝复合模材料中，PET阴阳膜层2由外至内依次为：PET膜201，附着力促进层202，以及真空镀铝层203；
其中，PET膜201的厚度为12μm，附着力促进层202的厚度为1.2μm，真空镀铝层203的厚度为0.05μm；
其中，所述附着力促进层202为改性丙烯酸树脂层，其可以由丙烯酸树脂乳液胶粘剂固化形成。
例如，可以以甲基丙烯酸甲酯、丙烯酸、丙烯酸丁酯，水性环氧树脂，烷基酚聚氧乙烯醚类非离子乳化剂，三烯丙基异三聚氰酸酯等为原料，通过混合搅拌聚合共聚，以得到对应的丙烯酸乳液胶粘剂；
然后，将聚丙烯酸乳液胶粘剂涂布于PET膜201的一侧，固化后形成附着力促进层202。
实施例6
请参考图1以及图3，本发明所提供的拉丝复合模材料中，VMPET阴阳膜层2由外至内依次为：VMPET膜201，附着力促进层202，以及真空镀铝层203；
其中，VMPET膜201的厚度为12μm，附着力促进层202的厚度为1.2μm，真空镀铝层203的厚度为0.05μm；
其中，所述附着力促进层202为改性丙烯酸树脂层，其可以由丙烯酸树脂乳液胶粘剂固化形成。
尽管已用具体实施例来说明和描述了本发明，然而应意识到，在不背离本发明的精神和范围的情况下可以作出许多其它的更改和修改。因此，这意味着在所附权利要求中包括属于本发明范围内的所有这些变化和修改。

Claims (10)

1.一种拉丝膜复合材料，其特征在于，所述拉丝膜复合材料依次包括：
拉丝膜层，PET/VMPET阴阳膜层，牛皮纸层，以及聚丙烯层。
2.根据权利要求1所述的拉丝膜复合材料，其特征在于，所述拉丝膜层的厚度为：10-100μm；
和/或，所述PET/VMPET阴阳膜层的厚度为：12μm；
和/或，所述牛皮纸层的厚度为：35-120μm；
和/或，所述聚丙烯层的厚度为：30-90μm。
3.根据权利要求1所述的拉丝膜复合材料，其特征在于，所述拉丝膜层包括PET拉丝薄膜。
优选的，所述PET拉丝薄膜为双向拉伸聚酯薄膜；
更优选的，所述PET拉丝薄膜的厚度为10～100μm。
4.根据权利要求1所述的拉丝膜复合材料，其特征在于，所述PET/VMPET阴阳膜层上还设置有附着力促进层以及真空镀铝层。
5.根据权利要求4所述的拉丝膜复合材料，其特征在于，所述附着力促进层为改性丙烯酸树脂层。
6.根据权利要求5所述的拉丝膜复合材料，其特征在于，所述丙烯酸树脂层主要由如下原料制备得到：
丙烯酸单体，环氧树脂，乳化剂，以及交联剂。
7.根据权利要求3所述的拉丝膜复合材料，其特征在于，PET拉丝薄膜的表面还设置有保护涂层。
8.根据权利要求7所述的拉丝膜复合材料，其特征在于，所述保护涂层的主要原料包括：
有机硅改性聚丙烯酸酯树脂，氟碳树脂，纯丙树脂，助剂，以及溶剂。
9.一种包装材料，其特征在于，所述包装材料包含权利要求1-8中任一项所述的拉丝膜复合材料。
10.一种包装产品，其特征在于，所述包装产品的外包装结构中包含权利要求9所述的包装材料。
CN201811177570.2A 2018-10-10 2018-10-10 一种拉丝膜复合材料以及包含其的包装材料和包装产品 Pending CN109367175A (zh)