CN109280574A - A kind of formula of biodegradable wear-resistant material - Google Patents
A kind of formula of biodegradable wear-resistant material Download PDFInfo
- Publication number
- CN109280574A CN109280574A CN201811421059.2A CN201811421059A CN109280574A CN 109280574 A CN109280574 A CN 109280574A CN 201811421059 A CN201811421059 A CN 201811421059A CN 109280574 A CN109280574 A CN 109280574A
- Authority
- CN
- China
- Prior art keywords
- type
- nonmetallic
- extreme pressure
- wear
- formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention is a kind of formula of biodegradable wear-resistant material, raw material in formula forms by weight percentage: industrial oleic acid 5-15%, phenolic antioxidant 1-5%, amine type antioxidant 1-10%, the nonmetallic extreme pressure anti-wear additives 5-15% of p-type, toluenesulfonic acid 3-9%, the nonmetallic extreme pressure anti-wear additives 2-3% of p-type, sulfurized polyisobutylene 1-5%, the nonmetallic extreme pressure anti-wear additives 11-19% of p-type, sodium carboxymethylcellulose 5-7%, ashless detergent dispersant 3-5%, di-iso-octyldiphenylamine 3-5%, calcium mahogany sulfonate 1-5%, sulphosuccinates 5-10%, di-iso-octyldiphenylamine 1-1.5%, demulsifier 4-5%, viscosity modifier 2-4%, wear-resistant material biodegradable at this time can be biodegradable, with good ring Guaranteed cost.
Description
Technical field
The present invention is a kind of formula of biodegradable wear-resistant material.
Background technique
With the development of the times, social progress, more and more Technology applications are in life, present wear-resistant material conduct
One kind of new material, more universal applies in life, and in existing technology, wear-resistant material is all non-degradable, this
Sample can cause a degree of pollution when some wear-resistant materials do not need or service life reaches to environment.
Summary of the invention
In view of the above existing problems in the prior art, the present invention provides a kind of formula of biodegradable wear-resistant material,
It can be biodegradable, there is good environmental-protecting performance.
To achieve the goals above, the invention is realized by the following technical scheme: a kind of biodegradable wear-resistant material,
Raw material in formula forms by weight percentage: industrial oleic acid 5-15%, phenolic antioxidant 1-5%, amine type are anti-oxidant
The nonmetallic extreme pressure anti-wear additives 5-15% of agent 1-10%, p-type, toluenesulfonic acid 3-9%, the nonmetallic extreme pressure anti-wear additives 2-3% of p-type, vulcanization are poly-
The nonmetallic extreme pressure anti-wear additives 11-19% of isobutene 1-5%, p-type, sodium carboxymethylcellulose 5-7%, ashless detergent dispersant 3-5%, two
Di-iso-octyldiphenylamine 3-5%, calcium mahogany sulfonate 1-5%, sulphosuccinates 5-10%, di-iso-octyldiphenylamine 1-1.5%, demulsification
Agent 4-5%, viscosity modifier 2-4%.
It the utility model has the advantages that preparing biodegradable wear-resistant material by this method, can be biodegradable, have good
Environmental-protecting performance.
Specific embodiment
Embodiment 1
A kind of formula of biodegradable wear-resistant material, the raw material in formula forms by weight percentage is respectively: industry oil
Acid 5%, phenolic antioxidant 1%, amine type antioxidant 1%, the nonmetallic extreme pressure anti-wear additives 5% of p-type, toluenesulfonic acid 3%, p-type are nonmetallic
It is the nonmetallic extreme pressure anti-wear additives 11% of extreme pressure anti-wear additives 2%, sulfurized polyisobutylene 1%, p-type, sodium carboxymethylcellulose 5%, ashless peace and quiet
Dispersing agent 3%, di-iso-octyldiphenylamine 3%, calcium mahogany sulfonate 1%, sulphosuccinates 5%, di-iso-octyldiphenylamine 1%, demulsification
Agent 4%, viscosity modifier 2%, wear-resistant material biodegradation rate biodegradable at this time are slower.
Embodiment 2
A kind of formula of biodegradable wear-resistant material, the raw material in formula forms by weight percentage is respectively: industry oil
Acid 15%, phenolic antioxidant 5%, amine type antioxidant 10%, the nonmetallic extreme pressure anti-wear additives 15% of p-type, toluenesulfonic acid 9%, p-type are non-
It is the nonmetallic extreme pressure anti-wear additives 19% of metal extreme pressure anti-wear additives 3%, sulfurized polyisobutylene 5%, p-type, sodium carboxymethylcellulose 7%, ashless
Detergent-dispersant additive 5%, di-iso-octyldiphenylamine 5%, calcium mahogany sulfonate 5%, sulphosuccinates 10%, di-iso-octyldiphenylamine
1.5%, demulsifier 5%, viscosity modifier 4%, wear-resistant material environmental-protecting performance biodegradable at this time are poor.
Embodiment 3
A kind of formula of biodegradable wear-resistant material, the raw material in formula forms by weight percentage is respectively: industry oil
Sour 10%, phenolic antioxidant 3%, amine type antioxidant 6%, the nonmetallic extreme pressure anti-wear additives 10% of p-type, toluenesulfonic acid 6%, the non-gold of p-type
Belong to extreme pressure anti-wear additives 2.3%, sulfurized polyisobutylene 1.5%, the nonmetallic extreme pressure anti-wear additives 11.9% of p-type, sodium carboxymethylcellulose
5.7%, ashless detergent dispersant 3.5%, di-iso-octyldiphenylamine 3.5%, calcium mahogany sulfonate 1.5%, sulphosuccinates 8%, two
Di-iso-octyldiphenylamine 1.28%, demulsifier 4.5%, viscosity modifier 2.4%, wear-resistant material biodegradable at this time can be given birth to
Object degradation, has good environmental-protecting performance.
Claims (4)
1. a kind of formula of biodegradable wear-resistant material, which is characterized in that the raw material in formula forms by weight percentage
It is respectively: industrial oleic acid 5-15%, phenolic antioxidant 1-5%, amine type antioxidant 1-10%, the nonmetallic extreme pressure anti-wear additives 5- of p-type
15%, the nonmetallic extreme pressure anti-wear additives 2-3% of toluenesulfonic acid 3-9%, p-type, sulfurized polyisobutylene 1-5%, the nonmetallic extreme pressure anti-wear additives of p-type
11-19%, sodium carboxymethylcellulose 5-7%, ashless detergent dispersant 3-5%, di-iso-octyldiphenylamine 3-5%, calcium mahogany sulfonate 1-
5%, sulphosuccinates 5-10%, di-iso-octyldiphenylamine 1-1.5%, demulsifier 4-5%, viscosity modifier 2-4%.
2. the formula of biodegradable wear-resistant material according to claim 1, which is characterized in that the raw material in formula is pressed
Weight percent composition is respectively: industrial oleic acid 5%, phenolic antioxidant 1%, amine type antioxidant 1%, the nonmetallic extreme pressure of p-type are anti-
The nonmetallic extreme pressure anti-wear additives 2% of grinding agent 5%, toluenesulfonic acid 3%, p-type, sulfurized polyisobutylene 1%, the nonmetallic extreme pressure anti-wear additives of p-type
11%, sodium carboxymethylcellulose 5%, ashless detergent dispersant 3%, di-iso-octyldiphenylamine 3%, calcium mahogany sulfonate 1%, succinate
Sulfonate 5%, di-iso-octyldiphenylamine 1%, demulsifier 4%, viscosity modifier 2%.
3. the formula of biodegradable wear-resistant material according to claim 1, which is characterized in that the raw material in formula is pressed
Weight percent composition is respectively: industrial oleic acid 15%, phenolic antioxidant 5%, amine type antioxidant 10%, the nonmetallic extreme pressure of p-type
The nonmetallic extreme pressure anti-wear additives 3% of antiwear additive 15%, toluenesulfonic acid 9%, p-type, sulfurized polyisobutylene 5%, the nonmetallic extreme pressure anti-wear additives of p-type
19%, sodium carboxymethylcellulose 7%, ashless detergent dispersant 5%, di-iso-octyldiphenylamine 5%, calcium mahogany sulfonate 5%, succinate
Sulfonate 10%, di-iso-octyldiphenylamine 1.5%, demulsifier 5%, viscosity modifier 4%.
4. the formula of biodegradable wear-resistant material according to claim 1, which is characterized in that the raw material in formula is pressed
Weight percent composition is respectively: industrial oleic acid 10%, phenolic antioxidant 3%, amine type antioxidant 6%, the nonmetallic extreme pressure of p-type
The nonmetallic extreme pressure anti-wear additives 2.3% of antiwear additive 10%, toluenesulfonic acid 6%, p-type, sulfurized polyisobutylene 1.5%, the nonmetallic extreme pressure of p-type are anti-
Grinding agent 11.9%, sodium carboxymethylcellulose 5.7%, ashless detergent dispersant 3.5%, di-iso-octyldiphenylamine 3.5%, calcium mahogany sulfonate
1.5%, sulphosuccinates 8%, di-iso-octyldiphenylamine 1.28%, demulsifier 4.5%, viscosity modifier 2.4%.