CN109234024B - 一种饮用水管清洗剂、饮用水管的清洗方法以及饮用水管的养护方法 - Google Patents
一种饮用水管清洗剂、饮用水管的清洗方法以及饮用水管的养护方法 Download PDFInfo
- Publication number
- CN109234024B CN109234024B CN201811352985.9A CN201811352985A CN109234024B CN 109234024 B CN109234024 B CN 109234024B CN 201811352985 A CN201811352985 A CN 201811352985A CN 109234024 B CN109234024 B CN 109234024B
- Authority
- CN
- China
- Prior art keywords
- water
- water pipe
- pipe
- parts
- cleaning agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供了一种水管清洗剂，以质量分数计，包括12～50重量份的天然有机酸、10～50重量份的柠檬酸、10～15重量份的天然表面活性剂、10～15重量份的天然杀菌剂以及10～25重量份的水。本发明提供了一种水管清洗剂，通过清洗剂和水管内壁的水垢、铁锈、污泥发生物理、化学反应，能够有效的清除水垢、铁锈、污泥和实现高效杀菌。本发明的水管清洗剂均为可以食用材料，对水管无二次污染，即便有残留也不会对人体产生其他伤害；而且清理过程简便，清理设备简单易得，清洗剂和清洗过程成本低，接受程度高，适于大规模推广和应用，具有广阔的发展前景。
Description
技术领域
本发明属于重防腐涂料技术领域，涉及一种水管清洗剂、水管的清洗方法以及水管的养护方法，尤其涉及一种饮用水管清洗剂、饮用水管的清洗方法以及饮用水管的养护方法。
背景技术
水管是供水的管道，水管的分类有三种，第一类是金属管，如内搪塑料的热镀铸铁管、铜管、不锈钢管以及早期的镀锌管等，其中，镀锌管作为水管，使用几年后，管内产生大量锈垢，流出的黄水不仅污染洁具，而且夹杂着不光滑内壁滋生的细菌，锈蚀造成水中重金属含量过高，严重危害人体的健康，所以目前国家已出条例禁止当饮用水管；铜管具有耐腐蚀、消菌等优点，是水管中的上等品，但是铜管价格贵，焊接的施工费用更高，所以很少有家庭装修采用焊接式铜管；不锈钢管，安全、卫生、健康以及耐用，消除了塑料管道污染的问题，价格也比铜管节省很多，是目前首选的金属水管材料。第二类是塑料管，如UPVC、PB、PP-R、PE-RT、PPH、PP-B以及PEX等。而第三类是塑复金属管，如塑复钢管，铝塑复合管、外层熔接型铝塑复合管、钢塑复合管和双金属复合型等。现代装修水管都是采用埋墙式施工，“隐蔽工程”是一个非常重要的问题，不仅仅是水管渗漏和爆裂将带来难以弥补的后果，更主要的是供水管道的饮用水安全问题。质量决定水质，正所谓“水质好不好，关键看管道”，因而，供水管路的卫生性能、产品寿命、材料强度、耐腐蚀性能、经济性能、施工性能、热膨胀性能、保温性能以及环保性能等，都是考量其是否合格的重要指标。
但是在我国，楼盘的居住和使用年限为70年，时间跨度大，造成了各个楼盘，由于过去的材料局限，供水管道有水泥管、铸铁管、钢管、镀锌管、PP、PE以及铝塑复合管等等诸多种类，所以造成了现阶段存在结构复杂，情况多样性大等问题，虽然目前国家已经禁止了镀锌管等材料作为供水管道，但是在90年代末到2010年前，主体还是以铸铁管和镀锌管为主，这种管材长时间使用后会产生腐蚀，加上自来水体在输送过程会产生污泥，砂石、油污、藻类、细菌及水中的各种重金属便渐渐堆积，附着于水管的管壁，这些平常看不见但附着在水管内的有害物质，会一点点地跟着水流被带出来，经由人们的生活饮食用水、洗漱用水渐渐被人体消化吸收和肌肤触摸吸收，危害人体健康。
而且现代人们的生活水平日益提高，对与饮用水的关注度也越来越关注，对饮用水的要求也不仅仅在于水量、水压，更加关注水质安全。现在虽然有些家庭通过安装***，解决引用水问题，但是***作为末端设备，无法解决水管污浊问题，而且指标不治本，不管是前期的产品成本和后期的过滤器耗材的成本，都会大大增加家庭的生活成本。目前，虽然也有部分企业开始用机器清洗自来水管，但是效果不明显，只能清除污泥和部分水垢，不能彻底清除铁锈和细菌；也有文献指出，利用物理方法震动或者超声波清洗管道内壁，但是这种方式仍然无法除去牢固的铁锈和水垢，更无法清除细菌，还会损伤水管自身和水管的安装结构；还有技术指出，使用盐酸，硫酸等无机酸来清洗水管，虽然可以有效清除铁锈和污垢问题，但是会严重损伤水管本身。
因此，如何找到一种更为简便适宜的方法，能够解决上述饮用水管中存在的水质安全隐患的问题，克服关键的“最后一公里”的难题，已成为业内亟待解决的问题之一，也是提高民生保障的关键环节之一。
发明内容
有鉴于此，本发明要解决的技术问题在于提供一种水管清洗剂、水管的清洗方法以及水管的养护方法，特别是一种饮用水管清洗剂、饮用水管的清洗方法以及饮用水管的养护方法。本发明提供的水管清洗剂，通过发生化学和物理变化，不仅能够清除污泥和水垢，而且可有清除铁锈以及细菌，还能够清除水管内残留的有害重金属，并不会损失水管本身。
本发明提供了一种水管清洗剂，以质量分数计，包括：
优选的，所述天然有机酸包括柠檬酸、山楂酸、醋酸、酒石酸、维生素C和熊果酸中的一种或多种；
所述天然表面活性剂包括橙油、皂角和腰果油中的一种或多种；
所述天然杀菌剂包括大蒜素、ε-聚赖氨酸、姜提取液和茶油中的一种或多种；
所述水管清洗剂还包括3～10重量份的玉米改性吸水剂。
优选的，所述水管清洗剂可用于清洗水泥水管、铸铁水管、钢水管、镀锌水管、PP水管、PE水管以及铝塑复合水管中的一种或多种；
所述水管包括自来水水管。
本发明还提供了一种水管的清洗方法，包括以下步骤：
1)将上述技术方案任意一项所述的水管清洗剂和水，从入户端送入自来水管路中，静置，然后排出清理后的污水。
优选的，所述水管清洗剂和水的质量比为1：(1～15)；
所述入户端为用户的自来水供水入口处；
所述入户端设置有进水口，或者进水口和阀门。
优选的，所述自来水管路包括水泥管、铸铁管、钢管、镀锌管、PP管、PE管以及铝塑复合管中的一种或多种；
所述静置的时间为15～120min；
所述污水从用户的自来水管路出口中排出；
所述步骤1)的次数为1～5次。
本发明还提供了一种水管的养护方法，包括以下步骤：
A)将水管内镀膜液，从入户端送入自来水金属管路中，静置置换后，排出镀膜后的残液；
所述金属管路为经过上述技术方案任意一项所述的清洗方法清洗后的金属管路。
优选的，所述水管内镀膜液，以质量分数计，包括：
杀菌金属盐 15～30 重量份；
络合剂 0.01～0.3 重量份；
水 60～85 重量份；
所述静置置换的时间为10～360min。
优选的，所述杀菌金属盐包括银盐、铜盐、钛盐和金盐中的一种或多种；
所述络合剂包括杂多酸盐、克丙炔醇乙氧基化合物、硫酸铈、吡啶嗡盐、酒石酸钾、三乙醇胺、酒石酸钾钠、柠檬酸钠和氨水中的一种或多种；
所述水管包括铸铁水管、钢水管和镀锌水管中的一种或多种。
优选的，所述银盐包括硝酸银、甲基磺酸银、二十烷酸银和碘化银中的一种或多种；
通过盐酸检测所述残液中的银离子，当有白色沉淀时，表明金属管路镀膜完全；
所述镀膜后的残液从用户的自来水管路出口中排出。
本发明提供了一种水管清洗剂，以质量分数计，包括12～50重量份的天然有机酸、10～50重量份的柠檬酸、10～15重量份的天然表面活性剂、10～15重量份的天然杀菌剂以及10～25重量份的水。与现有技术相比，本发明针对现有的供水管路，特别是家庭自来水用水管路种类繁多，使用年限较长，存在的铁锈、污泥，砂石、油污、藻类、细菌及水中的各种重金属渐渐堆积，附着于水管的管壁的问题。而目前的清洗自来水管的方法又存在只能清除污泥和部分水垢，不能彻底清除铁锈和细菌，还会损伤水管自身和水管的安装结构等局限性。
本发明创造性的提供了一种水管清洗剂，通过发生化学和物理变化，能够清除污垢、铁锈以及细菌，更利用柠檬酸具有螯合作用的特点，能够清除水管内残留的有害重金属；同时，本发明全部采用天然原料，安全环保无污染，再利用天然杀菌剂、天然表面活性剂和柠檬酸构成的杀菌体系，更加有效的杀除水管内的有害菌。采用本发明提供的水管清洗剂，从住户自来水的入水管处连接一个外来供水器，通过外来供水器把水管清洗剂输送到室内的水管内，清洗剂在水管内停留一段时间，通过清洗剂和水管内壁的水垢、铁锈、污泥发生物理、化学反应，有效的清除水垢、铁锈、污泥和实现高效杀菌，最后再排出污水即可。
本发明的水管清洗剂均为可以食用材料，对水管无二次污染，即便有残留也不会对人体产生其他伤害；而且清理过程简便，清理设备简单易得，清洗剂和清洗过程成本低，接受程度高，适于大规模推广和应用，具有广阔的发展前景。
实验结果表明，采用本发明提供的清洗方法，清洗杀菌后，水质清澈透明，用氢氧化钠滴定无沉淀，取水样检测无菌落。
具体实施方式
为了进一步理解本发明，下面结合实施例对本发明优选实施方案进行描述，但是应当理解，这些描述只是为了进一步说明本发明的特征和优点，而不是对发明权利要求的限制。
本发明所有原料，对其来源没有特别限制，在市场上购买的或按照本领域技术人员熟知的常规方法制备的即可。
本发明所有原料，对其纯度没有特别限制，本发明优选采用分析纯或饮用水设备领域使用的常规纯度。
本发明提供了一种水管清洗剂，以质量分数计，包括：
本发明原则上对所述天然有机酸没有特别限制，以本领域技术人员熟知的天然有机酸即可，本领域技术人员可以根据实际应用情况、产品要求以及质量要求进行选择和调整，本发明为更好的实现对水管中水垢、铁锈、污泥和细菌的去除，同时不伤及水管材质，还保证安全对人体无伤害，所述天然有机酸优选为可以和金属氧化物反应，但与金属反应缓慢的酸类，具体可以包括柠檬酸、山楂酸、醋酸、酒石酸、维生素C和熊果酸中的一种或多种，更优选为醋酸、酒石酸或维生素C，更优选为醋酸。
本发明原则上对所述天然有机酸的加入量没有特别限制，本领域技术人员可以根据实际应用情况、产品要求以及质量要求进行选择和调整，本发明为更好的实现对水管中水垢、铁锈、污泥和细菌的去除，同时不伤及水管材质，还保证安全对人体无伤害，所述天然有机酸的加入量优选为12～50重量份，更优选为17～45重量份，更优选为22～40重量份，更优选为27～35重量份。
本发明原则上对所述柠檬酸的加入量没有特别限制，本领域技术人员可以根据实际应用情况、产品要求以及质量要求进行选择和调整，本发明为更好的实现对水管中水垢、铁锈、污泥和细菌的去除，同时不伤及水管材质，还保证安全对人体无伤害，所述柠檬酸的加入量优选为10～50重量份，更优选为15～45重量份，更优选为20～40重量份，更优选为25～35重量份。
本发明原则上对所述天然表面活性剂没有特别限制，以本领域技术人员熟知的天然表面活性剂即可，本领域技术人员可以根据实际应用情况、产品要求以及质量要求进行选择和调整，本发明为更好的实现对水管中水垢、铁锈、污泥和细菌的去除，同时不伤及水管材质，还保证安全对人体无伤害，所述天然表面活性剂优选包括橙油、皂角和腰果油中的一种或多种，更优选为橙油、皂角或腰果油，更优选为橙油。
本发明原则上对所述天然表面活性剂的加入量没有特别限制，本领域技术人员可以根据实际应用情况、产品要求以及质量要求进行选择和调整，本发明为更好的实现对水管中水垢、铁锈、污泥和细菌的去除，同时不伤及水管材质，还保证安全对人体无伤害，所述天然表面活性剂的加入量优选为10～15重量份，更优选为11～14重量份，更优选为12～13重量份。
本发明原则上对所述天然杀菌剂没有特别限制，以本领域技术人员熟知的天然杀菌剂即可，本领域技术人员可以根据实际应用情况、产品要求以及质量要求进行选择和调整，本发明为更好的实现对水管中水垢、铁锈、污泥和细菌的去除，同时不伤及水管材质，还保证安全对人体无伤害，所述天然杀菌剂优选包括大蒜素、ε-聚赖氨酸、姜提取液和茶油中的一种或多种，更优选为大蒜素、ε-聚赖氨酸、姜提取液或茶油，更优选为大蒜素。
本发明原则上对所述天然杀菌剂的加入量没有特别限制，本领域技术人员可以根据实际应用情况、产品要求以及质量要求进行选择和调整，本发明为更好的实现对水管中水垢、铁锈、污泥和细菌的去除，同时不伤及水管材质，还保证安全对人体无伤害，所述天然杀菌剂的加入量优选为10～15重量份，更优选为11～14重量份，更优选为12～13重量份。
本发明原则上对所述水的加入量没有特别限制，本领域技术人员可以根据实际应用情况、产品要求以及质量要求进行选择和调整，本发明为更好的实现对水管中水垢、铁锈、污泥和细菌的去除，同时不伤及水管材质，还保证安全对人体无伤害，所述水的加入量优选为10～25重量份，更优选为12～23重量份，更优选为15～20重量份。
本发明为更好的实现对水管中水垢、铁锈、污泥和细菌的去除，同时不伤及水管材质，还要保证安全对人体无伤害，所述水管清洗剂优选还包括玉米改性吸水剂，更优选为3～10重量份的玉米改性吸水剂，更优选为4～9重量份，更优选为5～8重量份，更优选为6～7重量份。
本发明上述步骤提供了一种水管清洗剂，本发明对所述水管清洗剂中水管种类没有特别限制，以本领域技术人员熟知的常用的自来水供水水管即可，本领域技术人员可以根据实际应用情况、产品要求以及质量要求进行选择和调整，本发明为更好的实现对水管中水垢、铁锈、污泥和细菌的去除，所述水管即为自来水管线，所述水管清洗剂优选可用于清洗水泥水管、铸铁水管、钢水管、镀锌水管、PP水管、PE水管以及铝塑复合水管中的一种或多种，更优选为水泥水管、铸铁水管、钢水管、镀锌水管、PP水管、PE水管或铝塑复合水管。
本发明还提供了一种水管的清洗方法，包括以下步骤：
1)将上述技术方案任意一项所述的水管清洗剂和水，从入户端送入自来水管路中，静置，然后排出清理后的污水。
本发明对上述水管的清洗方法中所需水管清洗剂中原料的选择和组成，以及相应的优选原则，与前述水管清洗剂中所对应原料的选择和组成，以及相应的优选原则均可以进行对应，在此不再一一赘述。
本发明原则上对所述水管清洗剂和水的加入比例没有特别限制，本领域技术人员可以根据实际应用情况、产品要求以及质量要求进行选择和调整，本发明为更好的实现对水管中水垢、铁锈、污泥和细菌的去除，同时不伤及水管材质，还保证安全对人体无伤害，所述水管清洗剂和水的质量比优选为1：(1～15)，更优选为1：(3～12)，更优选为1：(5～10)，更优选为1：(7～8)。
本发明对所述入户端的定义没有特别限制，以本领域技术人员熟知的水管入户端的常规定义即可，本领域技术人员可以根据实际应用情况、产品要求以及质量要求进行选择和调整，本发明所述入户端优选为用户的自来水供水入口处，即进水总入口出，可以理解为自来水供水管线进入个人住户、集体用户、工矿企业、学校、事业单位或政府机关等之前的分支进水总管线的出口处。
本发明为更加便于清洗和过程控制，提高使用效果，所述入户端设置有进水口，或者设置有进水口和阀门。本发明对于进水口的结构、型号和尺寸选择等，以及阀门的结构、型号和尺寸选择等没有特别限制，以本领域技术人员熟知的用于自来水管线的进水口和阀门即可，本领域技术人员可以根据实际应用情况、产品要求以及质量要求进行选择和调整。
本发明对所述静置的条件没有特别限制，本领域技术人员可以根据实际应用情况、产品要求以及质量要求进行选择和调整，本发明所述静置的时间优选为15～120min，更优选为30～100min，更优选为45～90min，更优选为60～75min。本发明所述静置的压力优选为常压或加压，更优选为常压。本发明所述常压是指将水管清洗剂和水充满自来水管路即可，而无需再进行加压操作。如在自来水供水入口处加入水管清洗剂和水，在用户的终端中的一处排出原有水管中的自来水或空气，直到本发明送入的水管清洗剂和水完全充满自来水管路中即可。
本发明提供的水管清洗方法在静置完成后，直接排出清理后的污水即可，即将污水从用户的自来水管路出口中的任意一个排出。本发明提供的水管清洗剂均为可以食用材料，对水管无二次污染，即便有残留也不会对人体产生其他伤害。本发明为更好的实现对水管中水垢、铁锈、污泥和细菌的去除，上述清洗步骤优选可以进行一次或多次，本发明所述步骤1)的次数优选为1～5次，更优选为2～4次，更优选为2～3次。
本发明为提供适用性和实用性更广泛的水管清洗和后续保证的方法，更好的实现对水管内壁的清洗和保养，更好的提高水管清洁度，保证杀菌性能，完整和细化后续的保养过程，本发明还提供了一种水管的养护方法，包括以下步骤：
A)将水管内镀膜液，从入户端送入自来水金属管路中，静置置换后，排出镀膜后的残液；
所述金属管路为经过上述技术方案任意一项所述的清洗方法清洗后的金属管路。
本发明对上述水管的养护方法中所需原料和名词，以及相应的优选原则，与前述水管的清洗方法中所需原料和名词，以及相应的优选原则均可以进行对应，在此不再一一赘述。
本发明原则上对所述水管内镀膜液的具体组成没有特别限制，本领域技术人员可以根据实际应用情况、产品要求以及质量要求进行选择和调整，本发明为更好的实现对水管内壁的镀膜，更好的提高水管清洁度，保证杀菌性能，本发明所述水管内镀膜液，以质量分数计，优选包括：
杀菌金属盐15～30重量份；
络合剂0.01～0.3重量份；
水60～85重量份。
本发明原则上对所述杀菌金属盐没有特别限制，以本领域技术人员熟知的常规杀菌金属的盐即可，本领域技术人员可以根据实际应用情况、产品要求以及质量要求进行选择和调整，本发明为更好的实现对水管内壁的镀膜，更好的提高水管清洁度，保证杀菌性能，所述杀菌金属盐优选包括银盐、铜盐、钛盐和金盐中的一种或多种，更优选为银盐、铜盐、钛盐或金盐，更优选为银盐。具体可以包括硝酸银、甲基磺酸银、二十烷酸银和碘化银中的一种或多种，更优选为硝酸银、甲基磺酸银、二十烷酸银或碘化银，更优选包括硝酸银。
本发明原则上对所述杀菌金属盐的加入量没有特别限制，本领域技术人员可以根据实际应用情况、产品要求以及质量要求进行选择和调整，本发明为更好的实现对水管内壁的镀膜，更好的提高水管清洁度，保证杀菌性能，所述杀菌金属盐的加入量优选为15～30重量份，更优选为17～28重量份，更优选为20～25重量份，具体可以为20重量份。
本发明原则上对所述络合剂没有特别限制，本领域技术人员可以根据实际应用情况、产品要求以及质量要求进行选择和调整，本发明为更好的实现对水管内壁的镀膜，更好的提高水管清洁度，保证杀菌性能，所述络合剂优选包括杂多酸盐、克丙炔醇乙氧基化合物、硫酸铈、吡啶嗡盐、酒石酸钾、三乙醇胺、酒石酸钾钠、柠檬酸钠和氨水中的一种或多种，更优选为杂多酸盐、克丙炔醇乙氧基化合物、硫酸铈、吡啶嗡盐、酒石酸钾、三乙醇胺、酒石酸钾钠、柠檬酸钠或氨水。
本发明原则上对所述络合剂的加入量没有特别限制，本领域技术人员可以根据实际应用情况、产品要求以及质量要求进行选择和调整，本发明为更好的实现对水管内壁的镀膜，更好的提高水管清洁度，保证杀菌性能，所述络合剂的加入量优选为0.01～0.3重量份，更优选为0.05～0.25重量份，更优选为0.1～0.2重量份，具体可以为0.05重量份。
本发明原则上对所述水的加入量没有特别限制，本领域技术人员可以根据实际应用情况、产品要求以及质量要求进行选择和调整，本发明为更好的实现对水管内壁的镀膜，更好的提高水管清洁度，保证杀菌性能，所述水的加入量优选为60～85重量份，更优选为65～80重量份，更优选为70～75重量份，具体可以为80重量份。
本发明为更好的实现对水管内壁的镀膜，更好的提高水管清洁度，保证杀菌性能，所述水管即为自来水金属管线，具体可以包括铸铁水管、钢水管和镀锌水管中的一种或多种，更优选为铸铁水管、钢水管或镀锌水管。
本发明对所述入户端的定义没有特别限制，以本领域技术人员熟知的水管入户端的常规定义即可，本领域技术人员可以根据实际应用情况、产品要求以及质量要求进行选择和调整，本发明所述入户端优选为用户的自来水供水入口处，即进水总入口出，可以理解为自来水供水管线进入个人住户、集体用户、工矿企业、学校、事业单位或政府机关等之前的分支进水总管线的出口处。
本发明为更加便于镀膜和过程控制，提高使用效果，所述入户端设置有进水口，或者设置有进水口和阀门。本发明对于进水口的结构、型号和尺寸选择等，以及阀门的结构、型号和尺寸选择等没有特别限制，以本领域技术人员熟知的用于自来水管线的进水口和阀门即可，本领域技术人员可以根据实际应用情况、产品要求以及质量要求进行选择和调整。
本发明对所述静置置换的条件没有特别限制，本领域技术人员可以根据实际应用情况、产品要求以及质量要求进行选择和调整，本发明所述静置置换的时间优选为10～360min，更优选为60～300min，更优选为120～240min，更优选为150～210min。本发明所述静置置换的压力优选为常压或加压，更优选为常压。本发明所述常压是指将水管内镀膜液充满自来水管路即可，而无需再进行加压操作。如在自来水供水入口处加入水管内镀膜液，在用户的终端中的一处排出原有水管中的自来水或空气，直到本发明送入的水管内镀膜液完全充满自来水管路中即可。
本发明提供的水管内镀膜的方法在静置置换完成后，直接排出镀膜后的残液即可，即将镀膜后的残液从用户的自来水管路出口中的任意一个排出。而且通过盐酸检测所述残液中的银离子，当有白色沉淀时，能够判断金属管路镀膜完全。
本发明上述步骤提供的金属水管内镀膜的镀膜液，通过化学置换作用，利用金属水管中的铁、铝等金属置换可溶性银盐中的银离子，从而在水管内壁形成致密的杀菌金属层，利用杀菌金属的杀菌性保障饮用水的清洁。本发明提供的采用该镀膜液的水管内壁镀膜方法，能够防止污垢和菌落的再次生成，即使常年使用的水管壁，通过结合本发明特有的清洗方法，清洗后的管壁能够形成新的金属层，去除原有污垢、铁锈、水垢和细菌等，再经过镀膜后，杀菌金属层会有效的阻止金属水管管壁被水中的氧氧化和污垢的产生，从根本上减少铁锈和细菌的产生，从而解决金属水管持续的再次污染和生成污垢问题，解决水管的保洁和杀菌问题，达到了持久养护的作用。
本发明上述步骤提供了一种饮用水管清洗剂、饮用水管的清洗方法以及饮用水管的养护方法。本发明通过发生化学和物理变化，能够清除污垢、铁锈以及细菌，更利用柠檬酸具有螯合作用的特点，能够清除水管内残留的有害重金属；同时，本发明全部采用天然原料，安全环保无污染，再利用天然杀菌剂、天然表面活性剂和柠檬酸构成的杀菌体系，更加有效的杀除水管内的有害菌。本发明采用天然有机酸可以和金属氧化物反应，但与金属反应缓慢，可以清除铁锈和碱性污垢，同时不伤及水管本体，而且水管清洗剂均为可以食用材料，对水管无二次污染，即便有残留也不会对人体产生其他伤害，安全性高。
本发明采用本发明提供的水管清洗剂，从住户自来水的入水管处连接一个外来供水器，通过外来供水器把水管清洗剂输送到室内的水管内，清洗剂在水管内停留一段时间，通过清洗剂和水管内壁的水垢、铁锈、污泥发生物理、化学反应，有效的清除水垢、铁锈、污泥和实现高效杀菌，最后再排出污水即可。
本发明提供的饮用水管的清洗方法，清理过程简便，清理设备简单易得，清洗剂和清洗过程成本低，接受程度高，适于大规模推广和应用，具有广阔的发展前景。
实验结果表明，采用本发明提供的清洗方法，清洗杀菌后，水质清澈透明，用氢氧化钠滴定无沉淀，取水样检测无菌落。
为了进一步说明本发明，以下结合实施例对本发明提供的一种水管清洗剂、水管的清洗方法以及水管的养护方法进行详细描述，但是应当理解，这些实施例是在以本发明技术方案为前提下进行实施，给出了详细的实施方式和具体的操作过程，只是为进一步说明本发明的特征和优点，而不是对本发明权利要求的限制，本发明的保护范围也不限于下述的实施例。
实施例1
清洗剂配方：
醋酸30
柠檬酸40
橙油10
大蒜素10
玉米淀粉改性吸水剂5
纯净水20
清洗方法：
在使用家庭的供水的入口处增加一个入水口和阀门，通过水泵将按照上述比例调配好的水管清洗剂和水(1：10)输送到室内的用水管内，通过清洗剂和水管内壁的水垢、铁锈、污泥发生物理、化学反应，有效的清除水垢、铁锈、污泥。利用大蒜素和橙油、柠檬酸的杀菌作用，有效杀除水管内的有害菌。清洗剂在水管内停留60分钟后，排出污水后再次用水泵将水管清洗剂和水(1：20)输送到水管内停留30分钟。排出清水后达到清洗目的。
对清洗前和清洗后的水管进行对比检测。采用常温的沸腾后的自来水(凉白开水)作为检测介质。
水管清洗前，放空水管后，在水管进水阀处急速通入凉白开水，在出水口取水样用肉眼观察，有浑浊现象，同时用氢氧化钠滴定有沉淀。取水样利用菌落测数器进行菌落检测，测算后每升水含3000个，证明水管内含有二次菌落污染。
水管通过清洗杀菌后，水管内用凉白开水冲洗，水质清澈透明，用氢氧化钠滴定无沉淀。取水样利用菌落测数器进行菌落检测，取水样检测菌落，无菌落。
实施例2
清洗剂配方：
山楂酸 20
柠檬酸 30
橙油 10
大蒜素 10
玉米淀粉改性吸水剂 8
纯净水 22
在使用家庭的供水的入口处增加一个入水口和阀门，通过水泵将按照上述比例调配好的水管清洗剂和水(1：10)输送到室内的用水管内，通过清洗剂和水管内壁的水垢、铁锈、污泥发生物理、化学反应，有效的清除水垢、铁锈、污泥。利用大蒜素和橙油、柠檬酸的杀菌作用，有效杀除水管内的有害菌。清洗剂在水管内停留60分钟后，排出污水后再次用水泵将水管清洗剂和水(1：20)输送到水管内停留30分钟。排出清水后达到清洗目的。
对清洗后的水管进行检测。采用常温的沸腾后的自来水(凉白开水)作为检测介质。
水管通过清洗杀菌后，水管内用凉白开水冲洗，水质清澈透明，用氢氧化钠滴定无沉淀。取水样利用菌落测数器进行菌落检测，取水样检测菌落，无菌落。
实施例3
清洗剂配方：
醋酸 10
山楂酸 10
柠檬酸 30
橙油 10
大蒜素 10
玉米淀粉改性吸水剂 6
纯净水 24
在使用家庭的供水的入口处增加一个入水口和阀门，通过水泵将按照上述比例调配好的水管清洗剂和水(1：10)输送到室内的用水管内，通过清洗剂和水管内壁的水垢、铁锈、污泥发生物理、化学反应，有效的清除水垢、铁锈、污泥。利用大蒜素和橙油、柠檬酸的杀菌作用，有效杀除水管内的有害菌。清洗剂在水管内停留60分钟后，排出污水后再次用水泵将水管清洗剂和水(1：20)输送到水管内停留30分钟。排出清水后达到清洗目的。
对清洗后的水管进行检测。采用常温的沸腾后的自来水(凉白开水)作为检测介质。
水管通过清洗杀菌后，水管内用凉白开水冲洗，水质清澈透明，用氢氧化钠滴定无沉淀。取水样利用菌落测数器进行菌落检测，取水样检测菌落，无菌落。
水管镀银液配方：
硝酸银 25
蒸馏水 74.9
柠檬酸钠 0.1
镀膜方法：
利用水泵将水管镀银液抽到清洗后的水管内。停留1小时发生化学置换反应，利用铁，铝金属置换可溶性银盐中的银离子。在水管内壁形成致密的金属银层，利用金属银的杀菌性保障饮用水的清洁。在镀膜结束后，可以用盐酸检测流出来的镀液残留的银离子。有白色沉淀为水管镀膜完全。
对镀银后形成致密金属涂层的水管，进行如下检测。
水管通过清洗杀菌镀膜后，水管内用凉白开水冲洗，水质清澈透明，用氢氧化钠滴定无沉淀。取水样利用菌落测数器进行菌落检测，取水样检测菌落，无菌落。将凉白开水放入水管停留一周后检测，水质清澈透明，取水样用菌落测数器进行菌落检测，无菌落。
实施例4
清洗剂配方：
维生素C 5
山楂酸 10
柠檬酸 35
橙油 10
大蒜素 10
玉米淀粉改性吸水剂 6
纯净水 24
在使用家庭的供水的入口处增加一个入水口和阀门，通过水泵将按照上述比例调配好的水管清洗剂和水(1：10)输送到室内的用水管内，通过清洗剂和水管内壁的水垢、铁锈、污泥发生物理、化学反应，有效的清除水垢、铁锈、污泥。利用大蒜素和橙油、柠檬酸的杀菌作用，有效杀除水管内的有害菌。清洗剂在水管内停留60分钟后，排出污水后再次用水泵将水管清洗剂和水(1：20)输送到水管内停留30分钟。排出清水后达到清洗目的。
对清洗后的水管进行检测。采用常温的沸腾后的自来水(凉白开水)作为检测介质。
水管通过清洗杀菌后，水管内用凉白开水冲洗，水质清澈透明，用氢氧化钠滴定无沉淀。取水样利用菌落测数器进行菌落检测，取水样检测菌落，无菌落。
水管镀银液配方：
硝酸银 25
蒸馏水 74.9
柠檬酸钠 0.1
镀膜方法：
利用水泵将水管镀银液抽到清洗后的水管内。停留1小时发生化学置换反应，利用铁，铝金属置换可溶性银盐中的银离子。在水管内壁形成致密的金属银层，利用金属银的杀菌性保障饮用水的清洁。在镀膜结束后，可以用盐酸检测流出来的镀液残留的银离子。有白色沉淀为水管镀膜完全。
对镀银后形成致密金属涂层的水管，进行如下检测。
水管通过清洗杀菌镀膜后，水管内用凉白开水冲洗，水质清澈透明，用氢氧化钠滴定无沉淀。取水样利用菌落测数器进行菌落检测，取水样检测菌落，无菌落。将凉白开水放入水管停留一周后检测，水质清澈透明，取水样用菌落测数器进行菌落检测，无菌落。
以上对本发明提供的一种饮用水管清洗剂、饮用水管的清洗方法以及饮用水管的养护方法进行了详细的介绍，本文中应用了具体个例对本发明的原理及实施方式进行了阐述，以上实施例的说明只是用于帮助理解本发明的方法及其核心思想，包括最佳方式，并且也使得本领域的任何技术人员都能够实践本发明，包括制造和使用任何装置或***，和实施任何结合的方法。应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以对本发明进行若干改进和修饰，这些改进和修饰也落入本发明权利要求的保护范围内。本发明专利保护的范围通过权利要求来限定，并可包括本领域技术人员能够想到的其他实施例。如果这些其他实施例具有不是不同于权利要求文字表述的结构要素，或者如果它们包括与权利要求的文字表述无实质差异的等同结构要素，那么这些其他实施例也应包含在权利要求的范围内。
Claims (6)
1.一种水管的养护方法，其特征在于，包括以下步骤：
A）将水管内镀膜液，从入户端送入自来水金属管路中，静置置换后，排出镀膜后的残液；
所述水管内镀膜液，以质量分数计，由以下材料组成：
杀菌金属盐 15~30 重量份；
络合剂 0.01~0.3 重量份；
水 60~85 重量份；
所述静置置换的时间为10~360min；
所述金属管路为经过清洗后的金属管路；
所述清洗方法，包括以下步骤：
1）将水管清洗剂和水，从入户端送入自来水管路中，静置，然后排出清理后的污水；
所述水管清洗剂以质量分数计，由以下材料组成：
天然有机酸 12~50 重量份；
柠檬酸 10~50 重量份；
天然表面活性剂 10~15 重量份；
天然杀菌剂 10~15 重量份；
水 10~25 重量份；
玉米改性吸水剂 3~10 重量份；
所述天然有机酸包括柠檬酸、山楂酸、醋酸、酒石酸、维生素C和熊果酸中的一种或多种；
所述天然表面活性剂包括橙油、皂角和腰果油中的一种或多种；
所述天然杀菌剂包括大蒜素、ε-聚赖氨酸、姜提取液和茶油中的一种或多种。
2.根据权利要求1所述的养护方法，其特征在于，所述水管清洗剂可用于清洗水泥水管、铸铁水管、钢水管、镀锌水管、PP水管、PE水管以及铝塑复合水管中的一种或多种；
所述水管包括自来水水管。
3.根据权利要求1所述的养护方法，其特征在于，所述水管清洗剂和水的质量比为1：（1~15）；
所述入户端为用户的自来水供水入口处；
所述入户端设置有进水口，或者进水口和阀门。
4.根据权利要求1所述的养护方法，其特征在于，所述自来水管路包括水泥管、铸铁管、钢管、镀锌管、PP管、PE管以及铝塑复合管中的一种或多种；
所述静置的时间为15~120min；
所述污水从用户的自来水管路出口中排出；
所述步骤1）的次数为1~5次。
5.根据权利要求1所述的养护方法，其特征在于，所述杀菌金属盐包括银盐、铜盐、钛盐和金盐中的一种或多种；
所述络合剂包括杂多酸盐、克丙炔醇乙氧基化合物、硫酸铈、吡啶嗡盐、酒石酸钾、三乙醇胺、酒石酸钾钠、柠檬酸钠和氨水中的一种或多种；
所述水管包括铸铁水管、钢水管和镀锌水管中的一种或多种。
6.根据权利要求5所述的养护方法，其特征在于，所述银盐包括硝酸银、甲基磺酸银、二十烷酸银和碘化银中的一种或多种；
通过盐酸检测所述残液中的银离子，当有白色沉淀时，表明金属管路镀膜完全；
所述镀膜后的残液从用户的自来水管路出口中排出。