CN109180072A - A kind of colour artificial stone formula and its manufacture craft - Google Patents
A kind of colour artificial stone formula and its manufacture craft Download PDFInfo
- Publication number
- CN109180072A CN109180072A CN201811230142.1A CN201811230142A CN109180072A CN 109180072 A CN109180072 A CN 109180072A CN 201811230142 A CN201811230142 A CN 201811230142A CN 109180072 A CN109180072 A CN 109180072A
- Authority
- CN
- China
- Prior art keywords
- colored
- formula
- artificial stone
- parts
- stone plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of colored artificial stone formula and its manufacture crafts, wherein colored artificial stone formula includes foundation stone plate prescription and colored adhesive formula, the foundation stone plate prescription weight fraction ratio are as follows: 100 parts of rubble, 65-70 parts of cullet, 60-65 parts of clay, the weight percent of the colored adhesive formula are as follows: saturated polyester resin 25%, initiator 0.7%, promotor 0.3%, glass powder 39%, mountain flour 39% and pigment appropriate；The present invention is intended to provide a kind of colored artificial stone formula and its manufacture craft heat-resisting, ageing-resistant, surface is colorful.
Description
Technical field
The present invention relates to ceramic fields, particularly say, especially a kind of colored artificial stone formula.
Background technique
Existing artificial stone mostly uses calcium carbonate and aluminium hydroxide to carry out filler, and density is big, weight is big, transport and construction
Inconvenience, wearability is bad, and surface patterns are single.
Summary of the invention
It is an object of the invention to be directed to above-mentioned situation, a kind of colored artificial stone formula and its manufacture craft are provided.
The technical scheme of the present invention is realized as follows: a kind of colour artificial stone formula, including foundation stone plate prescription and colour
Adhesive formula, the foundation stone plate prescription weight fraction ratio are as follows: 100 parts of rubble, 65-70 parts of cullet, 60-65 parts of clay, institute
State the weight percent of colored adhesive formula are as follows: saturated polyester resin 25%, initiator 0.7%, promotor 0.3%, glass
Powder 39%, mountain flour 39% and pigment appropriate.
A kind of colour artificial stone formula, the powder fineness partial size of the glass powder are 70-250 mesh, the powder of the mountain flour
Fineness partial size is 70-250 mesh.
A kind of manufacture craft of colour artificial stone, comprising the following steps:
S1, the marmorean foundation stone plate of production: the raw material of foundation stone plate is crushed, the non-80-100 mesh of granularity, stirring is equal
It is poured into after even in slabstone mold, compression moulding is then placed in kiln and is calcined, and takes out after the completion of calcining cooling up to Dali
The foundation stone plate of stone；
S2, production colored adhesive: by the formula of weight percent: saturated polyester resin: 25%, initiator: 0.7%,
Promotor: 0.3% and pigment appropriate be stirred and mix well, then be added glass powder (70-250 mesh): 39%, mountain flour
(70-250 mesh): 39% futher stirs uniformly to obtain the final product；
S3, foundation stone plate are in conjunction with colored adhesive: the resulting foundation stone plate of S1 be put into mold and is laid flat, it is then that colour is viscous
Mixture is injected into mold and integrally covers foundation stone plate, and colored adhesive can demould after the curing be complete with a thickness of 5 millimeters
Obtain colored artificial stone；
S4: deburring: the colored artificial stone that demoulding obtains, which is carried out deburring, makes surfacing.
In a kind of manufacture craft of above-mentioned colored artificial stone, the weight of the composition of raw materials of the foundation stone plate in the step S1
Portion rate are as follows: 100 parts of rubble, 65-70 parts of cullet, 60-65 parts of clay.
In a kind of manufacture craft of above-mentioned colored artificial stone, the temperature calcined in kiln in the step S1 is
1100 DEG C -1250 DEG C, calcination time is 11-12 hours.
The beneficial effects of the present invention are, foundation stone plate uses rubble, cullet and clay, is tightly combined, and relative weight is low,
Facilitate construction or transport, colored adhesive covers the solidification of foundation stone plate surface, improves heat-resisting, ageing-resistant performance, can be according to practical need
Relevant color is added, keeps surface colorful, and not fugitive color.
Specific embodiment
A kind of colour artificial stone formula, including foundation stone plate prescription and colored adhesive formula, the foundation stone plate prescription weight
Portion rate are as follows: 100 parts of rubble, 65-70 parts of cullet, 60-65 parts of clay, the weight percent of the colored adhesive formula
Are as follows: saturated polyester resin 25%, initiator 0.7%, promotor 0.3%, glass powder 39%, mountain flour 39% and pigment appropriate,
The powder fineness partial size of the glass powder is 70-250 mesh, and the powder fineness partial size of the mountain flour is 70-250 mesh.
A kind of manufacture craft of colour artificial stone, comprising the following steps:
S1, the marmorean foundation stone plate of production: the raw material of foundation stone plate is crushed, the non-80-100 mesh of granularity, stirring is equal
It is poured into after even in slabstone mold, compression moulding is then placed in kiln and is calcined, and takes out after the completion of calcining cooling up to Dali
The foundation stone plate of stone；
S2, production colored adhesive: by the formula of weight percent: saturated polyester resin: 25%, initiator: 0.7%,
Promotor: 0.3% and pigment appropriate be stirred and mix well, then be added glass powder (70-250 mesh): 39%, mountain flour
(70-250 mesh): 39% futher stirs uniformly to obtain the final product；
S3, foundation stone plate are in conjunction with colored adhesive: the resulting foundation stone plate of S1 be put into mold and is laid flat, it is then that colour is viscous
Mixture is injected into mold and integrally covers foundation stone plate, and colored adhesive can demould after the curing be complete with a thickness of 5 millimeters
Obtain colored artificial stone；
S4: deburring: the colored artificial stone that demoulding obtains, which is carried out deburring, makes surfacing.
The weight fraction ratio of the composition of raw materials of foundation stone plate in the step S1 are as follows: 100 parts of rubble, cullet 65-70
Part, 60-65 part of clay, the temperature calcined in the step S1 in kiln is 1100 DEG C -1250 DEG C, calcination time 11-
12 hours.
In the S2 step, operated at 25-35 DEG C of environment temperature in the production process, it can be first by a small amount of benzene of initiator
It after ethylene melts uniformly, is then added in saturated polyester resin, promotor is then added and different face is added according to actual needs
Material, which is stirred, to be mixed well.
The foregoing is merely presently preferred embodiments of the present invention, is not intended to limit the invention, it is all in spirit of the invention and
Within principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (5)
1. a kind of colour artificial stone formula, which is characterized in that including foundation stone plate prescription and colored adhesive formula, the foundation stone plate
Formulation weight portion rate are as follows: 100 parts of rubble, 65-70 parts of cullet, 60-65 parts of clay, the weight of the colored adhesive formula
Percentage are as follows: saturated polyester resin 25%, initiator 0.7%, promotor 0.3%, glass powder 39%, mountain flour 39% and appropriate
Pigment.
2. a kind of colored artificial stone formula according to claim 1, which is characterized in that the powder fineness grain of the glass powder
Diameter is 70-250 mesh, and the powder fineness partial size of the mountain flour is 70-250 mesh.
3. a kind of manufacture craft of colour artificial stone, which comprises the following steps:
S1, the marmorean foundation stone plate of production: the raw material of foundation stone plate is crushed, the non-80-100 mesh of granularity, after mixing evenly
It pours into slabstone mold, compression moulding is then placed in kiln and is calcined, and takes out after the completion of calcining cooling up to marmorean
Foundation stone plate；
S2, production colored adhesive: by the formula of weight percent: saturated polyester resin: 25%, initiator: 0.7%, promoting
Agent: 0.3% and pigment appropriate be stirred and mix well, then be added glass powder (70-250 mesh): 39%, mountain flour (70-250
Mesh): 39% futher stirs uniformly to obtain the final product；
S3, foundation stone plate are in conjunction with colored adhesive: the resulting foundation stone plate of S1 being put into mold and is laid flat, then by colored adhesive
It is injected into mold and integrally covers foundation stone plate, colored adhesive can demould to obtain after the curing be complete with a thickness of 5 millimeters
Colored artificial stone；
S4: deburring: the colored artificial stone that demoulding obtains, which is carried out deburring, makes surfacing.
4. a kind of manufacture craft of colored artificial stone according to claim 3, which is characterized in that the base in the step S1
The weight fraction ratio of the composition of raw materials of slabstone are as follows: 100 parts of rubble, 65-70 parts of cullet, 60-65 parts of clay.
5. a kind of manufacture craft of colored artificial stone according to claim 3, which is characterized in that kiln in the step S1
The temperature inside calcined is 1100 DEG C -1250 DEG C, and calcination time is 11-12 hours.