CN109337109A - A kind of preparation process of fluorine-containing agricultural film - Google Patents
A kind of preparation process of fluorine-containing agricultural film Download PDFInfo
- Publication number
- CN109337109A CN109337109A CN201811263927.9A CN201811263927A CN109337109A CN 109337109 A CN109337109 A CN 109337109A CN 201811263927 A CN201811263927 A CN 201811263927A CN 109337109 A CN109337109 A CN 109337109A
- Authority
- CN
- China
- Prior art keywords
- agricultural film
- fluorine
- film
- containing agricultural
- preparation process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation processes of fluorine-containing agricultural film, comprising the following steps: Step 1: by handling with a thickness of the upper and lower surface of 80-120um pet film by low-temperature plasma;Step 2: polytetrafluoroethylene (PTFE) and fluorocarbon resin is respectively coated in the upper and lower surface of the pet film by low-temperature plasma processing to get preliminary agricultural film is arrived;Step 3 dries above-mentioned preliminary agricultural film, that is, obtains fluorine-containing agricultural film, and a kind of preparation process of fluorine-containing agricultural film of the present invention is greater than 90% by the agricultural film light transmittance that the technique obtains, and thickness is very thin, and intensity is good, alternative glass.
Description
Technical field
The present invention relates to a kind of preparation processes of fluorine-containing agricultural film.
Background technique
Existing agricultural film thickness is larger, and light transmittance is poor, thickness do it is thin after, intensity can be decreased obviously again.
Summary of the invention
The purpose of the present invention is to provide a kind of preparation process of fluorine-containing agricultural film, the agricultural film light transmittance obtained by the technique
Greater than 90%, and thickness is very thin, and intensity is good, alternative glass.
To achieve the goals above, the technical scheme is to design a kind of preparation processes of fluorine-containing agricultural film, including with
Lower step:
Step 1: by passing through at low-temperature plasma with a thickness of the upper and lower surface of 80-120um pet film
Reason;
Step 2: being respectively coated in the upper and lower surface of the pet film by low-temperature plasma processing
Polytetrafluoroethylene (PTFE) and fluorocarbon resin are to get arriving preliminary agricultural film;
Above-mentioned preliminary agricultural film is dried, that is, obtains fluorine-containing agricultural film by step 3.
The advantages and beneficial effects of the present invention are: a kind of preparation process of fluorine-containing agricultural film of the present invention, is obtained by the technique
The agricultural film light transmittance obtained is greater than 90%, and thickness is very thin, and intensity is good, alternative glass.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following embodiment is only used for more
Add and clearly demonstrate technical solution of the present invention, and not intended to limit the protection scope of the present invention.
Embodiment:
A kind of preparation process of fluorine-containing agricultural film, comprising the following steps:
Step 1: by passing through at low-temperature plasma with a thickness of the upper and lower surface of 80-120um pet film
Reason;
Step 2: being respectively coated in the upper and lower surface of the pet film by low-temperature plasma processing
Polytetrafluoroethylene (PTFE) and fluorocarbon resin are to get arriving preliminary agricultural film;
Above-mentioned preliminary agricultural film is dried, that is, obtains fluorine-containing agricultural film by step 3.
All kinds of parameter lists that the fluorine-containing agricultural film of above-mentioned technique preparation compares common ETFE film are as follows:
The above is only a preferred embodiment of the present invention, it is noted that those skilled in the art are come
It says, without departing from the technical principles of the invention, several improvements and modifications can also be made, these improvements and modifications are also answered
It is considered as protection scope of the present invention.
Claims (1)
1. a kind of preparation process of fluorine-containing agricultural film, which comprises the following steps:
Step 1: by passing through at low-temperature plasma with a thickness of the upper and lower surface of 80-120um pet film
Reason;
Step 2: being respectively coated in the upper and lower surface of the pet film by low-temperature plasma processing
Polytetrafluoroethylene (PTFE) and fluorocarbon resin are to get arriving preliminary agricultural film;
Above-mentioned preliminary agricultural film is dried, that is, obtains fluorine-containing agricultural film by step 3.