CN109265116A - A kind of cement plate coating and production method - Google Patents
A kind of cement plate coating and production method Download PDFInfo
- Publication number
- CN109265116A CN109265116A CN201811255918.5A CN201811255918A CN109265116A CN 109265116 A CN109265116 A CN 109265116A CN 201811255918 A CN201811255918 A CN 201811255918A CN 109265116 A CN109265116 A CN 109265116A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement plate
- production method
- adhesive
- dope layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to building materials technical field, in particular a kind of cement plate coating and production method, including dope layer.In the present invention, use magnesia, silicate, crushed crude pearlite, mica powder, adhesive, vegetable protein glue and adhesive as the main mixing material of cement plate, has preferable thermal insulation property, and it is not easy affected by environment, by adding antibacterial agent in the coating, it can effectively prevent the bacterial adsorption in air in cement plate surface, safety and sanitation.
Description
Technical field
The present invention relates to building materials technical field, specially a kind of cement plate coating and production method.
Background technique
Currently there are most of cement plate, after mounting, can cement plate surface be arranged coating, existing water
Mud plate coating, uses for a long time, and bacterium can form bacterial layer in plate face, therefore harm health, proposes one kind regarding to the issue above
Cement plate coating and production method.
Summary of the invention
The purpose of the present invention is to provide a kind of cement plate coating and production methods, to solve to propose in above-mentioned background technique
The problem of.
To achieve the above object, the invention provides the following technical scheme:
A kind of cement plate coating and production method, including dope layer and production method, the dope layer main component include
Magnesia, silicate, crushed crude pearlite, mica powder, adhesive, vegetable protein glue and antibacterial agent, magnesia, silicon in the dope layer
Hydrochlorate, crushed crude pearlite, mica powder, adhesive, vegetable protein glue and antibacterial agent ratio be magnesia 2-4 parts, silicate 30-50
Part, 10-25 parts of crushed crude pearlite, 15-30 parts of mica powder, 2-5 parts of adhesive, 0.2-0.6 parts of vegetable protein glue, 1-2 parts of antibacterial agent.
Preferably, the production method of the dope layer includes the following steps:
1, magnesia, silicate, crushed crude pearlite, mica powder, the vegetable protein glue for weighing corresponding mass are put into agitator tank；
2, water is added in agitator tank, starts to stir, mixing speed is 60 turns/1min, mixing time 15min-
30min；
3, the adhesive for weighing corresponding mass, which is added in agitator tank, to be stirred, and speed of agitator is 60 turns/1min, stirring
Time is 5min-8min；
4, the antibacterial agent for weighing corresponding mass, which is added in agitator tank, to be stirred, and speed of agitator is 30 turns/1min, stirring
Time is 10min-15min, obtains dope layer.
5, preferred, described adhesive is one of polyacrylate emulsion, styrene-acrylic emulsion.
Preferably, the antibacterial agent is mixed by isothiazolinone, nano zeolite and nanoscale zinc powder, the different thiophene
Oxazoline ketone, nano zeolite, nanoscale zinc powder mixed proportion be 1:2:5, the partial size of the nano zeolite is 50-100nm,
The partial size of the nanoscale zinc powder is 30-50nm.
Compared with prior art, the beneficial effects of the present invention are:
1, in the present invention, magnesia, silicate, crushed crude pearlite, mica powder, adhesive, vegetable protein glue and bonding are used
Main mixing material of the agent as cement plate, has preferable thermal insulation property, and be not easy affected by environment.
2, in the present invention, by adding antibacterial agent in the coating, it can effectively prevent the bacterial adsorption in air at cement
Plate surface, safety and sanitation.
Specific embodiment
The following is a clear and complete description of the technical scheme in the embodiments of the invention, it is clear that described embodiment
Only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, the common skill in this field
Art personnel every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
The present invention provides a kind of technical solution:
A kind of cement plate coating and production method, including dope layer and production method, the dope layer main component include
Magnesia, silicate, crushed crude pearlite, mica powder, adhesive, vegetable protein glue and antibacterial agent, magnesia, silicic acid in dope layer
Salt, crushed crude pearlite, mica powder, adhesive, vegetable protein glue and antibacterial agent ratio be magnesia 2-4 parts, silicate 30-50
Part, 10-25 parts of crushed crude pearlite, 15-30 parts of mica powder, 2-5 parts of adhesive, 0.2-0.6 parts of vegetable protein glue, antibacterial agent 1-2
Part.
Further, the production method of dope layer includes the following steps:
1, magnesia, silicate, crushed crude pearlite, mica powder, the vegetable protein glue for weighing corresponding mass are put into agitator tank；
2, water is added in agitator tank, starts to stir, mixing speed is 60 turns/1min, mixing time 15min-
30min；
3, the adhesive for weighing corresponding mass, which is added in agitator tank, to be stirred, and speed of agitator is 60 turns/1min, stirring
Time is 5min-8min；
4, the antibacterial agent for weighing corresponding mass, which is added in agitator tank, to be stirred, and speed of agitator is 30 turns/1min, stirring
Time is 10min-15min, obtains dope layer.
Further, adhesive is one of polyacrylate emulsion, styrene-acrylic emulsion.
Further, antibacterial agent is mixed by isothiazolinone, nano zeolite and nanoscale zinc powder, isothiazolinone,
Nano zeolite, nanoscale zinc powder mixed proportion be 1:2:5, the partial size of nano zeolite is 50-100nm, nanoscale zinc powder
Partial size be 30-50nm.
The cement plate coating using magnesia, silicate, crushed crude pearlite, mica powder, adhesive, vegetable protein glue and glues
Main mixing material of the mixture as cement plate, has preferable thermal insulation property, and be not easy it is affected by environment, by the coating
Antibacterial agent is added, can effectively prevent the bacterial adsorption in air in cement plate surface, safety and sanitation are suitable for promoting the use of.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (4)
1. a kind of cement plate coating and production method, including dope layer and production method, it is characterised in that: the dope layer is main
Ingredient includes magnesia, silicate, crushed crude pearlite, mica powder, adhesive, vegetable protein glue and antibacterial agent, in the dope layer
Magnesia, silicate, crushed crude pearlite, mica powder, adhesive, vegetable protein glue and antibacterial agent ratio be magnesia 2-4 parts, silicon
30-50 parts of hydrochlorate, 15-30 parts of mica powder, 2-5 parts of adhesive, 0.2-0.6 parts of vegetable protein glue, resists 10-25 parts of crushed crude pearlite
1-2 parts of microbial inoculum.
2. a kind of cement plate coating according to claim 1 and production method, it is characterised in that: the production of the dope layer
Method includes the following steps:
1) magnesia, silicate, crushed crude pearlite, mica powder, the vegetable protein glue for, weighing corresponding mass are put into agitator tank；
2) water, is added in agitator tank, starts to stir, mixing speed is 60 turns/1min, mixing time 15min-30min；
3) adhesive for, weighing corresponding mass, which is added in agitator tank, to be stirred, and speed of agitator is 60 turns/1min, mixing time
For 5min-8min；
4) antibacterial agent for, weighing corresponding mass, which is added in agitator tank, to be stirred, and speed of agitator is 30 turns/1min, mixing time
For 10min-15min, dope layer is obtained.
3. a kind of cement plate coating according to claim 1 and production method, it is characterised in that: described adhesive is poly- third
One of olefin(e) acid lotion, styrene-acrylic emulsion.
4. a kind of cement plate coating according to claim 1 and production method, it is characterised in that: the antibacterial agent is by different thiophene
Oxazoline ketone, nano zeolite and nanoscale zinc powder mix, the isothiazolinone, nano zeolite, nanoscale zinc powder
Mixed proportion is 1:2:5, and the partial size of the nano zeolite is 50-100nm, and the partial size of the nanoscale zinc powder is 30-50nm.