CN109294486A - A kind of glued board modified polyvinylalcohol adhesive - Google Patents
A kind of glued board modified polyvinylalcohol adhesive Download PDFInfo
- Publication number
- CN109294486A CN109294486A CN201811035365.2A CN201811035365A CN109294486A CN 109294486 A CN109294486 A CN 109294486A CN 201811035365 A CN201811035365 A CN 201811035365A CN 109294486 A CN109294486 A CN 109294486A
- Authority
- CN
- China
- Prior art keywords
- starch
- polyvinyl alcohol
- glued board
- zeolite powder
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of glued board modified polyvinylalcohol adhesives, it is related to glued board technical field, is made of following component: the composite modified polyvinyl alcohol of starch, activation nano zeolite powder, rosin resin, hydroxymethyl cellulose, fatty acid loss water sorbit ester, deionized water.Glued board adhesive provided by the invention not only has good water resistance, while having quick-drying effect.
Description
Technical field
The invention belongs to glued board technical fields, and in particular to a kind of glued board modified polyvinylalcohol adhesive.
Background technique
Glued board is an important board kind in wood-based plate, and since glued board has, deformation is small, breadth is big, construction is inconvenient, no
Easy warpage, the features such as tensile strength perpendicular to grain is big, obtain extensively in furniture, compartment, shipbuilding, military project, packaging and other industrial departments
Using glued board is that wood single-plate is bonded together by adhesive, is then made by cold moudling, it is seen then that adhesive
Can adhesion strength to glued board, service life there is strong influence, and existing glued board adhesive is to wood single-plate
Adhesion strength it is general, easy degumming after glued board long-time use.
Summary of the invention
The purpose of the present invention is being directed to existing problem, a kind of glued board modified polyvinylalcohol adhesive is provided.
The present invention is achieved by the following technical solutions:
A kind of glued board modified polyvinylalcohol adhesive, is made of following component by weight: the composite modified poly- second of starch
Enol 85-88, activation nano zeolite powder 19-24, rosin resin 6-8, hydroxymethyl cellulose 6-10, fatty acid loss water sorbit ester
3.5-3.9, deionized water 56-60.
Further, the composite modified polyvinyl alcohol preparation method of the starch the following steps are included:
(1) starch uniformly pretreatment of starch: is added to the polyoxometallate that mass fraction is 6.5% by 1:10 mass ratio
In aqueous solution, be heated to 76 DEG C, with 1200r/min revolving speed stir 40min, then filtered, drying to constant weight to get;
(2) the composite modified polyvinyl alcohol of starch: polyvinyl alcohol is dissolved in deionized water, be configured to mass fraction be 15% it is poly-
In vinyl alcohol aqueous solution, 55 DEG C are then heated to, polyvinyl alcohol water solution is stirred continuously with 1800r/min revolving speed, is stirred
It is above-mentioned resulting by pretreated starch into the polyvinyl alcohol water solution being stirred continuously after mixing 10min, it is small to continue stirring 1
When, obtain polyvinylalcohols starch mixed liquor, 70 DEG C adjusted the temperature to polyvinylalcohols starch mixed liquor, keeps the temperature 5min, then to
The 3- chlorine-2-hydroxyl propanesulfonate of its quality 0.62% is added in polyvinylalcohols starch mixed liquor, with the stirring of 1200r/min revolving speed
35min obtains mixed system, and mixed system is added in reaction kettle, under inert gas atmosphere, adds into mixed system
The ammonium persulfate of its quality 0.1% and 0.12% diethyl amino propylamine, at 88 DEG C, with 800r/min revolving speed stirring 2 hours, so
After carry out cooling discharging, it is dry to get the composite modified polyvinyl alcohol of starch by rotary evaporation.
Further, step (1) starch is that soybean starch and Faba bean starch are mixed by 10:1 mass ratio.
Further, step (1) the polyoxometallic acid saline solution is 12- tungstophosphoric acid aqueous solutions of potassium.
Further, step (2) inert gas is neon.
Further, step (2) pretreated starch and the polyvinyl alcohol mass ratio of passing through is 1:3.
Further, the activation nano zeolite powder, preparation method thereof are as follows: be with chloroform by 2- chloroethyl sulfonic acid chloride
Medium carries out dispersion impregnation to nano zeolite powder, specifically: 2- chloroethyl sulfonic acid chloride is dissolved in by 1.2:55 mass ratio
In chloroform, the nano zeolite powder of chloroform quality 10% is then added again, at a temperature of 0.02MPa vacuum degree, 112 DEG C,
With 2500r/min revolving speed stirring 2 hours, then filtered, cleaned using dehydrated alcohol, drying to constant weight to get.
Further, the nano zeolite powder to be 100nm zeolite powder and the zeolite powder of 80nm mixed by 1:3 mass ratio and
At carrying out composite bioactive treatment with the 100nm zeolite powder different from 80nm, can effectively form mastoid process knot in adhesive
Structure improves the contact area between adhesive and plank, promotes to interpenetrate between adhesive and plank.
The utility model has the advantages that the present invention, by being activated to nano zeolite powder, so that treated, nano zeolite powder has
There are bigger large specific surface area and better compatibility, is not easy to gather, can be evenly dispersed in adhesive system, and and glue
Between the composite modified polyvinyl alcohol complex macromolecular chain of starch in glutinous agent system, covalent bond can be preferably formed, thus
When adhesive solidifies, the composite modified polyvinyl alcohol complex macromolecular chain of starch can be cooperateed with to form stable cross-linked network structure,
The bonding strength of adhesive is greatly improved, simultaneously as when being stored, since activation nano zeolite powder is in adhesive
Play the role of evenly dispersed absorption in system, can preferably remain moisture in adhesive system and other components
Stability, and then the storage period of adhesive is significantly extended, by the present invention to the activation processing and starch of nano zeolite powder
The synergistic effect of composite modified polyvinyl alcohol, can be effectively solved that being thermally deformed for conventional adhesive is larger, stability difference
Defect, when the adhesive filled with activation nano zeolite powder in the biggish situation of the temperature difference in use, can be by multiple with starch
The bonding action between modified polyvinylalcohol is closed, keeps adhesive mechanical property not influenced significantly, the present invention passes through starch
Composite modified polyvinyl alcohol enables to hydrophobic grouping internal in compound to be exposed, so that the knot of starch and polyvinyl alcohol
Structure is more unfolded, and by the secondary key in composite modified action breaks down starch molecule, forms a certain amount of active group,
Under the high temperature conditions, it can crosslink and react between timber, form uniform space net structure, it is strong to increase its cohesion
Degree promotes the composite modified polyvinyl alcohol of starch and wood surface to form stable chemical bond, so that the water resistance of adhesive is improved,
Meanwhile the rate of drying of adhesive is also greatly enhanced.
Specific embodiment
Embodiment 1
A kind of glued board modified polyvinylalcohol adhesive, is made of following component by weight: the composite modified poly- second of starch
Enol 85, activation nano zeolite powder 19, rosin resin 6, hydroxymethyl cellulose 6, fatty acid loss water sorbit ester 3.5, deionization
Water 56.
Further, the composite modified polyvinyl alcohol preparation method of the starch the following steps are included:
(1) starch uniformly pretreatment of starch: is added to the polyoxometallate that mass fraction is 6.5% by 1:10 mass ratio
In aqueous solution, be heated to 76 DEG C, with 1200r/min revolving speed stir 40min, then filtered, drying to constant weight to get;
(2) the composite modified polyvinyl alcohol of starch: polyvinyl alcohol is dissolved in deionized water, be configured to mass fraction be 15% it is poly-
In vinyl alcohol aqueous solution, 55 DEG C are then heated to, polyvinyl alcohol water solution is stirred continuously with 1800r/min revolving speed, is stirred
It is above-mentioned resulting by pretreated starch into the polyvinyl alcohol water solution being stirred continuously after mixing 10min, it is small to continue stirring 1
When, obtain polyvinylalcohols starch mixed liquor, 70 DEG C adjusted the temperature to polyvinylalcohols starch mixed liquor, keeps the temperature 5min, then to
The 3- chlorine-2-hydroxyl propanesulfonate of its quality 0.62% is added in polyvinylalcohols starch mixed liquor, with the stirring of 1200r/min revolving speed
35min obtains mixed system, and mixed system is added in reaction kettle, under inert gas atmosphere, adds into mixed system
The ammonium persulfate of its quality 0.1% and 0.12% diethyl amino propylamine, at 88 DEG C, with 800r/min revolving speed stirring 2 hours, so
After carry out cooling discharging, it is dry to get the composite modified polyvinyl alcohol of starch by rotary evaporation.
Further, step (1) starch is that soybean starch and Faba bean starch are mixed by 10:1 mass ratio.
Further, step (1) the polyoxometallic acid saline solution is 12- tungstophosphoric acid aqueous solutions of potassium.
Further, step (2) inert gas is neon.
Further, step (2) pretreated starch and the polyvinyl alcohol mass ratio of passing through is 1:3.
Further, the activation nano zeolite powder, preparation method thereof are as follows: be with chloroform by 2- chloroethyl sulfonic acid chloride
Medium carries out dispersion impregnation to nano zeolite powder, specifically: 2- chloroethyl sulfonic acid chloride is dissolved in by 1.2:55 mass ratio
In chloroform, the nano zeolite powder of chloroform quality 10% is then added again, at a temperature of 0.02MPa vacuum degree, 112 DEG C,
With 2500r/min revolving speed stirring 2 hours, then filtered, cleaned using dehydrated alcohol, drying to constant weight to get.
Further, the nano zeolite powder to be 100nm zeolite powder and the zeolite powder of 80nm mixed by 1:3 mass ratio and
At.
Embodiment 2
A kind of glued board modified polyvinylalcohol adhesive, is made of following component by weight: the composite modified poly- second of starch
Enol 88, activation nano zeolite powder 24, rosin resin 8, hydroxymethyl cellulose 10, fatty acid loss water sorbit ester 3.9, deionization
Water 60.
Further, the composite modified polyvinyl alcohol preparation method of the starch the following steps are included:
(1) starch uniformly pretreatment of starch: is added to the polyoxometallate that mass fraction is 6.5% by 1:10 mass ratio
In aqueous solution, be heated to 76 DEG C, with 1200r/min revolving speed stir 40min, then filtered, drying to constant weight to get;
(2) the composite modified polyvinyl alcohol of starch: polyvinyl alcohol is dissolved in deionized water, be configured to mass fraction be 15% it is poly-
In vinyl alcohol aqueous solution, 55 DEG C are then heated to, polyvinyl alcohol water solution is stirred continuously with 1800r/min revolving speed, is stirred
It is above-mentioned resulting by pretreated starch into the polyvinyl alcohol water solution being stirred continuously after mixing 10min, it is small to continue stirring 1
When, obtain polyvinylalcohols starch mixed liquor, 70 DEG C adjusted the temperature to polyvinylalcohols starch mixed liquor, keeps the temperature 5min, then to
The 3- chlorine-2-hydroxyl propanesulfonate of its quality 0.62% is added in polyvinylalcohols starch mixed liquor, with the stirring of 1200r/min revolving speed
35min obtains mixed system, and mixed system is added in reaction kettle, under inert gas atmosphere, adds into mixed system
The ammonium persulfate of its quality 0.1% and 0.12% diethyl amino propylamine, at 88 DEG C, with 800r/min revolving speed stirring 2 hours, so
After carry out cooling discharging, it is dry to get the composite modified polyvinyl alcohol of starch by rotary evaporation.
Further, step (1) starch is that soybean starch and Faba bean starch are mixed by 10:1 mass ratio.
Further, step (1) the polyoxometallic acid saline solution is 12- tungstophosphoric acid aqueous solutions of potassium.
Further, step (2) inert gas is neon.
Further, step (2) pretreated starch and the polyvinyl alcohol mass ratio of passing through is 1:3.
Further, the activation nano zeolite powder, preparation method thereof are as follows: be with chloroform by 2- chloroethyl sulfonic acid chloride
Medium carries out dispersion impregnation to nano zeolite powder, specifically: 2- chloroethyl sulfonic acid chloride is dissolved in by 1.2:55 mass ratio
In chloroform, the nano zeolite powder of chloroform quality 10% is then added again, at a temperature of 0.02MPa vacuum degree, 112 DEG C,
With 2500r/min revolving speed stirring 2 hours, then filtered, cleaned using dehydrated alcohol, drying to constant weight to get.
Further, the nano zeolite powder to be 100nm zeolite powder and the zeolite powder of 80nm mixed by 1:3 mass ratio and
At.
Embodiment 3
A kind of glued board modified polyvinylalcohol adhesive, is made of following component by weight: the composite modified poly- second of starch
Enol 86, activation nano zeolite powder 21, rosin resin 7, hydroxymethyl cellulose 8, fatty acid loss water sorbit ester 3.6, deionization
Water 58.
Further, the composite modified polyvinyl alcohol preparation method of the starch the following steps are included:
(1) starch uniformly pretreatment of starch: is added to the polyoxometallate that mass fraction is 6.5% by 1:10 mass ratio
In aqueous solution, be heated to 76 DEG C, with 1200r/min revolving speed stir 40min, then filtered, drying to constant weight to get;
(2) the composite modified polyvinyl alcohol of starch: polyvinyl alcohol is dissolved in deionized water, be configured to mass fraction be 15% it is poly-
In vinyl alcohol aqueous solution, 55 DEG C are then heated to, polyvinyl alcohol water solution is stirred continuously with 1800r/min revolving speed, is stirred
It is above-mentioned resulting by pretreated starch into the polyvinyl alcohol water solution being stirred continuously after mixing 10min, it is small to continue stirring 1
When, obtain polyvinylalcohols starch mixed liquor, 70 DEG C adjusted the temperature to polyvinylalcohols starch mixed liquor, keeps the temperature 5min, then to
The 3- chlorine-2-hydroxyl propanesulfonate of its quality 0.62% is added in polyvinylalcohols starch mixed liquor, with the stirring of 1200r/min revolving speed
35min obtains mixed system, and mixed system is added in reaction kettle, under inert gas atmosphere, adds into mixed system
The ammonium persulfate of its quality 0.1% and 0.12% diethyl amino propylamine, at 88 DEG C, with 800r/min revolving speed stirring 2 hours, so
After carry out cooling discharging, it is dry to get the composite modified polyvinyl alcohol of starch by rotary evaporation.
Further, step (1) starch is that soybean starch and Faba bean starch are mixed by 10:1 mass ratio.
Further, step (1) the polyoxometallic acid saline solution is 12- tungstophosphoric acid aqueous solutions of potassium.
Further, step (2) inert gas is neon.
Further, step (2) pretreated starch and the polyvinyl alcohol mass ratio of passing through is 1:3.
Further, the activation nano zeolite powder, preparation method thereof are as follows: be with chloroform by 2- chloroethyl sulfonic acid chloride
Medium carries out dispersion impregnation to nano zeolite powder, specifically: 2- chloroethyl sulfonic acid chloride is dissolved in by 1.2:55 mass ratio
In chloroform, the nano zeolite powder of chloroform quality 10% is then added again, at a temperature of 0.02MPa vacuum degree, 112 DEG C,
With 2500r/min revolving speed stirring 2 hours, then filtered, cleaned using dehydrated alcohol, drying to constant weight to get.
Further, the nano zeolite powder to be 100nm zeolite powder and the zeolite powder of 80nm mixed by 1:3 mass ratio and
At.
Comparative example 1: it is distinguished with embodiment 1 and is only that the starch that the composite modified polyvinyl alcohol of starch is replaced with to equivalent.
Comparative example 2: it is distinguished with embodiment 1 and is only that the polyethylene that the composite modified polyvinyl alcohol of starch is replaced with to equivalent
Alcohol.
Comparative example 3: it is not only in that with 1st area of embodiment and the composite modified polyvinyl alcohol of starch is replaced with into polyvinyl alcohol and starch
Equivalent physical mixture.
Comparative example 4: it is only that nano zeolite powder without activation processing with the difference of embodiment 1.
Comparative example 5: it is only that with the difference of embodiment 1 and active zeolite powder is replaced with into equivalent nano-bentonite.
Control group 1: the mongolicum Turcz. with Modified Starch Adhesive of application number 201711278649.X preparation.
Control group 2: application number: the polyvinyl alcohol gluing agent of 201510630538.5 preparations.
Embodiment and comparative example adhesive property are detected:
(1) the equal paper slip of several areas, thickness the first glutinous time test of adhesive: is pasted on to the table of vial with adhesive
A paper slip is torn every 5s in face, until paper slip is stuck when tearing downwards, paper slip can be destroyed when time be just glutinous when
Between;
(2) it the storage period test of adhesive: is tested by GB/T 7751-1987 standard;
(3) the resistance to room temperature of adhesive is aqueous: by adhesive with 30g/m2Coating weight is uniformly coated on label, later pastes label
On vial clean in advance and flatten, by the vial of label room temperature, relative humidity 68% environment in place 3
It after it, is vertically immersed in 25 DEG C of water, for several times every 12h rotary glass bottle, sees label whether there is or not alice or fall off, it is parallel with 3
At least 1 alice or the time before falling off indicate water resisting time in sample;
Table 1
As can be seen from Table 1, the glutinous time at the beginning of the present invention prepares glued board adhesive is short, and storage period is long, water-tolerant.
Drying time: sample adhesive is coated on label paper, is affixed on vial, is weighed on assay balance at once,
Weight includes bottle, trade mark, the moisture in adhesive and solid four quality sums (W1).Drying at room temperature after having claimed, often
It is primary every 2h weighing, the corresponding quality of 2h, 4h, 6h, 8h (W2, W3, W4, W5 etc.) can be obtained.Later, by sample in drying
It is placed 2 days in device, is completely dried sample and is re-weighed once.This inferior quality is considered bottle, trade mark and three matter with solid
The sum of amount (WH).Aqueous quality is set as W in adhesive, then W=W1-WH, and the biodiversity lost within 2h is W1-W2.
Thus calculate the ratio that moisture content is lost in 2h: fluid loss=(W1-W2)/W uses same method, available 4h, 6h,
The dehydration ratio of 8h.Using the time as horizontal axis, dehydration ratio is the longitudinal axis, obtains the drying curve of adhesive.It is looked on drying curve
Time used when dehydration 80% out, the drying time as the sample;
Table 2
As can be seen from Table 2, glued board prepared by the present invention is short with modified polyvinylalcohol adhesive drying time, rate of drying
Fastly.
Claims (8)
1. a kind of glued board modified polyvinylalcohol adhesive, which is characterized in that be made by weight of following component: starch
Composite modified polyvinyl alcohol 85-88, activation nano zeolite powder 19-24, rosin resin 6-8, hydroxymethyl cellulose 6-10, fatty acid
Sorbitan ester 3.5-3.9, deionized water 56-60.
2. a kind of glued board modified polyvinylalcohol adhesive as described in claim 1, which is characterized in that the starch is compound
Modified polyvinylalcohol preparation method the following steps are included:
(1) starch uniformly pretreatment of starch: is added to the polyoxometallate that mass fraction is 6.5% by 1:10 mass ratio
In aqueous solution, be heated to 76 DEG C, with 1200r/min revolving speed stir 40min, then filtered, drying to constant weight to get;
(2) the composite modified polyvinyl alcohol of starch: polyvinyl alcohol is dissolved in deionized water, be configured to mass fraction be 15% it is poly-
In vinyl alcohol aqueous solution, 55 DEG C are then heated to, polyvinyl alcohol water solution is stirred continuously with 1800r/min revolving speed, is stirred
It is above-mentioned resulting by pretreated starch into the polyvinyl alcohol water solution being stirred continuously after mixing 10min, it is small to continue stirring 1
When, obtain polyvinylalcohols starch mixed liquor, 70 DEG C adjusted the temperature to polyvinylalcohols starch mixed liquor, keeps the temperature 5min, then to
The 3- chlorine-2-hydroxyl propanesulfonate of its quality 0.62% is added in polyvinylalcohols starch mixed liquor, with the stirring of 1200r/min revolving speed
35min obtains mixed system, and mixed system is added in reaction kettle, under inert gas atmosphere, adds into mixed system
The ammonium persulfate of its quality 0.1% and 0.12% diethyl amino propylamine, at 88 DEG C, with 800r/min revolving speed stirring 2 hours, so
After carry out cooling discharging, it is dry to get the composite modified polyvinyl alcohol of starch by rotary evaporation.
3. a kind of glued board modified polyvinylalcohol adhesive as claimed in claim 2, which is characterized in that step (1) is described
Starch is that soybean starch and Faba bean starch are mixed by 10:1 mass ratio.
4. a kind of glued board modified polyvinylalcohol adhesive as claimed in claim 2, which is characterized in that step (1) is described
Polyoxometallic acid saline solution is 12- tungstophosphoric acid aqueous solutions of potassium.
5. a kind of glued board modified polyvinylalcohol adhesive as claimed in claim 2, which is characterized in that step (2) is described
Inert gas is neon.
6. a kind of glued board modified polyvinylalcohol adhesive as claimed in claim 2, which is characterized in that step (2) is described
It is 1:3 by pretreated starch and polyvinyl alcohol mass ratio.
7. a kind of glued board modified polyvinylalcohol adhesive as described in claim 1, which is characterized in that the activation nanometer
Zeolite powder carries out dispersion dipping to nano zeolite powder the preparation method comprises the following steps: by 2- chloroethyl sulfonic acid chloride using chloroform as medium
Processing, specifically: 2- chloroethyl sulfonic acid chloride is dissolved in chloroform by 1.2:55 mass ratio, then adds chloroform again
The nano zeolite powder of quality 10%, at a temperature of 0.02MPa vacuum degree, 112 DEG C, with 2500r/min revolving speed stirring 2 hours, then
Filtered, cleaned using dehydrated alcohol, drying to constant weight to get.
8. a kind of glued board modified polyvinylalcohol adhesive as claimed in claim 7, which is characterized in that the nano zeolite
Powder is mixed for the zeolite powder of 100nm zeolite powder and 80nm by 1:3 mass ratio.