CN109337299A - A kind of modified vinyl anchoring adhesive and preparation method thereof - Google Patents
A kind of modified vinyl anchoring adhesive and preparation method thereof Download PDFInfo
- Publication number
- CN109337299A CN109337299A CN201811057139.4A CN201811057139A CN109337299A CN 109337299 A CN109337299 A CN 109337299A CN 201811057139 A CN201811057139 A CN 201811057139A CN 109337299 A CN109337299 A CN 109337299A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- anchoring adhesive
- epoxy
- vinyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of modified vinyl anchoring adhesives and preparation method thereof, the modified vinyl anchoring adhesive includes component A and B component, and the component A includes the raw material of following mass fraction: 35-60 parts of vinyl ester resin, the polymerizable olefinic of olefinic be modifying agent 15-30 parts polymerizable, 5-10 parts of toughener, 0.1-2 parts of coupling agent, 0.5-5 parts of promotor, 10-20 parts of filler;The B component includes: 25-40 parts of curing agent, 10-25 parts of initiator, 10-20 parts of diluent.Bar planting adhesive force prepared by the present invention is strong, ageing-resistant performance is good, curing time is short, can use with rust, the anchoring of suitable various types of materials.
Description
Technical field
The present invention relates to chemical material field, in particular to a kind of modified vinyl anchoring adhesive and preparation method thereof.
Background technique
In building field, with the development and growth of some new industries in China, not only the dosage of anchoring adhesive is increasing,
And it is also higher and higher to the quality requirement of anchoring adhesive.There are many shortcomings for original adhesive technology and adhesive, such as with
Hot melt glue or polystyrene colloidal are unfavorable for the health of decoration construction personnel wherein there is 40% or more low molecule solvent.
Market major part anchoring adhesive has that brittleness is big, volatilization deal is big, pollution air, low appearances of gelatin viscosity are trickled phenomenon and storage life
The disadvantages of short.
In real engineer operation, bar planting construction team can encounter the repairing work of many road surfaces, bridge, ground etc..This
Require the process time-consuming of bar planting short, high-quality.Current problem is: the curing time in order to shorten anchoring adhesive, manufacturer's meeting
The curing agent and promotor of selection addition large dosage.Curing time is shortened although doing so, the elasticity and toughness of glue are straight
Line decline.Many workers reaction does not have also etc. and to be fully cured, and glue has just split.In order to solve this problem, inventor optimizes
Raw material, adjustment curing agent dosage, finally obtain that a kind of curing time is short, can effectively improve the anchoring adhesive of construction efficiency.The plant
The phenomenon that muscle glue is not in cracking in the curing process, and cementitiousness, ageing-resistant performance are met the quality standard.
It is well known that anchoring adhesive is for reinforcing bar, screw rod heeling-in in various building structure;Railway, highway, bridge, water conservancy change
Extension project is reinforced;Billboard, tunnel pipeline, overpass soundproof plate and guardrail are fixed.But in use, constructor
Member must by the rebar surface to be fixed carry out processing of rust removing and with acetone or alcohol wipe it is clean, otherwise will affect fixation.
But in face of some heavy constructions, derusting staff inevitably will appear careless mistake, may finally make because of these minor issues
At serious consequence.In order to settle the matter once and for all, in this application, inventor obtains one by modified vinyl resin
The anchoring adhesive that kind reinforcing bar can be used with rust, it is as a result satisfactory by live pullout tests.At present it is demonstrated experimentally that institute of the present invention
The anchoring adhesive stated to rust area be 2-6% reinforcing bar can normal use, the target of research staff is, from now on by adjusting raw material
Type and proportion, develop to rust area be 10% or so reinforcing bar can also normal use anchoring adhesive.
In conclusion the present invention provides, a kind of cohesive force is strong, ageing-resistant performance is good, curing time is short, can use with rust
Anchoring adhesive.
Summary of the invention
The object of the present invention is to provide a kind of modified vinyl anchoring adhesives and preparation method thereof.The modified anchoring adhesive is viscous
Knot power and under the premise of resistance to ag(e)ing meets the quality standard, curing time is short, band become rusty area≤6% reinforcing bar can normal use,
Bar planting effect is not influenced.
A kind of modified vinyl anchoring adhesive, including component A and B component, the component A include the original of following mass fraction
Material: 35-60 parts of vinyl ester resin, olefinic are modifying agent 15-30 parts polymerizable, 5-10 parts of toughener, 0.1-2 parts of coupling agent, promote
Into 0.5-5 parts of agent, 10-20 parts of filler;The B component includes: 25-40 parts of curing agent, 10-25 parts of initiator, diluent 10-20
Part.
Preferably, the vinyl ester resin is selected from: bisphenol-A epoxy vinyl esters, flame retardant type epoxy vinyl ester, phenolic aldehyde
The combination of one or more of epoxy vinyl ester.
The preferred FX-431 of bisphenol-A epoxy vinyl esters
The preferred FX-451 of flame retardant type epoxy vinyl ester
Epoxy novolac vinyl esters preferred FX-470S, coloration 0-10Gardner, acid value 6-18KOH mg/g, viscosity 700-
1000mpa.s, vinyl ester resin used in the present invention can be selected from the ethylene of prosperous chemical industry goods and materials Co., Ltd of Changzhou side production
Base ester resin.
The polymerizable modifying agent of olefinic is selected from: acrylic acid, methyl methacrylate, epoxy acrylate, polyurethane third
The combination of one or more of olefin(e) acid ester.
Preferably, the polymerizable modifying agent of the olefinic is selected from: 2-5 parts of acrylic acid, 5-10 parts of epoxy acrylate and poly- ammonia
The combination that 8-15 parts of ester acrylate;5-8 parts of methyl methacrylate, 2-10 parts of epoxy acrylate and urethane acrylate
8-12 parts of combination;1-3 parts of acrylic acid, 4-6 parts of methyl methacrylate, 5-8 parts of epoxy acrylate and polyurethane acroleic acid
The combination that 5-13 parts of ester.
In a preferred embodiment of the present invention, the component A of the modified vinyl anchoring adhesive includes: vinyl esters
45-60 parts of resin, 2-5 parts of acrylic acid, 5-10 parts of epoxy acrylate, 8-15 parts of urethane acrylate, 5-10 parts of toughener,
0.5-1.5 parts of coupling agent, 1-4 parts of promotor, 15-20 parts of filler;The B component includes: 30-40 parts of curing agent, initiator 15-
22 parts, 15-20 parts of diluent.
In another preferred embodiment of the present invention, the component A of the modified vinyl anchoring adhesive includes: vinyl
45-60 parts of ester resin, 2-10 parts of epoxy acrylate, 8-12 parts of urethane acrylate, increases 5-8 parts of methyl methacrylate
Tough dose 5-10 parts, 0.5-1.5 parts of coupling agent, 1-4 parts of promotor, 15-20 parts of filler;The B component includes: curing agent 30-40
Part, 15-22 parts of initiator, 15-20 parts of diluent.
In an also preferred embodiment of the invention, the component A of the modified vinyl anchoring adhesive includes: vinyl
45-60 parts of ester resin, 1-3 parts of acrylic acid, 4-6 parts of methyl methacrylate, 5-8 parts of epoxy acrylate, polyurethane acroleic acid
5-13 parts of ester, 5-10 parts of toughener, 0.5-1.5 parts of coupling agent, 1-4 parts of promotor, 15-20 parts of filler;The B component includes:
30-40 parts of curing agent, 15-22 parts of initiator, 15-20 parts of diluent.
It is furthermore preferred that the additive is selected from: 1-3 parts of acrylic acid, 4-6 parts of methyl methacrylate, epoxy acrylate
5-8 parts and urethane acrylate 5-13 parts of combination.
Most preferably, the additive is selected from: 3 parts of acrylic acid, 5 parts of methyl methacrylate, 7 parts of epoxy acrylate and
The combination that 10 parts of urethane acrylate.
The toughener is selected from: the group of one or both of nitrile rubber, acrylonitrile-butadiene-styrene copolymer
It closes.
The coupling agent is selected from: γ-(the third oxygen of 2,3- epoxy) propyl trimethoxy silicane, 3- glycydoxy
The combination of one or more of trimethoxy silane, mercaptopropyl trimethoxysilane.
The promotor is selected from: the combination of one or more of N.N- dimethylaniline, triethanolamine.
The curing agent is selected from: vinyl triamine, diethylenetriamine, tetraethylenepentamine, two one of base triamine or
Two or more combinations.
The initiator is selected from: benzoyl peroxide, peroxidating 2,4 dichloro benzene formyl, cyclohexanone peroxide, peroxidating
The combination of one or more of methyl ethyl ketone.
The diluent is the fumed silica handled with silane coupling agent, and wherein silane coupling agent is selected from: 2- (3,
4- 7-oxa-bicyclo[4.1.0) ethyl trimethoxy silane, gamma-aminopropyl-triethoxy-silane, aminopropyl trimethoxysilane, N- β (ammonia
Ethyl)-γ-aminopropyltrimethoxysilane, one or more of triamido silane combination.
The filler is selected from: the combination of one or more of titanium dioxide, talcum powder, dolomite dust, quartz sand.
A method of modified vinyl anchoring adhesive is prepared, is included the following steps:
(1) under room temperature, device is added in vinyl ester resin, the polymerizable modifying agent of olefinic, coupling agent, toughener and promotor
It is stirred evenly in ware, adds filler, continued to stir, be warming up to 65-80 DEG C, vacuumize, A group is prepared after stirring 2-3h
Point;
(2) under room temperature, curing agent, initiator and diluent is stirred evenly, B component is prepared;
(3) in mass ratio it is that 100:4-8 is mixed by component A and B component, quickly stirs 15-30min and modified second is prepared
Alkenyl anchoring adhesive.
Modified vinyl anchoring adhesive of the present invention is in the fixation of various equipment and/or railway, highway, bridge, water conservancy
Application in engineering.
The beneficial effects of the present invention are inventor is made by the proportion of modified ethenyl resin and optimization each component
The bar planting adhesive force that must be prepared is strong, heat and moisture aging resistance is good, while curing time is short in the higher environment of temperature not
Influence operable time, can with rust use, to band become rusty area≤6% reinforcing bar can normal use, do not influence bar planting effect.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only section Example of the invention, rather than all.Based on the embodiments of the present invention, those of ordinary skill in the art exist
Every other embodiment obtained under the premise of creative work is not made, shall fall within the protection scope of the present invention.
The preparation of 1 modified vinyl anchoring adhesive 1 of embodiment
Under room temperature, by 60 parts of FX-451,5 parts of acrylic acid, 10 parts of epoxy acrylate, 15 parts of urethane acrylate, fourth
10 parts of nitrile rubber, γ-(the third oxygen of 2,3- epoxy) 1 part of propyl trimethoxy silicane, in 2 parts of addition stirred tanks of N.N- dimethylaniline
It stirs evenly, adds 20 parts of quartz sand, continue to stir, be warming up to 80 DEG C, vacuumize, component A is prepared after stirring 3h;Often
Under temperature, at 10 parts of vinyl triamine, 30 parts of diethylenetriamine, 22 parts of benzoyl peroxide, gamma-aminopropyl-triethoxy-silane
20 parts of fumed silica of reason stir evenly, and B component is prepared;Component A and B component are mixed in mass ratio for 100:4
It closes, quickly stirs 30min and modified vinyl anchoring adhesive 1 is prepared.
The preparation of 2 modified vinyl anchoring adhesive 2 of embodiment
Under room temperature, by 60 parts of FX-451,8 parts of methyl methacrylate, 10 parts of epoxy acrylate, polyurethane acroleic acid
12 parts of ester, 10 parts of nitrile rubber, γ-(the third oxygen of 2,3- epoxy) 1 part of propyl trimethoxy silicane, 2 parts of N.N- dimethylaniline plus
Enter in stirred tank and stir evenly, add 20 parts of quartz sand, continue to stir, be warming up to 80 DEG C, vacuumize, is prepared into after stirring 3h
To component A;Under room temperature, by 10 parts of vinyl triamine, 30 parts of diethylenetriamine, 22 parts of benzoyl peroxide, three second of γ-aminopropyl
20 parts of fumed silica of oxysilane processing stir evenly, and B component is prepared;In mass ratio by component A and B component
For 100:4 mixing, quickly stirs 30min and modified vinyl anchoring adhesive 2 is prepared.
The preparation of 3 modified vinyl anchoring adhesive 3 of embodiment
Under room temperature, by 60 parts of FX-451,3 parts of acrylic acid, 6 parts of methyl methacrylate, 8 parts of epoxy acrylate, poly- ammonia
13 parts of ester acrylate, 10 parts of nitrile rubber, γ-(the third oxygen of 2,3- epoxy) 1 part of propyl trimethoxy silicane, N.N- dimethyl benzene
It is stirred evenly in 2 parts of addition stirred tanks of amine, adds 20 parts of quartz sand, continue to stir, be warming up to 80 DEG C, vacuumize, stir 3h
After component A is prepared;Under room temperature, by 10 parts of vinyl triamine, 30 parts of diethylenetriamine, 22 parts of benzoyl peroxide, γ-ammonia
20 parts of fumed silica of propyl-triethoxysilicane processing stir evenly, and B component is prepared;By component A and B component
It is mixed in mass ratio for 100:4, quickly stirs 30min and modified vinyl anchoring adhesive 3 is prepared.
The preparation of 4 modified vinyl anchoring adhesive 4 of embodiment
Under room temperature, by 60 parts of FX-451,3 parts of acrylic acid, 6 parts of methyl methacrylate, 13 parts of urethane acrylate,
2 parts of 10 parts of nitrile rubber, γ-(the third oxygen of 2,3- epoxy) 1 part of propyl trimethoxy silicane, N.N- dimethylaniline addition stirred tanks
In stir evenly, add 20 parts of quartz sand, continue to stir, be warming up to 80 DEG C, vacuumize, stir 3h after component A is prepared;
Under room temperature, by 10 parts of vinyl triamine, 30 parts of diethylenetriamine, 22 parts of benzoyl peroxide, gamma-aminopropyl-triethoxy-silane
20 parts of fumed silica of processing stir evenly, and B component is prepared;It is in mass ratio 100:4 by component A and B component
Mixing quickly stirs 30min and modified vinyl anchoring adhesive 4 is prepared.
The preparation of 5 modified vinyl anchoring adhesive 5 of embodiment
Under room temperature, by 60 parts of FX-451,3 parts of acrylic acid, 6 parts of methyl methacrylate, 8 parts of epoxy acrylate, butyronitrile
10 parts of rubber, γ-(the third oxygen of 2,3- epoxy) 1 part of propyl trimethoxy silicane stir in 2 parts of addition stirred tanks of N.N- dimethylaniline
It mixes uniformly, adds 20 parts of quartz sand, continue to stir, be warming up to 80 DEG C, vacuumize, component A is prepared after stirring 3h;Room temperature
Under, by 10 parts of vinyl triamine, 30 parts of diethylenetriamine, 22 parts of benzoyl peroxide, gamma-aminopropyl-triethoxy-silane processing
20 parts of fumed silica stir evenly, B component is prepared;It is in mass ratio that 100:4 is mixed by component A and B component,
Quickly modified vinyl anchoring adhesive 5 is prepared in stirring 30min.
The preparation of the non-modified vinyl anchoring adhesive of comparative example 1 comparison 1
Under room temperature, by 60 parts of FX-451,10 parts of nitrile rubber, γ-(2,3- the third oxygen of epoxy) propyl trimethoxy silicane 1
It is stirred evenly in 2 parts of part, N.N- dimethylaniline addition stirred tanks, adds 20 parts of quartz sand, continue to stir, be warming up to 80
DEG C, it vacuumizes, component A is prepared after stirring 3h;Under room temperature, by 10 parts of vinyl triamine, 30 parts of diethylenetriamine, peroxidating
22 parts of benzoyl, gamma-aminopropyl-triethoxy-silane processing 20 parts of fumed silica stir evenly, B group is prepared
Point;In mass ratio it is that 100:4 is mixed by component A and B component, quickly stirs 30min and non-modified vinyl anchoring adhesive is prepared
Comparison 1.
The test of 1 anchoring adhesive safe performance indexes of performance test
By anchoring adhesive prepared in the above embodiments according to quality standard, its safe performance indexes is tested, as a result such as
Shown in following table:
1 anchoring adhesive safe performance indexes of table
Bond strength 1 in above-mentioned table indicates: Ribbed Bar and concrete is glutinous under C30 ∮ 25L=150mm drawing condition
Knotting strength;Bond strength 2 indicates: the bond strength of Ribbed Bar and concrete under C60 ∮ 25L=125mm drawing condition.
The difference of embodiment 1-5 is only that the difference of the polymerizable modifying agent of olefinic, and comparative example 1, which does not add olefinic, to gather
Close modifying agent.According to the above results as can be seen that the polymerizable modifying agent of olefinic selects acrylic acid, methyl methacrylate, epoxy
When the combination of acrylate and urethane acrylate, effect is best.When olefinic polymerizable modifying agent selection epoxy acrylate,
When urethane acrylate and acrylic or methacrylic acid methyl esters, as shown in the result of embodiment 1 or embodiment 2, anchoring adhesive
Performance parameter it is still fine.When in the polymerizable modifying agent of olefinic without epoxy acrylate, as described in Example 4, anchoring adhesive
Shear strength significantly reduce;When in the polymerizable modifying agent of olefinic without urethane acrylate, such as the result institute of embodiment 5
Show, the viscosity of anchoring adhesive is declined.Therefore, available to draw a conclusion according to above-mentioned experiment: 1, olefinic is polymerizable changes for addition
Property agent anchoring adhesive of the anchoring adhesive than not adding olefinic polymerizable modifying agent preparation colloidal property and to cohere ability good;2, olefinic
Polymerizable modifying agent urethane acrylate can enhance the ability of cohering of anchoring adhesive, but elasticity is bad, and brittleness is larger, only again
The epoxy acrylate of certain number is added, elasticity can be improved and the problem of brittleness, it is good to prepare bonding dynamics, elastic and soft
The all good anchoring adhesive of toughness.
The test of 2 heat and moisture aging resistance of performance test
Anchoring adhesive prepared by embodiment 1-3 and comparative example 1 is bonded tensile shear carbon steel by GB/T 7124-1986
After test piece, solidify at room temperature.Antirust treatment (exposing bonding site) is done into the shearing test piece of after curing completely, is put into damp and hot old
Change chamber, degradation is carried out in (50 ± 2) DEG C, the environment of 95% or more humidity.It is old by GB/T 7124-1986 measurement
The shear strength under test piece room temperature after change, and compared with the test piece before aging.As a result as shown in the table:
The test of 2 heat and moisture aging resistance of table
Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparison 1 | |
Shear strength/MPa before aging | 22.3 | 25.1 | 29.2 | 16.7 |
Shear strength/MPa after aging 500h | 22.0 | 24.0 | 29.0 | 14.3 |
Shear strength/MPa after aging 2000h | 21.3 | 22.8 | 28.7 | 8.9 |
Shear strength/MPa after aging 5000h | 21.0 | 22.6 | 28.5 | 7.2 |
It can be seen that the anchoring adhesive of the polymerizable modifying agent preparation of addition olefinic than not modified plant according to above-mentioned test result
Muscle glue heat and moisture aging resistance significantly improves.Reason is analyzed, is because of addition 3 parts of acrylic acid, 6 parts of methyl methacrylate, ring
8 parts of oxypropylene acid esters, 13 parts of the urethane acrylate conduct polymerizable modifying agent of olefinic, so that the crosslinking in cross-linking process is close
Spend moderate, cohesive force, elasticity and flexibility compare balance, avoid pursuing the high-intensitive bullet for cohering ability and ignoring colloid simply
Property and ageing-resistant performance.
The test of 3 curing performance of performance test
By anchoring adhesive prepared by the application most preferred embodiment 3 and certain commercially available chemical materials company anchoring adhesive product-
The curing time of SHB injecting type anchoring adhesive and operable time are compared, as a result as shown in the table:
3 anchoring adhesive curing performance of table
It can be seen from the above results when environment temperature is-5-5 DEG C lower, anchoring adhesive prepared by the present invention embodies not
Advantage in terms of curing performance out is identical as commercially available SHB anchoring adhesive curing time.But when environment temperature is increased to 20-40
DEG C when, commercially available anchoring adhesive curing time is respectively 50,30,20min, and the curing time of embodiment 3 is 41,20,11min, Gu
The change time significantly shortens, and there is no shorten for operable time.The improvement of this curing time carries out engineering in the hot summer
Will be highly beneficial when repairing, it not only saves maintenance time, higher temperature softening colloid is more avoided, to reduce cohesion
Degree.
Performance test 4 can be with rust service performance test
This experiment anchoring adhesive used is anchoring adhesive prepared by embodiment 3, by the reinforcing bar of different band rust area according to applying
Work standard bar planting carries out live pullout tests, the influence by the size judgement of draft with rust area for bar planting effect.
The scene pullout tests rule is as follows: anchoring adhesive is carried out according to GB 50367-2013 " concrete structure reinforcement design specification "
Test, strength grade of concrete used are C30, and reinforcing bar is the hot rolling plain bar of HPB300, diameter 25mm, implantation depth
200mm, maintenance measured draft and damage -form after 7 days.Test result is as follows shown in table:
Table 4 can be with rust service performance test
Draft (KN) | Damage -form | |
Band rust area 0 | 240.7 | Taper is destroyed, and reinforcing bar is extracted |
Band rust area 1% | 237.3 | Taper is destroyed, and reinforcing bar is extracted |
Band rust area 2% | 236.8 | Taper is destroyed, and reinforcing bar is extracted |
Band rust area 4% | 233.9 | Taper is destroyed, and reinforcing bar is extracted |
Band rust area 6% | 231.0 | Taper is destroyed, and reinforcing bar is extracted |
Band rust area 8% | 180.3 | Taper is destroyed, and reinforcing bar is extracted |
It can be seen from the data in above-mentioned table when band rust area is 1-6%, although draft decreases,
But reduction is not significant, has 240.7KN to be reduced to 231.0KN, can be used normally in construction.When band rust area is 8%,
Draft is remarkably decreased, and has been unable to normal use, could be used after needing to remove rust staining.Therefore, prepared by the application
Anchoring adhesive for rust area≤6% reinforcing bar can normal use, do not influence bar planting effect.
The preparation of 6 modified vinyl anchoring adhesive 6 of embodiment
Under room temperature, by 60 parts of FX-451,1 part of acrylic acid, 4 parts of methyl methacrylate, 5 parts of epoxy acrylate, poly- ammonia
5 parts of ester acrylate, 10 parts of nitrile rubber, γ-(the third oxygen of 2,3- epoxy) 1 part of propyl trimethoxy silicane, N.N- dimethyl benzene
It is stirred evenly in 2 parts of addition stirred tanks of amine, adds 20 parts of quartz sand, continue to stir, be warming up to 80 DEG C, vacuumize, stir 3h
After component A is prepared;Under room temperature, by 10 parts of vinyl triamine, 30 parts of diethylenetriamine, 22 parts of benzoyl peroxide, γ-ammonia
20 parts of fumed silica of propyl-triethoxysilicane processing stir evenly, and B component is prepared;By component A and B component
It is mixed in mass ratio for 100:4, quickly stirs 30min and modified vinyl anchoring adhesive 6 is prepared.
The preparation of 7 modified vinyl anchoring adhesive 7 of embodiment
Under room temperature, by 60 parts of FX-451,2 parts of acrylic acid, 5 parts of methyl methacrylate, 6 parts of epoxy acrylate, poly- ammonia
8 parts of ester acrylate, 10 parts of nitrile rubber, γ-(the third oxygen of 2,3- epoxy) 1 part of propyl trimethoxy silicane, N.N- dimethyl benzene
It is stirred evenly in 2 parts of addition stirred tanks of amine, adds 20 parts of quartz sand, continue to stir, be warming up to 80 DEG C, vacuumize, stir 3h
After component A is prepared;Under room temperature, by 10 parts of vinyl triamine, 30 parts of diethylenetriamine, 22 parts of benzoyl peroxide, γ-ammonia
20 parts of fumed silica of propyl-triethoxysilicane processing stir evenly, and B component is prepared;By component A and B component
It is mixed in mass ratio for 100:4, quickly stirs 30min and modified vinyl anchoring adhesive 7 is prepared.
The preparation of 8 modified vinyl anchoring adhesive 8 of embodiment
Under room temperature, by 60 parts of FX-451,3 parts of acrylic acid, 5 parts of methyl methacrylate, 7 parts of epoxy acrylate, poly- ammonia
10 parts of ester acrylate, 10 parts of nitrile rubber, γ-(the third oxygen of 2,3- epoxy) 1 part of propyl trimethoxy silicane, N.N- dimethyl benzene
It is stirred evenly in 2 parts of addition stirred tanks of amine, adds 20 parts of quartz sand, continue to stir, be warming up to 80 DEG C, vacuumize, stir 3h
After component A is prepared;Under room temperature, by 10 parts of vinyl triamine, 30 parts of diethylenetriamine, 22 parts of benzoyl peroxide, γ-ammonia
20 parts of fumed silica of propyl-triethoxysilicane processing stir evenly, and B component is prepared;By component A and B component
It is mixed in mass ratio for 100:4, quickly stirs 30min and modified vinyl anchoring adhesive 8 is prepared.
Anchoring adhesive prepared by embodiment 3 and 6-8 is tested its safe performance indexes, as a result according to quality standard
It is as shown in the table:
5 anchoring adhesive safe performance indexes of table
Performance parameter | Embodiment 3 | Embodiment 6 | Embodiment 7 | Embodiment 8 |
Tensile splitting strength | 18Mpa | 14Mpa | 15Mpa | 20Mpa |
Compression strength | 85MPa | 73MPa | 81MPa | 90MPa |
Bending strength | 72MPa | 67MPa | 70MPa | 77MPa |
Steel-steel stretches shearing strength | 29MPa | 21MPa | 25MPa | 33MPa |
Bond strength 1 | 22MPa | 19MPa | 20MPa | 27MPa |
Bond strength 2 | 29MPa | 26MPa | 26MPa | 32MPa |
Non-volatile content | 99.6% | 99.4% | 99.4% | 99.6% |
Bond strength 1 in above-mentioned table indicates: Ribbed Bar and concrete is glutinous under C30 ∮ 25L=150mm drawing condition
Knotting strength;Bond strength 2 indicates: the bond strength of Ribbed Bar and concrete under C60 ∮ 25L=125mm drawing condition.
According to above-mentioned comparative experiments can be seen that when additive select acrylic acid 1-3 parts, 4-6 parts of methyl methacrylate,
The combination that 5-8 parts and urethane acrylate 5-13 parts of epoxy acrylate, properties are all more excellent, meanwhile, when selection propylene
When sour 3 parts, 5 parts of methyl methacrylate, 7 parts of epoxy acrylate, 10 parts of urethane acrylate, in all experiments, respectively
Item performance parameter presents best.
The above specific embodiment only schematically illustrates the content of present invention, does not represent the limitation of the content of present invention.
It may occur to persons skilled in the art that be that specific structure can have other versions in the present invention.
Claims (7)
1. a kind of modified vinyl anchoring adhesive, including component A and B component, the component A include the raw material of following mass fraction:
35-60 parts of vinyl ester resin, olefinic be modifying agent 15-30 parts polymerizable, 5-10 parts of toughener, 0.1-2 parts of coupling agent, promotor
0.5-5 parts, 10-20 parts of filler;The B component includes: 25-40 parts of curing agent, 10-25 parts of initiator, 10-20 parts of diluent.
2. anchoring adhesive according to claim 1, which is characterized in that the polymerizable modifying agent of olefinic is selected from: acrylic acid, first
The combination of one or more of base methyl acrylate, epoxy acrylate, urethane acrylate.
3. anchoring adhesive according to claim 2, which is characterized in that the polymerizable modifying agent of olefinic is selected from: acrylic acid 2-5
Part, 5-10 parts of epoxy acrylate and 8-15 parts of urethane acrylate of combination;5-8 parts of methyl methacrylate, epoxy third
The combination or 1-3 parts of acrylic acid, 4-6 parts of methyl methacrylate, ring that 2-10 parts and urethane acrylate 8-12 parts of olefin(e) acid ester
The combination that 5-8 parts and urethane acrylate 5-13 parts of oxypropylene acid esters.
4. anchoring adhesive according to claim 3, which is characterized in that the polymerizable modifying agent of olefinic is selected from: acrylic acid 1-3
Part, 4-6 parts of methyl methacrylate, 5-8 parts of epoxy acrylate and 5-13 parts of urethane acrylate of combination.
5. anchoring adhesive according to claim 1, which is characterized in that the vinyl ester resin is selected from: bisphenol-A epoxy ethylene
The combination of one or more of base ester, flame retardant type epoxy vinyl ester, epoxy novolac vinyl esters.
6. a kind of method for preparing modified vinyl anchoring adhesive described in claim 1, includes the following steps:
(1) under room temperature, vinyl ester resin, the polymerizable modifying agent of olefinic, coupling agent, toughener and promotor are added in vessel
It stirs evenly, adds filler, continue to stir, be warming up to 65-80 DEG C, vacuumize, component A is prepared after stirring 2-3h;
(2) under room temperature, curing agent, initiator and diluent is stirred evenly, B component is prepared;
(3) in mass ratio it is that 100:4-8 is mixed by component A and B component, quickly stirs 15-30min and modified vinyl is prepared
Anchoring adhesive.
7. any anchoring adhesive of claim 1-5 is in the fixation of various equipment and/or railway, highway, bridge, hydraulic engineering
In application.