CN109294438A - A kind of poly- silicon ceramics corrosion-inhibiting coating - Google Patents
A kind of poly- silicon ceramics corrosion-inhibiting coating Download PDFInfo
- Publication number
- CN109294438A CN109294438A CN201811208954.6A CN201811208954A CN109294438A CN 109294438 A CN109294438 A CN 109294438A CN 201811208954 A CN201811208954 A CN 201811208954A CN 109294438 A CN109294438 A CN 109294438A
- Authority
- CN
- China
- Prior art keywords
- poly
- solution
- silicon ceramics
- silicone resin
- mixing slurry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of poly- silicon ceramics corrosion-inhibiting coatings, it is related to anti-corrosion material field, including poly- silicon ceramics mixing slurry A, solution B and solution C, according to weight percent, poly- silicon ceramics mixing slurry A includes alumina silicate, silica, ceramic powder, poly- silicone resin and mica powder;B solution includes polysiloxanes and RSPM;C solution includes silane coupling agent and HP2000 silicone resin, the present invention can not only act on metal, timber, glass and rubber etc., and classification surface forms corrosion prevention film mostly, carrying construction is carried out convenient for worker, and the corrosion prevention film formed has the performance of strong adsorption force, salt spray resistance, high temperature resistant and acid and alkali-resistance.
Description
Technical field
The present invention relates to anti-corrosion material field more particularly to a kind of poly- silicon ceramics corrosion-inhibiting coatings.
Background technique
Current corrosion-inhibiting coating coating type is various, such as metal class surface covering, wall surface coating and floor coatings etc.
It is varied.
But the existing coating applied to smooth surfaces such as rubber or glass is generally difficult to persistently, then with the time
It can gradually fall off, simultaneously because needing corrosion-resistant article various, the corrosion-inhibiting coating type of every one kind article surface is different, causes to fill
It repairs or maintenance personal needs to carry the anticorrosion coating material of plurality of classes, also will cause puzzlement inconvenient to carry, therefore how
Enabling to coating that can persistently act on big multi-class surface formation corrosion-inhibiting coating becomes those skilled in the art urgently
Problem to be solved.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies in the prior art, a kind of poly- silicon ceramics are provided
Corrosion-inhibiting coating, most of article surfaces that act on which can be lasting form corrosion-inhibiting coating.
The present invention is to be achieved by the following technical programs:
A kind of poly- silicon ceramics corrosion-inhibiting coating, including poly- silicon ceramics mixing slurry A, solution B and solution C, according to weight percent,
The poly- silicon ceramics mixing slurry A includes alumina silicate 3% -5%, silica 1 0% -15%, ceramic powder 20-25%, poly- silicon tree
Rouge 50% one 60%, mica powder 3%-10%;The B solution includes polysiloxanes 90% -95% and RSPM 5% -
10%;C solution includes silane coupling agent 90% -95% and HP2000 silicone resin 5% -10%.
According to the above technical scheme, it is preferable that including poly- silicon ceramics mixing slurry A, solution B and solution C, according to weight percent
Than the poly- silicon ceramics mixing slurry A includes alumina silicate 4%, silica 1 2%, ceramic powder 22%, poly- silicone resin 55%, mica
Powder 7%;The B solution includes polysiloxanes 93% and RSPM 7%;C solution includes silane coupling agent 92% and HP2000
Silicone resin 8%.
A kind of preparation method of poly- silicon ceramics corrosion-inhibiting coating, comprising the following steps:
1) sorting of poly- silicon ceramics mixing slurry A, according to weight percent, including alumina silicate 3% -5%, silica
10% -15%, ceramic powder 20-25%, poly- silicone resin 50% one 60%, mica powder 3%-10%, then dispersion mashing, filtering;
2) according to weight percent, the polysiloxanes for choosing 5% -10% RSPM dissolution 90% -95% obtains solution
B;
3) according to weight percent, the HP2000 silicon tree of 90% -95% silane coupling agent dissolution 5% -10% is chosen
Rouge obtains solution C;
4) by three kinds of poly- silicon ceramics mixing slurry A, solution B, solution C independent packagings by weight percentage.
According to the above technical scheme, it is preferable that the following steps are included:
1) sorting of poly- silicon ceramics mixing slurry A, according to weight percent, including alumina silicate 4%, silica 1 2%, pottery
Porcelain powder 22%, poly- silicone resin 55%, mica powder 7%, then dispersion mashing, filtering;
2) according to weight percent, the polysiloxanes for choosing 7% RSPM dissolution 93% obtains solution B;
3) according to weight percent, the HP2000 silicone resin for choosing 92% silane coupling agent dissolution 8% obtains solution C;
4) by three kinds of poly- silicon ceramics mixing slurry A, solution B, solution C independent packagings by weight percentage.
According to the above technical scheme, it is preferable that the dispersion mashing in step 1) is implemented by high speed disperser.
The beneficial effects of the present invention are: being mixed between poly- silicon ceramics mixing slurry A, solution B and solution C in the present invention
It is chemically reacted in the case where stirring evenly, there are extremely strong adsorption capacities for finished product, can act on metal, timber, glass
And the surfaces such as rubber form corrosion prevention film, and the corrosion prevention film formed has strong adsorption capacity, salt spray resistance, high temperature resistant and acid and alkali-resistance
Performance.
Detailed description of the invention
Fig. 1 shows the coating performance figure of embodiment according to the present invention.
Specific embodiment
In order to make those skilled in the art more fully understand technical solution of the present invention, with reference to the accompanying drawing and most
The present invention is described in further detail for good embodiment.
Embodiment one:
The present invention provides a kind of poly- silicon ceramics corrosion-inhibiting coatings, including poly- silicon ceramics mixing slurry A, solution B and solution C, press
According to weight percent, the poly- silicon ceramics mixing slurry A includes alumina silicate 3%, silica 1 4%, ceramic powder 20%, poly- silicon tree
Rouge 60%, mica powder 3%;The B solution includes polysiloxanes 90% and RSPM 10%;C solution includes silane coupling agent
90% and HP2000 silicone resin 10%.
Embodiment two:
Poly- silicon ceramics corrosion-inhibiting coating, including poly- silicon ceramics mixing slurry A, solution B and solution C, it is described according to weight percent
Poly- silicon ceramics mixing slurry A includes alumina silicate 5%, silica 1 0%, ceramic powder 25%, poly- silicone resin 50%, mica powder 10%;
The B solution includes polysiloxanes 95% and RSPM5%;C solution includes silane coupling agent 95% and HP2000 silicone resin
5%.
Embodiment three:
Poly- silicon ceramics corrosion-inhibiting coating, according to above scheme, it is preferred that including poly- silicon ceramics mixing slurry A, solution B and solution
C, according to weight percent, the poly- silicon ceramics mixing slurry A includes alumina silicate 4%, silica 1 2%, ceramic powder 22%, is gathered
Silicone resin 55%, mica powder 7%;The B solution includes polysiloxanes 93% and RSPM 7%;C solution includes silane coupled
Agent 92% and HP2000 silicone resin 8%.
According to above-described embodiment, it is preferred that the size of silica is 1000 mesh;
According to above-described embodiment, it is preferred that silane coupling agent KH550;
According to above-described embodiment, it is preferred that the size of mica powder is 1000 mesh;
According to above-described embodiment, it is preferred that silicone resin is wacker chemicals organic siliconresin HP2000.
The method for preparing poly- silicon ceramics corrosion-inhibiting coating, comprising the following steps:
1) sorting of poly- silicon ceramics mixing slurry A, according to weight percent, including alumina silicate 3% -5%, silica
10% -15%, ceramic powder 20-25%, poly- silicone resin 50 one 60%, mica powder 3%-10%, then dispersion mashing, filtering;
2) according to weight percent, the polysiloxanes for choosing the RSPM dissolution 90% -95% of 5%-10% obtains solution B;
3) according to weight percent, the HP2000 silicon tree of 90% -95% silane coupling agent dissolution 5% -10% is chosen
Rouge obtains solution C;
4) by three kinds of poly- silicon ceramics mixing slurry A, solution B, solution C independent packagings by weight percentage.
According to above-described embodiment, it is preferable that the following steps are included:
1) sorting of poly- silicon ceramics mixing slurry A, according to weight percent, including alumina silicate 4%, silica 1 2%, pottery
Porcelain powder 22%, poly- silicone resin 55%, mica powder 7%, then dispersion mashing, filtering;
2) according to weight percent, the polysiloxanes for choosing 7% RSPM dissolution 93% obtains solution B;
3) according to weight percent, the HP2000 silicone resin for choosing 92% silane coupling agent dissolution 8% obtains solution C;
4) by three kinds of poly- silicon ceramics mixing slurry A, solution B, solution C independent packagings by weight percentage.
According to above-described embodiment, it is preferable that the dispersion mashing in step 1) is implemented by high speed disperser.
Form of construction work: before use, poly- silicon ceramics mixing slurry A, solution B and solution C are successively poured into another first
Uniform stirring is carried out in empty barrel, is then surface-treated using spraying or brushing mode.
Spraying: using high-pressure airless spraying gun, and the pressure of spray gun is larger, and jet size is greater than 0.36mm, 40 ° of spray angle-
70°。
It brushes: being suitable for precoating and small area coating, reach defined thickness of dry film, it is small to be greater than 8 for (25 DEG C) of brush interval again
When.
The beneficial effects of the present invention are: being mixed between poly- silicon ceramics mixing slurry A, solution B and solution C in the present invention
It is chemically reacted in the case where stirring evenly, there are extremely strong adsorption capacities for finished product, can act on metal, timber, glass
And the surfaces such as rubber form corrosion prevention film, and the corrosion prevention film formed has strong adsorption capacity, salt spray resistance, high temperature resistant and acid and alkali-resistance
Performance.
The above is only a preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, various improvements and modifications may be made without departing from the principle of the present invention, these improvements and modifications are also answered
It is considered as protection scope of the present invention.
Claims (5)
1. a kind of poly- silicon ceramics corrosion-inhibiting coating, which is characterized in that including poly- silicon ceramics mixing slurry A, solution B and solution C, according to weight
Percentage is measured, the poly- silicon ceramics mixing slurry A includes alumina silicate 3% -5%, silica 1 0% -15%, ceramic powder 20-
25%, poly- silicone resin 50% one 60% and mica powder 3%-10%;The B solution include polysiloxanes 90% -95% and
RSPM 5% -10%;C solution includes silane coupling agent 90% -95% and HP2000 silicone resin 5% -10%.
2. a kind of poly- silicon ceramics corrosion-inhibiting coating according to claim 1, which is characterized in that including poly- silicon ceramics mixing slurry A,
Solution B and solution C, according to weight percent, the poly- silicon ceramics mixing slurry A includes alumina silicate 4%, silica 1 2%, pottery
Porcelain powder 22%, poly- silicone resin 55%, mica powder 7%;The B solution includes polysiloxanes 93% and RSPM 7%;C solution packet
Include silane coupling agent 92% and HP2000 silicone resin 8%.
3. a kind of preparation method of poly- silicon ceramics corrosion-inhibiting coating, which comprises the following steps:
1) sorting of poly- silicon ceramics mixing slurry A, according to weight percent, including alumina silicate 3% -5%, silica 1 0% -
15%, ceramic powder 20-25%, poly- silicone resin 50 one 60% and mica powder 3%-10%, then dispersion mashing, filtering;
2) according to weight percent, the polysiloxanes for choosing 5% -10% RSPM dissolution 90% -95% obtains solution B;
3) according to weight percent, the HP2000 silicone resin for choosing 90% -95% silane coupling agent dissolution 5% -10% is obtained
To solution C;
4) by three kinds of poly- silicon ceramics mixing slurry A, solution B, solution C independent packagings by weight percentage.
4. the preparation method of poly- silicon ceramics corrosion-inhibiting coating according to claim 3, which comprises the following steps:
1) sorting of poly- silicon ceramics mixing slurry A, according to weight percent, including alumina silicate 4%, silica 1 2%, ceramic powder
22%, poly- silicone resin 55%, mica powder 7%, then dispersion mashing, filtering;
2) according to weight percent, the polysiloxanes for choosing 7% RSPM dissolution 93% obtains solution B;
3) according to weight percent, the HP2000 silicone resin for choosing 92% silane coupling agent dissolution 8% obtains solution C;
4) by three kinds of poly- silicon ceramics mixing slurry A, solution B, solution C independent packagings by weight percentage.
5. the preparation method of poly- silicon ceramics corrosion-inhibiting coating according to claim 4, which is characterized in that the dispersion in step 1) is beaten
Slurry is implemented by high speed disperser.