CN109338042A - A kind of dedicated refining slag of ladle for reducing P element content in molten steel - Google Patents
A kind of dedicated refining slag of ladle for reducing P element content in molten steel Download PDFInfo
- Publication number
- CN109338042A CN109338042A CN201811429186.7A CN201811429186A CN109338042A CN 109338042 A CN109338042 A CN 109338042A CN 201811429186 A CN201811429186 A CN 201811429186A CN 109338042 A CN109338042 A CN 109338042A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- steel
- refining slag
- molten steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of dedicated refining slags of the ladle for reducing P element content in molten steel, comprise the following components in parts by weight: 5-10 parts of silica, 70-80 parts of active lime powder, 10-12 parts of Fluorspar Powder, AD3020-30 parts, 3-7 parts of magnesia powder, 10-12 parts of molybdenum powder, 3-5 parts of tungsten powder, 7-9 parts of chromium powder, 40-50 parts of pre-melted refining slag.Beneficial effects of the present invention, since this invention takes above-mentioned technical proposals, compared with prior art, the present invention has fusing point low, and viscosity coefficient of dross is small, good fluidity, slagging are fast;Slag charge sulfur capacity is big, preferable desulfurization, deoxidation, dephosphorization effect, while can effectively adsorb steel inclusion, improves Molten Steel Cleanliness, can reduce the advantages of steel-making cost again.The P element in steel is reduced, and steel is enabled to be resistant to low temperature.
Description
Technical field
The present invention relates to a kind of field of metallurgy, the dedicated essence of specifically a kind of ladle for reducing P element content in molten steel
Refine slag.
Background technique
Currently, the ladle refining slag that steel mill of China uses is mostly used in refining furnace, have fritting and non-fritting, add
In refining furnace refining 30-50min after entering, the purpose of molten steel of refining, balanced molten steel composition is played.But for current some matter
Amount requires less high steel grade, and many steel mills are all reluctant by refining furnace, if because one heat steel water is averaged by refining furnace
Cost will at least increase by 80 yuan or more, in the case where existing market profit margin is smaller and smaller, all not upper essence of many steel mills
Refining.But as market is higher and higher to product quality requirement, if the quantity of slag is big under converter, molten iron is not again preprocessed, section is smelted
It plays fastly, Molten Steel Cleanliness will be caused to reduce in this way, phosphorus sulfur content is higher, leads to cast internal segregation aggravation in bad process of setting, has
Evil material collection, can cause to cast when serious it is bad it is internal there is defect, it is final to influence mentioning for internal quality of steel plate and mechanical performance
Height influences client's use, limit product sale, to influence the profit of enterprise.
Summary of the invention
The purpose of the present invention is to provide topics, to solve the problems mentioned in the above background technology.
To achieve the above object, this explanation provides the following technical solutions: a kind of steel for reducing P element content in molten steel
Dedicated refining slag is wrapped, is comprised the following components in parts by weight: 5-10 parts of silica, 70-80 parts of active lime powder, Fluorspar Powder
10-12 parts, AD3020-30 parts, 3-7 parts of magnesia powder, 10-12 parts of molybdenum powder, 3-5 parts of tungsten powder, 7-9 parts of chromium powder, pre-melted refining slag
40-50 parts.
Further, it comprises the following components in parts by weight: 5 parts of silica, 70 parts of active lime powder, Fluorspar Powder 10
Part, AD3020 parts, 3 parts of magnesia powder, 10 parts of molybdenum powder, 3 parts of tungsten powder, 7 parts of chromium powder, 40 parts of pre-melted refining slag.
Further, it comprises the following components in parts by weight: 8 parts of silica, 75 parts of active lime powder, Fluorspar Powder 11
Part, AD3025 parts, 4 parts of magnesia powder, 11 parts of molybdenum powder, 4 parts of tungsten powder, 8 parts of chromium powder, 45 parts of pre-melted refining slag.
Further, it comprises the following components in parts by weight: 0 part of silica 1,80 parts of active lime powder, Fluorspar Powder 12
Part, AD3030 parts, 7 parts of magnesia powder, 12 parts of molybdenum powder, 5 parts of tungsten powder, 9 parts of chromium powder, 50 parts of pre-melted refining slag.
Compared with prior art, the beneficial effects of the present invention are: beneficial effects of the present invention, since this invention takes upper
Technical solution is stated, compared with prior art, the present invention has fusing point low, and viscosity coefficient of dross is small, good fluidity, slagging are fast;Slag charge sulphur
Capacity is big, preferable desulfurization, deoxidation, dephosphorization effect, while can effectively adsorb steel inclusion, improves Molten Steel Cleanliness, again
The advantages of steel-making cost can be reduced.The P element in steel is reduced, and steel is enabled to be resistant to low temperature.
Specific embodiment
The following is a clear and complete description of the technical scheme in the embodiments of the invention, it is clear that described embodiment
Only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's every other embodiment obtained without making creative work belongs to what the present invention protected
Range.
Embodiment 1:
A kind of dedicated refining slag of ladle for reducing P element content in molten steel, comprises the following components in parts by weight: dioxy
5 parts of SiClx, 70 parts of active lime powder, 10 parts of Fluorspar Powder, AD3020 parts, 3 parts of magnesia powder, 10 parts of molybdenum powder, 3 parts of tungsten powder, chromium powder
7 parts, 40 parts of pre-melted refining slag.
Embodiment 2:
A kind of dedicated refining slag of ladle for reducing P element content in molten steel, comprises the following components in parts by weight: dioxy
8 parts of SiClx, 75 parts of active lime powder, 11 parts of Fluorspar Powder, AD3025 parts, 4 parts of magnesia powder, 11 parts of molybdenum powder, 4 parts of tungsten powder, chromium powder
8 parts, 45 parts of pre-melted refining slag.
Embodiment 3:
A kind of dedicated refining slag of ladle for reducing P element content in molten steel, comprises the following components in parts by weight: dioxy
10 parts of SiClx, 80 parts of active lime powder, 12 parts of Fluorspar Powder, AD3030 parts, 7 parts of magnesia powder, 12 parts of molybdenum powder, 5 parts of tungsten powder, chromium
9 parts of powder, 50 parts of pre-melted refining slag.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, nothing
By from the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by institute
Attached claim rather than foregoing invention limit, it is intended that will fall within the meaning and scope of the equivalent elements of the claims
All changes be included within the present invention.
Although not each embodiment is only wrapped in addition, it should be understood that present specification is described in terms of embodiments
Containing an independent technical solution, this narrating mode of invention book is merely for the sake of clarity, and those skilled in the art should
As a whole by invention book, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (4)
1. a kind of dedicated refining slag of ladle for reducing P element content in molten steel, which is characterized in that including following parts by weight
Component: 5-10 parts of silica, 70-80 parts of active lime powder, 10-12 parts of Fluorspar Powder, AD3020-30 parts, 3-7 parts of magnesia powder,
10-12 parts of molybdenum powder, 3-5 parts of tungsten powder, 7-9 parts of chromium powder, 40-50 parts of pre-melted refining slag.
2. the dedicated refining slag of a kind of ladle for reducing P element content in molten steel according to claim 1, feature exist
In comprising the following components in parts by weight: 5 parts of silica, 70 parts of active lime powder, 10 parts of Fluorspar Powder, AD3020 parts, magnesia
3 parts of powder, 10 parts of molybdenum powder, 3 parts of tungsten powder, 7 parts of chromium powder, 40 parts of pre-melted refining slag.
3. the dedicated refining slag of a kind of ladle for reducing P element content in molten steel according to claim 1, feature exist
In comprising the following components in parts by weight: 8 parts of silica, 75 parts of active lime powder, 11 parts of Fluorspar Powder, AD3025 parts, magnesia
4 parts of powder, 11 parts of molybdenum powder, 4 parts of tungsten powder, 8 parts of chromium powder, 45 parts of pre-melted refining slag.
4. the dedicated refining slag of a kind of ladle for reducing P element content in molten steel according to claim 1, feature exist
In comprising the following components in parts by weight: 0 part of silica 1,80 parts of active lime powder, 12 parts of Fluorspar Powder, AD3030 parts, magnesia
7 parts of powder, 12 parts of molybdenum powder, 5 parts of tungsten powder, 9 parts of chromium powder, 50 parts of pre-melted refining slag.