CN109337655A - 高效环保载冷剂及其制备方法 - Google Patents
高效环保载冷剂及其制备方法 Download PDFInfo
- Publication number
- CN109337655A CN109337655A CN201811168954.8A CN201811168954A CN109337655A CN 109337655 A CN109337655 A CN 109337655A CN 201811168954 A CN201811168954 A CN 201811168954A CN 109337655 A CN109337655 A CN 109337655A
- Authority
- CN
- China
- Prior art keywords
- refrigerating medium
- environment friendly
- parts
- efficiency environment
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及制冷剂技术领域,具体涉及高效环保载冷剂及其制备方法;包括以下原料:有机酸盐、丙烯、乙二醇、防腐剂、水;一种高效环保载冷剂的制备方法,包括如下步骤:S1、按上述配方取有机酸盐、丙烯、乙二醇、防腐剂、水,备用;S2、将有机酸盐与水置于真空容器中混合6小时,制得第一溶液;S3、将S2制得的第一溶液依次加入丙酸、乙二醇与防腐剂混合均匀,即制得高效环保载冷剂;本载冷剂加入了防腐剂,能够在保证高效制冷情况下,不会对承载设备造成腐蚀,使设备使用安全性大幅度提高。
Description
技术领域
本发明涉及制冷剂技术领域,具体涉及高效环保载冷剂及其制备方法。
背景技术
载冷剂是在间接冷却的制冷装置中,完成将被冷却***的热量传递给制冷剂的中间冷却介质;载冷剂的种类较多,可以是气体、液体及固体,常用载冷剂水、盐水和乙二醇,然而现有的载冷剂在适用性和环保性有所不足,对承载设备有一定的腐蚀性,从而造成安全隐患。
发明内容
本发明的目的在于提供一种高效环保载冷剂及其制备方法,不仅能保证载冷剂的适用性与环保性,而且能够解决腐蚀设备问题。
为解决上述的技术问题,本发明采用以下技术方案:
高效环保载冷剂,包括以下原料:有机酸盐、丙烯、乙二醇、防腐剂、水。
进一步,包括以下组分原料:有机酸盐20-30份、丙烯10-20份、乙二醇30-40份、防腐剂2-8份、水50-70份。
进一步,包括以下组分原料:机酸盐25份、丙烯15份、乙二醇35份、防腐剂6份、水60份。
进一步,所述有机酸盐为二甲酸、磷酸盐、亚硝酸、钠盐、乙酸钠或亚磷酸中的一种。
进一步,所述水为超纯水。
一种高效环保载冷剂的制备方法,包括如下步骤:
S1、按上述配方取有机酸盐、丙烯、乙二醇、防腐剂、水,备用;
S2、将有机酸盐与水置于真空容器中混合5-8小时,制得第一溶液;
S3、将S2制得的第一溶液依次加入丙酸、乙二醇与防腐剂混合均匀,即制得高效环保载冷剂;
进一步,在所述的制备方法中,在步骤S2中有机酸盐与水的比例为1:5。
与现有技术相比,本发明有益效果是:
1.本载冷剂比热大,粘度低等特性,有利于设备的持久运行。
2.本载冷剂加入了一定量防腐剂,不会对承载设备造成腐蚀,使设备使用安全性大幅度提高。
3.本载冷剂适用性较高,无须更换设备,直接使用即可,且有较高的环保性。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白,以下结合实施例,对本发明进行进一步详细说明。应当理解,此处所描述的具体实施例仅仅用以解释本发明,并不用于限定本发明。
实施例1:
高效环保载冷剂,包括以下原料:有机酸盐、丙烯、乙二醇、防腐剂、水;本载冷剂加入了防腐剂,能够在保证高效制冷情况下,不会对承载设备造成腐蚀,使设备使用安全性大幅度提高。
实施例2:
高效环保载冷剂,包括以下组分原料:有机酸盐10份、丙烯5份、乙二醇30份、防腐剂4份、水55份;本载冷剂加入了防腐剂,能够在保证高效制冷情况下,不会对承载设备造成腐蚀,使设备使用安全性大幅度提高。
实施例3:
高效环保载冷剂,包括以下组分原料:有机酸盐15份、丙烯10份、乙二醇35份、防腐剂6份、水60份;本载冷剂加入了防腐剂,能够在保证高效制冷情况下,不会对承载设备造成腐蚀,使设备使用安全性大幅度提高。
实施例4:
高效环保载冷剂,包括以下组分原料:有机酸盐20份、丙烯15份、乙二醇40份、防腐剂8份、水65份;本载冷剂加入了防腐剂,能够在保证高效制冷情况下,不会对承载设备造成腐蚀,使设备使用安全性大幅度提高。
实施例5:
在实施例1-4的基础上,所述有机酸盐为二甲酸、磷酸盐、亚硝酸、钠盐、乙酸钠或亚磷酸中的一种。
实施例6:
在实施例1-4的基础上,所述水为超纯水。
实施例7:
高效环保载冷剂,包括以下组分原料:有机酸盐10份、丙烯5份、乙二醇30份、防腐剂4份、水55份;
以上所述的一种高效环保载冷剂的制备方法,包括如下步骤:
S1、按上述配方取有机酸盐、丙烯、乙二醇、防腐剂、水,备用;
S2、将有机酸盐与水置于真空容器中混合5-8小时,制得第一溶液;
S3、将S2制得的第一溶液依次加入丙酸、乙二醇与防腐剂混合均匀,即制得高效环保载冷剂;
本发明在常温下制备,将有机酸盐与水置于真空容器中混合6小时,制得第一溶液;将S2制得的第一溶液依次加入丙酸、乙二醇与防腐剂混合均匀,即制得高效环保载冷剂。
实施例8:
高效环保载冷剂,包括以下组分原料:有机酸盐15份、丙烯10份、乙二醇35份、防腐剂6份、水60份
以上所述一种高效环保载冷剂的制备方法,包括如下步骤:
S1、按上述配方取有机酸盐、丙烯、乙二醇、防腐剂、水,备用;
S2、将有机酸盐与水置于真空容器中混合5-8小时,制得第一溶液;
S3、将S2制得的第一溶液依次加入丙酸、乙二醇与防腐剂混合均匀,即制得高效环保载冷剂;
本发明在常温下制备,将有机酸盐与水置于真空容器中混合6小时,制得第一溶液;将S2制得的第一溶液依次加入丙酸、乙二醇与防腐剂混合均匀,即制得高效环保载冷剂。
实施例9:
高效环保载冷剂,包括以下组分原料:有机酸盐20份、丙烯15份、乙二醇40份、防腐剂8份、水65份;
以上所述一种高效环保载冷剂的制备方法,包括如下步骤:
S1、按上述配方取有机酸盐、丙烯、乙二醇、防腐剂、水,备用;
S2、将有机酸盐与水置于真空容器中混合5-8小时,制得第一溶液;
S3、将S2制得的第一溶液依次加入丙酸、乙二醇与防腐剂混合均匀,即制得高效环保载冷剂;
本发明在常温下制备,将有机酸盐与水置于真空容器中混合6小时,制得第一溶液;将S2制得的第一溶液依次加入丙酸、乙二醇与防腐剂混合均匀,即制得高效环保载冷剂。
尽管这里参照本发明的多个解释性实施例对本发明进行了描述,但是,应该理解,本领域技术人员可以设计出很多其他的修改和实施方式,这些修改和实施方式将落在本申请公开的原则范围和精神之内。更具体地说,在本申请公开权利要求的范围内,可以对主题组合布局的组成部件和/或布局进行多种变型和改进。除了对组成部件和/或布局进行的变形和改进外,对于本领域技术人员来说,其他的用途也将是明显的。
Claims (7)
1.高效环保载冷剂,其特征在于:包括以下原料:有机酸盐、丙烯、乙二醇、防腐剂、水。
2.根据权利要求1所述的高效环保载冷剂,其特征在于:包括以下组分原料:有机酸盐20-30份、丙烯10-20份、乙二醇30-40份、防腐剂2-8份、水50-70份。
3.根据权利要求1所述的高效环保载冷剂,其特征在于:包括以下组分原料:有机酸盐25份、丙烯15份、乙二醇35份、防腐剂6份、水60份。
4.根据权利要求1所述的高效环保载冷剂,其特征在于:所述有机酸盐为二甲酸、磷酸盐、亚硝酸、钠盐、乙酸钠或亚磷酸中的一种。
5.根据权利要求1所述的高效环保载冷剂,其特征在于:所述水为超纯水。
6.根据权利要求1-3任意一条权利要求所述的高效环保载冷剂的制备方法,其特征在于:包括如下步骤:
S1、按上述配方取有机酸盐、丙烯、乙二醇、防腐剂、水,备用;
S2、将有机酸盐与水置于真空容器中混合5-8小时,制得第一溶液;
S3、将S2制得的第一溶液依次加入丙酸、乙二醇与防腐剂混合均匀,即制得高效环保载冷剂;
7.根据权利要求6所述的高效环保载冷剂的制备方法,其特征在于:在步骤S2中有机酸盐与水的比例为1:5。