CN109264731A - The ultrapure sodium metasilicate of high-temperature silicon disulfide rubber reinforcing agent - Google Patents
The ultrapure sodium metasilicate of high-temperature silicon disulfide rubber reinforcing agent Download PDFInfo
- Publication number
- CN109264731A CN109264731A CN201811094694.4A CN201811094694A CN109264731A CN 109264731 A CN109264731 A CN 109264731A CN 201811094694 A CN201811094694 A CN 201811094694A CN 109264731 A CN109264731 A CN 109264731A
- Authority
- CN
- China
- Prior art keywords
- sodium metasilicate
- reinforcing agent
- rubber reinforcing
- temperature silicon
- silicon disulfide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the ultrapure sodium metasilicate of high-temperature silicon disulfide rubber reinforcing agent, it is characterised in that: process flow is quartz sand, soda ash-mixing-calcining-molding-sodium silicate solid.The high-temperature silicon disulfide rubber reinforcing agent of the technology of the present invention production is stablized with sodium metasilicate with modulus, impurity is few, and it is industry highest quality that total solid amount is high, the high-temperature silicon disulfide rubber reinforcing agent produced with product of the present invention, the primary partial size of product can reach nanoscale, 200 every gram of square meter of BET specific surface area, with excellent dispersibility and very high specific surface area, make product that there is the high grade of transparency, high anti-yellowing excellent performance, quality are stablized, and the imported product of similar high value can be substituted.
Description
Technical field:
The present invention relates to high-temperature silicon disulfide rubber, green tire field, specially a kind of high-temperature silicon disulfide rubber reinforcing agent
With ultrapure sodium metasilicate.
Background technique:
High-temperature silicon disulfide rubber reinforcing agent currently on the market is unstable with ultrapure sodium silicate modulus, and impurity is more, total solid amount
It is low, cause the high-temperature silicon disulfide rubber reinforcing agent transparency produced not high, anti-yellowing property is low, and overall quality is poor, our skill
The high-temperature silicon disulfide rubber reinforcing agent of art production is stablized with sodium metasilicate with modulus, and impurity is few, always measures the advantages that high admittedly, can replace
For the imported product of similar high value.
Summary of the invention:
The technical problem to be solved by the present invention lies in overcoming the defects of the prior art, provides a kind of high-temperature silicon disulfide rubber
The ultrapure sodium metasilicate of reinforcing agent.
The technical problems to be solved by the invention are realized using following technical scheme.
The ultrapure sodium metasilicate of high-temperature silicon disulfide rubber reinforcing agent, it is characterised in that: process flow is that quartz sand, soda ash-are mixed
Conjunction-calcining-molding-sodium silicate solid;
Chemical equation is Na2CO3+Si02-Na2Si03+CO2↑
Specifically: soda ash and quartz sand are uniformly mixed in 1:2 ratio, send into horse-shoe flame furnace, carries out at high temperature
Frit reaction is slowly flowed out by two sides fluid groove, is wandered to chain-and-slat forming machine, and feed liquid is divided automatically and is pressed into yin by pressure roller
In mould, it is shaped to blocks of solid, continues cool to head, is fallen in the feed bin of lower section, is transported to warehouse for finished product and is cooled to room temperature,
Sodium metasilicate is obtained, is put in storage.
Further technology: the soda ash and quartz sand incorporation time ± 30 seconds 3 minutes.
Further technology: pool depth is 1.6 meters in the horse-shoe flame furnace, dissolves area in 50 ㎡ or more, furnace
Equipped with two brunched burner nozzles, every alternating of automatic reverse in 30 minutes is primary, and two sides are equipped with offset dog-hole, and liquid surface height controlling is 1.45
Rice fluctuates < ± 5 centimetre, 3.8pa micro-positive pressure in furnace.
Further technology: 1510 DEG C ± 10 DEG C of frit reaction temperature.
Further technology: melting charge is after frit reaction, and the residence time is maintained at 36-38 hours in furnace.
Further technology: before the mixing step, testing to quartz sand and soda ash, and disqualified upon inspection is retracted,
Again quartz sand and soda ash are chosen, after the assay was approved weighing mixing.
Further technology: testing to sodium metasilicate before storage, examines qualified storage, unqualified to send into horse-shoe flame furnace
Calcining.
The utility model has the advantages that the high-temperature silicon disulfide rubber reinforcing agent of the technology of the present invention production is stablized with sodium metasilicate with modulus, it is miscellaneous
Matter is few, and total solid amount is high, is industry highest quality, the high-temperature silicon disulfide rubber reinforcing agent produced with product of the present invention, product original
Raw partial size can reach nanoscale, and 200 every gram of square meter of BET specific surface area makes with excellent dispersibility and very high specific surface area
Product has the high grade of transparency, high anti-yellowing excellent performance, and quality is stablized, and can substitute the imported product of similar high value.
Detailed description of the invention
Fig. 1 is process flow diagram of the invention.
Specific embodiment:
In order to be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, tie below
Specific embodiment is closed, the present invention is further explained.
Fig. 1, a kind of ultrapure sodium metasilicate of high-temperature silicon disulfide rubber reinforcing agent, process flow are quartz sand+soda ash-mixing-
Calcining-molding-sodium silicate solid;
Chemical equation is Na2CO3+Si02-Na2Si03+CO2↑
Specifically: soda ash and quartz sand are uniformly mixed in 2:1 ratio, send into horse-shoe flame furnace, carries out at high temperature
Frit reaction is slowly flowed out by two sides fluid groove, is wandered to chain-and-slat forming machine, and feed liquid is divided automatically and is pressed into yin by pressure roller
In mould, it is shaped to blocks of solid, continues cool to head, is fallen in the feed bin of lower section, is transported to warehouse for finished product and is cooled to room temperature,
Sodium metasilicate is obtained, is put in storage.
Soda ash and quartz sand incorporation time ± 30 seconds 3 minutes.
It by data comparison, can give, for mixing time at ± 30 seconds 3 minutes, the quality of product was in stable and higher
In quality.
Pool depth is 1.6 meters in horse-shoe flame furnace, dissolves area in 50 ㎡ or more, is equipped with two brunched burner nozzles in furnace, every 30
Minute automatic reverse alternating is primary, and two sides are equipped with offset dog-hole, and liquid surface height controlling fluctuates < ± 5 centimetre at 1.45 meters,
3.8pa micro-positive pressure in furnace.
1510 DEG C ± 10 DEG C of frit reaction temperature.
Melting charge is after frit reaction, and the residence time is maintained at 36-38 hours in furnace.
It before mixing step, tests to quartz sand and soda ash, disqualified upon inspection is retracted, and chooses quartz sand and pure again
Alkali, after the assay was approved weighing mixing;Test stone is quartz sand:
Soda ash:
GB210.1-2004 (soda ash national standard) | High-class product index (%) | Standard (%) of the present invention |
Total alkali content | 97.9 | 98 |
Chloride | 0.7 | 0.65 |
Iron | 0.0035 | 0.0022 |
Water-insoluble | 0.03 | 0.03 |
It tests before storage to sodium metasilicate, examines qualified storage, unqualified send is calcined into horse-shoe flame furnace;Examine mark
Standard is sodium metasilicate:
The basic principles, main features and advantages of the present invention have been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (4)
1. the ultrapure sodium metasilicate of high-temperature silicon disulfide rubber reinforcing agent, it is characterised in that: process flow is that quartz sand, soda ash-are mixed
Conjunction-calcining-molding-sodium silicate solid;
Chemical equation is Na2CO3+Si02-Na2Si03+CO2↑
Specifically: soda ash and quartz sand are uniformly mixed in 1:2 ratio, send into horse-shoe flame furnace, is melted at high temperature
Reaction, is slowly flowed out by two sides fluid groove, is wandered to chain-and-slat forming machine, feed liquid is divided automatically and is pressed into former by pressure roller
In, it is shaped to blocks of solid, continues cool to head, is fallen in the feed bin of lower section, is transported to warehouse for finished product and is cooled to room temperature, obtain
To sodium metasilicate, storage;
The soda ash and quartz sand incorporation time ± 30 seconds 3 minutes;
1510 DEG C ± 10 DEG C of frit reaction temperature;
Melting charge is after frit reaction, and the residence time is maintained at 36-38 hours in furnace.
2. the ultrapure sodium metasilicate of high-temperature silicon disulfide rubber reinforcing agent according to claim 1, it is characterised in that: described
Pool depth is 1.6 meters in horse-shoe flame furnace, dissolves area and is equipped with two brunched burner nozzles in 50 ㎡ or more, furnace, every 30 minutes automatic
Commutation is alternately primary, and two sides are equipped with offset dog-hole, and liquid surface height controlling is at 1.45 meters, fluctuation < ± 5 centimetre, in furnace
3.8pa micro-positive pressure.
3. the ultrapure sodium metasilicate of high-temperature silicon disulfide rubber reinforcing agent according to claim 1, it is characterised in that: described
It before mixing step, tests to quartz sand and soda ash, disqualified upon inspection is retracted, and chooses quartz sand and soda ash again, is examined
It weighs and mixes after qualification.
4. the ultrapure sodium metasilicate of high-temperature silicon disulfide rubber reinforcing agent according to claim 1, it is characterised in that: before storage
It tests to sodium metasilicate, examines qualified storage, unqualified send is calcined into horse-shoe flame furnace.